CN103981716A - Preparation method of organosilicon modified aqueous polyurethane for leather, and product prepared by using it - Google Patents
Preparation method of organosilicon modified aqueous polyurethane for leather, and product prepared by using it Download PDFInfo
- Publication number
- CN103981716A CN103981716A CN201410193116.1A CN201410193116A CN103981716A CN 103981716 A CN103981716 A CN 103981716A CN 201410193116 A CN201410193116 A CN 201410193116A CN 103981716 A CN103981716 A CN 103981716A
- Authority
- CN
- China
- Prior art keywords
- aqueous polyurethane
- leather
- modified aqueous
- organic silicon
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of organosilicon modified aqueous polyurethane for leather. The method comprises the steps of raw material vacuum dehydration, prepolymerization reaction, chain extension, water dispersion, solvent removal and the like. The invention also discloses the organosilicon modified aqueous polyurethane prepared by suing the method. Aqueous polyurethane is modified by carrying out chain extension through adopting hydroxy-containing organic silicone oil, the obtained product has the respective excellent performances of organosilicon and polyurethane, is environmentally-friendly and non-toxic, has excellent performances, and is suitable for leather treatment, and leather treated by the product has a smooth surface, and a soft, plump and elastic leather body, so the product can improve the water resistance, the oil resistance and the wear resistance of leather.
Description
Technical field
The present invention relates to technical field of macromolecules, relate to especially preparation method and the goods of a kind of leather organic silicon modified aqueous polyurethane.
Background technology
Along with the enhancing of people's environmental consciousness, material safety problem is all the more paid attention to, compound with more and more higher standard and the requirement of other daily necessitiess propositions such as adhesive, leather coating to packing.Aqueous polyurethane (WPU) is to adopt the polyaminoester emulsion of water as decentralized medium, except having solvent borne polyurethane excellent properties, also have the advantages such as use is simple, nontoxic, non-environmental-pollution, its product is successfully applied to the industries such as light textile, leather, timber processing, building, papermaking.But because aqueous polyurethane adopts water as solvent, the surface tension of WATER AS FLOW MEDIUM is too large, heat content is high, make that in its film forming procedure, surface spreading is poor, drying time is long, film forming and base material are compound poor, mechanical property reduction; And impel the hydrophilic radical of aqueous polyurethane stable dispersion in WATER AS FLOW MEDIUM, can cause aqueous polyurethane film forming poor water resistance and easily water suction; Difficulties in dispersion that when aqueous polyurethane emulsion dispersion, high-viscosity organic phase can cause, emulsion particle diameter is large and emulsion solid content is lower.
Both at home and abroad the modification of aqueous polyurethane is had from molecular scale and carries out the modification of polyalcohol MOLECULE DESIGN, or specific molecular structure or element are introduced to polyalcohol change macromolecular main chain to improve various application performances, or carry out nano combined lifting mechanical property at micro-scale, or utilize renewable resource to reduce costs, or be cross-linked to promote film forming characteristics etc. in film forming procedure introducing particular functional group reaction.
Organosilicon has been used to the modification of polyurethane very early, have high temperature resistant because the Si-O-Si key in the middle of its strand has compared with large cohesive energy, the performance that hydrolysis etc. are good, and this chain belongs to flexible chain, there is the advantages such as low temperature compliance is good, surface tension is low, good biocompatibility and with it, base polyurethane prepolymer for use as is carried out the modification of physics or chemistry, can improve the combination property of adhesive.Wherein taking silicon oxygen bond (SiO-Si-) as skeleton, the polysiloxanes of composition is most widely used.Block polymers of polyurethane is with the excellent properties of polysiloxanes and polyurethane, show good low temperature compliance, dielectricity, surface enrichment and good biocompatibility etc., overcome the shortcoming of polysiloxanes bad mechanical property, also made up the poor deficiency of polyurethane weatherability.
Conventionally because organosiloxane and polyurethane segment solubility parameters differ greatly, compatibility is very poor, adopts physical blending mode to have the even film layering of serious phase-separated state, and mechanical property and emulsion bin stability are poor thus.
