CN103910450A - Preparation process of hydrogen-rich water - Google Patents
Preparation process of hydrogen-rich water Download PDFInfo
- Publication number
- CN103910450A CN103910450A CN201410166247.0A CN201410166247A CN103910450A CN 103910450 A CN103910450 A CN 103910450A CN 201410166247 A CN201410166247 A CN 201410166247A CN 103910450 A CN103910450 A CN 103910450A
- Authority
- CN
- China
- Prior art keywords
- hydrogen water
- rich hydrogen
- powder
- hydrogen
- subsequent use
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a preparation process of hydrogen-rich water. The preparation process comprises the following steps of modifying tourmaline powder, mixing the modified tourmaline powder with brucite powder, active carbon and polyethylene powder, which are directly bought from the market to prepare a hydrogen-rich water mixture, heating the hydrogen-rich water mixture to prepare a hydrogen-rich water ball, placing the hydrogen-rich water ball into a closed reaction tank, introducing the degassed pure water into the reaction tank, stirring the degassed pure water and the hydrogen-rich water ball to prepare the hydrogen-rich water, and filtering and filling the hydrogen-rich water. The hydrogen molecule content in the processed water is 20 times that in ordinary weak alkaline ion water, the capacity for eliminating the acid substances in the human body can be improved by 20 times, the high hydrogen content, weak alkalinity, negative potential and small-molecular water are integrated, the acidity and alkalinity of the human body can be balanced, and different diseases can be effectively prevented.
Description
Technical field
The present invention relates to tap water field, especially a kind of preparation technology of rich hydrogen water.
Background technology
Medical research shows a lot of diseases, including old and feeble, be all due to cylinder accumulation the free radical that cannot remove in time cause.Free radical can produce, and in fact it is all producing all the time in large quantities, has only produced harm from excessive a small amount of (about 2%) the radical pair body of plastosome, and as cleaning not in time, consequence is hardly imaginable.We are familiar to lure its excessive reason into, as excessive stress, voracity, excessive drinking, smoking, overworked, ultraviolet radiation or even breathing etc.And the water of hydrogen just has effect of removing organism interior free yl.Hydrogen itself is exactly a kind of best antioxidant.Because hydrogen molecule is very fine, enter the interior energy of body rapid osmotic to whole body, and permeates cell membranes, in the middle of taking away, be difficult to the pernicious active oxygen of eliminating, and be neutralized into water and excrete, and can not affect the running of other benign activity oxygen and body function, and most important, destroyed and oxidized cell can be restored." hydrogen " in water has the strongest redox ability, most of antioxidant that we often eat is as vitamin b6 usp and be not easy through cytolemma, and can not be pointedly only pernicious active oxygen elimination, still more, eat a large amount of vitamin b6 usps, be also difficult to store and absorption in body.According to the experimental analysis that too field professor does, the antioxidant capacity of hydrogen and cell restorability are the most severe so far.
The peroxidation lethality of oxyradical can cause the generation of the aspect pathologies such as tumour, inflammation, aging, leukemia and the heart, liver, lung, skin, oxyradical also can give rise to diseases as arteriosclerosis, hypertension, heart trouble, phlebitis, osteoarthritis, cataract, cancer, immunity system disease, metabolic system disease, irritated abnormalism disease and Parkinson's disease, senile dementia etc., oxyradical promotes degeneration, and acceleration whole body is aging.Research at present finds that at least 70 kinds of above diseases are all relevant with oxyradical.And remove the most safe and reliable effective means of free radical no more than utilizing active hydrogen and oxyradical generation neutralization reaction, produce human life and healthy needing most and the most healthy water.
