CN104031293A - Safe, environment-friendly and nontoxic modified calcium carbonate and preparation method thereof - Google Patents
Safe, environment-friendly and nontoxic modified calcium carbonate and preparation method thereof Download PDFInfo
- Publication number
- CN104031293A CN104031293A CN201410214985.8A CN201410214985A CN104031293A CN 104031293 A CN104031293 A CN 104031293A CN 201410214985 A CN201410214985 A CN 201410214985A CN 104031293 A CN104031293 A CN 104031293A
- Authority
- CN
- China
- Prior art keywords
- calcium carbonate
- parts
- modified calcium
- modified
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a safe, environment-friendly and nontoxic modified calcium carbonate and a preparation method thereof. The modified calcium carbonate is prepared from the following raw materials in parts by weight: 90 to 95 parts of calcium carbonate, 2 to 3 parts of clam shell power, 2 to 3 parts of smashed yellow cinnamon leaves, 4 to 5 parts of alkenyl succinic anhydride, 2 to 3 parts of porous starch, 1 to 2 parts of sodium hyaluronate, 2 to 4 parts of easy-to-disperse fibers, 2 to 3 parts of urea, 4 to 6 parts of potash feldspar powder, 5 to 7 parts of high density polyethylene, 4 to 6 parts of nylon 66, 1 to 2 parts of tea polyphenol and 3 to 4 parts of modified titanium dioxide. The formula of the modified calcium carbonate is formed by adopting environment-friendly raw materials, so that the utilization of waste materials is realized, i.e., the waste of resources is avoided; a large quantity of safe and nontoxic components are added; the surface of the calcium carbonate is modified by utilizing the high-molecular polymers, so that the modified calcium carbonate has a high-molecular polymer layer. Thus, the bonding force of the modified calcium carbonate is enhanced while the performance of the modified calcium carbonate is not decreased. The modified calcium carbonate disclosed by the invention is applied to the production of preservative film aids, degradable plastics additives, pigment or paint additives and other functional products.
Description
Technical field
The present invention relates to industrial filler field, modified calcium carbonate that particularly a kind of safety and environmental protection is nontoxic and preparation method thereof.
Background technology
Calcium carbonate is a kind of very important functional inorganic filling, is widely used in the industrial circles such as plastics, rubber, coating and papermaking.In the Application Areas of calcium carbonate, large multi-product belongs to the category of polymkeric substance, such as plastics, rubber, tackiness agent, coating etc., and occupy the important market share.Vital role has been played in performance and the application of properties-correcting agent to nano-calcium carbonate.For example, dispersion agent add the reunion that can reduce nano particle, improve dispersed; Adding of surface-modifying agent can improve the consistency of nano-calcium carbonate in polymeric system.As can be seen here, dispersion agent and surface-modifying agent are vital for the application of nano-calcium carbonate.But, adding of dispersion agent and surface-modifying agent, makes nano-calcium carbonate temperature use window greatly to diminish, and reason is that conventional dispersion agent and coupling agent is at high temperature easy to decompose, cause bubble, cracking, defect, distortion etc., thereby affect outward appearance, resistance toheat and the mechanical property of material.Changing the performance of traditional calcium carbonate product, improve its application performance to meet the needs of novel material, development of new techniques, is calcium carbonate industry urgent problem.
Summary of the invention
The object of this invention is to provide modified calcium carbonate that a kind of safety and environmental protection is nontoxic and preparation method thereof.
In order to realize object of the present invention, the present invention passes through following scheme implementation:
The modified calcium carbonate that safety and environmental protection is nontoxic, is made up of the raw material of following weight part: calcium carbonate 90-95, river shell powder 2-3, pulverizing leaf of Yellow cinnamon 2-3, alkenyl succinic anhydride 4-5, porous-starch 2-3, hyaluronate sodium 1-2, easy loosen collagen fibre 2-4, urea 2-3, feldspar in powder 4-6, high density polyethylene(HDPE) 5-7, nylon 664-6, tea-polyphenol 1-2, modifying titanium dioxide 3-4;
Described modifying titanium dioxide is made up of the raw material of following weight part: aluminium hydroxide 2-4, nano titanium oxide 50-60, silicon carbide 4-6, methyl methacrylate 5-7, antimonous oxide 3-4, terephthalic acid 3-4, dioctyl maleate 3-5, ethylene glycol 5-6, water 50-60; First preparation method adds methyl methacrylate, nano titanium oxide, aluminium hydroxide, ethylene glycol, water to stir, form suspension, at 45-50 DEG C, dry to water content 2-3%, then add immediately terephthalic acid, dioctyl maleate mix and blend 25-35 minute, then add all the other remaining components, under 1200-1500 rev/min of condition, stir, at 50-60 DEG C, dry, be ground into ultrafine powder and get final product.
The nontoxic modified calcium carbonate of a kind of safety and environmental protection of the present invention, made by following concrete steps:
(1) calcium carbonate, river shell powder, alkenyl succinic anhydride, porous-starch, urea, feldspar in powder, nylon 66 are added in high-speed kneading machine, be warming up between 70-80 DEG C, insulated and stirred half an hour, continue to add high density polyethylene(HDPE), continue to be warming up to 110-130 DEG C, be incubated and pour out after 15-20 minute;
(2) by adding appropriate deionized water and all the other remaining components except modifying titanium dioxide by pouring out material while hot, stir and grind 2-3 hour, form suspension stand-by;
(3) suspension is mixed with modifying titanium dioxide, stir 10-15 minute under 800-1000 rev/min, dry, be ground into ultrafine powder and get final product.
