CN103899070A - Diatom ooze modular product for improving indoor environment and manufacturing method thereof - Google Patents
Diatom ooze modular product for improving indoor environment and manufacturing method thereof Download PDFInfo
- Publication number
- CN103899070A CN103899070A CN201410175916.0A CN201410175916A CN103899070A CN 103899070 A CN103899070 A CN 103899070A CN 201410175916 A CN201410175916 A CN 201410175916A CN 103899070 A CN103899070 A CN 103899070A
- Authority
- CN
- China
- Prior art keywords
- diatom ooze
- module
- skeleton
- improving
- indoor environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a diatom ooze modular product for improving the indoor environment and a manufacturing method of the diatom ooze modular product. The diatom ooze modular product comprises a diatom ooze module and hanging parts. The diatom ooze module comprises diatom ooze and a framework. The framework is composed of a plurality of main rods and/or auxiliary rods, the main rods and/or the auxiliary rods are connected to form the integral framework in a warp and weft knitting or welding or binding mode, the framework is embedded into or cast in the diatom ooze, and the hanging parts are connected with the diatom ooze module. According to the diatom ooze modular product for improving the indoor environment and the manufacturing method of the diatom ooze modular product, the prefabricating machining method can be adopted, the defects that when machining is directly carried out on a wall, performance cannot be controlled, and surface performance is poor are overcome, and the indoor visual environment can be improved; due to the fact that the framework is adopted, strength of the diatom ooze modular product is improved, the diatom ooze modular product is prevented from being broken, the indoor surface area is increased, models of the diatom ooze modular product can be enriched, and efficiency for improving the indoor air environment can be improved; the diatom ooze modular product is easy to machine and low in manufacturing cost, and facilitates industrial production, popularization and use.
Description
Technical field
The present invention relates to a kind of diatom ooze goods and manufacture method thereof, be specifically related to a kind of for improving diatom ooze modularization goods and the manufacture method thereof of indoor environment.
Background technology
That present interior architecture ornament materials ubiquity pollutes is high, variability is few, and indoor environment after finishing exists the potential safety hazards such as hazardous material exceeds standard, toxic gas release.Diatom ooze is the nonmetallic mineral material of a kind of porous light weight, soft-touch, excellent adsorption, nonpoisonous and tasteless, acid-fast alkali-proof, low-density and insulation.Diatom ooze belongs to a kind of high activity sorbing material with it and is well-known, unique " molecular sieve " structures shape its there is extremely strong adsorption function and ion exchanging function.Can realize the absorption of the airborne hazardous substances such as PARA FORMALDEHYDE PRILLS(91,95), dust, reach the object of improving indoor air environment.But the construction of traditional diatom ooze is generally the integral construction to large area metope, and can not well control the appearance characteristics such as moulding and color of diatom ooze metope.In the time that needs are changed interior decoration layout or household visual environment is transformed, need the diatom ooze of whole face wall to demolish.Not only site operation trouble, but also may cause the waste of resource and produce unnecessary building waste.In prior art, the patent relevant with diatom ooze has more the field such as composition, proportioning and production and construction method of present diatom ooze product, because product directly goes up that wall construction ubiquity performance is uncontrollable, surface property is not good, decorative effect simple and purposes is more single conventionally, after moulding easily damaged, be difficult for the problems such as processing.
Summary of the invention
The object of the invention is for deficiency of the prior art, provide a kind of for improving diatom ooze modularization goods and the manufacture method thereof of indoor environment.
The present invention addresses the above problem the technical scheme of taking to be: described for improving the diatom ooze modularization goods of indoor environment, comprise diatom ooze module, suspender, described diatom ooze module comprises diatom ooze and skeleton, described skeleton is made up of some main bones and/or fibula, described main bone and/or described fibula are by being interconnected to the described skeleton of entirety through knitting device, welding or binding, described skeleton is embedded in or waters and casts from described diatom ooze, and described suspender is connected with described diatom ooze module.
The invention has the beneficial effects as follows: the present invention can take the method for prefabricated processing, avoided, in the metope defect that performance is uncontrollable, surface property is not good that directly processing there will be, being beneficial to and improving Visual Environment; Owing to having adopted skeleton, product strength is increased, in avoiding diatom ooze goods to break, make modularization goods be shaped to for possibility based on skeleton, when increase chamber internal surface is long-pending, be conducive to enrich the moulding of modularization goods, be improved the efficiency of improving of indoor air environment; Diatom ooze goods are become and can, for the diatom ooze module hanging, be conducive to enrich the expression effect of diatom ooze module; The present invention is easy to processing, and cost of manufacture is low, is convenient to realize suitability for industrialized production and promotes the use of.