Hydrogen molecule can in and body in pernicious oxyradical, the various diseases that hydrogen molecule causes for oxyradical has good preventive and therapeutic action, utilize the redoxomorphism of hydrogen molecule can also make human body strengthen resistance of oxidation, delaying senility speed, but because hydrogen has inflammable and explosive property, take in hydrogen by respiratory tract and have in the use certain limitation, more satisfactory method is that hydrogen is dissolved in the water at present, make the saturated solution of Fu Qing, make it take in hydrogen by drinking approach, the approach that has increased hydrogen applications, has improved security.Saturated solution how to prepare rich hydrogen is key problem in technology, utilize tourmalinite hydrogen manufacturing to have been reported, as Chinese patent 200810128419.X and Chinese patent 01137400.4, but because tourmalinite does not have modification, bad dispersibility hydrogen output in water is few, the requirement that does not reach rich hydrogen water.
In view of the foregoing, now invent a kind of preparation technology of rich hydrogen water.
Summary of the invention
The object of the invention is in order to overcome deficiency of the prior art, a kind of preparation technology of rich hydrogen water is provided, in water after treatment, hydrogen molecule content is 20 times of common alkaline ionized water, the ability of removing body inner acidic material strengthens 20 times, integrate high hydrogen amount, weakly alkaline, negative potential, micromolecular water, balance health potential of hydrogen, effectively prevents and treats various diseases.
The present invention to achieve these goals, adopt following technical scheme: a kind of preparation technology of rich hydrogen water, to tourmaline powder modification, tourmaline powder after modification and brucite powder, gac, the polyethylene powder mix and blend directly bought from market are made to rich hydrogen water mixture, to rich hydrogen water mixture, rich hydrogen water polo is made in heating, packs in airtight retort, passes into the pure water after degassed, stirring makes rich hydrogen water, filters filling.
The properties-correcting agent that the massfraction that adds polyvinyl alcohol 1788 to stir to be at normal temperatures mixed with tourmaline powder in tourmaline powder is 0.3-0.9%, for subsequent use; The slip that the massfraction that adds absolute ethyl alcohol and stirring to be mixed with tourmaline powder in tourmaline powder is 15-25%, the heating installation of putting into temperature and be 50-60 ℃ stirs after 10-30min, for subsequent use; Getting properties-correcting agent for subsequent use and slip, is to mix at 3: 100 in mass ratio, after stirring 10-30min, makes modified verdelite powder solution, and modified verdelite powder solution is filtered, is dried, and makes modified verdelite powder, for subsequent use.
In rich hydrogen water mixture, the assembly weight percent of each component is: get modified verdelite powder 40-60% for subsequent use, brucite powder 20-30%, the gac 15-25%, the polyethylene powder 6-8% that directly buy from market, above each component by weight ratio sum is 100%.
It is that the heating installation of 120-135 ℃ heats 30-40min and makes rich hydrogen water polo that rich hydrogen water mixture is put into temperature, and the diameter of rich hydrogen water polo is 2-4mm, and the rich hydrogen water polo making is packed in airtight retort, for subsequent use.
To pure water in vacuum tightness be-carry out vacuum outgas under the state of 0.02-0.01mpa, pure water after vacuum outgas packs in for subsequent use retort that has rich hydrogen water polo, stir 20-50 minute, pure water after vacuum outgas and rich hydrogen water polo are fully contacted produce chemical reaction to make rich hydrogen water, the hydrogen concentration that contains of rich hydrogen water is greater than 1.4ppm, be less than-400mv of negative potential, will pack rich hydrogen water storage tank or directly filling into after the rich hydrogen water filtration making.
The invention has the beneficial effects as follows: hydrogen molecule content of the present invention is 20 times of common alkaline ionized water, the ability of removing body inner acidic material strengthens 20 times, integrate high hydrogen amount, weakly alkaline, negative potential, micromolecular water, balance health potential of hydrogen, effectively prevents and treats various diseases.
