CN103953179A - Laminating method of hot melt adhesive wall cloth - Google Patents
Laminating method of hot melt adhesive wall cloth Download PDFInfo
- Publication number
- CN103953179A CN103953179A CN201410215195.1A CN201410215195A CN103953179A CN 103953179 A CN103953179 A CN 103953179A CN 201410215195 A CN201410215195 A CN 201410215195A CN 103953179 A CN103953179 A CN 103953179A
- Authority
- CN
- China
- Prior art keywords
- hot melt
- wall paper
- metope
- wall cloth
- melt adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a laminating method of hot melt adhesive wall cloth. The method comprises the steps of metope treatment, wall cloth cutting, wall cloth pre-hanging, hot pressing laminating and the like, and is characterized in that a household iron is used to press and laminate the hot melt adhesive wall cloth compounded with a hot melt adhesive net film at the back at a certain speed, the construction is simple, and the indoor decoration environmental protection problem caused by blistering, swelling and hindering of volatilization of volatiles due to impermeability of the wall cloth because of the unique permeability of the net film is solved.
Description
Technical field
The invention discloses a kind of applying method of hot melt viscosity wall paper, particularly a kind of applying method of indoor decoration hot melt viscosity wall paper.
Background technology
The existing wall paper construction in interior decoration field, has two kinds of methods of cold laminating and thermal-adhering.Cold applying method time need to first brush one deck adhesive because of laminating on metope or wall paper, manual brush irregular, directly cause the quality of laminating, be coated with many and can have penetrated wall paper, painting has been lacked bonding not firm, has the series of problems such as foaming bulge phenomenon and glue needs are natural drying, the environmental protection of glue simultaneously.And thermal-adhering can address the above problem, make the laminating of wall paper become simple.
Existing published hot sticking method, as Chinese invention patent CN200710079628.5 has proposed a kind of applying method of breadth textile wall paper, the method is coated hot-melt adhesive in the time of thermal-adhering, be by scraper by the PUR blade coating melting the membranoid substance to moulding in release liners, there is no gas permeability, and low, the molten finger of hot-melt adhesive fusing point is high, the open hour are long owing to using as thermal-adhering, must carry out blade coating production as the base of film by release liners, return sticky problem to solve rolling.Chinese invention patent CN200710079628.5 has proposed the adhesive-bonded fabric that a kind of surface is meldable fibre, but only uses as the bonding intermediate of two-layer fabrics, is not used for directly and metope laminating.Can produce thus following defect:
(1) air-locked glued membrane is unfavorable for distributing of moisture residual in body of wall and unwanted volatile matter;
(2) because of airtight, when laminating, also have bubble and bulge phenomenon, and can address this problem thoroughly with ventilative nethike embrane, make the surface more smooth of wall paper attractive in appearance;
(3) because being subject to the restriction of device for coating and release liners fabric width, the general fabric width with release liners glued membrane in market is 1.0 meters, with fabric width be the wall paper fabric compound tense of 3.0 meters, need to splice with three width glued membranes.When splicing, easily produce dislocation, cause slot and the defect such as overlapping, thereby directly affect and the laminating quality of metope.
Chinese invention patent CN201010288731.2 has also proposed a kind of applying method of wall paper, has equally above-mentioned defect.
In order to overcome above-mentioned defect, the present invention proposes a kind of back side and be compounded with the applying method of the hot melt viscosity wall paper of hot-melt adhesive film.
Summary of the invention
The object of the present invention is to provide a kind of applying method of hot melt adhesion wall paper, by using a kind of back side to be compounded with the hot melt viscosity wall paper of hot-melt adhesive film, make construction simple, solve the interior decoration environmental issue that the volatilization of volatilizable thing in the airtight foaming causing of wall paper, bulge and obstruction body of wall causes simultaneously.
An applying method for hot melt adhesion wall paper, is characterized in that comprising the following steps:
(1) carry out dust removal processing with the metope that dust catcher is decorated wish, and cut the hot melt viscosity wall paper of same size by this metope size;
(2) the hot melt adhesion wall paper steel nail cutting is temporarily fixed on to above-mentioned metope, then with the family expenses flatiron that is heated to 90-160 DEG C, under manual pressure, the hot melt adhesion wall paper that is layed onto in advance metope is pressurizeed, and press certain direction with 0.20-0.50 m
2the speed of/min moves flatiron, until all hot melt adhesion wall papers and metope good bond;
Described hot melt viscosity wall paper refer in particular to envers be compounded with hot melt net, fabric width be no more than 4 meters, as decorative material for wall surface use fabric; The grammes per square metre of described hot melt net is 30-80g/m
2, be with molten finger be that 100-300g/10min/160 DEG C, fusing point are that EVA PUR spray after hot melt of 60-80 DEG C forms.
