CN103928545A - 模块式太阳能电池板及成型方法 - Google Patents
模块式太阳能电池板及成型方法 Download PDFInfo
- Publication number
- CN103928545A CN103928545A CN201410173258.1A CN201410173258A CN103928545A CN 103928545 A CN103928545 A CN 103928545A CN 201410173258 A CN201410173258 A CN 201410173258A CN 103928545 A CN103928545 A CN 103928545A
- Authority
- CN
- China
- Prior art keywords
- cell panel
- pvc
- modular
- energy cell
- solar energy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种模块式太阳能电池板及成型方法，包括太阳能芯片，所述太阳能芯片位于硬PVC壳腔内，PVC糊料密封包覆在太阳能芯片上且硬PVC壳腔被PVC糊料密封填充构成浇注式太阳能电池模块，多块浇注式太阳能电池模块间串联或并联或串并联构成模块式太阳能电池板。优点：一是采用PVC糊作为太阳能芯片模芯密封的成形材料，不仅具有良好的耐紫外线、耐低温、耐候性，而且阻燃达到V-1至V-0级；二是可以根据用户的不同需求用模块式太阳能电池板成形所需太阳能板的外形，不仅从根本上改变了本领域技术人员常期以来认为PVC糊料不能作为太阳能电池密封成形材料的技术偏见，不能随实际的地形地貌分布采光发电的技术偏见；三是由于本申请模块式太阳能电池板既能收卷携带，又能根据所遇的地形地貌展开采光发电，因此它既能随人用于陆地采光发电，也能随船浮在湖中或海洋面上发光。
Description
技术领域
本发明涉及一种既便于携带安装、使用，又能随时收拢存放，同时又具有优异的耐候性、密封性和浮动性或刚性的模块式太阳能电池板及成型方法，属太阳能电池板制造领域。
背景技术
1、CN 102694043A、名称“太阳能电池板”，它包括包括太阳能电池片，其上表面和下表面均铺设有一层乙烯-醋酸乙烯共聚物。其特点是在所述太阳能电池片上表面的乙烯-醋酸乙烯共聚物之上有聚全氟乙丙烯膜，在所述太阳能电池片下表面的乙烯-醋酸乙烯共聚物之下有玻璃钢加强面板。所述太阳能电池板四周边缘采用密封胶条密封。这种太阳能电池板重量轻，容易搬运和安装。
2、CN102376791A、名称“太阳能电池板”，该太阳能电池板包括：多个太阳能电池，各个太阳能电池包括基板和位于所述基板的表面上的电极部；互连器，其被构成为将所述多个太阳能电池中的至少一个太阳能电池电连接到所述多个太阳能电池中的另一个太阳能电池；以及导电粘合膜，其包括树脂和散布在所述树脂中的多个导电颗粒，所述导电粘合膜位于所述多个太阳能电池中的所述至少一个太阳能电池的所述电极部和所述互连器之间，以将所述多个太阳能电池中的所述至少一个太阳能电池的所述电极部电连接到所述互连器，其中，所述互连器的宽度等于或大于所述导电粘合膜的宽度。
3、CN102760787A、名称“太阳能电池板”，它包括：玻璃板，镀膜层，电池板以及壳，其特征是：表面固定有防反射膜的玻璃板位于上方；外周是外壳；固定有反光膜的内壳在中部；电池板在下方；在玻璃板、内壳和电池板形成的空间为密封的，内有保护性气体。
4、CN103280478A、名称“太阳能电池板”，包括铝合金制的方形框体（1），所述方形框体（1）内固定太能电池板本体，所述方形框体（1）由四根框架条（10）拼合固定而成，其特征在于：所述框架条（10）包括横截面为L形的框架本体，所述框架本体的长侧边边缘侧设有U形的电池板固定槽（11），相邻并对接的框架本体间通过插口（13）及插条（12）的插销结构拼合，同时插条及插口上设有固定孔，销钉插入固定孔并通过注胶固定。