The present invention is compared with existing rich hydrogen water technology of preparing: can generating negative ion; All to drink alkalescent water (pH value 7.3～8.8); Can purify water, remove residual chlorine; Be all activation mineralization tap water, increase water mineral more than 9 kinds; Can make water become small-micelle water.But the potential value of the rich hydrogen wetting system of common system reaches-100 arrive-200mv on the market, and the present invention can make reach-500mv of water potential value, and the reductibility of the hydrogen water of making is than powerful 2～5 times of the rich hydrogen wetting system of common system; The rich hydrogen wetting system of common system on the market cannot generate hydrogen and hydrogen water, or few hydrogen, and the present invention's water after treatment can be rich in hydrogen, can effectively suppress human senescence, suppress the various diseases such as hypertension, heart trouble, skin aging and diabetes, be the first-selection of cancer patient.
Accompanying drawing explanation
Below in conjunction with accompanying drawing, the invention will be further described:
Fig. 1 is, preparation technology's schema.
Embodiment
Below in conjunction with embodiment and embodiment, the present invention is described in further detail:
Embodiment 1
The properties-correcting agent that the massfraction that adds polyvinyl alcohol 1788 to stir to be at normal temperatures mixed with tourmaline powder in tourmaline powder is 0.4%, for subsequent use; The slip that the massfraction that adds absolute ethyl alcohol and stirring to be mixed with tourmaline powder in tourmaline powder is 15%, the heating installation of putting into temperature and be 50 ℃ stirs after 10min, for subsequent use; Getting properties-correcting agent for subsequent use and slip, is to mix at 3: 100 in mass ratio, after stirring 15min, makes modified verdelite powder solution, and modified verdelite powder solution is filtered, is dried, and makes modified verdelite powder, for subsequent use.
In rich hydrogen water mixture, the assembly weight percent of each component is: get modified verdelite powder 59% for subsequent use, and brucite powder 20%, gac 15%, the polyethylene powder 6% directly bought from market, above each component by weight ratio sum is 100%; It is the rich hydrogen water polo that the heating installation of 120 ℃ heats 30-40min and make 2-4mm that rich hydrogen water mixture is put into temperature, and the rich hydrogen water polo making is packed in airtight retort, for subsequent use; By pure water in vacuum tightness be-pass in for subsequent use confined reaction tank that rich hydrogen water polo is housed after degassed under the state of 0.02mpa, stir 20 minutes, make rich hydrogen water, after filtering, pack rich hydrogen water storage tank or directly filling into.
Embodiment 2
The properties-correcting agent that the massfraction that adds polyvinyl alcohol 1788 to stir to be at normal temperatures mixed with tourmaline powder in tourmaline powder is 0.3%, for subsequent use; The slip that the massfraction that adds absolute ethyl alcohol and stirring to be mixed with tourmaline powder in tourmaline powder is 25%, the heating installation of putting into temperature and be 55 ℃ stirs after 15min, for subsequent use; Getting properties-correcting agent for subsequent use and slip, is to mix at 3: 100 in mass ratio, after stirring 10min, makes modified verdelite powder solution, and modified verdelite powder solution is filtered, is dried, and makes modified verdelite powder, for subsequent use.
In rich hydrogen water mixture, the assembly weight percent of each component is: get modified verdelite powder 50% for subsequent use, and brucite powder 28%, gac 16%, the polyethylene powder 6% directly bought from market, above each component by weight ratio sum is 100%; It is the rich hydrogen water polo that the heating installation of 125 ℃ heats 30-40min and make 2-4mm that rich hydrogen water mixture is put into temperature, and the rich hydrogen water polo making is packed in airtight retort, for subsequent use; By pure water in vacuum tightness be-pass in for subsequent use confined reaction tank that rich hydrogen water polo is housed after degassed under the state of 0.01mpa, stir 20 minutes, make rich hydrogen water, after filtering, pack rich hydrogen water storage tank or directly filling into.
Embodiment 3
The properties-correcting agent that the massfraction that adds polyvinyl alcohol 1788 to stir to be at normal temperatures mixed with tourmaline powder in tourmaline powder is 0.7%, for subsequent use; The slip that the massfraction that adds absolute ethyl alcohol and stirring to be mixed with tourmaline powder in tourmaline powder is 20%, the heating installation of putting into temperature and be 53 ℃ stirs after 28min, for subsequent use; Getting properties-correcting agent for subsequent use and slip, is to mix at 3: 100 in mass ratio, after stirring 20min, makes modified verdelite powder solution, and modified verdelite powder solution is filtered, is dried, and makes modified verdelite powder, for subsequent use.