Accompanying drawing explanation
Fig. 1 is broken section structural representation of the present invention;
Fig. 2 is perspective view of the present invention;
Fig. 3 is the back side of the present invention effect schematic diagram;
Fig. 4 is part sectioned view of the present invention;
Fig. 5 is U-shaped metal suspender of the present invention and uses state diagram;
Fig. 6 is hanging part of the present invention, background color coating and decoration figure layer schematic diagram;
Fig. 7 is link of the present invention and hook schematic diagram;
Fig. 8 is cross-sectional view of the present invention
In figure, each several part implication is as follows:
1 diatom ooze module; 11 diatom oozes; 2 skeletons; 21 main bones; 22 fibulas; 23 metallic frameworks; 3 suspenders; 31U shape metal suspender; 32 Pear-Shaped suppending holes; 4 hanging parts; 41 links; 42 hooks; 5 background color coatings; 6 decorate figure layer.
The specific embodiment
The specific embodiment one: present embodiment is described in conjunction with Fig. 1, described in present embodiment for improving the diatom ooze modularization goods of indoor environment, comprise diatom ooze module 1, suspender 3, described diatom ooze module 1 comprises diatom ooze 11 and skeleton 2, described skeleton 2 is made up of some main bones 21 and/or fibula 22, described main bone 21 and/or described fibula 22 are interconnected to the described skeleton 2 of entirety by braiding, welding or binding, described skeleton 2 is embedded in or waters and casts from described diatom ooze 11, and described suspender 3 is connected with described diatom ooze module 1.
The technique effect of present embodiment is: utilize the connection of described suspender 3 and described diatom ooze module 1, can realize the free suspension of described diatom ooze module 1 at indoor wall, by described skeleton 2 is set in described diatom ooze module 1, product strength is increased; By described skeleton 2 being set in avoiding diatom ooze goods to break, modularization goods are shaped to for possibility based on described skeleton 2, increasing chamber internal surface and be conducive to enrich in long-pending the moulding of modularization goods, be not only conducive to improve improving efficiency but also being conducive to enrich the expression effect of described diatom ooze module 1 indoor air environment; Can make the prefabricated processing of goods become possibility by this embodiment, avoid directly processing at metope the defect that performance is uncontrollable, surface property is not good of appearance, be beneficial to and improve Visual Environment.
The specific embodiment two: in conjunction with Fig. 1 and Fig. 2, present embodiment is described, for improving the diatom ooze modularization goods of indoor environment, described skeleton 2 is preferably metallic framework 23 described in present embodiment.
The technique effect of present embodiment is: by using described metallic framework 23, but relative minimizing the consumption of material improved intensity and the toughness of goods, in reducing framework material volume accounting, make overall structure more firm; Because the metal that described metallic framework 23 uses is convenient to suitability for industrialized production and is had certain plasticity and ductility, so be not only beneficial to batch production, be also beneficial to the realization of various different skeleton mouldings.
The specific embodiment three: in conjunction with Fig. 1 and Fig. 2, present embodiment is described, for improving the diatom ooze modularization goods of indoor environment, described metallic framework 23 is preferably stainless steel insert, aluminum alloy framework or copper skeleton described in present embodiment.
The technique effect of present embodiment is: by selecting stainless steel insert, aluminum alloy framework or copper skeleton, reduced described for improve indoor environment diatom ooze modularization goods manufacturing cost and antirust, guarantee that the aspect such as ornamental has promoted the performance of product, is beneficial to promoting the use of of this technology.
The specific embodiment four: present embodiment is described in conjunction with Fig. 1, Fig. 2 and Fig. 3, described in present embodiment for improving the diatom ooze modularization goods of indoor environment, described suspender 3 is connected with the described skeleton 2 in described diatom ooze module 1, the part that described suspender 3 is connected with described skeleton is placed in described diatom ooze module 1 inside, and remainder is placed in described diatom ooze module 1 outside.
The technique effect of present embodiment is: can make described diatom ooze module 1 be able to hang at metope by described suspender 3 is set, realizing any combination of diatom ooze modularization goods installs, not only make diatom ooze modular product be easy to change and install, also make decorative effect versatile and flexible, bring into play it and improve the effect of Visual Environment.
