CN103963307A - 一种用于电子行业的黑色膨体双向拉伸聚四氟乙烯膜及其制备方法 - Google Patents
一种用于电子行业的黑色膨体双向拉伸聚四氟乙烯膜及其制备方法 Download PDFInfo
- Publication number
- CN103963307A CN103963307A CN201410129661.4A CN201410129661A CN103963307A CN 103963307 A CN103963307 A CN 103963307A CN 201410129661 A CN201410129661 A CN 201410129661A CN 103963307 A CN103963307 A CN 103963307A
- Authority
- CN
- China
- Prior art keywords
- black
- film
- polyterafluoroethylene
- preparation
- biaxially
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种用于电子行业的黑色膨体双向拉伸聚四氟乙烯膜及其制备方法，包括以下步骤：混料；制坯；推压；压延；重叠脱脂处理；纵向拉伸；弧形双向拉伸；横向拉伸后烧结固化。本发明制备的黑色膨体双向拉伸聚四氟乙烯膜用于电子密封行业，其黑色聚四氟乙烯微孔膜的厚度为20um～50um，宽度为1～2m，孔隙率为80%以上，本发明用于电子设备黑色膜或密封行业，可达到良好的密封和防震，可防腐蚀，防水散热，防辐射。
Description
技术领域：
本发明涉及膜领域，更具体的说是涉及一种用于电子行业的黑色膨体双向拉伸聚四氟乙烯膜及其制备方法。
背景技术：
膨化聚四氟乙烯微孔膜经多向拉伸（即膨化处理）、压延、热处理等工艺而形成的一种多孔材料，是一种柔韧而富有弹性的微孔材料，孔隙率高时可具有透水功能，孔径分布均匀，具有杀菌、过滤功能膜，材料的表面平整、柔软，但是在扫描电镜下可以看到材料的内部存在大量0.2μm～2μm的微孔，其孔隙率可占到80%以上。这一材料具有以下特点：无危害、重量轻、耐腐蚀、耐环境变化，克服了纯聚四氟乙烯密封材料的冷流性（蠕变），该材料密封均匀、耐老化、弹性好、不会随着时间而硬化或脆化，使用温度范围从-240℃～260℃，其具有许多传统的过滤膜不具有的突出的优点，其适用性广，广泛应用于服装，家庭，医药，农业以及化工等领域。
发明内容：
本发明的目的是针对现有技术的不足之处，提供一种用于电子行业的黑色膨体双向拉伸聚四氟乙烯膜；本发明的另一目的在于提供黑色膨体双向拉伸聚四氟乙烯膜的制备方法。
为达到上述目的，本发明采取下述技术方案：
一种用于电子行业的黑色膨体双向拉伸聚四氟乙烯膜的制备方法，包括如下步骤：包括以下步骤：
（1）混料：将黑色聚四氟乙烯分散树脂粉末、烃类助挤剂和5‰～8‰染色剂三者按比例充分混合，在50℃～70℃下静置24小时，形成物料。
（2）制坯：将物料在40℃～50℃下预压成Φ120mm的圆柱形坯；
（3）推压：将圆柱形坯放置在推压机上，在55℃～60℃条件下推压成Φ20mm的圆条。
（4）压延：将圆条放置在压延机上，在50℃条件下压延成含油基带，厚度为130um～180um，宽度为20～35cm。
（5）重叠脱脂处理：将2～4层含油基带重叠合并，将含油基带在260℃～280℃下脱脂，去除助挤剂，得到脱脂基带。
（6）纵向拉伸：将脱脂基带在260℃～280℃进行第一次纵向拉伸，拉伸倍数为4～10倍后，获得纵向拉伸基础膜。
（7）弧形双向拉伸：再将纵向拉伸基础膜进行弧形双向拉伸2～5倍，得到延伸基础膜。
（8）横向拉伸后烧结固化：将延伸基础膜在拉膜机上在120℃～200℃下横向拉伸，然后在320℃～350℃烧结固化50秒，获得厚度为20～50um，宽1m～2m的黑色膨体双向拉伸聚四氟乙烯膜。
作为优选，所述黑色聚四氟乙烯分散树脂粉末的标准比重为2.15。
作为优选，所述染色剂为PTFE颜料分散液。
上述技术方案所制备得到的黑色膨体双向拉伸聚四氟乙烯膜。
本发明的有益效果在于：
