CN103969126B - 多孔金属材料柔软度的检测方法 - Google Patents
多孔金属材料柔软度的检测方法 Download PDFInfo
- Publication number
- CN103969126B CN103969126B CN201410218713.5A CN201410218713A CN103969126B CN 103969126 B CN103969126 B CN 103969126B CN 201410218713 A CN201410218713 A CN 201410218713A CN 103969126 B CN103969126 B CN 103969126B
- Authority
- CN
- China
- Prior art keywords
- metal material
- porous metal
- platform plane
- pliability
- testing sample
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供了一种多孔金属材料柔软度的检测方法，一定尺寸的多孔金属材料放置于具有一定高度L1的平台平面上，使一定长度的多孔金属材料被置于平台平面外，呈悬空，被置于平台平面外的多孔金属材料为待测样品，距待测样品在平台平面外的尾端一定距离A3处放置一定重量的重力源，静置15~30s，测量待测样品自然弯曲后在平台平面外的尾部离平台平面底部的高度L2，根据公式D=（L1-L2）/（S* ρ）即可计算得到柔软度的数值，其中D为柔软度，S为待测样品的面积，ρ为多孔金属材料的面密度。本发明方法操作简单，所用设备简单，不需要投入很大的检测成本，能直接在生产现场就可迅速有效地反映出多孔金属材料的实际柔软度，更好的指导生产，降低生产不良率。
Description
技术领域
本发明涉及一种柔软度的检测方法，特别涉及一种多孔金属材料柔软度的检测方法。
背景技术
镍氢电池的核心骨架材料——泡沫镍是一种典型的多孔金属材料，其柔软度是影响电池性能的重要指标之一。一直以来，因为泡沫镍本身具备的多孔特性，对于泡沫镍的柔软度指标，在生产中未有一种快速、简便、成本低的方法和设备进行表征，不能及时指导泡沫镍生产，其柔软度性能指标无法得到真实有效的保障，因此也就无法有效提升电池的制造工艺。
其它多孔金属材料，如泡沫铜、泡沫镍铁等在应用于催化剂载体、过滤材料等领域时，也同样存在柔软度无法有效检测的问题。
因此，开发出一种能有效检测多孔金属材料柔软度的方法，是行业内急切需要解决的重大技术难题。
发明内容
本发明旨在提供一种操作简单的多孔金属材料柔软度的检测方法。本发明通过以下方案实现：
一种多孔金属材料柔软度的检测方法，包括如下步骤：
（Ⅰ）一定尺寸的多孔金属材料放置于具有一定高度L1的平台平面上，多孔金属的长度为A1；放置方式为使一定长度的多孔金属材料被置于平台平面外，呈悬空，被置于平台平面外的多孔金属材料即为待测样品，待测样品的长度为A2；其中A2与A1的比值不大于1/2；
（Ⅱ）距待测样品在平台平面外的尾端一定距离A3处放置一定重量的重力源，静置15~30s；其中A3与第（Ⅰ）步中的A2比值范围为1/5~1/2；所述重力源的重量是待测样品重量的15～50倍；
（Ⅲ）测量待测样品自然弯曲后在平台平面外的尾部离平台平面底部的高度，其值为L2；
（Ⅳ）根据公式（1）计算得到柔软度的数值
D=（L1-L2）/（S*ρ）………………………(1)
公式（1）中，D为柔软度，S为待测样品的面积，ρ为多孔金属材料的面密度。
为节约检测成本，所述放置于平台平面上的多孔金属材料的长度为20~40cm，宽度为2~5cm，多孔金属材料待测样品的长度为5~10cm。