上述背景技术存在的不足之处：太阳电池板均采用整块太阳能电池片构成，因而既不能卷筒携带，也无法随遇而安布放太阳能电池板。
发明内容
设计目的：设计一种既便于携带安装、使用，又能随时收拢存放，同时又具有优异的耐候性、密封性和浮动性的模块式太阳能电池板及成型方法。
设计方案：为了实现上述设计目的。1、本发明采用PVC糊料作为太阳能模块密封材料的设计，是本发明的技术特征之一。这样设计的目的在于：它改变长期以来本领域技术人员认为的PVC糊由于分散性能良好，只能用于软材料领域使用，如人造革、搪胶玩具、软质商标、墙纸、油漆涂料、发泡塑胶等，不能作为太阳能电池密封成形材料的技术偏见。本申请反其道之，采用PVC糊作为太阳能电池密封成形材料，不仅可以使太阳能板根据用户需要成形为各种形状，而且所成形的太阳能电池易于浇注、透光效果好、耐热、抗冲击、抗撕裂，并且可以实现少量、多品种化生产，更重要的是该材料实现了太阳能电池密封长期在户外的全密封、全天候的耐候使用。2、将多块太阳能电池模块串联或并联或串并联构成模块式太阳能电池板的设计，是本发明的技术特征之二。这样设计的目的在于：由于太阳能芯片采用单晶硅或多晶硅制造，而单晶硅或多晶硅单晶硅具有金刚石晶格，晶体硬而脆，因此现有太阳能电池的制作中，需要将太阳能电池片正面采用高的交联度的EVA、高粘结强度的封装剂（中性硅酮树脂胶）、高透光率高强度的钢化玻璃等，背面采用刚性背板支撑，四周采用刚性框架密封，不仅制造成本高，体重、易碎，而且不能便携使用，使太阳能电池的使用仅仅局限在固定环境状态下的使用。
本申请在PVC糊中添加用于吸收紫外线的吸收剂，因为紫外线吸收剂能吸收阳光或荧光源中紫外线部分，而本身结构不起变化，它能将高能量的紫外线光能转换成热能或无破坏性的较长光波释放出来，从而保护添加有紫外线吸收剂的物质免遭紫外线破坏，在PVC糊中添加紫外线吸收剂能有效阻止阳光中的紫外线对太阳能电池密封模块的破坏，延长模块式太阳能电池板的使用寿命。
本申请在PVC糊中添加抗氧剂的目的在于：由于塑化后的PVC糊塑料在光、热、氧、溶剂、助剂、HCl等因素作用下易老化，即降解或交联，使其物理机械性能变坏，缩短使用寿命。本申请PVC糊中加入抗氧剂有效地抑制或降低塑料大分子的热氧化、光氧化反应速度，显著地提高塑化后的PVC糊塑料的耐热、耐光性能，延缓塑化后的PVC糊塑料的降解、老化过程，改善PVC糊所制模块式太阳能电池板的耐侯性，延长塑化后的PVC糊塑料制品使用寿命。
本申请在PVC糊中添加低温增塑剂的目的在于：由于低温增塑剂与PVC糊树脂具有良好的相容性，增塑效果好，不易离析、不易渗出，并且低温增塑剂可降低塑化后的PVC糊塑料的玻璃化温度，使其柔韧性好，能够改善塑化后的PVC糊塑料的耐寒性能，使其在寒冷地区仍有较好的使用性能。
本申请在PVC糊中添加稳定剂的目的在于：PVC糊料在高温下塑化或高温下使用，极易放出HCL，形成不稳定的聚烯结构。同时，HCL具有自催化作用，会使PVC进一步降解。另外，假如有氧存在或有铁、铝、锌、锡、铜和镉等离子存在，都会对PVC降解起催化作用，加速其老化。因此塑料将出现各种不良现象，如变色、变形、龟裂、机械强度下降、缘性能下降、发脆等。为了解决这些问题，PVC糊塑料中必须加进不同品种，不同数目的稳定剂。
技术方案1：一种模块式太阳能电池板，包括太阳能芯片，所述太阳能芯片位于硬PVC壳腔内，PVC糊料密封包覆在太阳能芯片上且硬PVC壳腔被PVC糊料密封填充构成浇注式太阳能电池模块，多块浇注式太阳能电池模块间串联或并联或串并联构成模块式太阳能电池板。
技术方案2：一种模块式太阳能电池板制作方法，浇注式太阳能电池模块制作：根据用户所需太阳能芯片的大小制作硬PVC壳，将太阳能芯片悬空在硬PVC壳型腔中，然后将PVC糊料注入到硬PVC壳型腔中，加温15-30分钟，使硬PVC壳型腔中的PVC糊料固化，即得浇注式太阳能电池模块，最后根据客户所需功率的大小，将多块浇注式太阳能电池模块之间采用连接件连接，并将多块浇注式太阳能电池模块电源输出端采用串联或并联或串并联方式连接即可。
