CN103923539A - 一种新型高耐候水性氟碳外墙乳胶涂料 - Google Patents
一种新型高耐候水性氟碳外墙乳胶涂料 Download PDFInfo
- Publication number
- CN103923539A CN103923539A CN201410184239.9A CN201410184239A CN103923539A CN 103923539 A CN103923539 A CN 103923539A CN 201410184239 A CN201410184239 A CN 201410184239A CN 103923539 A CN103923539 A CN 103923539A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- coating
- thinned
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种新型高耐候水性氟碳外墙乳胶涂料。以重量份计,本发明由以下组分组成:水:30~50,聚氧乙烯醚:0.1~0.3,异丙酮:0.1~0.3,乙烯基双硬脂酰胺:0.6~0.8,二甲基硅油:0.3~0.6,氟化钠:0.3~0.5,1,2-丙二醇:3~5,碳酸氢钠:1~3,钛白粉:10~20,轻质碳酸钙:20~30,氟碳乳液:30~40。与现有技术相比,本发明具有如下有益效果:(1)本发明的化学稳定性及耐热、耐污等性能超群,涂抹后长期不会老化,且具有逼真的金属光泽和高耐候性能;(2)制备工艺简单,成本低廉。
Description
技术领域
本发明属于涂料技术领域,更具体是涉及一种新型高耐候水性氟碳外墙乳胶涂料。
背景技术
金属氟碳外墙涂料是近年来为了满足对建筑涂料超耐久的需要,运用氟化学技术研究开发生产的以氟氯乙烯及乙烯基化合物为基料的常温固化金属氟碳涂料。其化学稳定性及耐热、耐污等性能超群,涂抹后长期不会老化,其突出优点在于具有逼真的金属光泽和高耐候性能。因其材料特性,金属氟碳涂料的使用范围十分广泛,尤其是在建筑外墙施工、仿制铝板幕墙施工中越来越受到人们的还原并加以运用。
发明内容
本发明的目的在于克服现有技术存在的不足,提供一种新型高耐候水性氟碳外墙乳胶涂料。
为达到上述目的,本发明采取了如下的技术方案:
一种新型高耐候水性氟碳外墙乳胶涂料,以重量份计,由以下组分组成:
水:30~50,聚氧乙烯醚:0.1~0.3,异丙酮:0.1~0.3,
乙烯基双硬脂酰胺:0.6~0.8,二甲基硅油:0.3~0.6,
氟化钠:0.3~0.5,1,2-丙二醇:3~5,碳酸氢钠:1~3,
钛白粉:10~20,轻质碳酸钙:20~30,氟碳乳液:30~40。
所述的新型高耐候水性氟碳外墙乳胶涂料的制备工艺为:将粉料、水及其他原料逐步加入到带有高速搅拌装置的烧瓶中进行分散,再通过砂磨机磨细,然后将氟碳乳液加入,混合均匀后过滤,出料,即为产品。
与现有技术相比,本发明具有如下有益效果:
(1)本发明的化学稳定性及耐热、耐污等性能超群,涂抹后长期不会老化,且具有逼真的金属光泽和高耐候性能;
(2)制备工艺简单,成本低廉。
具体实施方式
以下结合具体实施例来对本发明作进一步的描述。
实施例1
一种新型高耐候水性氟碳外墙乳胶涂料,以重量份计,由以下组分组成:
水:40,聚氧乙烯醚:0.2,异丙酮:0.2,
乙烯基双硬脂酰胺:0.7,二甲基硅油:0.5,
氟化钠:0.4,1,2-丙二醇:4,碳酸氢钠:2,
钛白粉:16,轻质碳酸钙:26,氟碳乳液:35。
实施例2
一种新型高耐候水性氟碳外墙乳胶涂料,以重量份计,由以下组分组成:
水:30,聚氧乙烯醚:0.1,异丙酮:0.1,
乙烯基双硬脂酰胺:0.6,二甲基硅油:0.3,
氟化钠:0.3,1,2-丙二醇:3,碳酸氢钠:1,
钛白粉:10,轻质碳酸钙:20,氟碳乳液:30。
实施例3
一种新型高耐候水性氟碳外墙乳胶涂料,以重量份计,由以下组分组成:
水:50,聚氧乙烯醚:0.3,异丙酮:0.3,
乙烯基双硬脂酰胺:0.8,二甲基硅油:0.6,
氟化钠:0.5,1,2-丙二醇:5,碳酸氢钠:3,
钛白粉:20,轻质碳酸钙:30,氟碳乳液:40。
所述的新型高耐候水性氟碳外墙乳胶涂料的制备工艺为:将粉料、水及其他原料逐步加入到带有高速搅拌装置的烧瓶中进行分散,再通过砂磨机磨细,然后将氟碳乳液加入,混合均匀后过滤,出料,即为产品。
Claims (4)
1.一种新型高耐候水性氟碳外墙乳胶涂料,其特征在于,以重量份计,由以下组分组成:
水:30~50,聚氧乙烯醚:0.1~0.3,异丙酮:0.1~0.3,
乙烯基双硬脂酰胺:0.6~0.8,二甲基硅油:0.3~0.6,
氟化钠:0.3~0.5,1,2-丙二醇:3~5,碳酸氢钠:1~3,
钛白粉:10~20,轻质碳酸钙:20~30,氟碳乳液:30~40。
2.根据权利要求1所述的一种新型高耐候水性氟碳外墙乳胶涂料,其特征在于,以重量份计,由以下组分组成:
水:40,聚氧乙烯醚:0.2,异丙酮:0.2,
乙烯基双硬脂酰胺:0.7,二甲基硅油:0.5,
氟化钠:0.4,1,2-丙二醇:4,碳酸氢钠:2,
钛白粉:16,轻质碳酸钙:26,氟碳乳液:35。
3.根据权利要求1所述的一种新型高耐候水性氟碳外墙乳胶涂料,其特征在于,以重量份计,由以下组分组成:
水:30,聚氧乙烯醚:0.1,异丙酮:0.1,
乙烯基双硬脂酰胺:0.6,二甲基硅油:0.3,
氟化钠:0.3,1,2-丙二醇:3,碳酸氢钠:1,
钛白粉:10,轻质碳酸钙:20,氟碳乳液:30。
4.根据权利要求1所述的一种新型高耐候水性氟碳外墙乳胶涂料,其特征在于,以重量份计,由以下组分组成:
水:50,聚氧乙烯醚:0.3,异丙酮:0.3,
乙烯基双硬脂酰胺:0.8,二甲基硅油:0.6,
氟化钠:0.5,1,2-丙二醇:5,碳酸氢钠:3,
钛白粉:20,轻质碳酸钙:30,氟碳乳液:40。