CN103911608B - Slider of zipper fastener black coating bronze method and be applied to the black bronze liquid medicine of the method - Google Patents
Slider of zipper fastener black coating bronze method and be applied to the black bronze liquid medicine of the method Download PDFInfo
- Publication number
- CN103911608B CN103911608B CN201310004490.8A CN201310004490A CN103911608B CN 103911608 B CN103911608 B CN 103911608B CN 201310004490 A CN201310004490 A CN 201310004490A CN 103911608 B CN103911608 B CN 103911608B
- Authority
- CN
- China
- Prior art keywords
- slider
- black
- bronze
- zipper fastener
- liquid medicine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of new slider of zipper fastener black coating bronze method, a kind of black bronze liquid medicine that is applied to this black coating bronze method is provided simultaneously, wherein slider of zipper fastener black coating bronze method, comprises the step that next coming in order carry out: a) oil removing; B) pickling; C) black bronze processing; D) varnish. Adopt the present invention, slider of zipper fastener surface can be pure black, and overlay coating wearability is strong, durable in use, and this technique yields is high, product with stable quality.
Description
Technical field
The present invention relates to a kind of slider of zipper fastener method for treating surface layer, more particularly, relate to a kind of slider of zipper fastener black coating bronze method and be applied to the black bronze liquid medicine of the method.
Background technology
The slide fastener of application in daily life, some need to make black, but due to technical limitations, existing technique cannot be produced the slider of zipper fastener of ater, the dark gram of Singapore technique of the many employings of black coating bronze technique of existing slider of zipper fastener substitutes, and its surface plating structure is CuSe compound normally, and color and luster presents dark gram of Singapore look or brownish black conventionally, inconsistent with the color and luster of black zipper tooth, can cause the cooperation color and luster poor effect of whole piece slide fastener.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of new slider of zipper fastener black coating bronze method, a kind of black bronze liquid medicine that is applied to this black coating bronze method is provided simultaneously, adopt this technique and black bronze liquid medicine can produce the slider of zipper fastener of ater, there is not shade deviation in this slider of zipper fastener and black slide fastener, arranging effect is good.
Above-mentioned technical problem can be realized by following technological means: a kind of slider of zipper fastener black coating bronze method, is characterized in that: described slider of zipper fastener black coating bronze method comprises the step that next coming in order carry out:
A) oil removing is placed on pre-copper facing rear zipper head in degreasing tank and cleans with clear water after oil removing 2-4 minute;
B) sulfuric acid solution that the slider of zipper fastener after oil removing is put into 3-8% by pickling soaks 1-3 minute, then cleans with clear water;
C) black bronze is processed the slider of zipper fastener after pickling is soaked in black bronze liquid medicine, under 95-110 DEG C of condition, soaks 3～7 minutes, then cleans with clear water;
D) varnish and will after slider of zipper fastener oven dry after treatment black bronze, carry out surface spraying varnish PROCESS FOR TREATMENT, and then dry.
In step a), slider of zipper fastener best oil removing time in degreasing tank is 3 minutes.
The sulfuric acid solution concentration adopting in step b) can be 5%.
The time of soaking in sulfuric acid solution in step b) can be 1 minute.
In step c), the soak time of slider of zipper fastener in black bronze liquid medicine can be 5 minutes.
The temperature conditions that in step c), slider of zipper fastener is processed in black bronze liquid medicine can be 105 DEG C.
A black bronze liquid medicine that is applied to above-mentioned slider of zipper fastener black coating bronze method, is characterized in that: in described black bronze liquid medicine formula, include the sodium chlorite of 30-40g/l and the NaOH of 35-45g/l.
Best results while including the sodium chlorite of 35g/l and the NaOH of 40g/l in described black bronze liquid medicine formula.
Usefulness of the present invention is: can realize to the outer surface of slider of zipper fastener and be plated to ater, almost there is no aberration with the slide fastener of black, color and luster collocation degree is good; Through planting thus the slider of zipper fastener of PROCESS FOR TREATMENT, its overlay coating composition is CuO, and stability is high, and wearability is strong, and fast colours is durable in use.
Brief description of the drawings
Fig. 1 is flow sheet of the present invention.