本发明与背景技术相比，一是采用PVC糊作为太阳能芯片模芯密封的成形材料，不仅具有良好的耐紫外线、耐低温、耐候性好，而且阻燃达到V-1至V-0级；二是可以根据用户的不同需求用模块式太阳能电池板成形所需太阳能板的外形，不仅从根本上改变了本领域技术人员常期以来认为PVC糊料不能作为太阳能电池密封成形材料的技术偏见，而改从根本上改变了太阳能芯片只能矩形分布而不能随造形分布的技术偏见；三是由于本申请模块式太阳能电池板既能收卷携带，又根随遇而展开采光发电，因此它既能随人用于陆地采光发电，也能随船浮在湖中或海洋面上发电。
附图说明
图1是模块式太阳能电池板的俯视结构示意图。
图2是模块式太阳能电池板的剖视结构示意图。
具体实施方式
实施例1：参照附图1和2。一种模块式太阳能电池板，包括太阳能芯片1，所述太阳能芯片1位于硬PVC壳腔内，PVC糊料2密封包覆在太阳能芯片1上且硬PVC壳腔被PVC糊料密封填充构成浇注式太阳能电池模块4，多块浇注式太阳能电池模块4间串联或并联或串并联（串并联是指先串联后并联或先并联后串联）构成模块式太阳能电池板5。所述太阳能芯片1电源线密封穿过PVC糊料2密封层及硬PVC壳密封壁。所述多块太阳能电池模块4之间采用柔性连接件或刚性连接件连接，柔性连接件如弹性橡胶片或弹性橡胶绳等，刚性加接件如塑料片、金属片、插接结构等等。本申请所说的PVC糊料是指含有增塑剂的PVC糊料。
实施例2：在实施例1的基础上，所述太阳能芯片1为单片封装，即单片太阳能电池（模块）。
实施例3：在实施例1的基础上，所述太阳能芯片1为多片封装，即多片太阳能芯片1被PVC糊料2密封包覆构成模块式太阳能电池板，多片太阳能芯片1之间的串并联系现有技术，在此不作叙述。
实施例4：在实施例1的基础上，所述PVC糊中含有紫外线吸收剂，紫外线吸收剂添加量为100份PVC糊树脂添加0.1份至0.8份紫外线吸收剂。所述紫外线吸收剂为紫外线吸收剂UV-531、紫外线吸收剂UV-327、紫外线吸收剂UV-326、紫外线吸收剂UV-74、紫外线吸收剂UV-9、紫外线吸收剂UV-P一种或一种以上的组合。
实施例5：在实施例1的基础上，所述PVC糊中含有抗氧剂。抗氧剂添加量为100份PVC糊树脂添加每种0.5份至1份抗氧剂。所述抗氧化剂为抗氧剂2246、抗氧剂1520、抗氧剂1098、抗氧剂1076、抗氧剂1010、抗氧剂300、抗氧剂264、抗氧剂168一种或一种以上组合。
实施例6：在实施例1的基础上，所述PVC糊中含有耐低温添加剂。耐低温添加剂添加量为100份PVC糊树脂添加5份至20份低温增塑剂。所述耐低温添加剂为已二酸二异癸酯(简称DIDA)、己二酸二辛酯(简称DOA)、壬二酸二辛酯(简称DOZ)、癸二酸二丁酸(简称DBS)、癸二酸二辛酯（简称DOS)、癸二酸二异辛酯（简称DIOS)一种或一种以上组合。
实施例7：在实施例1的基础上，所述PVC糊中含有稳定剂。稳定剂添加量为100份PVC糊树脂添加每种0.5份至5份稳定剂。所述稳定剂为辛基硫醇锡、辛基氧化锡、二月桂酸二正辛基锡、马来酸二正辛基锡、丁基硫醇锡、马来酸二丁基锡、月桂酸马来酸二丁基锡、月桂酸马来酸二丁基锡、双丁基氧化锡、二甲基氧化锡、环氧大豆油、环氧胡麻油、亚磷酸脂。
实施例8：在实施例1的基础上，所述PVC糊中含阻燃增塑剂。阻燃增塑剂添加量为100份PVC糊树脂添加5份至15份阻燃增塑剂。所述阻燃增塑剂为DP-45、磷酸三甲苯酯(TCP)、磷酸三苯酯(TPP)、磷酸三丁酯(TBP)、磷酸三辛酯(TOP)、磷酸二苯一辛酯(DPOP)一种或一种以上组合。