The present invention by use a kind of back side be compounded with hot-melt adhesive film hot melt viscosity wall paper, the method that just can fit with family expenses flatiron, make construction simple, simultaneously because of the distinctive gas permeability of nethike embrane, solve the interior decoration environmental issue that the volatilization of volatilizable thing in the airtight foaming causing of wall paper, bulge and obstruction body of wall causes.
With specific embodiment, the present invention is conducted further description below.
Specific embodiment
Step of the present invention by metope processing, cut wall paper, pre-hung wall paper, hot pressing and be sticked to form.
Described metope processing, refers to and metope is carried out to dust removal processing with dust catcher, to prevent that dust from affecting the bonding effect of hot melt adhesion wall paper.
The described wall paper that cuts, refers to by decorative effect needs, cuts and decorative zones hot melt viscosity of a size wall paper.
Described pre-hung wall paper, refers to that a hot melt adhesion wall paper steel nail cutting or other materials, method are temporarily fixed on the metope corresponding with construction area.
Described hot pressing laminating, refers to the household electric iron at 1 ~ 2KW with power, and temperature adjustment shelves are set between wool and fiber crops, are warmed up to 90 ~ 160 DEG C, to the hot melt adhesion wall paper that pre-fixes construction area from top to bottom, and from left to right, and with 0.2 ~ 0.5m
2the speed of/min is carried out the mobile pressurization of craft, the nethike embrane gum of hot melt adhesion wall paper is melted, the adhesion stress of generation and body of wall.
embodiment 1
Embodiment 1 carries out in laboratory.
Metope processing: make the imitative metope of 500mm × 500 mm with interior decoration fiberboard, and apply the white cement of a layer thickness 1mm on fiberboard surface, with dust catcher, imitative metope is carried out to dust removal processing after being dried.
Cut wall paper: by the size of 250mm × 250mm, cutting fabric grammes per square metre is 165 g/m with cutter
2jacquard fabric and the back side are compounded with 30 g/m
2the hot melt viscosity wall paper of EVA nethike embrane.
Pre-hung wall paper: the 250mm × 250mm hot melt viscosity wall paper cutting is faced to the mode of wall by nethike embrane, pre-fixed and imitate metope zone line with steel nail.
Hot pressing laminating: be the household electric iron of 1.0 KW with power, temperature adjustment shelves are set in " cotton " gear, after constant temperature, presses from top to bottom, and program from left to right, with 0.2m
2the speed of/min, carries out the mobile pressurization of craft to the hot melt viscosity wall paper pre-fixing on imitative metope, and the nethike embrane gum of hot melt viscosity wall paper is melted, and adheres on body of wall.
embodiment 2
Embodiment 2 carries out at actual indoor wall.
Metope processing: be 2.7m to indoor height, the wide smooth metope for 3.5m carries out dust removal process with dust catcher.
Cut wall paper: selecting fabric fabric width is that 3 meters, grammes per square metre are 165 g/m
2and the back side is compounded with 80 g/m
2the jacquard fabric hot melt viscosity wall paper of EVA nethike embrane cuts.Cutting method is: the short transverse of the fabric width direction of hot melt viscosity wall paper to body of wall, cuts out 2.7m × 3.5m size for subsequent use.
Pre-hung wall paper: by the hot melt adhesion wall paper cutting by nethike embrane in the face of wall, the mode of width to height, pre-fixes construction metope with steel nail.
Hot pressing laminating: be the household electric iron of 2.0 KW with power, temperature adjustment shelves are set in " fiber crops " gear, arrives after constant temperature, presses from top to bottom, and program from left to right, with 0.5m
2the speed of/min, carries out the mobile pressurization of craft to the hot melt viscosity wall paper pre-fixing on metope, and the nethike embrane gum of hot melt viscosity wall paper is melted, and adheres on body of wall.
Claims (2)
1. an applying method for hot melt adhesion wall paper, is characterized in that comprising the following steps:
Carry out dust removal processing with the metope that dust catcher is decorated wish, and cut the hot melt viscosity wall paper of same size by this metope size;
The hot melt adhesion wall paper steel nail cutting is temporarily fixed on to above-mentioned metope, then, with the family expenses flatiron that is heated to 90-160 DEG C, under manual pressure, the hot melt adhesion wall paper that is layed onto in advance metope is pressurizeed, and press certain direction with 0.20-0.50 m
2the speed of/min moves flatiron, until all hot melt adhesion wall papers and metope good bond;
Described hot melt viscosity wall paper refer in particular to envers be compounded with hot melt net, fabric width be no more than 4 meters, as decorative material for wall surface use fabric; The grammes per square metre of described hot melt net is 30-80g/m
2, be with molten finger be that 100-300g/10min/160 DEG C, fusing point are that EVA PUR spray after hot melt of 60-80 DEG C forms.
2. the applying method of hot melt adhesion wall paper according to claim 1, is characterized in that: the power of described family expenses flatiron is 1.0-2.0KW.