Summary of the invention
Object of the present invention, for overcoming the above-mentioned deficiency of prior art, provides the preparation method of a kind of excellent properties that has both organosilicon and polyurethane, environmental protection, nontoxic, a kind of leather organic silicon modified aqueous polyurethane of being applicable to leather processing;
The present invention also aims to, the leather organic silicon modified aqueous polyurethane that adopts said method to produce is provided.Smooth with goods of the present invention leather light after treatment face, leather body softness, plentiful and high resilience, improves water proofing property, grease proofness and the anti-wear performance of leather.
For achieving the above object, technical scheme provided by the invention is:
A preparation method for organic silicon modified aqueous polyurethane for leather, comprises the following steps:
(1) take raw material according to following percentage by weight:
(2) pretreatment of raw material: add polymer polyatomic alcohol, stabilizing agent in the reactor with agitator, thermometer, dewater under 110 DEG C-120 DEG C, vacuum-0.09MPa 1-2 hour;
(3) prepolymerization reaction: logical N
2under protection, add isocyanates, catalyst to reactor, at 75-85 DEG C of reaction 1-4 hour;
(4) chain extension: the organic silicone oil of hydrophilic chain extender, crosslinking agent, hydroxyl and acetone are added in reactor, at 60-80 DEG C of reaction 2-4h, cool to 20-50 DEG C, add acetone diluted, make organic silicon modified polyurethane performed polymer;
(5) aqueous dispersion: adjusting temperature is 0-20 DEG C, under high speed dispersion, add the mixture of neutralizer and deionized water to carry out emulsification, then add chain extender, strong agitation, rotating speed control is 1200-1700r/min, the about 10min of chain extension, finally sloughs solvent acetone by the decompression distillation under 50 DEG C ,-0.08Mpa condition of gained emulsion, obtains silicon oil modified aqueous polyurethane emulsion.
Described polymer polyatomic alcohol is that molecular weight is 500-5000, one or more of polyether polyol that average hydroxyl value is 10-300mgKOH/g, polyester polyol, polytetrahydrofuran diol, wherein, described polyester polyol is the polyalcohol of adipic acid series, described polyether polyol is any one or two kinds of of polyoxypropyleneglycol, polypropylene oxide triol, and described polytetrahydrofuran diol is polytetramethylene ether diol (PTMEG); Described isocyanates is isophorone diisocyanate, toluene 2, one or both of 4-vulcabond; Described hydrophily chain extender is one or more of dihydromethyl propionic acid (DMPA), dimethylolpropionic acid (DMBA), dicarboxyl half ester; Described stabilizing agent is one or both of BHT (age resistor-264), tetramethylene β-(3,5-di-tert-butyl-hydroxy phenyl) propionic acid pentaerythritol ester (antioxidant 1010); Described catalyst is one or more of the sub-tin of dibutyl tin laurate, monooctyl ester, triethylenediamine; Described hydroxy silicon oil is that hydroxy radical content is one or both of 2%, 8%; Described crosslinking agent is one or both of glycerine, trimethylolpropane; Described neutralizer is one or both of triethylamine, ammoniacal liquor; Described chain extender is one or more of ethylenediamine, butanediamine, isophorone diamine.
A leather organic silicon modified aqueous polyurethane that adopts preceding method to prepare, its raw material components by following percentage by weight is prepared from:
Described polymer polyatomic alcohol is that molecular weight is 500-5000, one or more of polyether polyol that average hydroxyl value is 10-300mgKOH/g, polyester polyol, polytetrahydrofuran diol, wherein, described polyester polyol is the polyalcohol of adipic acid series, described polyether polyol is any one or two kinds of of polyoxypropyleneglycol, polypropylene oxide triol, and described polytetrahydrofuran diol is polytetramethylene ether diol (PTMEG); Described isocyanates is isophorone diisocyanate, toluene 2, one or both of 4-vulcabond; Described hydrophily chain extender is one or more of dihydromethyl propionic acid (DMPA), dimethylolpropionic acid (DMBA), dicarboxyl half ester; Described stabilizing agent is one or both of BHT (age resistor-264), tetramethylene β-(3,5-di-tert-butyl-hydroxy phenyl) propionic acid pentaerythritol ester (antioxidant 1010); Described catalyst is one or more of the sub-tin of dibutyl tin laurate, monooctyl ester, triethylenediamine; Described hydroxy silicon oil is that hydroxy radical content is one or both of 2%, 8%; Described crosslinking agent is one or both of glycerine, trimethylolpropane; Described neutralizer is one or both of triethylamine, ammoniacal liquor; Described chain extender is one or more of ethylenediamine, butanediamine, isophorone diamine.