The specific embodiment five: present embodiment is described in conjunction with Fig. 2, Fig. 3 and Fig. 4, described in present embodiment for improving the diatom ooze modularization goods of indoor environment, described skeleton 2 in described diatom ooze module 1 is connected with U-shaped metal suspender 31, the part that described U-shaped metal suspender 31 is connected with described skeleton is placed in described diatom ooze module 1 inside, remainder is placed in described diatom ooze module 1 outside, and described U-shaped metal suspender 31 is connected by the mode of interspersed interlock, welding or binding with described skeleton 2.
The technique effect of present embodiment is: can install more easily by described U-shaped metal suspender 31 is set, improve the stability that described metallic framework and diatom ooze module hang, make being connected with interface of diatom ooze modularization goods more convenient and quicker.
The specific embodiment six: present embodiment is described in conjunction with Fig. 3, Fig. 4 and Fig. 5, different from the specific embodiment five for improving the diatom ooze modularization goods of indoor environment described in present embodiment: on described U-shaped metal suspender 31, to have Pear-Shaped suppending hole 32, described Pear-Shaped suppending hole 32 bottom holes are large, and upper hole is little.
The technique effect of present embodiment is: can make iron nail, wood screw or picture hanger be connected with U-shaped metal suspender more easily by described Pear-Shaped suppending hole 32 is set, when the rounded head on wall is by after the macropore of Pear-Shaped suppending hole bottom, can be engaged on nail by the effect Pear-Shaped suppending hole top aperture of gravity, and then make the metope that is placed in of diatom ooze module stability.
The specific embodiment seven: present embodiment is described in conjunction with Fig. 6, different from the specific embodiment six for improving the diatom ooze modularization goods of indoor environment described in present embodiment: on the side of described diatom ooze module 1, have the hanging part 4 being connected with described skeleton 2, described hanging part 4 arranges in pairs on the relative side of described diatom ooze module 1.
The technique effect of present embodiment is: can make diatom ooze module be extended on length or width by described hanging part 4 is set, increase the relative stability of polylith diatom ooze intermodule, and can be without being all connected with metope at each piece diatom ooze back side in the occasion having, overcome the defect of part special operation condition, be convenient to Fast Installation.
The specific embodiment eight: present embodiment is described in conjunction with Fig. 6 and Fig. 7, different from the specific embodiment seven for improving the diatom ooze modularization goods of indoor environment described in present embodiment: on a side of described diatom ooze module 1, to be provided with the link 41 being connected with described skeleton 2, on another relative side of described diatom ooze module 1, to be provided with the hook 42 being connected with described skeleton 2; Described hook 41 and described hook 42 arrange in pairs.
The technique effect of present embodiment is: can realize more flexibly the suspension of diatom ooze module by described link 41 and described hook 42 are set, in the time that hook 42 is hooked on link 41, hangs more stable and be not easy to come off; This hang is simple, is easy to realize.
The specific embodiment nine: present embodiment is described in conjunction with Fig. 6, Fig. 7 and Fig. 8, different from the specific embodiment eight for improving the diatom ooze modularization goods of indoor environment described in present embodiment: have in described diatom ooze module 1 front with kieselguhr and inorganic toner and be in harmonious proportion the background color coating 5 of being processed into, the thickness of described background color coating 5 is 0.1mm-2mm.
The technique effect of present embodiment is: described background color coating 5 is set can reduces the use of inorganic toner, be conducive to reduce the cost of production of integral module goods; Utilize background color coating 5 to carry out diatom ooze module floating and painted, both can protect diatom ooze module can also enrich the decorative effect of goods, be conducive to improve Visual Environment effect; Through overtesting, in the time that background color coating layer thickness value is less than 0.1mm or is greater than 2mm, difficulty of construction can increase, and manufacturing cost can increase to some extent; In the time that being less than 0.1mm, background color coating layer thickness value has that levelability is poor and the defect of color shading affects products appearance effect.
The specific embodiment ten: present embodiment is described in conjunction with Fig. 6, Fig. 7 and Fig. 8, different from the specific embodiment nine for improving the diatom ooze modularization goods of indoor environment described in present embodiment: in described background color coating 5, also to there is decoration figure layer 6, the primary raw material of described decoration figure layer 6 is the kieselguhr that adds inorganic toner, described decoration figure layer 6 with spraying, showering, push, smear or molding mode is made, the thickness of described decoration figure layer is 0.1mm-10mm.
The technique effect of present embodiment is: can make the decorative effect of diatom ooze modularization product surface be greatly enhanced by decorative coveringn 6 is set, have the effect that good Visual Environment improves; Decoration figure layer 6 is set on the basis of background color coating 5 and can pursues novelty and the singularity of pattern, and without the inhomogeneous and inadequate problem of levelability of misgivings color; Decoration figure layer with spraying, showering, push, smear or molding mode is made and can be made surface have the three-dimensional sense that rises and falls, in increasing surface area, there is better stereoscopic visual effect.
