CN103952080B - A kind of plant type environmental protection coating and preparation method thereof - Google Patents
A kind of plant type environmental protection coating and preparation method thereof Download PDFInfo
- Publication number
- CN103952080B CN103952080B CN201410217051.XA CN201410217051A CN103952080B CN 103952080 B CN103952080 B CN 103952080B CN 201410217051 A CN201410217051 A CN 201410217051A CN 103952080 B CN103952080 B CN 103952080B
- Authority
- CN
- China
- Prior art keywords
- environmental protection
- cocos nucifera
- protection coating
- plant type
- defoamer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a kind of plant type environmental protection coating and preparation method thereof, the raw material components of this coating and the parts by weight of each component are: cocos nucifera oil elite 0.1～0.2 part, Petiolus Trachycarpi oil 0.5～1 part, deionized water 25～30 parts, titanium dioxide 15～20 parts, Pulvis Talci 20～25 parts, Paris white 20～25 parts, auxiliary agent 6.5～10 parts；The method comprises the steps: that deionized water, titanium dioxide, Paris white, Pulvis Talci, the propylene glycol of 2/3 and the defoamer of 2/3 are joined in dispersion tank by proportioning by (1) and stirs, it is thus achieved that slip；(2) slip ground and stir；(3) adding cocos nucifera oil elite, Petiolus Trachycarpi oil, propylene glycol and remaining defoamer and levelling agent, mix homogeneously obtains finished product.This coating is without harmful substances such as formaldehyde, benzene class thing, heavy metals, there is the features such as ultra-fine greasy, plentiful, the strong covering power of film quality, and there is antibacterial, the fungicidal properties of natural excellence, can airtight execution, without poisonous and harmful volatile substance, it is ensured that health.
Description
Technical field
The invention belongs to technical field of coatings, especially a kind of plant type environmental protection coating and preparation method thereof.
Background technology
Along with the raising of modern people's living standard, the Environmental Protection Level of fitment material for family is required more and more higher.Existing decoration coating type is various, and is meeting the market requirement, and the R & D Level of environmental protection coating material is also being improved constantly by coating material production producer, but, existing environmental protection coating material is not very perfect, as only the index of volatile matter reduced the standard of complying with.Although the development trend of coating industry is to reach the coating of Diamond Search, tasteless health, but owing to being limited to the factors such as technology, on the market almost without the environmental protection coating material of real Diamond Search, some harmful substances (such as formaldehyde, benzene class thing, heavy metal etc.) wherein contained can have a strong impact on the living environment of people, and induce many chronic diseases, cause that the life and health of people is on the hazard.
Summary of the invention
It is an object of the invention to overcome the deficiencies in the prior art, it is provided that a kind of plant type environmental protection coating and preparation method thereof, solve the problem that existing coating contains the harmful substance crisis health such as formaldehyde, benzene class thing.
This invention address that existing technical problem is that takes techniques below scheme to realize:
A kind of plant type environmental protection coating, the parts by weight of its raw material components and each component are:
And, described cocos nucifera oil elite adopts following preparation method to obtain:
(1) by coconut palm skin clear water rinsed clean, by following weight ratio: the coconut palm skin cleaned up 1 part and 4 parts of mix homogeneously of hardening bath, coconut palm skin is fully immersed in hardening bath, soaks 12～15 hours, make coconut palm skin harden；
(2) coconut palm skin is pulled out after terminating by immersion from hardening bath, squeezes with roller squeezer, it is thus achieved that the mixed liquor of coconut palm skin slag, cocos nucifera oil and water；
(3) being filtered by mixed liquor, remove coconut palm skin slag, the mixed liquor obtaining the mixed liquor of cocos nucifera oil and water, cocos nucifera oil and water filters through 80～120 mesh filter screens, and the filtrate obtained is centrifugal treating under 15000～18000r/min rotating speed, and extracting centrifugal liquid obtains cocos nucifera oil；
(4) cocos nucifera oil of gained is preserved more than 5 days at 3 DEG C～7 DEG C, take filtrate after filtration and obtain cocos nucifera oil elite.