Beneficial effect of the present invention is:
1, preparation method provided by the invention, technique is simple, is suitable for suitability for industrialized production, and operating mode is easily controlled, constant product quality, safety and environmental protection, is of value to staff healthy.
2, preparation method provided by the invention adopts the organic silicone oil of hydroxyl to carry out chain extension modified aqueous polyurethane, the aqueous polyurethane product making, have both organosilicon and polyurethane excellent properties, environmental protection, nontoxic, be applicable to leather processing.
3, adopt after product treatment leather of the present invention, leather light face is smooth, leather body softness, and plentiful and high resilience, improves water proofing property, grease proofness and the anti-wear performance of leather.
Below in conjunction with embodiment, the present invention is further described.
Detailed description of the invention
Embodiment 1: the preparation method of organic silicon modified aqueous polyurethane for the leather that the present embodiment provides, its bag
Draw together following steps:
(1) take raw material according to following percentage by weight:
(2) pretreatment of raw material: add polymer polyatomic alcohol, stabilizing agent in the reactor with agitator, thermometer, dewater under 110 DEG C-120 DEG C, vacuum-0.09MPa 1-2 hour;
(3) prepolymerization reaction: logical N
2under protection, add isocyanates, catalyst to reactor, at 75-85 DEG C of reaction 1-4 hour;
(4) chain extension: the organic silicone oil of hydrophilic chain extender, crosslinking agent, hydroxyl and acetone are added in reactor, at 60-80 DEG C of reaction 2-4h, cool to 20-50 DEG C, add acetone diluted, make organic silicon modified polyurethane performed polymer;
(5) aqueous dispersion: adjusting temperature is 0-20 DEG C, under high speed dispersion, add the mixture of neutralizer and deionized water to carry out emulsification, then add chain extender, strong agitation, rotating speed control is 1200-1700r/min, the about 10min of chain extension, finally sloughs solvent acetone by the decompression distillation under 50 DEG C ,-0.08Mpa condition of gained emulsion, obtains silicon oil modified aqueous polyurethane emulsion.
Described polymer polyatomic alcohol is that molecular weight is 500-5000, one or more of polyether polyol that average hydroxyl value is 10-300mgKOH/g, polyester polyol, polytetrahydrofuran diol, wherein, described polyester polyol is the polyalcohol of adipic acid series, described polyether polyol is any one or two kinds of of polyoxypropyleneglycol, polypropylene oxide triol, and described polytetrahydrofuran diol is polytetramethylene ether diol (PTMEG); Described isocyanates is isophorone diisocyanate, toluene 2, one or both of 4-vulcabond; Described hydrophily chain extender is one or more of dihydromethyl propionic acid (DMPA), dimethylolpropionic acid (DMBA), dicarboxyl half ester; Described stabilizing agent is one or both of BHT (age resistor-264), tetramethylene β-(3,5-di-tert-butyl-hydroxy phenyl) propionic acid pentaerythritol ester (antioxidant 1010); Described catalyst is one or more of the sub-tin of dibutyl tin laurate, monooctyl ester, triethylenediamine; Described hydroxy silicon oil is that hydroxy radical content is one or both of 2%, 8%; Described crosslinking agent is one or both of glycerine, trimethylolpropane; Described neutralizer is one or both of triethylamine, ammoniacal liquor; Described chain extender is one or more of ethylenediamine, butanediamine, isophorone diamine.
