CN103980569B - A kind of magnetic rubber material and preparation method thereof - Google Patents
A kind of magnetic rubber material and preparation method thereof Download PDFInfo
- Publication number
- CN103980569B CN103980569B CN201410243323.3A CN201410243323A CN103980569B CN 103980569 B CN103980569 B CN 103980569B CN 201410243323 A CN201410243323 A CN 201410243323A CN 103980569 B CN103980569 B CN 103980569B
- Authority
- CN
- China
- Prior art keywords
- parts
- sulfuration
- magnetic rubber
- weight
- rubber material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention discloses a kind of magnetic rubber material, it is characterized in that comprising following component: mark 60 ~ 80 parts, glue; Neoprene latex 25 ~ 35 parts; Carbon black 20 ~ 30 parts; Dibutylester 15 ~ 25 parts; 3 ~ 7 parts, zinc oxide; 1 ~ 5 part, magnesium oxide; Nickel-zinc ferrite 40 ~ 50 parts; Stearic acid 1.5 ~ 2.5 parts; Captax 0.3 ~ 0.7 part; Altax 0.5 ~ 1.5 part; Accelerant N A-22? 0.3 ~ 0.7 part; Promotor TT0.03 ~ 0.07 part; Antioxidant 4010 0.4 ~ 0.8 part; Anti-aging agent RD 0.4 ~ 0.8 part; 1.4 ~ 1.8 parts, sulphur is with parts by weight.The present invention uses the steps such as mixing, sulfuration effectively to improve material plasticity number, and plasticity number is more than 0.55; The present invention carries out sulfuration again after magnetizing, can the magnetic of permanent maintenance material.
Description
Technical field
The present invention relates to a kind of elastomeric material and preparation method thereof, be specifically related to a kind of magnetic rubber material and preparation method thereof.
Background technology
Magnetic rubber is the magnetic elastomeric general name of band, is prepared from by sizing material, magnetic and other auxiliary agents.Magnetic rubber material all has boundless application prospect in a lot of field, such as telecommunications context, robot calculator field, etc., all need use band magnetic elastomeric material.
Existing magnetic rubber material is by after elastomeric material batch mixing mostly, then is magnetized by material, and causing existing magnetic rubber to there is magnetic can not keep, the not high all deficiencies of rubber plasticity-.
Summary of the invention
Goal of the invention: the object of the invention is for the deficiencies in the prior art, provides a kind of plasticity-strong, the magnetic rubber material that magnetic is forever solid, and the preparation method of this material.
Technical scheme: magnetic rubber material of the present invention, comprises following component:
Mark 60 ~ 80 parts, glue;
Neoprene latex 25 ~ 35 parts;
Carbon black 20 ~ 30 parts;
Dibutylester 15 ~ 25 parts;
3 ~ 7 parts, zinc oxide;
1 ~ 5 part, magnesium oxide;
Nickel-zinc ferrite 40 ~ 50 parts;
Stearic acid 1.5 ~ 2.5 parts;
Captax 0.3 ~ 0.7 part;
Altax 0.5 ~ 1.5 part;
Accelerant N A-220.3 ~ 0.7 part;
Promotor TT0.03 ~ 0.07 part;
Antioxidant 4010 0.4 ~ 0.8 part;
Anti-aging agent RD 0.4 ~ 0.8 part;
1.4 ~ 1.8 parts, sulphur
With parts by weight.
Preferably, described magnetic rubber material, comprises following component:
Mark 70 parts, glue;
Neoprene latex 30 parts;
Carbon black 25 parts;
Dibutylester 20 parts;
5 parts, zinc oxide;
3 parts, magnesium oxide;
Nickel-zinc ferrite 46 parts;
Stearic acid 2 parts;
Captax 0.5 part;
Altax 1 part;
Accelerant N A-220.5 part;
Promotor TT0.05 part;
Antioxidant 4010 0.6 part;
Anti-aging agent RD 0.6 part;
1.6 parts, sulphur
With parts by weight.
The preparation method of magnetic rubber material of the present invention, comprises the steps:
(1) mixing: each component is prepared by weight, carry out mixing;
(2) magnetize: the sizing material mixed is magnetized, magneticstrength 1000 ~ 1200GS, magnetize time 18 ~ 22min;
(3) sulfuration: send into again in vulcanizer after sizing material magnetizes and carry out sulfuration.
Beneficial effect: the present invention uses the steps such as mixing, sulfuration effectively to improve material plasticity number, and plasticity number is more than 0.55; The present invention carries out sulfuration again after magnetizing, can the magnetic of permanent maintenance material.
Embodiment
Below technical solution of the present invention is described in detail, but protection scope of the present invention is not limited to described embodiment.
The raw material used in the embodiment of the present invention is commercially available prod, originates as follows: the large golden cup SVR-3L of Vietnam's AA level marks glue (Guan Hua rubber and plastic trade Co., Ltd of Shenzhen); Chloroprene rubber (Guangzhou Tian Benfeng limited rubber company); Carbon black N550(Qingdao Zhong Xiangbokai Chemical Co., Ltd.); Dibutylester (Shenzhen Zhong Run leads to Chemical Co., Ltd.); Zinc oxide (Linyi mayor woods Chemical Co., Ltd.); Magnesium oxide (Linyi mayor woods Chemical Co., Ltd.); Nickel-zinc ferrite (Linyi mayor woods Chemical Co., Ltd.); Stearic acid (reported in Tianhe district of Guangzhou grand sight intelligence industry Chemicals 1801 stearic acid); Captax (Shijiazhuang City gathers hundred wide Chemical Industry Science Co., Ltd); Rubber accelerator DM(Shijiazhuang City gathers hundred wide Chemical Industry Science Co., Ltd); Accelerant N A-22(Shijiazhuang City gathers hundred wide Chemical Industry Science Co., Ltd); Promotor TT(Shijiazhuang City gathers hundred wide Chemical Industry Science Co., Ltd); Antioxidant 4010 (Bry Chemical Co., Ltd.); Anti-aging agent RD (Bry Chemical Co., Ltd.); Sulphur (Linyi Jin Huang Chemical Co., Ltd.).