The invention has the beneficial effects as follows: the present invention fills a prescription and adopts environmental protection raw material, utilization of waste material, do not cause the wasting of resources, the safety non-toxic compositions that add more, to its modifying surface, make it have high polymer layer with high molecular polymer, increased bonding force, can not reduce product performance, for the production of functional products such as preservative film auxiliary agent, degradative plastics additive, pigment or paint additives.
Specific embodiments
Below by specific examples, the present invention is described in detail.
The modified calcium carbonate that safety and environmental protection is nontoxic, by following weight part (kilogram) raw material make: calcium carbonate 90, river shell powder 2, pulverize leaf of Yellow cinnamon 2, alkenyl succinic anhydride 4, porous-starch 2, hyaluronate sodium 1, easily loosen collagen fibre 2, urea 2, feldspar in powder 4, high density polyethylene(HDPE) 5, nylon 664, tea-polyphenol 1, modifying titanium dioxide 3;
Described modifying titanium dioxide by following weight part (kilogram) raw material make: aluminium hydroxide 2, nano titanium oxide 50, silicon carbide 4, methyl methacrylate 5, antimonous oxide 3, terephthalic acid 3, dioctyl maleate 3, ethylene glycol 5, water 50; First preparation method adds methyl methacrylate, nano titanium oxide, aluminium hydroxide, ethylene glycol, water to stir, form suspension, at 45-50 DEG C, dry to water content 2-3%, then add immediately terephthalic acid, dioctyl maleate mix and blend 25-35 minute, then add all the other remaining components, under 1200-1500 rev/min of condition, stir, at 50-60 DEG C, dry, be ground into ultrafine powder and get final product.
The nontoxic modified calcium carbonate of a kind of safety and environmental protection of the present invention, made by following concrete steps:
(1) calcium carbonate, river shell powder, alkenyl succinic anhydride, porous-starch, urea, feldspar in powder, nylon 66 are added in high-speed kneading machine, be warming up between 70-80 DEG C, insulated and stirred half an hour, continue to add high density polyethylene(HDPE), continue to be warming up to 110-130 DEG C, be incubated and pour out after 15-20 minute;
(2) by adding appropriate deionized water and all the other remaining components except modifying titanium dioxide by pouring out material while hot, stir and grind 2-3 hour, form suspension stand-by;
(3) suspension is mixed with modifying titanium dioxide, stir 10-15 minute under 800-1000 rev/min, dry, be ground into ultrafine powder and get final product.
Performance Detection to modified calcium carbonate of the present invention and ordinary calcium carbonate is compared as follows:
First measure the tap density of the forward and backward calcium carbonate of modification, then calcium carbonate good modification and unmodified water-ground limestone are joined in polyvinyl chloride resin in 15% ratio respectively, make sample, test respectively both mechanical properties, comparing result sees the following form:
As can be seen from the above table, the loose bulk density of the calcium carbonate after modification diminishes, and illustrates that calcium carbonate split fully disperses, and it can also be seen that every mechanical property of calcium carbonate is all improved after modification.
Claims (2)
1. the modified calcium carbonate that safety and environmental protection is nontoxic, it is characterized in that, made by the raw material of following weight part: calcium carbonate 90-95, river shell powder 2-3, pulverizing leaf of Yellow cinnamon 2-3, alkenyl succinic anhydride 4-5, porous-starch 2-3, hyaluronate sodium 1-2, easy loosen collagen fibre 2-4, urea 2-3, feldspar in powder 4-6, high density polyethylene(HDPE) 5-7, nylon 66 4-6, tea-polyphenol 1-2, modifying titanium dioxide 3-4;
Described modifying titanium dioxide is made up of the raw material of following weight part: aluminium hydroxide 2-4, nano titanium oxide 50-60, silicon carbide 4-6, methyl methacrylate 5-7, antimonous oxide 3-4, terephthalic acid 3-4, dioctyl maleate 3-5, ethylene glycol 5-6, water 50-60; First preparation method adds methyl methacrylate, nano titanium oxide, aluminium hydroxide, ethylene glycol, water to stir, form suspension, at 45-50 DEG C, dry to water content 2-3%, then add immediately terephthalic acid, dioctyl maleate mix and blend 25-35 minute, then add all the other remaining components, under 1200-1500 rev/min of condition, stir, at 50-60 DEG C, dry, be ground into ultrafine powder and get final product.
2. the nontoxic modified calcium carbonate of a kind of safety and environmental protection according to claim 1, is characterized in that, is made up of following concrete steps:
(1) calcium carbonate, river shell powder, alkenyl succinic anhydride, porous-starch, urea, feldspar in powder, nylon 66 are added in high-speed kneading machine, be warming up between 70-80 DEG C, insulated and stirred half an hour, continue to add high density polyethylene(HDPE), continue to be warming up to 110-130 DEG C, be incubated and pour out after 15-20 minute;
(2) by adding appropriate deionized water and all the other remaining components except modifying titanium dioxide by pouring out material while hot, stir and grind 2-3 hour, form suspension stand-by;
(3) suspension is mixed with modifying titanium dioxide, stir 10-15 minute under 800-1000 rev/min, dry, be ground into ultrafine powder and get final product.