And, the raw material components of described hardening bath and the parts by weight of each component are:
And, described auxiliary agent is made up of propylene glycol, defoamer and levelling agent, and the weight proportion between propylene glycol, defoamer, levelling agent is: 5～7:1～2:0.5～1.
And, described defoamer is 7134 defoamer.
And, described levelling agent is 003 levelling agent.
The preparation method of a kind of plant type environmental protection coating, comprises the following steps:
(1) deionized water, titanium dioxide, Paris white, Pulvis Talci, the propylene glycol of 2/3 and the defoamer of 2/3 joined in dispersion tank by proportioning and stir, it is thus achieved that slip；
(2) slip is ground to the fineness of 30 μm, and stirs under the speed of 200r/min；
(3) add cocos nucifera oil elite, Petiolus Trachycarpi oil, propylene glycol, surplus defoamer and surplus levelling agent, mixing and stirring, obtain plant type environmental protection coating.
Advantages of the present invention and having the benefit effect that
This plant type environmental protection coating adopts cocos nucifera oil elite, Petiolus Trachycarpi oil, deionized water, titanium dioxide, Pulvis Talci, Paris white and auxiliary agent as raw material; and prepare the plant type environmental protection coating without harmful substances such as formaldehyde, benzene class thing, heavy metals; there is the features such as ultra-fine greasy, plentiful, the strong covering power of film quality; simultaneously; also there is antibacterial, the fungicidal properties of natural excellence, can airtight execution, without poisonous and harmful volatile substance; ensure that health, be conducive to environmental conservation.Meanwhile, the preparation method of this coating is simple, can be widely used for industrialization and produces.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is further described.
Embodiment 1:
A kind of plant type environmental protection coating, the weight ratio of its raw material components and each component is: cocos nucifera oil elite 0.1%, Petiolus Trachycarpi oil 0.5%, titanium dioxide 18%, Paris white 24%, Pulvis Talci 22%, deionized water 28%, propylene glycol 5.9%, defoamer 1%, levelling agent 0.5%.
Petiolus Trachycarpi oil in above-mentioned raw materials is obtained by public offering on the market, for instance Hubei Xin Ying combination company limited.
Propylene glycol in above-mentioned raw materials, defoamer and levelling agent composition auxiliary agent, defoamer can adopt 7134 defoamer, public offering on the market obtain, for instance Foochow angstrom enlightening specialization Science and Technology Ltd.；Levelling agent can adopt 003 levelling agent, public offering on the market obtain, for instance Chemical Industry Science Co., Ltd is won in Guangzhou.
Cocos nucifera oil elite in above-mentioned raw materials adopts following preparation method to obtain:
(1) by coconut palm skin clear water rinsed clean, by following weight ratio: the coconut palm skin cleaned up 1 part and 4 parts of mix homogeneously of hardening bath, coconut palm skin is fully immersed in hardening bath, coconut palm skin is fully immersed in hardening bath, soak 13 hours, make coconut palm skin harden.
In this step, hardening bath is made up of the component of following weight proportion: water 99.2%, sodium benzoate 0.2%, anhydrous calcium chloride 0.55%, sodium sulfite 0.05%.
(2) coconut palm skin is pulled out after terminating by immersion from hardening bath, squeezes with roller squeezer, it is thus achieved that the mixed liquor of coconut palm skin slag, cocos nucifera oil and water；
(3) being filtered by mixed liquor, remove coconut palm skin slag, the mixed liquor obtaining the mixed liquor of cocos nucifera oil and water, cocos nucifera oil and water filters through 120 mesh filter screens, and the filtrate obtained is centrifugal under 16000r/min rotating speed, and extracting centrifugal liquid obtains cocos nucifera oil；
(4) cocos nucifera oil of gained is preserved 7 days at 6 DEG C, take filtrate after filtration, namely obtain cocos nucifera oil elite.
The preparation method of this plant type environmental protection coating, comprises the following steps:
1,280g deionized water, 39g propylene glycol, 7g7134 defoamer, 180 titanium dioxides, 240g Paris white, 220g Pulvis Talci are added stirring in dispersion tank, it is thus achieved that slip；
2, the slip after dispersion is ground to the fineness of 30 μm, and stirs under the speed of 200r/min；
3, add 1g cocos nucifera oil elite, 5g Petiolus Trachycarpi oil, 20g propylene glycol, 3g7134 defoamer, 5g003 levelling agent, mix to uniformly, just obtain the plant type environmental protection coating of the present invention.