本发明针对多孔金属材料，提供了一种用于检测柔软度的方法。本方法操作简单、快速，所用设备简单，检测成本低，能直接在生产现场就可迅速有效地反映出多孔金属材料的实际柔软度，更好的指导生产，及时调整生产工艺参数，有效降低生产不良率。
具体实施方式
实施例1
一种多孔金属材料柔软度的检测方法，包括如下步骤：
（1）取长度为20cm，宽度为2cm，厚度为1.6mm，面密度为320g/m2的多孔金属材料——泡沫镍放置于高度L1为5cm的平台平面上，使泡沫镍材料被置于平台平面外，呈悬空，被置于平台平面外的泡沫镍材料即为待测样品，待测样品的长度为5cm；
（2）距待测样品在平台平面外的尾端1cm处放置重量为10g的砝码，静置15s；
（3）测量待测样品自然弯曲后在平台平面外的尾部离平台平面底部的高度L2为3cm；
（4）根据公式D=（L1-L2）/（S*ρ）即可计算得到柔软度的数值，其中D为柔软度，S为待测样品的体积，ρ为多孔金属材料的面密度，将数据代入公式中计算得出柔软度D为6.25cm/g。
实施例2
一种多孔金属材料柔软度的检测方法，包括如下步骤：
（1）取长度为40cm，宽度为3cm，厚度为1.8mm，面密度为300g/m2的多孔金属材料——泡沫铜放置于高度L1为5cm的平台平面上，使泡沫镍材料被置于平台平面外，呈悬空，被置于平台平面外的泡沫镍材料即为待测样品，待测样品的长度为8cm；
（2）距待测样品在平台平面外的尾端2cm处放置重量为15g的砝码，静置20s；
（3）测量待测样品自然弯曲后在平台平面外的尾部离平台平面底部的高度L2为2cm；
（4）根据公式D=（L1-L2）/S*ρ即可计算得到柔软度的数值，其中D为柔软度，S为待测样品的面积，ρ为多孔金属材料的面密度，将数据代入公式中计算得出柔软度D为4.17cm/g。
实施例3
一种多孔金属材料柔软度的检测方法，包括如下步骤：
（1）取长度为30cm，宽度为5cm，厚度为1.0mm，面密度为280g/m2的多孔金属材料——泡沫镍铁放置于高度L1为5cm的平台平面上，使泡沫镍材料被置于平台平面外，呈悬空，被置于平台平面外的泡沫镍材料即为待测样品，待测样品的长度为10cm；
（2）距待测样品在平台平面外的尾端2.5cm处放置重量为30g的砝码，静置30s；
（3）测量待测样品自然弯曲后在平台平面外的尾部离平台平面底部的高度L2为1cm；
（4）根据公式D=（L1-L2）/S*ρ即可计算得到柔软度的数值，其中D为柔软度，S为待测样品的面积，ρ为多孔金属材料的面密度，将数据代入公式中计算得出柔软度D为2.86cm/g。
Claims (2)
1.多孔金属材料柔软度的检测方法，其特征在于：包括如下步骤，
（Ⅰ）一定尺寸的多孔金属材料放置于具有一定高度L1的平台平面上，多孔金属的长度为A1；放置方式为使一定长度的多孔金属材料被置于平台平面外，呈悬空，被置于平台平面外的多孔金属材料即为待测样品，待测样品的长度为A2；其中A2与A1的比值不大于1/2；
（Ⅱ）距待测样品在平台平面外的尾端一定距离A3处放置一定重量的重力源，静置15~30s；其中A3与第（Ⅰ）步中的A2比值范围为1/5~1/2；所述重力源的重量是待测样品重量的15～50倍；
（Ⅲ）测量待测样品自然弯曲后在平台平面外的尾部离平台平面底部的高度，其值为L2；
（Ⅳ）根据公式（1）计算得到柔软度的数值
D=（L1-L2）/（S*ρ）………………………(1)
公式（1）中，D为柔软度，S为待测样品的面积，ρ为多孔金属材料的面密度。
2.如权利要求1所述的多孔金属材料柔软度的检测方法，其特征在于：所述放置于平台平面上的多孔金属材料的长度为20~40cm，宽度为2~5cm，多孔金属材料待测样品的长度为5~10cm。