CN1039238C - 有机硅酮结构密封胶 - Google Patents

有机硅酮结构密封胶 Download PDF

Info

Publication number
CN1039238C
CN1039238C CN94112678A CN94112678A CN1039238C CN 1039238 C CN1039238 C CN 1039238C CN 94112678 A CN94112678 A CN 94112678A CN 94112678 A CN94112678 A CN 94112678A CN 1039238 C CN1039238 C CN 1039238C
Authority
CN
China
Prior art keywords
organic
silicate
present
kilograms
sealing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN94112678A
Other languages
English (en)
Other versions
CN1110299A (zh
Inventor
玄兆国
宋晓峰
李海燕
王兆斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN94112678A priority Critical patent/CN1039238C/zh
Publication of CN1110299A publication Critical patent/CN1110299A/zh
Application granted granted Critical
Publication of CN1039238C publication Critical patent/CN1039238C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明涉及一种密封胶，适用于建筑隐形、半隐形玻璃幕墙及大理石壁面的结构性粘接密封，是由有机羟基硅酮、有机甲基硅酮、甲基肟基硅烷、二丁基二月桂酸锡、气相二氧化硅、硅酸盐、氨基硅烷组成，在常温下反应而成，具有优良的抗老化性能、高抗拉强度和成本低、易于生产的优点。

Description

有机硅酮结构密封胶
本发明涉及一种胶粘剂，具体地说是用于铝合金型材与玻璃、玻璃与玻璃、铝合金型材与铝合金型材、大理石与混凝土等之间进行结构性粘接的结构密封胶。
目前，国内市场出售的结构密封胶均为进口产品，国内尚无厂家生产。进口品有美国GE公司的SSG4000和DOW CORNING公司的759。这两种结构胶的缺点是由于添加碳黑，使抗老化性能下降，抗拉强度降低，另外该产品成本比较高。
本发明的目的在于提供一种具有优良的抗老化性能和高抗拉强度的、成本低的结构密封胶。
本发明的有机硅酮结构密封胶组成(重量份)是：
有机羟基硅酮              4-8；
有机甲基硅酮              1-4；
甲基肟基硅烷              0.1-0.6；
二丁基二月桂酸锡          0.005-0.01；
气相二氧化硅              0.4-1.2；
硅酸盐                    1-5；
氨基硅烷                  0.01-0.09。
其中，二甲基聚硅氧烷也称二甲基硅油。
本发明的制备方法是将上述原料在常温下真空混合搅拌30分钟，即得本发明。根据组份比例变更，可得到不同弹性的密封胶。本发明的结构密封胶为不流淌膏状体。根据需要，可添加不同颜色，可以是黑色，或者白色，或者棕色。所述的硅酸盐是指硅酸钙或硅酸镁。
本发明适用于铝合金型材与玻璃、铝合金型材之间、玻璃之间、大理石与混凝土等之间进行结构性粘接密封，用来制作高层建筑隐型和半隐型玻璃幕墙及大理石壁面。
本发明的优点是：
1、由于添加硅酸盐，提高了密封胶的抗老化性能，可提高隐形、半隐形玻璃幕墙的使用寿命；
2、由于用硅酸盐全部代替碳黑和部分地代替气相二氧化硅，降低了产品成本，可降低工程造价。
3、制造工艺简单，使用通用设备，工艺稳定。
下面通过实施例，可对本发明作进一步了解。
实施例1
将有机羟基硅酮            45公斤；
有机甲基硅酮              15公斤；
甲基肟基硅烷              3公斤；
气相二氧化硅              6公斤；
硅酸钙                    30公斤；
二丁基二月桂酸锡          0.04公斤；
氨基硅烷                  0.4公斤。
在常温下真空混合搅拌30分钟即得本发明结构密封胶119.44公斤。
实施例2
有机羟基硅酮              60公斤；
有机甲基硅酮              30公斤；
甲基肟基硅烷              4公斤；
气相二氧化硅              9公斤；
硅酸镁                    35公斤；
二丁基二月桂酸锡            0.08公斤；
氨基硅烷                    0.7公斤。
工艺条件与实施例1相同。制得本发明结构密封胶138.78公斤。
实施例3
有机羟基硅酮                70公斤；
有机甲基硅酮                10公斤；
甲基肟基硅烷                3.5公斤；
气相二氧化硅                6.5公斤；
硅酸钙                      40公斤；
二丁基二月桂酸锡            0.06公斤；
氨基硅烷                    0.6公斤。
工艺条件与实施例1相同。制得本发明结构密封胶130.66公斤。
将实施例1、2、3所得结构密封胶按ASTM标准进行性能测试并与GE公司的SSG4000及795比较结果如下：
         极端抗拉强度    抗老化性
实施例1    2.21Mpa          优
实施例2    2.41Mpa          优
实施例3    2.26Mpa          优
SSG4000    2.11Mpa          良
795        1.20Mpa          良

Claims (2)

1、一种对建筑隐形、半隐形玻璃幕墙及大理石壁面进行结构性粘接密封的有机硅酮结构密封胶，其特征在于：
该密封胶由下列物质组成(重量份)：
有机羟基硅酮          4-8；
有机甲基硅酮          1-4；
甲基肟基硅烷          0.1-0.6；
气相二氧化硅          0.4-1.2；
二丁基二月桂酸锡      0.005-0.01；
硅酸盐                1-5；
氨基硅烷              0.01-0.07。
2、根据权利要求1所述的有机硅酮结构密封胶，其特征在于所述的硅酸盐为硅酸钙或者硅酸镁。
CN94112678A 1994-12-16 1994-12-16 有机硅酮结构密封胶 Expired - Fee Related CN1039238C (zh)