CN104046995A - 一种铜防变色的方法 - Google Patents

一种铜防变色的方法 Download PDF

Info

Publication number
CN104046995A
CN104046995A CN201410283557.0A CN201410283557A CN104046995A CN 104046995 A CN104046995 A CN 104046995A CN 201410283557 A CN201410283557 A CN 201410283557A CN 104046995 A CN104046995 A CN 104046995A
Authority
CN
China
Prior art keywords
copper
variable color
water
preventing
discolouration
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410283557.0A
Other languages
English (en)
Other versions
CN104046995B (zh
Inventor
宋云
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuzhou Hengsheng Electronic Technology Co Ltd
Original Assignee
Wuzhou Hengsheng Electronic Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuzhou Hengsheng Electronic Technology Co Ltd filed Critical Wuzhou Hengsheng Electronic Technology Co Ltd
Priority to CN201410283557.0A priority Critical patent/CN104046995B/zh
Publication of CN104046995A publication Critical patent/CN104046995A/zh
Application granted granted Critical
Publication of CN104046995B publication Critical patent/CN104046995B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种铜防变色的方法，旨在提供一种防护性好，长时间不腐蚀、不退色的铜防变色的方法；该方法依次包括下述步骤：1)将1重量份铜防变色剂和6-10重量份水混合均匀，得到混合防变色液；2)将需要防变色的铜件浸泡在步骤1)中的混合防变色液中5-10min；3)将步骤2)浸泡后的铜件用清水冲洗干净；4)用热水冲洗后烘干进行下一步操作；其中：步骤1)所述的每升铜防变色剂由下述组分构成：羟基乙叉二膦酸50-100g，乙醇50-100g，过氧化氢80-150g，缓蚀剂20-40g，异硫氰酸酯10-20g，烷基硫酸盐8-15g，钼酸钠10-20g，三聚磷酸钠8-12g，余量为水；属于金属抗氧化技术领域。

