CN103903673A - 一种铝合金电缆 - Google Patents
一种铝合金电缆 Download PDFInfo
- Publication number
- CN103903673A CN103903673A CN201410160974.6A CN201410160974A CN103903673A CN 103903673 A CN103903673 A CN 103903673A CN 201410160974 A CN201410160974 A CN 201410160974A CN 103903673 A CN103903673 A CN 103903673A
- Authority
- CN
- China
- Prior art keywords
- copper
- aluminum alloy
- alloy cable
- magnesium
- aluminium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种铝合金电缆，所述电缆材料的组合物按重量百分比的组分为：0.02%-0.04%的铜，0.003%-0.03%的硼，0.04%-0.06%的铁，0.001%-0.05%的铬，0.001%-0.05%的锰，0.002%-0.03%的镁，0.001%-0.03%的镍，0.08%-0.15%的硅，0.001%-0.06%的钛，0.001%-0.03%的钒，0.005%-0.05%的锌，0.001%-0.01%的锆，0.05%-0.15%的稀土元素，余量为铝以及不可避免的杂质。本发明的突出优点在于铜、镁铬、铁等合金化元素的加入，特别是其特点含量的配比，使得铝合金电导率、抗拉强度、耐热性和稳定性都得到了提高，有利于工业成产和应用。
Description
技术领域：
本发明涉及电线电缆，尤其是一种铝合金电缆。
背景技术:
电线电缆的导体材质通常为铜、铝、铝合金三种，全球是贫铜富铝的资源现状，而铜资源越来越稀缺，尤其是我国70%以上的铜材依靠进口，铜价目前已是铝价的3倍以上，所以以铝节铜就迫在眉睫，但是铝导体在实际应用中就是柔韧性很差，多次弯曲后容易断裂，抗蠕性差、抗拉强度差、延展性差等缺陷，使得铝芯电缆事故频发，因此很多重要的易燃易爆场所限制铝芯电缆的使用。
8000系列铝合金导体不同于以往的纯铝导体，通过在纯铝材料的基础上添加了铜、铁、镁、硅和稀土元素等多种元素，经过特殊的工艺合成和退火处理等先进工艺，克服了纯铝电缆的不足，机械性能与铜基本接近。近年来我国快速采用了这种技术，广泛应用到各行各业中，但是，现有技术生产的铝合金导体的电导率、耐热性、稳定性、抗拉强度等指标在某些领域尚不能满足要求。
发明内容:
本发明为了解决现有技术问题提供一种高电导率、高耐热性、高稳定性、高抗拉强度的铝合金电缆。
为解决以上技术问题，本发明所述的一种铝合金电缆，在于包括下述重量百分比的元素：0.02%-0.04%的铜，0.003%-0.03%的硼，0.04%-0.06%的铁，0.001%-0.05%的铬，0.001%-0.05%的锰，0.002%-0.03%的镁，0.001%-0.03% 的镍，0.08%-0.15%的硅，0.001%-0.06%的钛，0.001%-0.03%的钒，0.005%-0.05%的锌，0.001%-0.01%的锆，0.05%-0.15%的稀土元素，余量为铝以及不可避免的杂质。
优选：0.005%-0.03%的镁。
优选：0.004%-0.01%的镍。
优选：0.001%-0.01%的钒。
本发明的突出优点之一在于铜、镁、铬、铁等合金化元素的加入，特别是其特定含量的配比，使得铝合金电导率、抗拉强度、耐热性和稳定性都得到了提高。
具体实施方式
实施例一：
0.025%的铜，0.015%的硼，0.045%的铁，0.02%的铬，0.02%的锰，0.008%的镁，0.008%的镍，0.10%的硅，0.02%的钛，0.02%的钒，0.02%的锌，0.004%的锆，0.08%的稀土元素，余量为铝以及不可避免的杂质。
余量为铝及不可避免的杂质。
实施例二：
0.035%的铜，0.02%的硼，0.05%的铁，0.04%的铬，0.04%的锰，0.02%的镁，0.02%的镍，0.15%的硅，0.04%的钛，0.025%的钒，0.035%的锌，0.008%的锆，0.12%的稀土元素，余量为铝以及不可避免的杂质。
申请人声明，本发明通过上述实施例来说明本发明的详细组成和工艺流程，但本发明并不局限于上述详细组成和工艺流程，即不意味着本发明必须依赖上述详细组成和工艺流程才能实施。所属技术领域的技术人员应该明了，对本发明的任何改进，对本发明产品各原料的等效替换及辅助成分的添加、 具体方式的选择等，均落在本发明的保护范围和公开范围之内。
Claims (4)
1.一种铝合金电缆，包括下述重量的组分：0.02%-0.04%的铜，0.003%-0.03%的硼，0.04%-0.06%的铁，0.001%-0.05%的铬，0.001%-0.05%的锰，0.002%-0.03%的镁，0.001%-0.03%的镍，0.08%-0.15%的硅，0.001%-0.06%的钛，0.001%-0.03%的钒，0.005%-0.05%的锌，0.001%-0.01%的锆，0.05%-0.15%的稀土元素，余量为铝以及不可避免的杂质。
2.如权利要求1所述的铝合金电缆，其特征在于：0.005%-0.03%的镁。
3.如权利要求1所述的铝合金电缆，其特征在于：0.004%-0.01%的镍。
4.如权利要求1所述的铝合金电缆，其特征在于：0.001%-0.01%的钒。