CN104058711B - A kind of water-proof building material - Google Patents
A kind of water-proof building material Download PDFInfo
- Publication number
- CN104058711B CN104058711B CN201410287829.4A CN201410287829A CN104058711B CN 104058711 B CN104058711 B CN 104058711B CN 201410287829 A CN201410287829 A CN 201410287829A CN 104058711 B CN104058711 B CN 104058711B
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- building material
- proof building
- oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention belongs to water-proof building material field, it is specifically related to design and the manufacture field of waterproof material, particularly relate to a kind of water-proof building material, it is characterized in that, consist of the following composition: magnesium oxide, quartz sand, acrylic emulsion, polyurethane, without tar asphalt, triethanolamine, expanded perlite, silicon oxide, sodium silicate, aluminium oxide, distilled water.
Description
Technical field
The invention belongs to water-proof building material field, be specifically related to design and the manufacture field of waterproof material, particularly relate to a kind of water-proof building material.
Background technology
In the prior art, the building enclosure of building to prevent the infiltration of rainwater, snow water and subsoil water；Prevent the erosion of the dampness in air, steam and other harmful gass and liquid；Separation structure to prevent oozing of plumbing from turning over.The material of these impermeable, seepages and erosion is referred to as waterproof material.
Buildings waterproof is and prevents water to the infiltration at some position of building from construction material and textural taked measure.Waterproof is used in roofing, hypogee, the under ground portion of building more and needs interior room and the water storage structures etc. of waterproof.By the difference of its measure taked and means, it is divided into material waterproofing and the big class of constructional waterproofing two.Material waterproofing is the path blocking water by construction material, to reach the purpose of waterproof or to increase the ability of anti-leakage, such as waterproof coiled material, coating waterproofing, concrete and cement mortar rigid waterproofing and clay, ash great soil group waterproof etc..Constructional waterproofing is then take suitable structural form, blocks the path of water, to reach the purpose of waterproof, such as waterstop and cavity structure etc..Main application fields includes the roofing of building construction, underground, exterior wall and indoor；The municipal works such as urban road bridges and the underground space；Highway and the bridge of high-speed railway, tunnel；The traffic engineering such as underground railway；The hydraulic engineerings such as flume, reservoir, dam body, natural flow station and water process, etc..Along with the development of social progress and Building technology, the application of architectural waterproof material also can extend to more areas.
Instantly, the water-proof building material glueability building industry use is poor, it is impossible to construct under freezing temperature;Freezing temperature environment is constructed, does not adopt the measure improving its glueability, it is impossible to the ornament materials such as tiling, marble, granite in construction surface.At present, the water-proof building material glueability that building trade uses is poor, it is impossible to construct under freezing temperature;Freezing temperature environment is constructed, does not adopt the measure improving its glueability, it is impossible to the ornament materials such as tiling, marble, granite in construction surface.
Summary of the invention
In order to solve the deficiencies in the prior art, the invention provides a kind of water-proof building material.
A kind of water-proof building material, it is characterised in that consist of the following composition: magnesium oxide, quartz sand, acrylic emulsion, polyurethane, without tar asphalt, triethanolamine, expanded perlite, silicon oxide, sodium silicate, aluminium oxide, distilled water.
Described a kind of water-proof building material, it is characterised in that material is grouped into by the one-tenth of following weight portion:
Magnesium oxide 20-40 part；
Quartz sand 35-55 part；
Acrylic emulsion 15-20 part；
Polyurethane 20-55 part；
The part of 25-40 without tar asphalt；
Triethanolamine 30-45 part；
Expanded perlite 20-35 part；
Silicon oxide 5-15 part；
Sodium silicate 25-35 part；
Aluminium oxide 25-35 part；
Distilled water 20-65 part.
Described a kind of water-proof building material, it is characterised in that material is grouped into by the one-tenth of following weight portion:
Magnesium oxide 20 parts；
Quartz sand 35 parts；
Acrylic emulsion 15 parts；
Polyurethane 20 parts；
Without tar asphalt 25 parts；
Triethanolamine 30 parts；
Expanded perlite 20 parts；
Silicon oxide 5 parts；
Sodium silicate 25 parts；
Aluminium oxide 25 parts；
Distilled water 20 parts.