A leather organic silicon modified aqueous polyurethane that adopts preceding method to prepare, its raw material components by following percentage by weight is prepared from:
Described polymer polyatomic alcohol is that molecular weight is 500-5000, one or more of polyether polyol that average hydroxyl value is 10-300mgKOH/g, polyester polyol, polytetrahydrofuran diol, wherein, described polyester polyol is the polyalcohol of adipic acid series, described polyether polyol is any one or two kinds of of polyoxypropyleneglycol, polypropylene oxide triol, and described polytetrahydrofuran diol is polytetramethylene ether diol (PTMEG); Described isocyanates is isophorone diisocyanate, toluene 2, one or both of 4-vulcabond; Described hydrophily chain extender is one or more of dihydromethyl propionic acid (DMPA), dimethylolpropionic acid (DMBA), dicarboxyl half ester; Described stabilizing agent is one or both of BHT (age resistor-264), tetramethylene β-(3,5-di-tert-butyl-hydroxy phenyl) propionic acid pentaerythritol ester (antioxidant 1010); Described catalyst be the sub-tin of dibutyl tin laurate, monooctyl ester,, triethylenediamine one or more; Described hydroxy silicon oil is that hydroxy radical content is one or both of 2%, 8%; Described crosslinking agent is one or both of glycerine, trimethylolpropane; Described neutralizer is one or both of triethylamine, ammoniacal liquor; Described chain extender is one or more of ethylenediamine, butanediamine, isophorone diamine.
Embodiment 2: preparation method and the goods of organic silicon modified aqueous polyurethane for the leather that the present embodiment provides, its step and component are substantially the same manner as Example 1, and its difference is:
(1) take raw material according to following percentage by weight:
Described polymer polyatomic alcohol is that molecular weight is 2000 poly-adipic acid Isosorbide-5-Nitrae butanediol ester dihydroxylic alcohols;
Described isocyanates is toluene 2,4-vulcabond;
Described hydrophily chain extender is dihydromethyl propionic acid (DMPA);
Described stabilizing agent is antioxidant 1010;
Described catalyst is dibutyl tin laurate;
Described hydroxy silicon oil is the hydroxy silicon oil of hydroxy radical content 8%;
Described crosslinking agent is trimethylolpropane;
Described neutralizer is triethylamine;
Described chain extender is ethylenediamine.
(2) pretreatment of raw material: add polymer polyatomic alcohol, stabilizing agent in the reactor with agitator, thermometer, dewater 2 hours under 110 DEG C, vacuum-0.09MPa.
(3) prepolymerization reaction: logical N
2under protection, add isocyanates, catalyst to reactor, 75 DEG C of reactions 4 hours.
(4) chain extension: the organic silicone oil of hydrophilic chain extender, crosslinking agent, hydroxyl and acetone are added in reactor, at 60 DEG C of reaction 4h, cool to 20 DEG C, add acetone diluted, make organic silicon modified polyurethane performed polymer.
(5) aqueous dispersion: regulating temperature is 20 DEG C, under high speed dispersion, add the mixture of neutralizer and deionized water to carry out emulsification, then add chain extender, strong agitation, rotating speed control is 1700r/min, chain extension 10min, finally sloughs solvent acetone by the decompression distillation under 50 DEG C ,-0.08Mpa condition of gained emulsion, obtains silicon oil modified aqueous polyurethane emulsion.
Embodiment 3: preparation method and the goods of organic silicon modified aqueous polyurethane for the leather that the present embodiment provides, its step and component and embodiment 1,2 are basic identical, and its difference is:
(1) take raw material according to following percentage by weight:
Described polymer polyatomic alcohol is that molecular weight is 2000 poly-adipic acid Isosorbide-5-Nitrae butanediol ester dihydroxylic alcohols;
Described isocyanates is isophorone diisocyanate;
Described hydrophily chain extender is dihydromethyl propionic acid (DMPA);
Described stabilizing agent is antioxidant 1010;
Described catalyst is dibutyl tin laurate;
Described hydroxy silicon oil is the hydroxy silicon oil of hydroxy radical content 8%;
Described crosslinking agent is trimethylolpropane;
Described neutralizer is triethylamine;
Described chain extender is ethylenediamine;
(2) pretreatment of raw material: add polymer polyatomic alcohol, stabilizing agent in the reactor with agitator, thermometer, dewater 1 hour under 120 DEG C, vacuum-0.09MPa.
