CN103978318A - 一种圆形三明治自钎钎料及其制备方法 - Google Patents
一种圆形三明治自钎钎料及其制备方法 Download PDFInfo
- Publication number
- CN103978318A CN103978318A CN201410170926.5A CN201410170926A CN103978318A CN 103978318 A CN103978318 A CN 103978318A CN 201410170926 A CN201410170926 A CN 201410170926A CN 103978318 A CN103978318 A CN 103978318A
- Authority
- CN
- China
- Prior art keywords
- alloy
- brazing filler
- wire
- sandwich self
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及钎料及其制备领域,特指一种圆形三明治自钎钎料及其制备方法,通过称取助剂并混合均匀成为膏状,然后将膏状混合物包裹在合金丝外侧,烘干成为药皮焊丝,随后再将该药皮焊丝与合金丝一起通过轧辊,形成合金薄带包裹在药皮焊丝外侧,得到圆形三明治自钎钎料,由芯部、中间层和外层三部分组成,所述芯部为合金丝,中间层为助剂,外层为合金薄带。由上述方案得到的钎料能够适用于不同场合的合金及助焊剂比例需求。
Description
技术领域
本发明涉及钎料及其制备领域,特指一种圆形三明治自钎钎料及其制备方法。
背景技术
钎焊技术的进步引入了“药芯焊丝”产品,由于采用了助焊剂与钎焊丝同步定比例添加的方式,节约钎焊材料的同时大大提高了焊接效率。尤其在铝钎焊领域,由于常规钎焊操作难度较大,“药芯焊丝”的引入还提高了钎焊成品率。
尽管如此,一些特殊场合的焊接接头需要更多的钎焊合金填充,而由于生产工艺限制,市售药芯焊丝的线径一般在2.0mm左右,并且钎剂(或焊粉)填充量一般在15%~20%左右。填充金属的量在部分应用场合下不能满足焊接需求,因此操作时需要同时添加多根焊丝。
因此,本发明人对此做进一步研究,研发出一种圆形三明治自钎钎料及其制备方法,本案由此产生。
发明内容
本发明的目的在于提供一种圆形三明治自钎钎料及其制备方法,使钎料能够适用于不同场合的合金及助焊剂比例需求。
为了实现上述目的,本发明的技术方案如下:
一种圆形三明治自钎钎料,由芯部、中间层和外层三部分组成,所述芯部为合金丝,中间层为助剂,外层为合金薄带。
进一步,所述的合金丝及合金箔可以为铝合金、铜合金或银合金。
进一步,所述中间层通过粘结剂与芯部合金丝相连。
一种圆形三明治自钎钎料制备方法,包括如下步骤:
称取助剂并混合均匀成为膏状,然后将膏状混合物包裹在合金丝外侧,烘干成为药皮焊丝,随后再将该药皮焊丝与合金丝一起通过轧辊,形成合金薄带包裹在药皮焊丝外侧,得到圆形三明治自钎钎料。
采用上述方案后,本发明与现有技术相比,具有以下优点:
1)与市售“药芯焊丝”相比,本专利方法更容易制备出大直径的焊丝,更适合对于钎焊时单位时间内钎料需求量较高的钎焊场合;
2)与市售“药芯焊丝”相比,本专利产品中钎剂(焊粉)与钎料(合金)比例更容易调整,并且可调范围更大;
3)与市售“药皮焊丝”相比,本专利产品中钎剂被保护在金属层内侧,降低了吸潮变质的可能性,即使钎剂从芯部合金上剥落,也不会从焊丝中脱落影响焊接效果;
4) 该产品制备方法可以很好保证芯部的焊丝在整个钎料的中央位置,不发生偏移。
附图说明
图1是本发明钎料的示意图;
图2是钎料的制作流程示意图。
具体实施方式
下面结合附图和具体实施例对本发明作进一步的说明。
实施例1
一、材料
选用直径为2.2mm的BAg45CuZn合金丝,选取氟化物、硼酸盐助焊剂及其助剂,焊带为0.2mm*10mm的BAg45CuZn合金。
二、制备方法
1,将氟化物、硼酸盐助焊剂及其助剂进行混合,过100目筛子;
2,将均匀粉体加入到粘结剂中,搅拌均匀,并加入到涂敷装置中;
3,选取2.2mm的BAg45CuZn合金丝,并使其通过带有涂覆装置的固定轨道,并在固定位置对焊丝进行涂覆,使合金丝四周均匀涂布膏体;
4,匀速通过加热管道,使合金丝与周边的膏体复合并呈半烘干状态;
5,半烘干后的药皮焊丝继续通过预定轨道,与下方BAg45CuZn合金薄带复合,随后通过轧辊使合金薄带完全包裹药皮焊条并适当减径;
6,减径完成的三明治焊丝经过烘干步骤,完成绕盘,最终得到直径为3.0mm的三明治自钎钎料。
本实施例制得的圆形三明治自钎钎料在304不锈钢表面上润湿性、渗透性优良、钎缝的力学性能优良,气密性优良。焊接较大接头时送丝速度快,效率高。
实施例2
一、材料
选用直径为1.2mm的BCu60ZnSn-R合金丝,选取氟化物、硼酸盐助焊剂及其助剂,焊带为0.1mm*5mm的BCu60ZnSn-R合金。
二、按照实施案例1的制备方法制备得到直径为1.5mm的三明治自钎钎料。
本实施例制得的三明治自钎钎料在碳钢表面上润湿性、渗透性优良、钎缝的力学性能优良,气密性优良。火焰钎焊碳钢与铜接头钎焊操作方便,效率高。
实施例3
一、材料
选用直径为1.2mm的Zn78Al22合金丝,选取氟化物助焊剂及其助剂,焊带为0.25mm*6.5mm的ER4047合金。
二、按照实施案例1的制备方法制备得到直径为2.0mm的三明治自钎钎料。
本实施例制得的三明治自钎钎料在6061铝合金表面上润湿性、渗透性优良、6061铝合金钎缝的力学性能优良,气密性优良。
实施例4
一、材料
选用直径为1.6mm的BAg50CuZnNi合金丝,选取氟化物、硼酸盐助焊剂及其助剂,焊带为0.3mm*6.0mm的BAg50CuZnNi合金。
二、按照实施案例1的制备方法制备得到直径为2.5mm的三明治自钎钎料。
本实施例制得的三明治自钎钎料在硬质合金表面上润湿性、渗透性优良,可用于钎焊硬质合金刀头。
上述仅为本发明的具体实施例,但本发明的设计构思并不局限于此,凡利用此构思对本发明进行非实质性的改动,均应属于侵犯本发明保护范围的行为。
Claims (4)
1.一种圆形三明治自钎钎料,其特征在于:由芯部、中间层和外层三部分组成,所述芯部为合金丝,中间层为助剂,外层为合金薄带。
2.根据权利要求1所述的一种圆形三明治自钎钎料,其特征在于:所述的合金丝及合金箔可以为铝合金、铜合金或银合金。
3.根据权利要求1所述的一种圆形三明治自钎钎料,其特征在于:所述中间层通过粘结剂与芯部合金丝相连。
4.一种圆形三明治自钎钎料制备方法,包括如下步骤:
称取助剂并混合均匀成为膏状,然后将膏状混合物包裹在合金丝外侧,烘干成为药皮焊丝,随后再将该药皮焊丝与合金丝一起通过轧辊,形成合金薄带包裹在药皮焊丝外侧,得到圆形三明治自钎钎料。