CN104045888A - Chloroprene rubber composition - Google Patents
Chloroprene rubber composition Download PDFInfo
- Publication number
- CN104045888A CN104045888A CN201410303895.6A CN201410303895A CN104045888A CN 104045888 A CN104045888 A CN 104045888A CN 201410303895 A CN201410303895 A CN 201410303895A CN 104045888 A CN104045888 A CN 104045888A
- Authority
- CN
- China
- Prior art keywords
- parts
- chloroprene rubber
- rubber composition
- chloroprene
- zinc oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a chloroprene rubber composition. The chloroprene rubber composition is prepared from the following raw materials in parts by weight: 10-20 parts of natural rubber, 30-40 parts of chloroprene rubber, 5-7 parts of a shockproof agent, 3-6 parts of zinc oxide, 4-9 parts of carbon back, 7-13 parts of stearic acid, 8-10 parts of pot clay, 8-11 parts of an anti-scorching agent and 4-9 parts of a foaming agent. The chloroprene rubber composition disclosed by the invention has the beneficial effects that a rubber material disclosed by the invention has high strength, good tensile properties and anti-aging properties.
Description
Technical field
The present invention relates to a kind of chloroprene rubber composition, belong to rubber technology field.
Background technology
Rubber (Rubber): the snappiness polymer materials with reversible deformation.At room temperature high resilience can produce compared with large deformation under very little External Force Acting, removes resilient after external force.Rubber belongs to complete amorphous polymer, and (T is g) low, and molecular weight is often very large, is greater than hundreds of thousands of for its second-order transition temperature.Rubber industry is one of important foundation industry of national economy.Bipeltate refers to that thereby processing rubber with specific whipping agent makes rubber have the processing means of characteristic performance, and bipeltate is because its special performance is widely used in various fields.
Summary of the invention
For the deficiencies in the prior art, the problem to be solved in the present invention is, a kind of rubber is provided, and has high strength, performance that tensile property is good and ageing-resistant.
For solving prior art problem, technical scheme provided by the invention is, a kind of chloroprene rubber composition, and its raw material by following parts by weight is made:
Natural rubber 10-20 part, chloroprene rubber 30-40 part, shockproof dose of 5-7 part, zinc oxide 3-6 part, carbon black 4-9 part, stearic acid 7-13 part, potter's clay 8-10 part, scorch retarder 8-11 part, whipping agent 4-9 part.
Optimisation technique scheme of the present invention is, a kind of chloroprene rubber composition, and its raw material by following parts by weight is made:
15 parts of natural rubbers, 35 parts of chloroprene rubbers, shockproof dose 6 parts, 4.5 parts, zinc oxide, 7 parts of carbon blacks, 10 parts of stearic acid, 9 parts, potter's clay, 10 parts of scorch retarder, 7 parts of whipping agents.
The invention has the beneficial effects as follows: elastomeric material of the present invention has high strength, performance that tensile property is good and ageing-resistant.
Embodiment
embodiment 1
A kind of chloroprene rubber composition, its raw material by following parts by weight is made:
10 parts of natural rubbers, 30 parts of chloroprene rubbers, shockproof dose 5 parts, 3 parts, zinc oxide, 4 parts of carbon blacks, 7 parts of stearic acid, 8 parts, potter's clay, 8 parts of scorch retarder, 4 parts of whipping agents.
embodiment 2
A kind of chloroprene rubber composition, its raw material by following parts by weight is made:
20 parts of natural rubbers, 40 parts of chloroprene rubbers, shockproof dose 7 parts, 6 parts, zinc oxide, 9 parts of carbon blacks, 13 parts of stearic acid, 10 parts, potter's clay, 11 parts of scorch retarder, 9 parts of whipping agents.
embodiment 3
A kind of chloroprene rubber composition, its raw material by following parts by weight is made:
15 parts of natural rubbers, 35 parts of chloroprene rubbers, shockproof dose 6 parts, 4.5 parts, zinc oxide, 7 parts of carbon blacks, 10 parts of stearic acid, 9 parts, potter's clay, 10 parts of scorch retarder, 7 parts of whipping agents.
Claims (2)
1. a chloroprene rubber composition, is characterized in that: its raw material by following parts by weight is made:
Natural rubber 10-20 part, chloroprene rubber 30-40 part, shockproof dose of 5-7 part, zinc oxide 3-6 part, carbon black 4-9 part, stearic acid 7-13 part, potter's clay 8-10 part, scorch retarder 8-11 part, whipping agent 4-9 part.
2. rubber according to claim 1, is characterized in that: its raw material by following parts by weight is made:
15 parts of natural rubbers, 35 parts of chloroprene rubbers, shockproof dose 6 parts, 4.5 parts, zinc oxide, 7 parts of carbon blacks, 10 parts of stearic acid, 9 parts, potter's clay, 10 parts of scorch retarder, 7 parts of whipping agents.