(3) prepolymerization reaction: logical N
2under protection, add isocyanates, catalyst to reactor, 85 DEG C of reactions 1 hour.
(4) chain extension: the organic silicone oil of hydrophilic chain extender, crosslinking agent, hydroxyl and acetone are added in reactor, at 60 DEG C of reaction 4h, cool to 50 DEG C, add acetone diluted, make organic silicon modified polyurethane performed polymer.
(5) aqueous dispersion: regulating temperature is 20 DEG C, under high speed dispersion, add the mixture of neutralizer and deionized water to carry out emulsification, then add chain extender, strong agitation, rotating speed control is 1400r/min, chain extension 10min, finally sloughs solvent acetone by the decompression distillation under 50 DEG C ,-0.08Mpa condition of gained emulsion, obtains silicon oil modified aqueous polyurethane emulsion.
Embodiment 4: preparation method and the goods of organic silicon modified aqueous polyurethane for leather that the present embodiment provides, its step and component and embodiment 1 or 2 or 3 basic identical, its difference is,
(1) take raw material according to following percentage by weight:
Described polymer polyatomic alcohol is that molecular weight is 2000 polytetramethylene ether diol;
Described isocyanates is toluene 2,4-vulcabond;
Described hydrophily chain extender is dihydromethyl propionic acid (DMPA);
Described stabilizing agent is antioxidant 1010;
Described catalyst is stannous octoate;
Described hydroxy silicon oil is the hydroxy silicon oil of hydroxy radical content 2%;
Described crosslinking agent is trimethylolpropane;
Described neutralizer is triethylamine;
Described chain extender is ethylenediamine.
(2) pretreatment of raw material: add polymer polyatomic alcohol, stabilizing agent in the reactor with agitator, thermometer, dewater 2 hours under 120 DEG C, vacuum-0.09MPa;
(3) prepolymerization reaction: logical N
2under protection, add isocyanates, catalyst to reactor, 75 DEG C of reactions 3 hours;
(4) chain extension: the organic silicone oil of hydrophilic chain extender, crosslinking agent, hydroxyl and acetone are added in reactor, at 70 DEG C of reaction 2h, cool to 40 DEG C, add acetone diluted, make organic silicon modified polyurethane performed polymer;
(5) aqueous dispersion: regulating temperature is 10 DEG C, under high speed dispersion, add the mixture of neutralizer and deionized water to carry out emulsification, then add chain extender, strong agitation, rotating speed control is 1200r/min, chain extension 10min, finally sloughs solvent acetone by the decompression distillation under 50 DEG C ,-0.08Mpa condition of gained emulsion, obtains silicon oil modified aqueous polyurethane emulsion.
Embodiment 5: preparation method and the goods of organic silicon modified aqueous polyurethane for leather that the present embodiment provides, its step and component and embodiment 1 or 2 or 3 or 4 basic identical, its difference is,
(1) take raw material according to following percentage by weight:
Described polymer polyatomic alcohol is that molecular weight is 2000 polyether polyol;
Described isocyanates is isophorone diisocyanate;
Described hydrophily chain extender is dihydromethyl propionic acid (DMPA);
Described stabilizing agent is antioxidant 1010;
Described catalyst is stannous octoate;
Described hydroxy silicon oil is the hydroxy silicon oil of hydroxy radical content 8%;
Described crosslinking agent is trimethylolpropane;
Described neutralizer is triethylamine;
Described chain extender is ethylenediamine;
(2) pretreatment of raw material: add polymer polyatomic alcohol, stabilizing agent in the reactor with agitator, thermometer, dewater 2 hours under 120 DEG C, vacuum-0.09MPa;
(3) prepolymerization reaction: logical N
2under protection, add isocyanates, catalyst to reactor, 80 DEG C of reactions 4 hours;
(4) chain extension: the organic silicone oil of hydrophilic chain extender, crosslinking agent, hydroxyl and acetone are added in reactor, at 80 DEG C of reaction 2h, cool to 30 DEG C, add acetone diluted, make organic silicon modified polyurethane performed polymer;
(5) aqueous dispersion: regulating temperature is 0 DEG C, under high speed dispersion, add the mixture of neutralizer and deionized water to carry out emulsification, then add chain extender, strong agitation, rotating speed control is 1200r/min, chain extension 10min, finally sloughs solvent acetone by the decompression distillation under 50 DEG C ,-0.08Mpa condition of gained emulsion, obtains silicon oil modified aqueous polyurethane emulsion.