The specific embodiment 11: in conjunction with Fig. 1 ~ Fig. 8, present embodiment is described, the manufacture method for the diatom ooze modularization goods that improve indoor environment described in present embodiment is: the first step, is mixed into mud paste by diatom ooze 11 and water; Second step, weaves, welds or be bundled into by described main bone 21 and/or described fibula 22 the described skeleton 2 that is interconnected to entirety; The 3rd step, by described suspender 3 and described skeleton 2 interspersed interlock, welding or binding; The 4th step, is filled in the described diatom ooze 11 of mud paste in the mould that is placed with described skeleton 2; The 5th step, is placed in concussion equipment by described mould and shakes; The 6th step, it is that 30% ~ 80% environment leaves standstill 24h that mould is placed in to relative humidity, forms the diatom ooze module 1 with intensity; The 7th step, by the mould removal of described diatom ooze module 1 outside; The 8th step, the surface of the described diatom ooze module 1 after the demoulding with spraying, showering, push, smear or molding mode arranges background color coating 5; The 9th step, in described background color coating 5 suitable position with spraying, showering, push, smear or molding mode arranges decoration figure layer 6.
The specific embodiment 12: present embodiment is described in conjunction with Fig. 1 ~ Fig. 8, described in present embodiment, be for the manufacture method of diatom ooze modularization goods and the difference of true mode 11 that improve indoor environment: the material of the described skeleton 2 that second step adopts is stainless steel, aluminium alloys or copper, described skeleton 2 is by forming metallic framework 23 through knitting device; At least establish a link 41 in one end of described metallic framework 23, at least establish a hook 42 at the other end.
The specific embodiment 13: present embodiment is described in conjunction with Fig. 1 ~ Fig. 8, described in present embodiment, be for the manufacture method of diatom ooze modularization goods and the difference of true mode 12 that improve indoor environment: the 5th step, is placed in concussion equipment by described mould and shakes 10～20 minutes; The 6th step, is placed in mould in climatic chamber, and the temperature of setting climatic chamber is 80 degrees Celsius, and relative humidity is 40%～45%, places 30～50 minutes; After complete, mould being placed in to relative humidity is that 30% ~ 80% environment leaves standstill 24h.
The specific embodiment 14: present embodiment is described in conjunction with Fig. 1 ~ Fig. 8, described in present embodiment, be for the manufacture method of diatom ooze modularization goods and the difference of true mode 13 that improve indoor environment: the 8th step, described diatom ooze module 1 after the demoulding is laid on horizontal plane, kieselguhr and inorganic toner are in harmonious proportion to be processed into water content be coloured diatom ooze of 70%～80%, and carry out showering in described diatom ooze module 1.
The specific embodiment 15: present embodiment is described in conjunction with Fig. 1 ~ Fig. 8, described in present embodiment, be for the manufacture method of diatom ooze modularization goods and the difference of true mode 14 that improve indoor environment: the 9th step, described diatom ooze module 1 is laid on horizontal plane, kieselguhr and inorganic toner are in harmonious proportion to be processed into water content be coloured diatom ooze of 50%～60%, the coloured diatom ooze that is 50%～60% by described water content is put into can extruded type molder tool bag, and in described background color coating 5 suitable position with described can extruded type molder tool bag, squeeze out and there is relief decorative pattern or decorative pattern, form and decorate figure layer 6.
Claims (10)
1. for improving the manufacture method of diatom ooze modularization goods of indoor environment, it is characterized in that: the first step, is mixed into mud paste by diatom ooze (11) and water; Second step, weaves main bone (21) and/or fibula (22), weld or is bundled into and be interconnected to overall skeleton (2); The 3rd step, by interspersed to suspender (3) and described skeleton (2) interlock, welding or binding; The 4th step, is filled in the described diatom ooze (11) of mud paste in the mould that is placed with described skeleton (2); The 5th step, is placed in concussion equipment by described mould and shakes; The 6th step, it is that 30%～80% environment leaves standstill 24h that described mould is placed in to relative humidity, forms the diatom ooze module (1) with intensity; The 7th step, by the outside described mould removal of described diatom ooze module (1); The 8th step, the surface of the described diatom ooze module (1) after the demoulding with spraying, showering, push, smear or molding mode arranges background color coating (5); The 9th step, in the upper suitable position of described background color coating (5) with spraying, showering, push, smear or molding mode arranges decoration figure layer (6).