本发明的黑色聚四氟乙烯微孔膜的膜的厚度为20um～50um，宽度为1m～2m，孔隙率为80%以上，用于电子设备密封或黑色膜制作，可达到良好的密封和防震，可防腐蚀，防水，散热，防辐射。
具体实施方式：
实施例1，一种用于电子行业的黑色膨体双向拉伸聚四氟乙烯膜及其制备方法，其步骤如下：将四川晨光216S黑色聚四氟乙烯分散树脂粉末（标准比重为2.15）、烃类助挤剂和5‰的瑞士寇蓝公司PTFE颜料分散液三者按比例充分混合，在50℃下静置24小时，形成物料；
（2）制坯：将物料在40℃下预压成Φ120mm的圆柱形坯；
（3）推压：将圆柱形坯放置在推压机上，在55℃条件下推压成Φ20mm的圆条；
（4）压延：将圆条放置在压延机上，在50℃条件下压延成含油基带，厚度为130um，宽度为20cm；
（5）重叠脱脂处理：将2层含油基带重叠合并，将含油基带在260℃下脱脂，去除助挤剂，得到脱脂基带；
（6）纵向拉伸：将脱脂基带在260℃进行第一次纵向拉伸，拉伸倍数为4倍后，获得纵向拉伸基础膜；
（7）弧形双向拉伸：再将纵向拉伸基础膜进行弧形双向拉伸2倍，得到延伸基础膜；
（8）横向拉伸后烧结固化：将延伸基础膜在拉膜机上在120℃下横向拉伸，然后在320℃烧结固化50秒，获得厚度为20um，宽1m的黑色膨体双向拉伸聚四氟乙烯膜。
实施例2，一种用于电子行业的黑色膨体双向拉伸聚四氟乙烯膜及其制备方法，其步骤如下：
（1）混料：将四川晨光216S黑色聚四氟乙烯分散树脂粉末（标准比重为2.15）、烃类助挤剂和8‰的瑞士寇蓝公司PTFE颜料分散液三者按比例充分混合，在60℃下静置24小时，形成物料；
（2）制坯：将物料在55℃下预压成Φ120mm的圆柱形坯；
（3）推压：将圆柱形坯放置在推压机上，在60℃条件下推压成Φ20mm的圆条；
（4）压延：将圆条放置在压延机上，在50℃条件下压延成含油基带，厚度为180um，宽度为30cm；
（5）重叠脱脂处理：将4层含油基带重叠合并，将含油基带在280℃下脱脂，去除助挤剂，得到脱脂基带；
（6）纵向拉伸：将脱脂基带在280℃进行第一次纵向拉伸，拉伸倍数为10倍后，获得纵向拉伸基础膜；
（7）弧形双向拉伸：再将纵向拉伸基础膜进行弧形双向拉伸5倍，得到延伸基础膜；
（8）横向拉伸后烧结固化：将延伸基础膜在拉膜机上在200℃下横向拉伸，然后在350℃烧结固化50秒，获得厚度为40um，宽2m的黑色膨体双向拉伸聚四氟乙烯膜。
上述实施例是对本发明进行的具体描述，只是对本发明进行进一步说明，不能理解为对本发明保护范围的限定，本领域的技术人员根据上述发明的内容作出一些非本质的改进和调整均落入本发明的保护范围之内。
Claims (4)
1.一种用于电子行业的黑色膨体双向拉伸聚四氟乙烯膜的制备方法，其特征在于：包括以下步骤：
（1）混料：将黑色聚四氟乙烯分散树脂粉末、烃类助挤剂和5‰～8‰染色剂三者按比例充分混合，在50℃～70℃下静置24小时，形成物料；
（2）制坯：将物料在40℃～50℃下预压成Φ120mm的圆柱形坯；
（3）推压：将圆柱形坯放置在推压机上，在55℃～60℃条件下推压成Φ20mm的圆条；
（4）压延：将圆条放置在压延机上，在50℃条件下压延成含油基带，厚度为130um～180um，宽度为20～35cm；
（5）重叠脱脂处理：将2～4层含油基带重叠合并，将含油基带在260℃～280℃下脱脂，去除助挤剂，得到脱脂基带；
（6）纵向拉伸：将脱脂基带在260℃～280℃进行第一次纵向拉伸，拉伸倍数为4～10倍后，获得纵向拉伸基础膜；
（7）弧形双向拉伸：再将纵向拉伸基础膜进行弧形双向拉伸2～5倍，得到延伸基础膜；
（8）横向拉伸后烧结固化：将延伸基础膜在拉膜机上在120℃～200℃下横向拉伸，然后在320℃～350℃烧结固化50秒，获得厚度为20～50um，宽1m～2m的黑色膨体双向拉伸聚四氟乙烯膜。
2.根据权利要求1所述的一种用于电子行业的黑色膨体双向拉伸聚四氟乙烯膜的制备方法，其特征在于：所述黑色聚四氟乙烯分散树脂粉末的标准比重为2.15。
3.根据权利要求1所述的一种用于电子行业的黑色膨体双向拉伸聚四氟乙烯膜的制备方法，其特征在于：所述染色剂为PTFE颜料分散液。
4.权利要求1所述的一种用于电子行业的黑色膨体双向拉伸聚四氟乙烯膜的制备方法所制备得到的黑色膨体双向拉伸聚四氟乙烯膜。