Embodiment 6: preparation method and the goods of organic silicon modified aqueous polyurethane for leather that the present embodiment provides, its step and component and embodiment 1 or 2 or 3 or 4 or 5 basic identical, its difference is,
(1) take raw material according to following percentage by weight:
Described polymer polyatomic alcohol is that molecular weight is 2000 polyester polyol;
Described isocyanates is toluene 2,4-vulcabond;
Described hydrophily chain extender is dihydromethyl propionic acid (DMPA);
Described stabilizing agent is antioxidant 1010;
Described catalyst is dibutyl tin laurate;
Described hydroxy silicon oil is the hydroxy silicon oil of hydroxy radical content 2%;
Described crosslinking agent is trimethylolpropane;
Described neutralizer is triethylamine;
Described chain extender is ethylenediamine.
(2) pretreatment of raw material: add polymer polyatomic alcohol, stabilizing agent in the reactor with agitator, thermometer, dewater 2 hours under 110 DEG C, vacuum-0.09MPa;
(3) prepolymerization reaction: logical N
2under protection, add isocyanates, catalyst to reactor, 80 DEG C of reactions 2 hours;
(4) chain extension: the organic silicone oil of hydrophilic chain extender, crosslinking agent, hydroxyl and acetone are added in reactor, at 80 DEG C of reaction 3h, cool to 50 DEG C, add acetone diluted, make organic silicon modified polyurethane performed polymer;
(5) aqueous dispersion: regulating temperature is 10 DEG C, under high speed dispersion, add the mixture of neutralizer and deionized water to carry out emulsification, then add chain extender, strong agitation, rotating speed control is 1700r/min, chain extension 10min, finally sloughs solvent acetone by the decompression distillation under 50 DEG C ,-0.08Mpa condition of gained emulsion, obtains silicon oil modified aqueous polyurethane emulsion.
The preparation method of organic silicon modified aqueous polyurethane for leather provided by the invention, and the leather organic silicon modified aqueous polyurethane that adopts said method to produce, have both organosilicon and polyurethane excellent properties, environmental protection, nontoxic, be applicable to leather processing; Smooth with goods of the present invention leather light after treatment face, leather body softness, plentiful and high resilience, has improved water proofing property, grease proofness and the anti-wear performance of leather.
The present invention is not limited to above-mentioned embodiment, and the every embodiment that can realize all similar of the object of the invention or be equal to, all within protection scope of the present invention.
Claims (10)
1. a preparation method for organic silicon modified aqueous polyurethane for leather, is characterized in that, comprises the following steps:
(1) take raw material according to following percentage by weight:
(2) pretreatment of raw material: add polymer polyatomic alcohol, stabilizing agent in the reactor with agitator, thermometer, dewater under 110 DEG C-120 DEG C, vacuum-0.09MPa 1-2 hour;
(3) prepolymerization reaction: logical N
2under protection, add isocyanates, catalyst to reactor, at 75-85 DEG C of reaction 1-4 hour;
(4) chain extension: the organic silicone oil of hydrophilic chain extender, crosslinking agent, hydroxyl and acetone are added in reactor, at 60-80 DEG C of reaction 2-4h, cool to 20-50 DEG C, add acetone diluted, make organic silicon modified polyurethane performed polymer;
(5) aqueous dispersion: adjusting temperature is 0-20 DEG C, under high speed dispersion, add the mixture of neutralizer and deionized water to carry out emulsification, then add chain extender, strong agitation, rotating speed control is 1200-1700r/min, the about 10min of chain extension, finally sloughs solvent acetone by the decompression distillation under 50 DEG C ,-0.08Mpa condition of gained emulsion, obtains the aqueous polyurethane emulsion of leather organic silicone oil modification.
