CN103966695B - A kind of health care ramee fabric and preparation method thereof - Google Patents
A kind of health care ramee fabric and preparation method thereof Download PDFInfo
- Publication number
- CN103966695B CN103966695B CN201410165449.3A CN201410165449A CN103966695B CN 103966695 B CN103966695 B CN 103966695B CN 201410165449 A CN201410165449 A CN 201410165449A CN 103966695 B CN103966695 B CN 103966695B
- Authority
- CN
- China
- Prior art keywords
- fiber
- ramee
- fabric
- powder
- spinning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of health care ramee fabric, is made up of the raw material of following weight portion: nano-chitosan 6-7, water 7-9, shea butter 2-3, plasticity starch 10-12,1-ethyl-3-methylimidazole acetate 60-70,1-allyl-3-methylimidazole villaumite 40-50, iron powder 2-4, tri-iron tetroxide 2-4, collagenous fiber 8-10, infrared ceramic powder 3-5, potassium acetate 2-4, ramee 70-80, cypress fiber 15-20, spin finish aid 0.2-0.4; Fabric of the present invention has the characteristic of ramee excellence, and with the addition of cypress fiber, there is skin of releiving, the performance of balance skin fat secretion, by adding iron powder, tri-iron tetroxide, infrared ceramic powder, fabric being had and launches far infrared and magnetic health care; The spinnability that spin finish aid of the present invention makes spinning melt reach good, fiber can be made without lousiness, and dyeing uniformity is good.
Description
Technical field
The present invention relates to a kind of weaving face fabric, particularly relate to a kind of ramee fabric.
Background technology
Current clothing fabric much adopts macromolecular material to make, irritant to skin, is unfavorable for health, and not only price is high but also to wear performance sometimes unsatisfactory for natural material.
String extracts from natural plants, there is moisture absorption, ventilative, environmental protection, non-stimulated feature, can be used for making clothes, home decoration etc., but string exists shortcomings such as insufficient strength is high, cracky, elasticity are good not, crease easily, need to carry out improvement in performance.
Summary of the invention
The object of the present invention is to provide a kind of health care ramee fabric and preparation method thereof, this fabric has skin of releiving, balance skin fat secretion, transmitting far infrared and magnetic health care.
Technical scheme of the present invention is as follows:
A kind of health care ramee fabric, is characterized in that being made up of the raw material of following weight portion: nano-chitosan 6-7, water 7-9, shea butter 2-3, plasticity starch 10-12,1-ethyl-3-methylimidazole acetate 60-70,1-allyl-3-methylimidazole villaumite 40-50, iron powder 2-4, tri-iron tetroxide 2-4, collagenous fiber 8-10, infrared ceramic powder 3-5, potassium acetate 2-4, ramee 70-80, cypress fiber 15-20, spin finish aid 0.2-0.4;
Described spin finish aid is made up of the raw material of following weight portion: shitosan 1-2, polyisobutene 1-2, alkyl phosphate diethanolamine salt 1-2, polyethylene glycol 1-2, alkylphenol polyoxyethylene 0.2-0.3, nanometer aluminium powder 0.1-0.2, microcrystalline cellulose 1-2, pyrophillite 7-8, water are appropriate; Preparation method is: pyrophyllite powder is broken into 300-400 order particle, adds alkylphenol polyoxyethylene, water stirs, and dispersion grinding is to 20-30 μm of slurry, and spraying dry, mixes with other residual componentss, stirs 20-30 minute, to obtain final product.
The production method of described health care ramee fabric, is characterized in that: comprise the following steps:
(1) shea butter is added to the water, under stirring, adds nano-chitosan;
(2) add plasticity starch, stir 10-15 minute, spraying dry obtains modification plasticity starch;
(3) collagenous fiber, ramee, cypress fiber powder are broken into 500-600 order fiber grain;
(4) more described fiber grain is mixed with 1-ethyl-3-methylimidazole acetate, 1-allyl-3-methylimidazole villaumite, feed double screw extruder after stirring, make spinning melt;
(5) add modification plasticity starch and other residual componentss, stir, obtain the spinning melt of modification;
(6) spinning melt of modification is carried out melt spinning, obtain spinning fibre;
(7) spinning fibre again through washing, bleaching, oil, dry, be woven into fabric and get final product.