Embodiment 2
A kind of plant type environmental protection coating, the weight ratio of its raw material components and each component is: cocos nucifera oil elite 0.2%, Petiolus Trachycarpi oil 0.8%, titanium dioxide 19%, Paris white 21%, Pulvis Talci 20%, deionized water 30%, propylene glycol 7%, 7134 defoamer 1.2%, 003 levelling agent 0.8%.
Wherein, cocos nucifera oil elite preparation method is identical with the cocos nucifera oil elite preparation method in embodiment 1, no longer repeats at this.
The preparation method of above-mentioned plant type environmental protection coating, comprises the following steps:
1,300g deionized water, 47g propylene glycol, the defoamer of 8g, 190g titanium dioxide, 210g Paris white, 200g Pulvis Talci are added stirring in dispersion tank, it is thus achieved that slip；
2, the slip after dispersion is ground to the fineness of 30 μm, and stirs under the speed of 200r/min；
3, add 2g cocos nucifera oil elite, 8g Petiolus Trachycarpi oil, 23g propylene glycol, 4g7134 defoamer, 8g003 levelling agent, mix to uniformly, just obtain the plant type environmental protection coating of the present invention.
The plant type environmental protection coating of the present invention is pure natural water paint.
It is emphasized that; embodiment of the present invention is illustrative; rather than it is determinate; therefore the present invention includes the embodiment that is not limited to described in detailed description of the invention; every other embodiments drawn according to technical scheme by those skilled in the art, also belong to the scope of protection of the invention.
Claims (6)
1. a plant type environmental protection coating, it is characterised in that the parts by weight of its raw material components and each component are:
Described cocos nucifera oil elite adopts following preparation method to obtain:
(1), by coconut palm skin clear water rinsed clean, by following weight ratio: the coconut palm skin cleaned up 1 part and 4 parts of mix homogeneously of hardening bath, coconut palm skin is fully immersed in hardening bath, soaks 12～15 hours, make coconut palm skin harden；
(2) soak and after terminating, coconut palm skin is pulled out from hardening bath, squeeze with roller squeezer, it is thus achieved that the mixed liquor of coconut palm skin slag, cocos nucifera oil and water；
(3) being filtered by mixed liquor, remove coconut palm skin slag, the mixed liquor obtaining the mixed liquor of cocos nucifera oil and water, cocos nucifera oil and water filters through 80～120 mesh filter screens, and the filtrate obtained is centrifugal treating under 15000～18000r/min rotating speed, and extracting centrifugal liquid obtains cocos nucifera oil；
(4) the cocos nucifera oil of gained is preserved more than 5 days at 3 DEG C～7 DEG C, take filtrate after filtration and obtain cocos nucifera oil elite.
2. a kind of plant type environmental protection coating according to claim 1, it is characterised in that: the raw material components of described hardening bath and the parts by weight of each component are:
3. a kind of plant type environmental protection coating according to any one of claim 1 to 2, it is characterised in that: described auxiliary agent is made up of propylene glycol, defoamer and levelling agent, and the weight proportion between propylene glycol, defoamer, levelling agent is: 5～7:1～2:0.5～1.
4. a kind of plant type environmental protection coating according to claim 3, it is characterised in that: described defoamer is 7134 defoamer.
5. a kind of plant type environmental protection coating according to claim 3, it is characterised in that: described levelling agent is 003 levelling agent.
6. the preparation method of plant type environmental protection coating as described in any one of claim 1 to 5, it is characterised in that comprise the following steps:
(1) deionized water, titanium dioxide, Paris white, Pulvis Talci, the propylene glycol of 2/3 and the defoamer of 2/3 joined in dispersion tank by proportioning and stir, it is thus achieved that slip；
(2) slip is ground to the fineness of 30 μm, and stirs under the speed of 200r/min；
(3) add cocos nucifera oil elite, Petiolus Trachycarpi oil, the propylene glycol of surplus, surplus defoamer and levelling agent, mixing and stirring, obtain plant type environmental protection coating.