CN103923596A - Adhesive special for sun board - Google Patents
Adhesive special for sun board Download PDFInfo
- Publication number
- CN103923596A CN103923596A CN201410114772.8A CN201410114772A CN103923596A CN 103923596 A CN103923596 A CN 103923596A CN 201410114772 A CN201410114772 A CN 201410114772A CN 103923596 A CN103923596 A CN 103923596A
- Authority
- CN
- China
- Prior art keywords
- parts
- mix
- mixing uniformly
- special adhesive
- coupling agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an adhesive for a sun board, and relates to the technical field of adhesives. The adhesive is prepared by the following steps: putting 100 parts of room temperature vulcanized silicone rubber and 20 parts of dimethyl silicone oil into a container; mixing uniformly in an environment in which the vacuum degree is -0.09MPa; adding 20 parts of methyltrissilane and 30 parts of tetrakissilane, and mixing uniformly; adding 70 parts of fumed silica; mixing uniformly under a vacuum container; adding a coupling agent KH550 and dibutyltin dilaurate, and mixing uniformly. Tetrakissilane is introduced to replace the conventional coupling agent KH560, so that the curing time of a product is shortened, and the compatibility with a solar panel is improved remarkably.
Description
Technical field
The present invention relates to sizing agent technical field, be specifically related to a kind of sunlight board special adhesive.
Background technology
Solar panel special adhesive was poor aspect bonding in the past, set time is also long, affects quality product and working efficiency.
Summary of the invention
Technical problem to be solved by this invention is to provide shorten a kind of set time, with the obviously sunlight board special adhesive of raising of solar panel consistency.
Technical problem to be solved by this invention realizes by the following technical solutions:
A kind of sunlight board special adhesive, is grouped into by the one-tenth of following weight part,
The better parts by weight of each component are:
The preparation method of aluminium look minute surface special adhesive of the present invention is as follows:
100 parts of room temperature vulcanized silicone rubbers are put into container with 20 parts of dimethyl silicone oils, mix under-0.09MPa environment in vacuum tightness, add again 30 parts of 20 parts of methyl tributanoximo silanes and four Diacetylmonoxime base silanes all to close evenly, then add 70 parts of thermal silicas, under vacuum condition, mix, finally add coupling agent KH550 and dibutyl tin laurate to mix.
The invention has the beneficial effects as follows: the present invention introduces four Diacetylmonoxime base silanes and replaces traditional silane coupling agent KH560, makes products solidifying time shorten, obviously improves with solar panel consistency.
Embodiment
For technique means, creation characteristic that the present invention is realized, reach object and effect is easy to understand, below in conjunction with specific embodiment, further set forth the present invention.
Embodiment 1
A kind of sunlight board special adhesive, synthesis technique: 100 parts of room temperature vulcanized silicone rubbers are put into container with 20 parts of dimethyl silicone oils, mix under-0.09MPa environment in vacuum tightness, add again 30 parts of 20 parts of methyl tributanoximo silanes and four Diacetylmonoxime base silanes all to close evenly, then add 70 parts of thermal silicas, under vacuum condition, mix, finally add appropriate coupling agent KH550 and dibutyl tin laurate to mix.
Embodiment 2
A kind of sunlight board special adhesive, synthesis technique: 100 parts of room temperature vulcanized silicone rubbers are put into container with 20 parts of dimethyl silicone oils, mix under-0.09MPa environment in vacuum tightness, add again 30 parts of 20 parts of methyl tributanoximo silanes and four Diacetylmonoxime base silanes all to close evenly, then add 70 parts of thermal silicas, under vacuum condition, mix, finally add 0.1 part of Silane coupling agent KH550 and 0.1 part of dibutyl tin laurate to mix.
Embodiment 3
A kind of sunlight board special adhesive, synthesis technique: 100 parts of room temperature vulcanized silicone rubbers are put into container with 25 parts of dimethyl silicone oils, mix under-0.09MPa environment in vacuum tightness, add again 25 parts of 15 parts of methyl tributanoximo silanes and four Diacetylmonoxime base silanes all to close evenly, then add 65 parts of thermal silicas, under vacuum condition, mix, finally add Silane coupling agent KH550 and dibutyl tin laurate to mix.
More than show and described ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; that in above-described embodiment and specification sheets, describes just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.The claimed scope of the present invention is defined by appending claims and equivalent thereof.
Claims (3)
1. a sunlight board special adhesive, is characterized in that: the one-tenth by following weight part is grouped into,
2. sunlight board special adhesive according to claim 1, is characterized in that: the one-tenth by following weight part is grouped into,
3. prepare the method that has sunlight board special adhesive described in claim 1 or 2 for one kind, it is characterized in that: 100 parts of room temperature vulcanized silicone rubbers are put into container with 20 parts of dimethyl silicone oils, mix under-0.09MPa environment in vacuum tightness, add again 30 parts of 20 parts of methyl tributanoximo silanes and four Diacetylmonoxime base silanes all to close evenly, then add 70 parts of thermal silicas, under vacuum condition, mix, finally add coupling agent KH550 and dibutyl tin laurate to mix.