CN103897500A - Long-acting polyethylene anticorrosive paint - Google Patents
Long-acting polyethylene anticorrosive paint Download PDFInfo
- Publication number
- CN103897500A CN103897500A CN201210569525.8A CN201210569525A CN103897500A CN 103897500 A CN103897500 A CN 103897500A CN 201210569525 A CN201210569525 A CN 201210569525A CN 103897500 A CN103897500 A CN 103897500A
- Authority
- CN
- China
- Prior art keywords
- parts
- resistance
- paint
- long
- acting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a long-acting polyethylene anticorrosive paint which comprises the following components: 20-50 parts of polyolefin resin, 12-16 parts of butyl ester, 2-5 parts of isopropanol, 4-6 parts of barium sulfate, 3-5 parts of xylene, and 10-25 parts of methyl cyclohexane. The paint also comprises 2-7 parts of aluminum tripolyphosphate. The paint has excellent chemical resistance, aging resistance, salt fog resistance and humidity and heat resistance; a paint film is hard, and has impact resistance, wear resistance, wide oil resistance, and wide solvent resistance; the paint can be used in cooperation with most high-performance antirust paints and finishing paints; and the paint has quite good adhesive force to a metal coating layer, has excellent construction characteristics under various atmospheric environments, and can be widely applied for corrosion prevention of industrial steel structures, concrete structures and metal surfaces.
Description
Technical field
The present invention relates to a kind of coating, especially a kind of long-acting polyethylene anti-corrosion coating.
Background technology
Domestic existing heavy-duty coating is take epoxy resin or chlorinated rubber as main film forming substance; epoxies heavy-duty coating is generally that two components form; need to before application, strictly press proportioning paint; and pot-life is shorter, must in 6-8 hour, be finished, otherwise becomes colloidin; its physical and mechanical property is stable not; exist weathering resistance poor, the problem such as the corrosionproof protection time is short, effect the is undesirable simultaneously weathering resistance of epoxies heavy-duty coating is poor, has limited its application out of doors.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of long-acting polyethylene anti-corrosion coating.
For solving the problems of the technologies described above, long-acting polyethylene anti-corrosion coating of the present invention, it comprises following component, polyolefin resin 20-50 part, butyl ester 12-16 part, Virahol 2-5 part, barium sulfate 4-6 part, dimethylbenzene 3-5 part, methylcyclohexane 10-25 part.
Described coating also comprises aluminium triphosphate 2-7 part.
Coating of the present invention has good anti-chemical, ageing resistance, salt fog resistance and humidity resistance; Paint film is hard, has shock-resistant, wear-resisting, oil resistant, solvent resistance widely; Can support the use with most of high-performance rust-inhibiting paint and finish paint; Metallic coating is had to good sticking power, under multiple Atmospheric Condition, there is superior construction property, can be widely used in Industrial Steel structure, cement structures and metallic surface anticorrosion.
Embodiment
Embodiment 1
Long-acting polyethylene anti-corrosion coating of the present invention, it comprises following component, 20 parts of polyolefin resines, 16 parts of butyl esters, 5 parts of Virahols, 6 parts, barium sulfate, 5 parts of dimethylbenzene, 10 parts of methylcyclohexanes, 2 parts of aluminium triphosphates.
Embodiment 2
Long-acting polyethylene anti-corrosion coating of the present invention, it comprises following component, 50 parts of polyolefin resines, 12 parts of butyl esters, 2 parts of Virahols, 4 parts, barium sulfate, 5 parts of dimethylbenzene, 10 parts of methylcyclohexanes, 7 parts of aluminium triphosphates.
Embodiment 3
Long-acting polyethylene anti-corrosion coating of the present invention, it comprises following component, 40 parts of polyolefin resines, 15 parts of butyl esters, 3 parts of Virahols, 5 parts, barium sulfate, 4 parts of dimethylbenzene, 20 parts of methylcyclohexanes, 5 parts of aluminium triphosphates.
The above, be only to preferred embodiment of the present invention, not the present invention done to other forms of restriction, and any those skilled in the art may utilize the technology contents of above-mentioned announcement to be changed or be modified as the equivalent embodiment of equal variation.Every the present invention program's content that do not depart from,, all drops in protection scope of the present invention any simple modification made for any of the above embodiments, equivalent variations and remodeling according to technical spirit of the present invention.
Claims (2)
1. a long-acting polyethylene anti-corrosion coating, is characterized in that: it comprises following component, polyolefin resin 20-50 part, butyl ester 12-16 part, Virahol 2-5 part, barium sulfate 4-6 part, dimethylbenzene 3-5 part, methylcyclohexane 10-25 part.
2. according to long-acting polyethylene anti-corrosion coating claimed in claim 1, it is characterized in that: described coating also comprises aluminium triphosphate 2-7 part.