Detailed description of the invention
Specific embodiment one:
Slider of zipper fastener black coating bronze method as shown in Figure 1 comprises the step that next coming in order carry out:
A) oil removing is placed on oil removing in degreasing tank by pre-copper facing rear zipper head and cleans with clear water after 2 minutes;
B) pickling is put into 5% sulfuric acid solution by the slider of zipper fastener after oil removing and is soaked 1 minute, then cleans with clear water;
C) black bronze is processed the slider of zipper fastener after pickling is soaked in black bronze liquid medicine, under 95 DEG C of conditions, soaks 3 minutes, then cleans with clear water;
D) varnish and will after slider of zipper fastener oven dry after treatment black bronze, carry out surface spraying varnish PROCESS FOR TREATMENT, and then dry.
Specific embodiment two
Described slider of zipper fastener black coating bronze method comprises the step that next coming in order carry out:
A) oil removing is placed on oil removing in degreasing tank by pre-copper facing rear zipper head and cleans with clear water after 3 minutes;
B) pickling is put into 5% sulfuric acid solution by the slider of zipper fastener after oil removing and is soaked 1 minute, then cleans with clear water;
C) black bronze is processed the slider of zipper fastener after pickling is soaked in black bronze liquid medicine, under 105 DEG C of conditions, soaks 5 minutes, then cleans with clear water;
D) varnish and will after slider of zipper fastener oven dry after treatment black bronze, carry out surface spraying varnish PROCESS FOR TREATMENT, and then dry.
Specific embodiment three
A) oil removing is placed on oil removing in degreasing tank by pre-copper facing rear zipper head and cleans with clear water after 4 minutes;
B) pickling is put into 8% sulfuric acid solution by the slider of zipper fastener after oil removing and is soaked 1 minute, then cleans with clear water;
C) black bronze is processed the slider of zipper fastener after pickling is soaked in black bronze liquid medicine, under 110 DEG C of conditions, soaks 3 minutes, then cleans with clear water;
D) varnish and will after slider of zipper fastener oven dry after treatment black bronze, carry out surface spraying varnish PROCESS FOR TREATMENT, and then dry.
Be applied in the formula of black bronze liquid medicine of above-mentioned three specific embodiments and include the sodium chloride of 10-30g/l and the copper sulphate of 10-30g/l.
In the time including the sodium chloride of 20g/l and the copper sulphate of 20g/l in black bronze liquid medicine formula, can reach optimum efficiency.
Above embodiment is for understanding the present invention, is not limitation of the present invention, and about the those of ordinary skill in field, these variations or modification should be understood to still belong to protection scope of the present invention.
Claims (7)
1. a slider of zipper fastener black coating bronze method, is characterized in that: described slider of zipper fastener black coating bronze method comprisesThe step that next coming in order carry out:
A) oil removing is placed on pre-copper facing rear zipper head in degreasing tank and cleans with clear water after oil removing 2-4 minute;
B) sulfuric acid solution that the slider of zipper fastener after oil removing is put into 3-8% by pickling soaks 1-3 minute, then usesClear water cleans;
C) black bronze is processed the slider of zipper fastener after pickling is soaked in black bronze liquid medicine, 95-110 DEG C of conditionThereby lower immersion forms the CuO film of an ater for 3～7 minutes in the surface of slider of zipper fastener, then carry out with clear waterClean, in described black bronze liquid medicine formula, include the sodium chlorite of 30-40g/l and the NaOH of 35-45g/l;
D) varnish and will after slider of zipper fastener oven dry after treatment black bronze, carry out surface spraying varnish PROCESS FOR TREATMENT,And then dry.
2. slider of zipper fastener black coating bronze method according to claim 1, is characterized in that: step is drawn in a)Begin chain oil removing time in degreasing tank is 3 minutes.
3. slider of zipper fastener black coating bronze method according to claim 2, is characterized in that: step is adopted in b)With sulfuric acid solution concentration be 5%.
4. slider of zipper fastener black coating bronze method according to claim 3, is characterized in that: step b) inThe time of soaking in sulfuric acid solution is 1 minute.
5. slider of zipper fastener black coating bronze method according to claim 1, is characterized in that: step is drawn in c)The soak time of begin chain in black bronze liquid medicine is 5 minutes.
6. slider of zipper fastener black coating bronze method according to claim 5, is characterized in that: step is drawn in c)The temperature conditions that begin chain is processed in black bronze liquid medicine is 105 DEG C.
7. slider of zipper fastener black coating bronze method according to claim 1, is characterized in that: described black bronze medicineIn water formula, include the sodium chlorite of 35g/l and the NaOH of 40g/l.