CN103981964B - 增强玻璃纤维高强防火保温石膏板 - Google Patents
增强玻璃纤维高强防火保温石膏板 Download PDFInfo
- Publication number
- CN103981964B CN103981964B CN201310335389.0A CN201310335389A CN103981964B CN 103981964 B CN103981964 B CN 103981964B CN 201310335389 A CN201310335389 A CN 201310335389A CN 103981964 B CN103981964 B CN 103981964B
- Authority
- CN
- China
- Prior art keywords
- plasterboard
- base material
- heat insulating
- glass fiber
- fireproof heat
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种增强玻璃纤维高强防火保温石膏板，其特征在于，具有：石膏板基材；至少一嵌入石膏板基材的网格布增强层；结合于石膏板基材表面的玻璃纤维棉和/或硅酸铝棉和/或岩棉保温层。本发明的有益效果是：整个材料自身防火A级防火材料，不添加任何易燃材料或非A级防火材料，从而使得整个石膏板具有较好的防火性能，保证用户使用的安全性；高强度的添加剂用量较大，能够有效提升强度，调节脱硫石膏添加的量来调节整体的密度；双层网格布结构能够有效提升石膏板的强度，而且在长度方向也有利于提高石膏板的韧性。
Description
技术领域
本发明涉及一种增强玻璃纤维高强防火保温石膏板。
背景技术
石膏板惯用的强度提高手段是将增强材料放入有粘结性的浆料中，诸如将玻璃纤维片材料或者玻璃纤维在内的增强材料。
对于增强石膏板的现有技术手段或多或少都存在一定的缺陷，在增强石膏板强度的同时，兼顾防火、保温是现有技术手段尚未妥善解决的技术问题。
发明内容
本发明的目的就是为了解决上述问题，提供一种增强玻璃纤维高强防火保温石膏板。
为了实现上述目的，本发明采用如下技术方案：
增强玻璃纤维高强防火保温石膏板，其特征在于，具有：
石膏板基材；
至少一嵌入石膏板基材的网格布增强层；
结合于石膏板基材表面的玻璃纤维棉和/或硅酸铝棉和/或岩棉保温层。
较为理想的是，所述石膏板基材为板状结构。
较为理想的是，网格布增强层包括靠近石膏板基材上表面的上层网格布增强层以及靠近石膏板基材下表面的下层网格布增强层。
较为理想的是，所述上层网格布增强层距离石膏板基材上表面的距离以及下层网格布增强层距离石膏板基材下表面的距离均为0.5mm-10mm。
较为理想的是，所述石膏板基材与保温层的厚度比值为1:1～3。
较为理想的是，所述网格布增强层中，网格布的目数为80-100目。
较为理想的是，石膏板基材的厚度为9.5mm-400mm。
较为理想的是，所述石膏板基材的浆料中，石膏粉料由α天然石膏、β石膏各占50％而构成。
较为理想的是，石膏板基材的浆料中，玻化微珠的添加量为浆料质量的3-5％。
较为理想的是，石膏板基材的浆料中，聚丙烯短纤维的添加量为浆料质量的3‰。
较为理想的是，石膏板基材的浆料中，所用添加剂由下列重量百分比的组分组成:
SMF保水剂0.2～1.0％；
F15减水剂0.1～0.4％；
1016胶粉0.05～0.3％；
SM减水剂0.2～1.0％；
F10减水剂0.1～0.4％；
JSS减胀剂0.1％；
QWS保水剂0.0125～0.015％；
QWS-1保水剂0.001～0.003％；
H11缓凝剂0.004～0.02％；
BOC0～0.03％；
LSG调凝剂0.2％。
较为理想的是，石膏板基材的浆料中，所用添加剂由下列重量百分比的组分组成:
SMF保水剂0.2～0.3％；
F15减水剂0.15～0.3％；
1016胶粉0.05～0.2％；
SM减水剂0.2～0.3％；
F10减水剂0.15～0.3％；
JSS减胀剂0.1％；
QWS保水剂0.0125～0.015％；
QWS-1保水剂0.00125～0.0027％；
H11缓凝剂0.004～0.02％；
BOC0～0.03％；
LSG调凝剂0.2％。
与现有技术相比，本发明具有如下有益效果：
(1)整个材料自身防火A级防火材料，不添加任何易燃材料或非A级防火材料，从而使得整个石膏板具有较好的防火性能，保证用户使用的安全性。
(2)增强类的添加剂用量较大，能够有效提升强度，调节脱硫石膏添加的量来调节整体的密度。
(3)双层网格布结构能够有效提升石膏板的强度，而且在长度方向也有利于提高石膏板的韧性。
附图说明
图1为增强玻璃纤维高强防火保温石膏板结构示意图。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体图示，进一步阐述本发明。