Description

一种铜防变色的方法
技术领域
本发明涉及一种金属防变色剂方法，具体的说，是涉及一种铜防变色的方法，属于金属抗氧化技术领域。
背景技术
铜金属光泽良好，且其导电性能几乎与银相当，而价格仅是银的二十分之一，因此从性价比上来说，铜粉是比较理想的一种导电填料。铜粉的这些特性使得其在导电胶、导电塑料、导电涂料等领域广泛使用。但是微细铜粉比表面积大，化学性质活泼，在空气中易发生氧化，导致材料颜色变暗，装饰性变差，而且氧化物是绝缘体，这样就使得导电材料很难在长时间的使用过程中保持良好的导电性能。因此，如何防止铜粉在材料的制备阶段以及使用过程中被氧化，是铜系材料应用研究的关键问题。但现有技术制备铜粉抗氧化剂存在成本高，且制备的铜粉抗氧化剂抗氧化时间短。
发明内容
针对上述问题，本发明的目的在于提供一种防护性好，长时间不腐蚀、不退色的铜防变色的方法。
为此，本发明提供的技术方案是这样的：该铜防变色的方法依次包括下述步骤：
1)将1重量份铜防变色剂和6-10重量份水混合均匀，得到混合防变色液；
2)将需要防变色的铜件浸泡在步骤1)中的混合防变色液中5-10min；
3)将步骤2)浸泡后的铜件用清水冲洗干净；
4)用热水冲洗后烘干进行下一步操作。
其中：
步骤1)所述的每升铜防变色剂由下述组分构成：羟基乙叉二膦酸50-100g，乙醇50-100g，过氧化氢80-150g，缓蚀剂20-40g，异硫氰酸酯10-20g，烷基硫酸盐8-15g，钼酸钠10-20g，三聚磷酸钠8-12g，余量为水。
进一步的，上述的铜防变色的方法，所述的混合防变色液的pH值为3-9。
进一步的，上述的铜防变色的方法，所述的混合防变色液的pH值为5-6.5。
进一步的，上述的铜防变色的方法，步骤4)所述的热水为100℃的水。
更进一步的，上述的铜防变色的方法，每升铜抗氧化剂含下述组分：羟基乙叉二膦酸70-90g，乙醇60-80g，过氧化氢100-120g，缓蚀剂25-35g，异硫氰酸酯12-18g，烷基硫酸盐10-12g，钼酸钠12-18g，三聚磷酸钠9-11g，余量为水。
更进一步的，上述的铜防变色的方法，所述的缓蚀剂为苯并三氮唑。
更进一步的，上述的铜防变色的方法，所述的烷基硫酸盐为十二烷基硫酸盐。
与现有技术相比，本发明提供的技术方案具有如下优点：
1、本发明提供的铜防变色的方法防护性好，长时间不腐蚀、不退色，具有良好防锈功能；
2、本发明提供的铜防变色的方法完全水溶性，气味小，不燃烧，安全可靠，稳定性优良，贮存方便。
3、本发明提供的铜防变色的方法对工件无不良影响，不损坏工件。
具体实施方式
下面结合具体实施，对本发明的权利要求做进一步的详细说明，任何人在本发明权利要求范围内所做的有限次的修改，仍在本发明的权利要求保护范围之内。
实施例1
本发明提供的一种铜防变色的方法，该方法依次包括下述步骤：
1)将1重量份铜防变色剂和10重量份水混合均匀，得到pH值为5混合防变色液；
2)将需要防变色的铜件浸泡在步骤1)中的混合防变色液中10min；
3)将步骤2)浸泡后的铜件用清水冲洗干净；
4)用100℃水冲洗后烘干进行下一步操作。
所用的铜防变色剂每升配方如下：羟基乙叉二膦酸50g，乙醇100g，过氧化氢80g，苯并三氮唑40g，异硫氰酸酯10g，十二烷基硫酸盐15g，钼酸钠10g，三聚磷酸钠12g。
实施例2
本发明提供的另一种铜防变色的方法，该方法依次包括下述步骤：
1)将1重量份铜防变色剂和6重量份水混合均匀，得到pH值为6.5混合防变色液；
2)将需要防变色的铜件浸泡在步骤1)中的混合防变色液中5min；
3)将步骤2)浸泡后的铜件用清水冲洗干净；
4)用100℃水冲洗后烘干进行下一步操作。
所用的铜防变色剂配方如下：羟基乙叉二膦酸50g，乙醇100g，过氧化氢50g，苯并三氮唑20g，异硫氰酸酯20g，十二烷基硫酸盐8g，钼酸钠20g，三聚磷酸钠8g。
实施例3
本发明提供的另一种铜防变色的方法，该方法依次包括下述步骤：
1)将1重量份铜防变色剂和7重量份水混合均匀，得到pH值为9混合防变色液；
2)将需要防变色的铜件浸泡在步骤1)中的混合防变色液中10min；
3)将步骤2)浸泡后的铜件用清水冲洗干净；
4)用100℃水冲洗后烘干进行下一步操作。
所用的铜防变色剂配方如下：羟基乙叉二膦酸70g，乙醇70g，过氧化氢100g，苯并三氮唑30g，异硫氰酸酯15g，十二烷基硫酸盐10g，钼酸钠15g，三聚磷酸钠10g。
实施例4
本发明提供的另一种铜防变色的方法，该方法依次包括下述步骤：
1)将1重量份铜防变色剂和8重量份水混合均匀，得到pH值为3混合防变色液；
2)将需要防变色的铜件浸泡在步骤1)中的混合防变色液中10min；
3)将步骤2)浸泡后的铜件用清水冲洗干净；
4)用100℃水冲洗后烘干进行下一步操作。
所用的铜防变色剂配方如下：羟基乙叉二膦酸80g，乙醇70g，过氧化氢120g，苯并三氮唑30g，异硫氰酸酯12g，十二烷基硫酸盐9g，钼酸钠10g，三聚磷酸钠11g。
实施例1至4中任意一种铜防变色剂制备方法如下：
1)上述质量数称取各个组分；
2)将步骤1)称取的组分放入烧瓶，加水至1L，然后在常温下搅拌20分钟混匀，即得铜防变色剂。

Claims (7)

1.一种铜防变色的方法，其特征在于，该方法依次包括下述步骤：
1)将1重量份铜防变色剂和6-10重量份水混合均匀，得到混合防变色液；
2)将需要防变色的铜件浸泡在步骤1)中的混合防变色液中5-10min；
3)将步骤2)浸泡后的铜件用清水冲洗干净；
4)用热水冲洗后烘干进行下一步操作。
其中：
步骤1)所述的每升铜防变色剂由下述组分构成：羟基乙叉二膦酸50-100g，乙醇50-100g，过氧化氢80-150g，缓蚀剂20-40g，异硫氰酸酯10-20g，烷基硫酸盐8-15g，钼酸钠10-20g，三聚磷酸钠8-12g，余量为水。
2.根据权利要求1所述的铜防变色的方法，其特征在于，所述的混合防变色液的pH值为3-9。
3.根据权利要求2所述的铜防变色的方法，其特征在于，所述的混合防变色液的pH值为5-6.5。
4.根据权利要求1所述的铜防变色的方法，其特征在于，步骤4)所述的热水为100℃的水。
5.根据权利要求1所述的铜防变色的方法，其特征在于，每升铜抗氧化剂含下述组分：羟基乙叉二膦酸70-90g，乙醇60-80g，过氧化氢100-120g，缓蚀剂25-35g，异硫氰酸酯12-18g，烷基硫酸盐10-12g，钼酸钠12-18g，三聚磷酸钠9-11g，余量为水。
6.根据权利要求1所述的铜防变色的方法，其特征在于，所述的缓蚀剂为苯并三氮唑。
7.根据权利要求1所述的铜防变色的方法，其特征在于，所述的烷基硫酸盐为十二烷基硫酸盐。
CN201410283557.0A 2014-06-23 2014-06-23 一种铜防变色的方法 Expired - Fee Related CN104046995B (zh)