In rich hydrogen water mixture, the assembly weight percent of each component is: get modified verdelite powder 55% for subsequent use, and brucite powder 20%, gac 17%, the polyethylene powder 8% directly bought from market, above each component by weight ratio sum is 100%; It is the rich hydrogen water polo that the heating installation of 130 ℃ heats 30-40min and make 2-4mm that rich hydrogen water mixture is put into temperature, and the rich hydrogen water polo making is packed in airtight retort, for subsequent use; By pure water in vacuum tightness be-pass in for subsequent use confined reaction tank that rich hydrogen water polo is housed after degassed under the state of 0.02mpa, stir 25 minutes, make rich hydrogen water, after filtering, pack rich hydrogen water storage tank or directly filling into.
Embodiment 4
The properties-correcting agent that the massfraction that adds polyvinyl alcohol 1788 to stir to be at normal temperatures mixed with tourmaline powder in tourmaline powder is 0.5%, for subsequent use; The slip that the massfraction that adds absolute ethyl alcohol and stirring to be mixed with tourmaline powder in tourmaline powder is 18%, the heating installation of putting into temperature and be 54 ℃ stirs after 30min, for subsequent use; Getting properties-correcting agent for subsequent use and slip, is to mix at 3: 100 in mass ratio, after stirring 25min, makes modified verdelite powder solution, and modified verdelite powder solution is filtered, is dried, and makes modified verdelite powder, for subsequent use.
In rich hydrogen water mixture, the assembly weight percent of each component is: get modified verdelite powder 53% for subsequent use, and brucite powder 25%, gac 15%, the polyethylene powder 7% directly bought from market, above each component by weight ratio sum is 100%; It is the rich hydrogen water polo that the heating installation of 130 ℃ heats 30-40min and make 2-4mm that rich hydrogen water mixture is put into temperature, and the rich hydrogen water polo making is packed in airtight retort, for subsequent use; By pure water in vacuum tightness be-pass in for subsequent use confined reaction tank that rich hydrogen water polo is housed after degassed under the state of 0.01mpa, stir 25 minutes, make rich hydrogen water, after filtering, pack rich hydrogen water storage tank or directly filling into.
Embodiment 5
The properties-correcting agent that the massfraction that adds polyvinyl alcohol 1788 to stir to be at normal temperatures mixed with tourmaline powder in tourmaline powder is 0.5%, for subsequent use; The slip that the massfraction that adds absolute ethyl alcohol and stirring to be mixed with tourmaline powder in tourmaline powder is 25%, the heating installation of putting into temperature and be 56 ℃ stirs after 30min, for subsequent use; Getting properties-correcting agent for subsequent use and slip, is to mix at 3: 100 in mass ratio, after stirring 30min, makes modified verdelite powder solution, and modified verdelite powder solution is filtered, is dried, and makes modified verdelite powder, for subsequent use.
In rich hydrogen water mixture, the assembly weight percent of each component is: get modified verdelite powder 45% for subsequent use, and brucite powder 25%, gac 24%, the polyethylene powder 6% directly bought from market, above each component by weight ratio sum is 100%; It is the rich hydrogen water polo that the heating installation of 122 ℃ heats 30-40min and make 2-4mm that rich hydrogen water mixture is put into temperature, and the rich hydrogen water polo making is packed in airtight retort, for subsequent use; By pure water in vacuum tightness be-pass in for subsequent use confined reaction tank that rich hydrogen water polo is housed after degassed under the state of 0.02mpa, stir 25 minutes, make rich hydrogen water, after filtering, pack rich hydrogen water storage tank or directly filling into.
