CN104051796A - Formulation and preparation method of storage battery colloid mother liquor - Google Patents
Formulation and preparation method of storage battery colloid mother liquor Download PDFInfo
- Publication number
- CN104051796A CN104051796A CN201410231916.8A CN201410231916A CN104051796A CN 104051796 A CN104051796 A CN 104051796A CN 201410231916 A CN201410231916 A CN 201410231916A CN 104051796 A CN104051796 A CN 104051796A
- Authority
- CN
- China
- Prior art keywords
- mother liquor
- preparation
- colloid mother
- raw material
- closed container
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention aims to provide a formulation and a preparation method of a storage battery colloid mother liquor. The colloid mother liquor having better quality is prepared through a series of the preparation method, and the quality of a storage battery adopting the colloid mother liquor is improved. The colloid mother liquor having better quality is prepared through a series of the preparation method, and the quality of the storage battery adopting the colloid mother liquor is improved; and by temperature controlled stirring, the quality of the colloid mother liquor is greatly improved, and the yield of the product is increased.
Description
Technical field
The present invention relates to storage battery and manufacture field, relate in particular to formula of a kind of accumulator colloid mother liquor and preparation method thereof.
Background technology
At present, making when storage battery, need to be prepared to being filled with colloid mother liquor in storage battery, and the preparation of present colloid mother liquor there is no a set of complete preparation technology, and the quality of the colloid mother liquor preparing is uneven, have a strong impact on the performance of storage battery.Therefore the preparation method who designs a kind of glue parent and the whole series thereof just seems particularly important.
Summary of the invention
The object of this invention is to provide formula of a kind of accumulator colloid mother liquor and preparation method thereof, produce the colloid mother liquor that has better quality by a series of preparation method, improve the quality of the storage battery that uses its colloid mother liquor.
The invention provides a kind of formula of accumulator colloid mother liquor, the percentage of described formula is as follows: silica 1 2% ~ 16%, pure water 80% ~ 87%, additive 0.4% ~ 0.6%.
Further improve and be: described silicon dioxide is high-purity, nano level silicon dioxide.
A preparation method for accumulator colloid mother liquor, preparation process is as follows:
Step 1: raw material is according to the above ratio put into closed container;
Step 2: use mixer to stir 25 min ~ 40min to the raw material in closed container;
Step 3: the raw material after abundant mix and blend is taken out, be finished product.
Further improve and be: when raw material stirring in described step 2, lower the temperature to injecting cold water in the interlayer of closed container, the temperature in described closed container need remain on 30 DEG C ~ 40 DEG C.
Beneficial effect of the present invention: produce the colloid mother liquor that has better quality by a series of preparation method, improve the quality of the storage battery that uses its colloid mother liquor, and by temperature control stirring, the quality of the colloid mother liquor making is greatly improved, and has increased the yield of product.
Embodiment
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, and this embodiment only, for explaining the present invention, does not form limiting the scope of the present invention.
Embodiment mono-
The present embodiment provides a kind of formula of accumulator colloid mother liquor, and the percentage of described formula is as follows: silica 1 4.5%, pure water 85%, additive 0.5%.
Further improve and be: described silicon dioxide is high-purity, nano level silicon dioxide.
A preparation method for accumulator colloid mother liquor, preparation process is as follows:
Step 1: raw material is according to the above ratio put into closed container;
Step 2: use mixer to stir 30min to the raw material in closed container;
Step 3: the raw material after abundant mix and blend is taken out, be finished product.
Further improve and be: when raw material stirring in described step 2, lower the temperature to injecting cold water in the interlayer of closed container, the temperature in described closed container need remain on 37 DEG C.
Embodiment bis-
The present embodiment provides a kind of formula of accumulator colloid mother liquor, and the percentage of described formula is as follows: silica 1 2.6%, pure water 87%, additive 0.4%.
Further improve and be: described silicon dioxide is high-purity, nano level silicon dioxide.
A preparation method for accumulator colloid mother liquor, preparation process is as follows:
Step 1: raw material is according to the above ratio put into closed container;
Step 2: use mixer to stir 25 min to the raw material in closed container;
Step 3: the raw material after abundant mix and blend is taken out, be finished product.
When raw material stirring in described step 2, lower the temperature to injecting cold water in the interlayer of closed container, the temperature in described closed container need remain on 30 DEG C.
Embodiment tri-
The present embodiment provides a kind of formula of accumulator colloid mother liquor, and the percentage of described formula is as follows: silica 1 6%, pure water 83.4%, additive 0.6%.
Described silicon dioxide is high-purity, nano level silicon dioxide.
A preparation method for accumulator colloid mother liquor, preparation process is as follows:
Step 1: raw material is according to the above ratio put into closed container;
Step 2: use mixer to stir 40min to the raw material in closed container;
Step 3: the raw material after abundant mix and blend is taken out, be finished product.
When raw material stirring in described step 2, lower the temperature to injecting cold water in the interlayer of closed container, the temperature in described closed container need remain on 40 DEG C.
Entering comparative example one, two, three can obtain: the colloid mother liquor quality that embodiment mono-produces is best, and the colloid mother liquor that embodiment bis-, three produces also meets use standard, produce the colloid mother liquor that has better quality by a series of preparation method, improve the quality of the storage battery that uses its colloid mother liquor, and pass through temperature control stirring, the quality of the colloid mother liquor making is greatly improved, and has increased the yield of product.
Claims (4)
1. a formula for accumulator colloid mother liquor, is characterized in that: the percentage of described formula is as follows: silica 1 2% ~ 16%, pure water 80% ~ 87%, additive 0.4% ~ 0.6%.
2. the formula of a kind of accumulator colloid mother liquor as claimed in claim 1, is characterized in that: described silicon dioxide is high-purity, nano level silicon dioxide.
3. a preparation method for accumulator colloid mother liquor as claimed in claim 1, is characterized in that: preparation process is as follows:
Step 1: raw material is according to the above ratio put into closed container;
Step 2: use mixer to stir 25 min ~ 40min to the raw material in closed container;
Step 3: the raw material after abundant mix and blend is taken out, be finished product.
4. the preparation method of a kind of accumulator colloid mother liquor as claimed in claim 3, it is characterized in that: when raw material stirring in described step 2, lower the temperature to injecting cold water in the interlayer of closed container, the temperature in described closed container need remain on 30 DEG C ~ 40 DEG C.