2. according to claim 1 for improving the manufacture method of diatom ooze modularization goods of indoor environment, it is characterized in that: second step, the material of the described skeleton (2) adopting is stainless steel, aluminium alloys or copper, and described skeleton (2) is by forming metallic framework (23) through knitting device; At least establish a link (41) in one end of described metallic framework (23), at least establish a hook (42) at the other end.
3. according to claim 2 for improving the manufacture method of diatom ooze modularization goods of indoor environment, it is characterized in that: the 5th step, is placed in concussion equipment by described mould and shakes 10～20 minutes; The 6th step, is placed in mould in climatic chamber, and the temperature of setting climatic chamber is 80 degrees Celsius, and relative humidity is 40%～45%, places 30～50 minutes; After complete, mould being placed in to relative humidity is that 30%～80% environment leaves standstill 24h.
4. according to claim 3 for improving the manufacture method of diatom ooze modularization goods of indoor environment, it is characterized in that: the 8th step, described diatom ooze module (1) after the demoulding is laid on horizontal plane, kieselguhr and inorganic toner are in harmonious proportion to be processed into water content be coloured diatom ooze of 70%～80%, and carry out showering in described diatom ooze module (1); The 9th step, described diatom ooze module (1) is laid on horizontal plane, kieselguhr and inorganic toner are in harmonious proportion to be processed into water content be coloured diatom ooze of 50%～60%, the coloured diatom ooze that is 50%～60% by described water content is put into can extruded type molder tool bag, and in the upper suitable position of described background color coating (5) with described can extruded type molder tool bag, squeeze out and there is relief decorative pattern or decorative pattern, form and decorate figure layer (6).
5. for improving the diatom ooze modularization goods of indoor environment, comprise diatom ooze (11), skeleton (2), suspender (3), hanging part (4), it is characterized in that: described diatom ooze (11) and described skeleton (2) form diatom ooze module (1) jointly, described skeleton (2) is made up of some main bones (21) and/or fibula (22), described main bone (21) and/or described fibula (22) are by braiding, welding or binding and be interconnected to entirety described skeleton (2), described skeleton (2) is embedded in or waters and casts from described diatom ooze (11), described suspender (3) is connected with described diatom ooze module (1), described suspender (3) is connected with the described skeleton (2) in described diatom ooze module (1), the part that described suspender (3) is connected with described skeleton (2) is placed in described diatom ooze module (1) inside, remainder is placed in described diatom ooze module (1) outside, on the side of described diatom ooze module (1), there is the hanging part (4) being connected with described skeleton (2), described hanging part (4) arranges in pairs on the relative side of described diatom ooze module (1).
6. according to claim 5 for improving the diatom ooze modularization goods of indoor environment, it is characterized in that: on a side of described diatom ooze module (1), be provided with the link (41) being connected with described skeleton (2), on another relative side of described diatom ooze module (1), be provided with the hook (42) being connected with described skeleton (2); Described hook (41) and described hook (42) arrange in pairs.
7. according to claim 6 for improving the diatom ooze modularization goods of indoor environment, it is characterized in that: described diatom ooze module (1) front has with diatom ooze (11) and inorganic toner and is in harmonious proportion the background color coating (5) of being processed into, and the thickness of described background color coating (5) is 0.1mm-2mm.
8. according to claim 7 for improving the diatom ooze modularization goods of indoor environment, it is characterized in that: in described background color coating (5), also have with diatom ooze (11) and inorganic toner be in harmonious proportion processing and through spraying, showering, push, smear or decoration figure layer (6) that molding mode is made, the thickness of described decoration figure layer (6) is 0.1mm-10mm.
According to described in claim 5,6,7 or 8 for improving the diatom ooze modularization goods of indoor environment, it is characterized in that: described skeleton (2) is preferably metallic framework (23), described metallic framework (23) can be iron skeleton, stainless steel insert, aluminum alloy framework or copper skeleton etc.
10. according to claim 9 for improving the diatom ooze modularization goods of indoor environment, it is characterized in that: the described metallic framework (23) in described diatom ooze module (1) is connected with U-shaped metal suspender (31), the part that described U-shaped metal suspender (31) is connected with described metallic framework (23) is placed in described diatom ooze module (1) inside, remainder is placed in described diatom ooze module (1) outside, described U-shaped metal suspender (31) passes through interspersed interlock with described metallic framework (23), the mode of welding or binding is connected, on described U-shaped metal suspender (31), have Pear-Shaped suppending hole (32), described Pear-Shaped suppending hole (32) bottom hole is large, upper hole is little.