Embodiment 6
The properties-correcting agent that the massfraction that adds polyvinyl alcohol 1788 to stir to be at normal temperatures mixed with tourmaline powder in tourmaline powder is 0.9%, for subsequent use; The slip that the massfraction that adds absolute ethyl alcohol and stirring to be mixed with tourmaline powder in tourmaline powder is 23%, the heating installation of putting into temperature and be 58 ℃ stirs after 25min, for subsequent use; Getting properties-correcting agent for subsequent use and slip, is to mix at 3: 100 in mass ratio, after stirring 18min, makes modified verdelite powder solution, and modified verdelite powder solution is filtered, is dried, and makes modified verdelite powder, for subsequent use.
In rich hydrogen water mixture, the assembly weight percent of each component is: get modified verdelite powder 55% for subsequent use, and brucite powder 20%, gac 18%, the polyethylene powder 7% directly bought from market, above each component by weight ratio sum is 100%; It is the rich hydrogen water polo that the heating installation of 127 ℃ heats 30-40min and make 2-4mm that rich hydrogen water mixture is put into temperature, and the rich hydrogen water polo making is packed in airtight retort, for subsequent use; By pure water in vacuum tightness be-pass in for subsequent use confined reaction tank that rich hydrogen water polo is housed after degassed under the state of 0.01mpa, stir 50 minutes, make rich hydrogen water, after filtering, pack rich hydrogen water storage tank or directly filling into.
Claims (5)
1. the preparation technology of a rich hydrogen water, it is characterized in that: to tourmaline powder modification, tourmaline powder after modification and brucite powder, gac, the polyethylene powder mix and blend directly bought from market are made to rich hydrogen water mixture, rich hydrogen water mixture heating is made to rich hydrogen water polo, pack in airtight retort, pass into the pure water after degassed, stir and make rich hydrogen water, filter filling.
2. the preparation technology of a kind of rich hydrogen water according to claim 1, is characterized in that: the properties-correcting agent that the massfraction that adds polyvinyl alcohol 1788 to stir to be at normal temperatures mixed with tourmaline powder in tourmaline powder is 0.3-0.9%, and for subsequent use; The slip that the massfraction that adds absolute ethyl alcohol and stirring to be mixed with tourmaline powder in tourmaline powder is 15-25%, the heating installation of putting into temperature and be 50-60 ℃ stirs after 10-30min, for subsequent use; Getting properties-correcting agent for subsequent use and slip, is to mix at 3: 100 in mass ratio, after stirring 10-30min, makes modified verdelite powder solution, and modified verdelite powder solution is filtered, is dried, and makes modified verdelite powder, for subsequent use.
3. the preparation technology of a kind of rich hydrogen water according to claim 1, it is characterized in that: in rich hydrogen water mixture, the assembly weight percent of each component is: get modified verdelite powder 40-60% for subsequent use, brucite powder 20-30%, the gac 15-25%, the polyethylene powder 6-8% that directly buy from market, above each component by weight ratio sum is 100%.
4. the preparation technology of a kind of rich hydrogen water according to claim 1, it is characterized in that: it is that the heating installation of 120-135 ℃ heats 30-40min and makes rich hydrogen water polo that rich hydrogen water mixture is put into temperature, the diameter of rich hydrogen water polo is 2-4mm, the rich hydrogen water polo making is packed in airtight retort, for subsequent use.
5. the preparation technology of a kind of rich hydrogen water according to claim 1, it is characterized in that: to pure water in vacuum tightness be-carry out vacuum outgas under the state of 0.02-0.01mpa, pure water after vacuum outgas packs in for subsequent use retort that has rich hydrogen water polo, stir 20-50 minute, pure water after vacuum outgas and rich hydrogen water polo are fully contacted produce chemical reaction to make rich hydrogen water, the hydrogen concentration that contains of rich hydrogen water is greater than 1.4ppm, be less than-400mv of negative potential, will pack rich hydrogen water storage tank or directly filling into after the rich hydrogen water filtration making.