CN103981705A - Protective film slurry for velvet-free anti-sticking curtain - Google Patents

Abstract

The invention belongs to the technical field of a curtain appliance, and particular relates to protective film slurry for a velvet-free anti-sticking curtain. The protective film slurry for the velvet-free anti-sticking curtain comprises the following components by weight percent: 60-80% of organic silicon, 0.5-1% of a cross-linking agent, 0.2-0.5% of a catalyst, 0.5-0.7% of glacial acetic acid and 18-38% of water. The protective film slurry can be applied to the curtain cloth and is capable of preventing dirt such as dust from attaching on the outer surface of the curtain.

Description

The diaphragm slurry of lint-free antiseized curtain

Technical field

The invention belongs to curtain apparatus technical field, relate in particular to a kind of diaphragm slurry of lint-free antiseized curtain.

Background technology

Modern curtain is of all kinds, of a great variety, but definitely the curtain of great majority attraction consumer eyeball is gay colours collocation and pattern, rather than the function of curtain itself.That is to say, selection when people are most of is the impact that is subject to outward appearance, but not the essence of things.But along with the popularization of green health, low-carbon environment-friendly living awareness, people are being transferred in function by outward appearance gradually also, and alternative multifunctional curtain can not meet people's demand in the market.Particularly current curtain, in the process of using, is easy to adhere to the impurity such as some dusts, thereby makes whole curtain become very dirty on the outer surface of curtain.

Summary of the invention

The object of the invention is to solve above-described technical problem, provide a kind of and can prevent that the dirts such as dust are attached to the diaphragm slurry of the lint-free antiseized curtain that can be applicable to Curtains Fabrics on the outer surface of curtain, its technical scheme is as follows:

The diaphragm slurry of lint-free antiseized curtain, is characterized in that, following component and percentage by weight, consists of:

Organosilicon: 60-80%,

Crosslinking agent: 0.5-1%,

Catalyst: 0.2-0.5%,

Glacial acetic acid: 0.5-0.7%,

Water: 18-38%.

The diaphragm slurry of the lint-free antiseized curtain that Curtains Fabrics provided by the invention is used, organosilyl effect is as mother liquor, organosilyl main chain is very submissive, its intermolecular active force a little less than than hydrocarbon many, therefore, low than the hydrocarbon viscosity of same molecular weight, a little less than surface tension, surface can be little, and film forming ability is strong, is widely used in textile industry; Glacial acetic acid, i.e. anhydrous acetic acid, organic compound, it is frozen into ice shape when low temperature, is one of important organic acid, is the raw material of manufacturing dyestuff, fabric printing and rubber industry.The effect of catalyst is more abundant for what make to mix between raw material.And crosslinking agent is small molecule compound, molecular weight is generally between 200-600, there are 2 or more for the reactive terminal of specific groups (amino, sulfydryl etc.), thereby can with 2 or more molecule respectively coupling these molecules are combined, thereby play connection function.

The invention has the beneficial effects as follows: the diaphragm slurry of lint-free antiseized curtain can well prevent that slurry and cloth starch adhesive face from having smooth feel a little anti-dirty special nature again with the attached adhesive of slurry face.

The specific embodiment

Illustrate embodiment below:

Embodiment 1:

The diaphragm slurry of lint-free antiseized curtain, is characterized in that, following component and percentage by weight, consists of:

Organosilicon: 60%,

Crosslinking agent: 1%,

Catalyst: 0.5%,

Glacial acetic acid: 0.7%,

Water: 37.8%.

Embodiment 2:

The diaphragm slurry of lint-free antiseized curtain, is characterized in that, following component and percentage by weight, consists of:

Organosilicon: 80%,

Crosslinking agent: 0.5%,

Catalyst: 0.2%,

Glacial acetic acid: 0.5%,

Water: 18.8%.

The invention has the beneficial effects as follows: the diaphragm slurry of lint-free antiseized curtain can well prevent that slurry and cloth starch adhesive face from having smooth feel a little anti-dirty special nature again with the attached adhesive of slurry face.

Claims (1)

1. the diaphragm of lint-free antiseized curtain slurry, is characterized in that, following component and percentage by weight, consists of:

Organosilicon: 60-80%,

Crosslinking agent: 0.5-1%,

Catalyst: 0.2-0.5%,

Glacial acetic acid: 0.5-0.7%,

Water: 18-38%.