实施例9：在上述实施例的基础上，一种模块式太阳能电池板制作方法，浇注式太阳能电池模块4制作：根据用户所需太阳能芯片1的大小制作硬PVC壳3，将太阳能芯片1悬空在硬PVC壳3型腔中，然后将PVC糊料2注入到硬PVC壳3型腔中，加温15-30分钟，使硬PVC壳3型腔中的PVC糊料2固化，即得浇注式太阳能电池模块4，最后根据客户所需功率的大小，将多块浇注式太阳能电池模块4之间采用连接件连接，并将多块浇注式太阳能电池模块4电源输出端采用串联或并联或串并联方式连接即可。所述加温为烘箱加温或烘道加温。
需要理解到的是：上述实施例虽然对本发明的设计思路作了比较详细的文字描述，但是这些文字描述，只是对本发明设计思路的简单文字描述，而不是对本发明设计思路的限制，任何不超出本发明设计思路的组合、增加或修改，均落入本发明的保护范围内。
Claims (17)
1.一种模块式太阳能电池板，包括太阳能芯片（1），其特征是：所述太阳能芯片（1）位于硬PVC壳腔内，PVC糊料（2）密封包覆在太阳能芯片（1）上且硬PVC壳腔被PVC糊料密封填充构成浇注式太阳能电池模块（4），多块浇注式太阳能电池模块（4）间串联或并联或串并联构成模块式太阳能电池板（5）。
2.根据权利要求1所述的模块式太阳能电池板，其特征是：所述太阳能芯片（1）电源线密封穿过PVC糊料（2）密封层及硬PVC壳壁。
3.根据权利要求1所述的模块式太阳能电池板，其特征是：所述太阳能芯片（1）为单片封装。
4.根据权利要求1所述的模块式太阳能电池板，其特征是：所述太阳能芯片（1）为多片封装。
5.根据权利要求1所述的模块式太阳能电池板，其特征是：所述多块太阳能电池模块（4）之间采用柔性连接件连接。
6.根据权利要求2所述的模块式太阳能电池板，其特征是：所述PVC糊料中含有紫外线吸收剂。
7.根据权利要求7所述的模块式太阳能电池板，其特征是：所述紫外线吸收剂为紫外线吸收剂UV-531、紫外线吸收剂UV-327、紫外线吸收剂UV-326、紫外线吸收剂UV-74、紫外线吸收剂UV-9、紫外线吸收剂UV-P。
8.根据权利要求2所述的模块式太阳能电池板，其特征是：所述PVC糊料中含有抗氧剂。
9.根据权利要求9所述的模块式太阳能电池板，其特征是：所述抗氧化剂为抗氧剂2246、抗氧剂1520、抗氧剂1098、抗氧剂1076、抗氧剂1010、抗氧剂300、抗氧剂264、抗氧剂168。
10.根据权利要求2所述的模块式太阳能电池板，其特征是：所述PVC糊料中含有耐低温添加剂。
11.根据权利要求11所述的模块式太阳能电池板，其特征是：所述耐低温添加剂为已二酸二异癸酯(简称DIDA)、己二酸二辛酯(简称DOA)、壬二酸二辛酯(简称DOZ)、癸二酸二丁酸(简称DBS)、癸二酸二辛酯（简称DOS)、癸二酸二异辛酯（简称DIOS)。
12.根据权利要求2所述的模块式太阳能电池板，其特征是：所述PVC糊料中含有稳定剂。
13.根据权利要求13所述的模块式太阳能电池板，其特征是：所述稳定剂为辛基硫醇锡、辛基氧化锡、二月桂酸二正辛基锡、马来酸二正辛基锡、丁基硫醇锡、马来酸二丁基锡、月桂酸马来酸二丁基锡、月桂酸马来酸二丁基锡、双丁基氧化锡、二甲基氧化锡、环氧大豆油、环氧胡麻油、亚磷酸脂。
14.根据权利要求2所述的模块式太阳能电池板，其特征是：所述PVC糊料中含阻燃增塑剂。
15.根据权利要求15所述的模块式太阳能电池板，其特征是：所述阻燃增塑剂为DP-45、磷酸三甲苯酯(TCP)、磷酸三苯酯(TPP)、磷酸三丁酯(TBP)、磷酸三辛酯(TOP)、磷酸二苯一辛酯(DPOP)。
16.一种模块式太阳能电池板制作方法，其特征是：浇注式太阳能电池模块（4）制作：根据用户所需太阳能芯片1的大小制作硬PVC壳（3），将太阳能芯片（1）悬空在硬PVC壳（3）型腔中，然后将PVC糊料（2）注入到硬PVC壳（3）型腔中，加温15-30分钟，使硬PVC壳（3）型腔中的PVC糊料（2）固化，即得浇注式太阳能电池模块（4），最后根据客户所需功率的大小，将多块浇注式太阳能电池模块（4）之间采用连接件连接，并将多块浇注式太阳能电池模块（4）电源输出端采用串联或并联或串并联方式连接即可。
17.根据权利要求17所述的模块式太阳能电池板，其特征是：所述加温为烘箱加温或烘道加温。