如图1所示，增强玻璃纤维高强防火保温石膏板，其具有：呈板状的石膏板基材1，其厚度可以在9.5mm-400mm之间变化，根据现场需要而进行任意加工，该石膏板基材中添加有玻璃纤维而作为增强材料；两嵌入石膏板基材的网格布增强层2；结合于石膏板基材表面的岩棉保温层3。
结合附图可以看出，两层网格布增强层的结构类型是：网格布增强层包括靠近石膏板基材上表面的上层网格布增强层2a以及靠近石膏板基材下表面的下层网格布增强层2b，这种结构有利于石膏板的加工，最大限度降低高强度石膏板的加工成本。
所述上层网格布增强层距离石膏板基材上表面的距离以及下层网格布增强层距离石膏板基材下表面的距离均为0.5mm-2mm之间，这与实际加工的工艺密切相关，由于铺设网格布的工艺是直接贴附于石膏浆料的，嵌入浆料的深度不宜太大。
在加工保温层的时候，考虑到岩棉结构的特性，其直接铺设于尚未凝固的浆料表层，而无需其他粘合剂就可以将岩棉结构直接结合于石膏板浆料表面，在石膏板成型之后岩棉就可以附着于石膏板，为保证保温的效果，所述石膏板基材与保温层的厚度比值为1:2，岩棉是蓬松状结构，在空气层中具有良好的保温隔热性能。
对于网格布的选用，其目数不能过小，在铺设网格布过程中否则不容易嵌入石膏浆料中，鉴于实际需要，所述网格布增强层中，网格布的目数为80-100目。
对于石膏板浆料的配比做出如下说明：
所述石膏板基材的浆料中，石膏粉料由α天然石膏、β石膏各占50％而构成，且石膏粉料占整个浆料的质量为85％-95％。
石膏板基材的浆料中，玻化微珠的添加量为浆料质量的3-5％。
石膏板基材的浆料中，聚丙烯短纤维的添加量为浆料质量的3‰。
且在浆料中添加有以下添加剂，参见表1。
表1所用添加剂作用及添加量
以上增强玻璃纤维高强防火保温石膏板的配料余量为水。
以上所述仅为本发明的优选实施方式，本发明的保护范围并不仅限于上述实施方式，凡是属于本发明原理的技术方案均属于本发明的保护范围。对于本领域的技术人员而言，在不脱离本发明的原理的前提下进行的若干改进，这些改进也应视为本发明的保护范围。
Claims (11)
1.增强玻璃纤维高强防火保温石膏板，其特征在于，具有：
石膏板基材；
至少一嵌入石膏板基材的网格布增强层；
结合于石膏板基材表面的玻璃纤维棉和/或硅酸铝棉和/或岩棉保温层；
其中，石膏板基材的浆料中，所用添加剂由下列重量百分比的组分组成:
SMF保水剂0.2～1.0%;
F15减水剂0.1～0.4%;
1016胶粉0.05～0.3%;
SM减水剂0.2～1.0%;
F10减水剂0.1～0.4%;
JSS减胀剂0.1%;
QWS保水剂0.0125～0.015%;
QWS-1保水剂0.001～0.003%;
H11缓凝剂0.004～0.02%；
BOC0～0.03%；
LSG调凝剂0.2%。
2.根据权利要求1所述的增强玻璃纤维高强防火保温石膏板，其特征在于，所述石膏板基材为板状结构。
3. 根据权利要求1所述的增强玻璃纤维高强防火保温石膏板，其特征在于，网格布增强层包括靠近石膏板基材上表面的上层网格布增强层以及靠近石膏板基材下表面的下层网格布增强层。
4. 根据权利要求3所述的增强玻璃纤维高强防火保温石膏板，其特征在于，所述上层网格布增强层距离石膏板基材上表面的距离以及下层网格布增强层距离石膏板基材下表面的距离均为0.5mm-10mm。
5. 根据权利要求1所述的增强玻璃纤维高强防火保温石膏板，其特征在于，所述石膏板基材与保温层的厚度比值为1:1～3。
6. 根据权利要求1所述的增强玻璃纤维高强防火保温石膏板，其特征在于，所述网格布增强层中，网格布的目数为80-100目。
7. 根据权利要求1所述的增强玻璃纤维高强防火保温石膏板，其特征在于，石膏板基材的厚度为9.5mm-400mm。
8. 根据权利要求1所述的增强玻璃纤维高强防火保温石膏板，其特征在于，所述石膏板基材的浆料中，石膏粉料由α天然石膏、β石膏各占50%而构成。
9. 根据权利要求1所述的增强玻璃纤维高强防火保温石膏板，其特征在于，石膏板基材的浆料中，玻化微珠的添加量为浆料质量的3-5%。
10. 根据权利要求1所述的增强玻璃纤维高强防火保温石膏板，其特征在于，石膏板基材的浆料中，聚丙烯短纤维的添加量为浆料质量的3‰。
11. 根据权利要求1所述的增强玻璃纤维高强防火保温石膏板，其特征在于，石膏板基材的浆料中，所用添加剂由下列重量百分比的组分组成:
SMF保水剂0.2～0.3%;
F15减水剂0.15～0.3%;
1016胶粉0.05～0.2%;
SM减水剂0.2～0.3%;
F10减水剂0.15～0.3%;
JSS减胀剂0.1%;
QWS保水剂0.0125～0.015%;
QWS-1保水剂0.00125～0.0027%;
H11缓凝剂0.004～0.02%；
BOC0～0.03%；
LSG调凝剂0.2%。