2. the preparation method of organic silicon modified aqueous polyurethane for leather according to claim 1, it is characterized in that, described polymer polyatomic alcohol is that molecular weight is 500-5000, one or more of polyether polyol that average hydroxyl value is 10-300mgKOH/g, polyester polyol, polytetrahydrofuran diol, wherein, described polyester polyol is the polyalcohol of adipic acid series, described polytetrahydrofuran diol is polytetramethylene ether diol (PTMEG), and described polyether polyol is one or both of polyoxypropyleneglycol, polypropylene oxide triol.
3. the preparation method of organic silicon modified aqueous polyurethane for leather according to claim 1, is characterized in that, described isocyanates is isophorone diisocyanate, toluene 2, one or both of 4-vulcabond.
4. the preparation method of organic silicon modified aqueous polyurethane for leather according to claim 1, it is characterized in that, described hydrophily chain extender is one or more of dihydromethyl propionic acid (DMPA), dimethylolpropionic acid (DMBA), dicarboxyl half ester.
5. the preparation method of organic silicon modified aqueous polyurethane for leather according to claim 1, it is characterized in that, described stabilizing agent is 2, one or both of 6-BHT (age resistor-264), tetramethylene β-(3,5-di-tert-butyl-hydroxy phenyl) propionic acid pentaerythritol ester (antioxidant 1010).
6. the preparation method of organic silicon modified aqueous polyurethane for leather according to claim 1, is characterized in that, described catalyst is one or more of the sub-tin of dibutyl tin laurate, monooctyl ester, triethylenediamine; Described hydroxy silicon oil is that hydroxy radical content is one or both of 2%, 8%
7. the preparation method of organic silicon modified aqueous polyurethane for leather according to claim 1, is characterized in that, described crosslinking agent is one or both of glycerine, trimethylolpropane; Described neutralizer is one or both of triethylamine, ammoniacal liquor.
8. the preparation method of organic silicon modified aqueous polyurethane for leather according to claim 1, is characterized in that, described chain extender is one or more of ethylenediamine, butanediamine, isophorone diamine.
9. a leather organic silicon modified aqueous polyurethane that adopts the described method of one of claim 1~8 to prepare, is characterized in that, its raw material components by following percentage by weight is prepared from:
10. leather organic silicon modified aqueous polyurethane according to claim 9, it is characterized in that, described polymer polyatomic alcohol is that molecular weight is 500-5000, one or more of polyether polyol that average hydroxyl value is 10-300mgKOH/g, polyester polyol, polytetrahydrofuran diol, wherein, described polyester polyol is the polyalcohol of adipic acid series, described polyether polyol is any one or two kinds of of polyoxypropyleneglycol, polypropylene oxide triol, and described polytetrahydrofuran diol is polytetramethylene ether diol (PTMEG); Described isocyanates is isophorone diisocyanate, toluene 2, one or both of 4-vulcabond; Described hydrophily chain extender is one or more of dihydromethyl propionic acid (DMPA), dimethylolpropionic acid (DMBA), dicarboxyl half ester; Described stabilizing agent is one or both of BHT (age resistor-264), tetramethylene β-(3,5-di-tert-butyl-hydroxy phenyl) propionic acid pentaerythritol ester (antioxidant 1010); Described catalyst is one or more of the sub-tin of dibutyl tin laurate, monooctyl ester, triethylenediamine; Described hydroxy silicon oil is that hydroxy radical content is one or both of 2%, 8%; Described crosslinking agent is one or both of glycerine, trimethylolpropane; Described neutralizer is one or both of triethylamine, ammoniacal liquor; Described chain extender is one or more of ethylenediamine, butanediamine, isophorone diamine.