CN103936365A - 一种含有尼龙纤维的防水抗裂砂浆 - Google Patents
一种含有尼龙纤维的防水抗裂砂浆 Download PDFInfo
- Publication number
- CN103936365A CN103936365A CN201410120373.2A CN201410120373A CN103936365A CN 103936365 A CN103936365 A CN 103936365A CN 201410120373 A CN201410120373 A CN 201410120373A CN 103936365 A CN103936365 A CN 103936365A
- Authority
- CN
- China
- Prior art keywords
- parts
- nylon fiber
- powder
- waterproof anti
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种含有尼龙纤维的防水抗裂砂浆,其是由下述重量份的原料制得:尼龙纤维2-4,仲醇聚氧乙烯醚0.3-0.5,环氧硬脂酸辛酯1-2,硅酸盐水泥80-90,硅灰石粉5-8,羟丙基甲基纤维素醚4-6、氯化钙1-2、尿素1-2、六偏磷酸钠1-2、可分散性乳胶粉7-12,脱硫石膏7-12、玻化微珠70-85、硅酸铝1-2、甲酸钙1-2,葡萄糖酸钠1-2,氯化石蜡1-2,浓度为15-20%的双氧水7-9,填充料8-12,氧化石蜡皂0.1-0.2,适量水。
Description
技术领域
本发明涉及保温砂浆领域,确切地说是一种含有尼龙纤维的防水抗裂砂浆。
背景技术
保温砂浆是指由阻隔型保温材料和砂浆材料混合而成的,用于构筑建筑表面保温层的一种建筑材料。
尼龙(Nylon)纤维学名为聚酰胺(polyamide)纤维﹐其原为杜邦公司所生产之聚己二酰己二胺之商品名﹐即一般[1]通称为尼龙六六(Nylon66)。聚酰胺纤维是第一个合成高分子聚合物商业化之合成纤维制品﹐其为在1937年由美国杜邦公司卡罗瑟斯(Caarothers)研究发明聚六甲基己二酰胺(即尼龙六六酰)﹐因而开启了合成纤维的第一页﹐其至今仍是聚酰胺纤维的代表。
发明内容
本发明的目的在于提供一种含有尼龙纤维的防水抗裂砂浆。
上述目的通过以下方案实现:
一种含有尼龙纤维的防水抗裂砂浆,其特征在于:其是由下述重量份的原料制得:尼龙纤维2-4,仲醇聚氧乙烯醚0.3-0.5,环氧硬脂酸辛酯1-2,硅酸盐水泥80-90,硅灰石粉5-8,羟丙基甲基纤维素醚4-6、氯化钙1-2、尿素1-2、六偏磷酸钠1-2、可分散性乳胶粉7-12,脱硫石膏7-12、玻化微珠70-85、硅酸铝1-2、甲酸钙1-2,葡萄糖酸钠1-2,氯化石蜡1-2,浓度为15-20%的双氧水7-9,填充料8-12,氧化石蜡皂0.1-0.2,适量水;
填充料由下列重量份的原料制成:硅藻土18-22、膨胀蛭石粉10-15,萤石矿渣粉5-8,环氧大豆油1-2,氮化铝粉末2-4、脂肪醇聚氧乙烯醚1-2,硅烷偶联剂KH5501.5-3,丙烯酸丁酯2-4,重钙粉1-2,3-氨丙基三甲氧基硅烷2-3、二缩三丙二醇二丙烯酸酯2-3、硬脂酸1-2;
填充料的制备方法是将硅藻土、膨胀蛭石粉、萤石矿渣粉混匀,放入煅烧炉中在600-700℃下煅烧2-3小时,冷却,放入10-12%氢氧化钠溶液中浸泡5-7小时,过滤取出,去离子水洗涤,烘干,再与其它剩余原料混合均匀后,即得。
所述的一种含有尼龙纤维的防水抗裂砂浆,其特征在于:
制备方法为:
将全部原料混匀后,300-380转/分钟匀速搅拌20-25分钟,包装后即得。
本发明的有益效果为:本发明防水抗裂效果好,加入双氧水,是的本发明微膨胀,保温性能优异,容重低。
具体实施方式
一种含有尼龙纤维的防水抗裂砂浆,其是由下述重量kg的原料制得:尼龙纤维4,仲醇聚氧乙烯醚0.5,环氧硬脂酸辛酯2,硅酸盐水泥85,硅灰石粉8,羟丙基甲基纤维素醚6、氯化钙2、尿素2、六偏磷酸钠2、可分散性乳胶粉12,脱硫石膏12、玻化微珠85、硅酸铝2、甲酸钙2,葡萄糖酸钠2,氯化石蜡1,浓度为15-20%的双氧水9,填充料12,氧化石蜡皂0.2,适量水;
填充料由下列重量kg的原料制成:硅藻土22、膨胀蛭石粉15,萤石矿渣粉8,环氧大豆油2,氮化铝粉末4、脂肪醇聚氧乙烯醚2,硅烷偶联剂KH5501.8,丙烯酸丁酯4,重钙粉2,3-氨丙基三甲氧基硅烷2.5、二缩三丙二醇二丙烯酸酯3、硬脂酸2;
填充料的制备方法是将硅藻土、膨胀蛭石粉、萤石矿渣粉混匀,放入煅烧炉中在700℃下煅烧3小时,冷却,放入12%氢氧化钠溶液中浸泡7小时,过滤取出,去离子水洗涤,烘干,再与其它剩余原料混合均匀后,即得。
所述的一种含有尼龙纤维的防水抗裂砂浆,制备方法为:
将全部原料混匀后,380转/分钟匀速搅拌25分钟,包装后即得。
所得产品测试结果如下:
Claims (2)
1.一种含有尼龙纤维的防水抗裂砂浆,其特征在于:其是由下述重量份的原料制得:尼龙纤维2-4,仲醇聚氧乙烯醚0.3-0.5,环氧硬脂酸辛酯1-2,硅酸盐水泥80-90,硅灰石粉5-8,羟丙基甲基纤维素醚4-6、氯化钙1-2、尿素1-2、六偏磷酸钠 1-2、可分散性乳胶粉 7-12,脱硫石膏7-12、玻化微珠70-85、硅酸铝1-2、甲酸钙1-2,葡萄糖酸钠1-2,氯化石蜡1-2,浓度为15-20%的双氧水7-9,填充料8-12,氧化石蜡皂0.1-0.2,适量水;
填充料由下列重量份的原料制成:硅藻土18-22、膨胀蛭石粉10-15,萤石矿渣粉5-8,环氧大豆油1-2,氮化铝粉末2-4、脂肪醇聚氧乙烯醚1-2,硅烷偶联剂KH550 1.5-3,丙烯酸丁酯2-4,重钙粉1-2,3-氨丙基三甲氧基硅烷2-3、二缩三丙二醇二丙烯酸酯2-3、硬脂酸1-2;
填充料的制备方法是将硅藻土、膨胀蛭石粉、萤石矿渣粉混匀,放入煅烧炉中在600-700℃下煅烧2-3小时,冷却,放入10-12%氢氧化钠溶液中浸泡5-7小时,过滤取出,去离子水洗涤,烘干,再与其它剩余原料混合均匀后,即得。
2.根据权利要求1所述的一种含有尼龙纤维的防水抗裂砂浆,其特征在于:
制备方法为:
将全部原料混匀后,300-380转/分钟匀速搅拌20-25分钟,包装后即得。