Described a kind of water-proof building material, it is characterised in that material is grouped into by the one-tenth of following weight portion:
Magnesium oxide 35 parts；
Quartz sand 45 parts；
Acrylic emulsion 18 parts；
Polyurethane 35 parts；
Without tar asphalt 30 parts；
Triethanolamine 40 parts；
Expanded perlite 25 parts；
Silicon oxide 10 parts；
Sodium silicate 30 parts；
Aluminium oxide 30 parts；
Distilled water 35 parts.
Described a kind of water-proof building material, it is characterised in that material is grouped into by the one-tenth of following weight portion:
Magnesium oxide 40 parts；
Quartz sand 55 parts；
Acrylic emulsion 20 parts；
Polyurethane 55 parts；
Without tar asphalt 40 parts；
Triethanolamine 45 parts；
Expanded perlite 35 parts；
Silicon oxide 15 parts；
Sodium silicate 35 parts；
Aluminium oxide 35 parts；
Distilled water 65 parts.
Specific embodiment:
Embodiment 1:
A kind of water-proof building material, it is characterised in that consist of the following composition: magnesium oxide, quartz sand, acrylic emulsion, polyurethane, without tar asphalt, triethanolamine, expanded perlite, silicon oxide, sodium silicate, aluminium oxide, distilled water.
Described a kind of water-proof building material, it is characterised in that material is grouped into by the one-tenth of following weight portion:
Magnesium oxide 20-40 part；
Quartz sand 35-55 part；
Acrylic emulsion 15-20 part；
Polyurethane 20-55 part；
The part of 25-40 without tar asphalt；
Triethanolamine 30-45 part；
Expanded perlite 20-35 part；
Silicon oxide 5-15 part；
Sodium silicate 25-35 part；
Aluminium oxide 25-35 part；
Distilled water 20-65 part.
Embodiment 2:
A kind of water-proof building material, it is characterised in that consist of the following composition: magnesium oxide, quartz sand, acrylic emulsion, polyurethane, without tar asphalt, triethanolamine, expanded perlite, silicon oxide, sodium silicate, aluminium oxide, distilled water.
Described a kind of water-proof building material, it is characterised in that material is grouped into by the one-tenth of following weight portion:
Magnesium oxide 20-40 part；
Quartz sand 35-55 part；
Acrylic emulsion 15-20 part；
Polyurethane 20-55 part；
The part of 25-40 without tar asphalt；
Triethanolamine 30-45 part；
Expanded perlite 20-35 part；
Silicon oxide 5-15 part；
Sodium silicate 25-35 part；
Aluminium oxide 25-35 part；
Distilled water 20-65 part.
Described a kind of water-proof building material, it is characterised in that material is grouped into by the one-tenth of following weight portion:
Magnesium oxide 20 parts；
Quartz sand 35 parts；
Acrylic emulsion 15 parts；
Polyurethane 20 parts；
Without tar asphalt 25 parts；
Triethanolamine 30 parts；
Expanded perlite 20 parts；
Silicon oxide 5 parts；
Sodium silicate 25 parts；
Aluminium oxide 25 parts；
Distilled water 20 parts.
Embodiment 3:
A kind of water-proof building material, it is characterised in that consist of the following composition: magnesium oxide, quartz sand, acrylic emulsion, polyurethane, without tar asphalt, triethanolamine, expanded perlite, silicon oxide, sodium silicate, aluminium oxide, distilled water.
Described a kind of water-proof building material, it is characterised in that material is grouped into by the one-tenth of following weight portion:
Magnesium oxide 20-40 part；
Quartz sand 35-55 part；
Acrylic emulsion 15-20 part；
Polyurethane 20-55 part；
The part of 25-40 without tar asphalt；
Triethanolamine 30-45 part；
Expanded perlite 20-35 part；
Silicon oxide 5-15 part；
Sodium silicate 25-35 part；
Aluminium oxide 25-35 part；
Distilled water 20-65 part.