Beneficial effect of the present invention
Fabric of the present invention has the characteristic of ramee excellence, and with the addition of cypress fiber, there is skin of releiving, the performance of balance skin fat secretion, by adding iron powder, tri-iron tetroxide, infrared ceramic powder, fabric being had and launches far infrared and magnetic health care; By adding the plasticity starch of nano-chitosan modification, adding the intensity of fiber, improve resistance to water, adding fabric drapability.The spinnability that spin finish aid of the present invention makes spinning melt reach good, fiber can be made without lousiness, and dyeing uniformity is good, and color and luster is excellent, and feel is more soft.
Detailed description of the invention
A kind of health care ramee fabric, is made up of the raw material of following weight portion (kilogram): nano-chitosan 6.5, water 8, shea butter 2.5, plasticity starch 11,1-ethyl-3-methylimidazole acetate 65,1-allyl-3-methylimidazole villaumite 45, iron powder 3, tri-iron tetroxide 3, collagenous fiber 9, infrared ceramic powder 4, potassium acetate 3, ramee 75, cypress fiber 17, spin finish aid 0.3;
Described spin finish aid is made up of the raw material of following weight portion (kilogram): shitosan 1.5, polyisobutene 1.5, alkyl phosphate diethanolamine salt 1.5, polyethylene glycol 1.5, alkylphenol polyoxyethylene 0.2, nanometer aluminium powder 0.1, microcrystalline cellulose 1.5, pyrophillite 7.5, water are appropriate; Preparation method is: pyrophyllite powder is broken into 350 order particles, adds alkylphenol polyoxyethylene, water stirs, dispersion grinding to 25 μm slurry, and spraying dry, mixes with other residual componentss, stirs 25 minutes, to obtain final product.
The production method of described health care ramee fabric, comprises the following steps:
(1) shea butter is added to the water, under stirring, adds nano-chitosan;
(2) add plasticity starch, stir 13 minutes, spraying dry obtains modification plasticity starch;
(3) collagenous fiber, ramee, cypress fiber powder are broken into 550 order fiber grains;
(4) more described fiber grain is mixed with 1-ethyl-3-methylimidazole acetate, 1-allyl-3-methylimidazole villaumite, feed double screw extruder after stirring, make spinning melt;
(5) add modification plasticity starch and other residual componentss, stir, obtain the spinning melt of modification;
(6) spinning melt of modification is carried out melt spinning, obtain spinning fibre;
(7) spinning fibre again through washing, bleaching, oil, dry, be woven into fabric and get final product.
Test data: after tested, the TENSILE STRENGTH of this fiber is 3.96cN/dtex.
Claims (2)
1. keep healthy a ramee fabric, it is characterized in that being made up of the raw material of following weight portion: nano-chitosan 6-7, water 7-9, shea butter 2-3, plasticity starch 10-12,1-ethyl-3-methylimidazole acetate 60-70,1-allyl-3-methylimidazole villaumite 40-50, iron powder 2-4, tri-iron tetroxide 2-4, collagenous fiber 8-10, infrared ceramic powder 3-5, potassium acetate 2-4, ramee 70-80, cypress fiber 15-20, spin finish aid 0.2-0.4;
Described spin finish aid is made up of the raw material of following weight portion: shitosan 1-2, polyisobutene 1-2, alkyl phosphate diethanolamine salt 1-2, polyethylene glycol 1-2, alkylphenol polyoxyethylene 0.2-0.3, nanometer aluminium powder 0.1-0.2, microcrystalline cellulose 1-2, pyrophillite 7-8, water are appropriate; Preparation method is: pyrophyllite powder is broken into 300-400 order particle, adds alkylphenol polyoxyethylene, water stirs, and dispersion grinding is to 20-30 μm of slurry, and spraying dry, mixes with other residual componentss, stirs 20-30 minute, to obtain final product.
2. the production method of health care ramee fabric according to claim 1, is characterized in that: comprise the following steps:
(1) shea butter is added to the water, under stirring, adds nano-chitosan;
(2) add plasticity starch, stir 10-15 minute, spraying dry obtains modification plasticity starch;
(3) collagenous fiber, ramee, cypress fiber powder are broken into 500-600 order fiber grain;
(4) more described fiber grain is mixed with 1-ethyl-3-methylimidazole acetate, 1-allyl-3-methylimidazole villaumite, feed double screw extruder after stirring, make spinning melt;
(5) add modification plasticity starch and other residual componentss, stir, obtain the spinning melt of modification;
(6) spinning melt of modification is carried out melt spinning, obtain spinning fibre;
(7) spinning fibre again through washing, bleaching, oil, dry, be woven into fabric and get final product.