CN103951922B - Acrylate timing belt - Google Patents
Acrylate timing belt Download PDFInfo
- Publication number
- CN103951922B CN103951922B CN201410143365.XA CN201410143365A CN103951922B CN 103951922 B CN103951922 B CN 103951922B CN 201410143365 A CN201410143365 A CN 201410143365A CN 103951922 B CN103951922 B CN 103951922B
- Authority
- CN
- China
- Prior art keywords
- parts
- timing belt
- acrylate
- band tooth
- band
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention belongs to the technical field of Timing Belt for Automobile, refers in particular to a kind of acrylate timing belt, is made up of the band back of the body, infantees, band tooth, core rope, the band tooth is made up of following parts by weight of component：70 80 parts of ACM, 30 20 parts of butadiene rubber, 0.5 2 parts of stearic acid, 14 parts of age resistor, 40 68 parts of high abrasion furnace black, 3-8 parts of odium stearate, 0.1-3 part of potassium stearate, 0.1-2 part of vulcanizing agent, 0.1-2 part of antiscorching agent；The present invention can adapt to various weather, and high temperature resistant, resistance to ozone, oil resistant, elongation be small, resistance to flexion, anti-wear performance are good, service life length, has a extensive future.
Description
Technical field
The invention belongs to the technical field of Timing Belt for Automobile, refers in particular to a kind of acrylate timing belt.
Background technology
Existing automobile synchronous belt is too high using HNBR production costs, it is therefore necessary to give because the requirement to temperature is too high
To improve.
The content of the invention
It is an object of the invention to provide a kind of low cost, various weather are adapted to, high temperature resistant, resistance to ozone, oil resistant, elongation be small,
Resistance to flexion, anti-wear performance are good, service life length, the automobile using acrylate timing belt having a extensive future.
The object of the present invention is achieved like this：
Acrylate timing belt, it is made up of the band back of the body, infantees, band tooth, core rope, the band tooth is by following parts by weight of component system
Into：
ACM 70-80 parts, butadiene rubber 30-20 parts,
Stearic acid 0.5-2 parts, age resistor 1-4 parts,
High abrasion furnace black 40-68 parts, 3-8 parts of odium stearate,
0.1-3 part of potassium stearate, 0.1-2 part of vulcanizing agent,
0.1-2 part of antiscorching agent.
Preferably, the band tooth is made up of following parts by weight of component：
75 parts of ACM, 25 parts of butadiene rubber,
1.25 parts of stearic acid, 2.5 parts of age resistor,
54 parts of high abrasion furnace black, 5.5 parts of odium stearate,
1.55 parts of potassium stearate, 1.05 parts of vulcanizing agent,
1.05 parts of antiscorching agent.
Preferably, the vulcanizing agent is in sulphur, organic sulfur compound, peroxide, metal oxide, benzoquinones, amine
One or more kinds of mixtures.
Preferably, the antiscorching agent is C14H15O2NS (anti-scorching agent CTP).
Preferably, the age resistor is C15H15N (antioxidant BLE).
The present invention is prominent and beneficial compared with prior art to be had the technical effect that：
The present invention can adapt to various weather, and high temperature resistant, resistance to ozone, oil resistant, elongation be small, resistance to flexion, anti-wear performance are good, makes
With long lifespan, have a extensive future.
Embodiment
Embodiment 1, acrylate timing belt, it is made up of the band back of the body, infantees, band tooth, core rope, the band tooth is by following parts by weight
Component is made：
70 parts of ACM, 30 parts of butadiene rubber,
0.5 part of stearic acid, 1 part of age resistor,
40 parts of high abrasion furnace black, 3 parts of odium stearate,
0.1 part of potassium stearate, 0.1 part of vulcanizing agent,
0.1 part of antiscorching agent.
Preferably, the vulcanizing agent is in sulphur, organic sulfur compound, peroxide, metal oxide, benzoquinones, amine
One or more kinds of mixtures.
Preferably, the antiscorching agent is C14H15O2NS。
Preferably, the age resistor is C15H15N。
Embodiment 2, the present embodiment is substantially the same manner as Example 1, and its difference is,
The band tooth is made up of following parts by weight of component：
75 parts of ACM, 25 parts of butadiene rubber,
1.25 parts of stearic acid, 2.5 parts of age resistor,
54 parts of high abrasion furnace black, 5.5 parts of odium stearate,
1.55 parts of potassium stearate, 1.05 parts of vulcanizing agent,
1.05 parts of antiscorching agent.
Embodiment 3, the present embodiment is substantially the same manner as Example 1, and its difference is,
The band tooth of acrylate timing belt is made up of following parts by weight of component：
80 parts of ACM, 20 parts of butadiene rubber,
2 parts of stearic acid, 4 parts of age resistor,
68 parts of high abrasion furnace black, 38 parts of odium stearate,
3 parts of potassium stearate, 2 parts of vulcanizing agent,
2 parts of antiscorching agent.
As shown in table 1, after testing, it is better than using the overall performance of acrylate timing belt made from the present embodiment 1,2,3
Like product（Acrylate timing belt and neoprene timing belt of the prior art）, overall performance holds with hydrogenated butyronitrile timing belt
It is flat, however, the cost that acrylate timing belt is manufactured using this formula is more much lower than hydrogenated butyronitrile timing belt so that product
Competitive advantage becomes apparent.
| Title | It is heat-resisting | Resistance to ozone |
| Acrylate timing belt | 150℃ | It is excellent |
| Neoprene timing belt | 100℃ | It is good |
| Hydrogenated butyronitrile timing belt | 150℃ | It is excellent |
Table 1
Above-described embodiment is only presently preferred embodiments of the present invention, is not limited the scope of the invention according to this, therefore：It is all according to
The equivalence changes that structure, shape, the principle of the present invention is done, all should be covered by within protection scope of the present invention.
Claims (3)
1. acrylate timing belt, it is made up of the band back of the body, infantees, band tooth, core rope, it is characterised in that the band tooth is by following weight
Part component is made：
The antiscorching agent is C14H15O2NS；
The age resistor is C15H15N。
2. acrylate timing belt according to claim 1, it is characterised in that：The band tooth is by following parts by weight of component system
Into：
3. acrylate timing belt according to claim 1, it is characterised in that：The vulcanizing agent is sulphur, organic sulfide
Mixture more than one or both of thing, peroxide, metal oxide, benzoquinones, amine.