Described a kind of water-proof building material, it is characterised in that material is grouped into by the one-tenth of following weight portion:
Magnesium oxide 35 parts；
Quartz sand 45 parts；
Acrylic emulsion 18 parts；
Polyurethane 35 parts；
Without tar asphalt 30 parts；
Triethanolamine 40 parts；
Expanded perlite 25 parts；
Silicon oxide 10 parts；
Sodium silicate 30 parts；
Aluminium oxide 30 parts；
Distilled water 35 parts.
Embodiment 4:
A kind of water-proof building material, it is characterised in that consist of the following composition: magnesium oxide, quartz sand, acrylic emulsion, polyurethane, without tar asphalt, triethanolamine, expanded perlite, silicon oxide, sodium silicate, aluminium oxide, distilled water.
Described a kind of water-proof building material, it is characterised in that material is grouped into by the one-tenth of following weight portion:
Magnesium oxide 20-40 part；
Quartz sand 35-55 part；
Acrylic emulsion 15-20 part；
Polyurethane 20-55 part；
The part of 25-40 without tar asphalt；
Triethanolamine 30-45 part；
Expanded perlite 20-35 part；
Silicon oxide 5-15 part；
Sodium silicate 25-35 part；
Aluminium oxide 25-35 part；
Distilled water 20-65 part.
Described a kind of water-proof building material, it is characterised in that material is grouped into by the one-tenth of following weight portion:
Magnesium oxide 40 parts；
Quartz sand 55 parts；
Acrylic emulsion 20 parts；
Polyurethane 55 parts；
Without tar asphalt 40 parts；
Triethanolamine 45 parts；
Expanded perlite 35 parts；
Silicon oxide 15 parts；
Sodium silicate 35 parts；
Aluminium oxide 35 parts；
Distilled water 65 parts.
Claims (4)
1. a water-proof building material, it is characterised in that be grouped into by the one-tenth of following weight portion:
Magnesium oxide 20-40 part；
Quartz sand 35-55 part；
Acrylic emulsion 15-20 part；
Polyurethane 20-55 part；
The part of 25-40 without tar asphalt；
Triethanolamine 30-45 part；
Expanded perlite 20-35 part；
Silicon oxide 5-15 part；
Sodium silicate 25-35 part；
Aluminium oxide 25-35 part；
Distilled water 20-65 part.
2. a kind of water-proof building material according to claim 1, it is characterised in that material is grouped into by the one-tenth of following weight portion:
Magnesium oxide 20 parts；
Quartz sand 35 parts；
Acrylic emulsion 15 parts；
Polyurethane 20 parts；
Without tar asphalt 25 parts；
Triethanolamine 30 parts；
Expanded perlite 20 parts；
Silicon oxide 5 parts；
Sodium silicate 25 parts；
Aluminium oxide 25 parts；
Distilled water 20 parts.
3. a kind of water-proof building material according to claim 1, it is characterised in that material is grouped into by the one-tenth of following weight portion:
Magnesium oxide 35 parts；
Quartz sand 45 parts；
Acrylic emulsion 18 parts；
Polyurethane 35 parts；
Without tar asphalt 30 parts；
Triethanolamine 40 parts；
Expanded perlite 25 parts；
Silicon oxide 10 parts；
Sodium silicate 30 parts；
Aluminium oxide 30 parts；
Distilled water 35 parts.
4. a kind of water-proof building material according to claim 1, it is characterised in that material is grouped into by the one-tenth of following weight portion:
Magnesium oxide 40 parts；
Quartz sand 55 parts；
Acrylic emulsion 20 parts；
Polyurethane 55 parts；
Without tar asphalt 40 parts；
Triethanolamine 45 parts；
Expanded perlite 35 parts；
Silicon oxide 15 parts；
Sodium silicate 35 parts；
Aluminium oxide 35 parts；
Distilled water 65 parts.