embodiment 1:a kind of magnetic rubber material, comprises following component:
Mark 60 parts, glue;
Neoprene latex 25 parts;
Carbon black 20 parts;
Dibutylester 15 parts;
3 parts, zinc oxide;
1 part, magnesium oxide;
Nickel-zinc ferrite 40 parts;
Stearic acid 1.5 parts;
Captax 0.3 part;
Altax 0.5 part;
Accelerant N A-220.3 part;
Promotor TT0.03 part;
Antioxidant 4010 0.4 part;
Anti-aging agent RD 0.4 part;
1.4 parts, sulphur
With parts by weight.
Preparation method, comprises the steps:
(1) mixing: each component is prepared by weight, carry out mixing;
(2) magnetize: the sizing material mixed is magnetized, magneticstrength 1000GS, magnetize time 18min;
(3) sulfuration: send into again in vulcanizer after sizing material magnetizes and carry out sulfuration.
embodiment 2:a kind of magnetic rubber material, comprises following component:
Mark 80 parts, glue;
Neoprene latex 35 parts;
Carbon black 30 parts;
Dibutylester 25 parts;
7 parts, zinc oxide;
5 parts, magnesium oxide;
Nickel-zinc ferrite 50 parts;
Stearic acid 2.5 parts;
Captax 0.7 part;
Altax 1.5 parts;
Accelerant N A-220.7 part;
Promotor TT0.07 part;
Antioxidant 4010 0.8 part;
Anti-aging agent RD 0.8 part;
1.8 parts, sulphur
With parts by weight.
Preparation method, comprises the steps:
(1) mixing: each component is prepared by weight, carry out mixing;
(2) magnetize: the sizing material mixed is magnetized, magneticstrength 1200GS, magnetize time 22min;
(3) sulfuration: send into again in vulcanizer after sizing material magnetizes and carry out sulfuration.
embodiment 3:a kind of magnetic rubber material, comprises following component:
Mark 70 parts, glue;
Neoprene latex 30 parts;
Carbon black 25 parts;
Dibutylester 20 parts;
5 parts, zinc oxide;
3 parts, magnesium oxide;
Nickel-zinc ferrite 46 parts;
Stearic acid 2 parts;
Captax 0.5 part;
Altax 1 part;
Accelerant N A-220.5 part;
Promotor TT0.05 part;
Antioxidant 4010 0.6 part;
Anti-aging agent RD 0.6 part;
1.6 parts, sulphur
With parts by weight.
Preparation method, comprises the steps:
(1) mixing: each component is prepared by weight, carry out mixing;
(2) magnetize: the sizing material mixed is magnetized, magneticstrength 1100GS, magnetize time 20min;
(3) sulfuration: send into again in vulcanizer after sizing material magnetizes and carry out sulfuration.
As mentioned above, although represented with reference to specific preferred embodiment and described the present invention, it shall not be construed as the restriction to the present invention self.Under the spirit and scope of the present invention prerequisite not departing from claims definition, various change can be made in the form and details to it.
Claims (3)
1. a magnetic rubber material, is characterized in that comprising following component:
Mark 60 ~ 80 parts, glue;
Neoprene latex 25 ~ 35 parts;
Carbon black 20 ~ 30 parts;
Dibutylester 15 ~ 25 parts;
3 ~ 7 parts, zinc oxide;
1 ~ 5 part, magnesium oxide;
Nickel-zinc ferrite 40 ~ 50 parts;
Stearic acid 1.5 ~ 2.5 parts;
Captax 0.3 ~ 0.7 part;
Altax 0.5 ~ 1.5 part;
Accelerant N A-220.3 ~ 0.7 part;
Promotor TT0.03 ~ 0.07 part;
Antioxidant 4010 0.4 ~ 0.8 part;
Anti-aging agent RD 0.4 ~ 0.8 part;
1.4 ~ 1.8 parts, sulphur
With parts by weight;
Collocation preparation method:
(1) mixing: each component is prepared by weight, carry out mixing;
(2) magnetize: the sizing material mixed is magnetized, magneticstrength 1000 ~ 1200GS, magnetize time 18 ~ 22min;
(3) sulfuration: send into again in vulcanizer after sizing material magnetizes and carry out sulfuration.
2. magnetic rubber material according to claim 1, is characterized in that comprising following component:
Mark 70 parts, glue;
Neoprene latex 30 parts;
Carbon black 25 parts;
Dibutylester 20 parts;
5 parts, zinc oxide;
3 parts, magnesium oxide;
Nickel-zinc ferrite 46 parts;
Stearic acid 2 parts;
Captax 0.5 part;
Altax 1 part;
Accelerant N A-220.5 part;
Promotor TT0.05 part;
Antioxidant 4010 0.6 part;
Anti-aging agent RD 0.6 part;
1.6 parts, sulphur
With parts by weight.
3. the preparation method of magnetic rubber material according to claim 1 and 2, is characterized in that comprising the steps:
(1) mixing: each component is prepared by weight, carry out mixing;
(2) magnetize: the sizing material mixed is magnetized, magneticstrength 1000 ~ 1200GS, magnetize time 18 ~ 22min;
(3) sulfuration: send into again in vulcanizer after sizing material magnetizes and carry out sulfuration.