CN103897415B - A kind of preparation method mixing plastic-wood floor material - Google Patents
A kind of preparation method mixing plastic-wood floor material Download PDFInfo
- Publication number
- CN103897415B CN103897415B CN201410146030.3A CN201410146030A CN103897415B CN 103897415 B CN103897415 B CN 103897415B CN 201410146030 A CN201410146030 A CN 201410146030A CN 103897415 B CN103897415 B CN 103897415B
- Authority
- CN
- China
- Prior art keywords
- agent
- inorganic non
- metallic materials
- floor material
- wood floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of preparation method mixing plastic-wood floor material, comprise the steps: to weigh Inorganic Non-metallic Materials, wood powder, PE particle, compatilizer, lubricant, antioxidant, ultraviolet-resistant absorbent, light stabilizer, heat stabilizer, antifungus agent, insect-proof agent and fireproof agent, by PE particle, lubricant, antioxidant, ultraviolet-resistant absorbent, light stabilizer, heat stabilizer, antifungus agent, insect-proof agent and fireproof agent are sent in batch mixer and are mixed 4 8min, then the Inorganic Non-metallic Materials mix homogeneously of 58 72% it is added thereto to, after continuously adding wood powder and compatilizer mix homogeneously, add remaining Inorganic Non-metallic Materials and be sufficiently stirred for 10 13min；Pelletize, is dried, delivers to extruder extrusion molding, cooling, and sanding obtains mixing plastic-wood floor material.In the present invention, above-mentioned mixing plastic-wood floor material impact strength is higher, and anti-pressure ability is excellent, and ability of anti-deformation has significantly improvement.
Description
Technical field
The present invention relates to plastic-wood floor field of material technology, particularly relate to a kind of system mixing plastic-wood floor material
Preparation Method.
Background technology
The human society of 21 century is due to the discharge of greenhouse gases, and earth environment is just experiencing a new conversion
In the epoch, it is necessary that the exploitation of environment-friendly and energy-efficient new industry has become social development institute.Mould lumber yard industry as one
The industry of environment-friendly type is subject to the people's attention, and it is achieving environmental protection and energy saving, can be recycled.Both moulded lumber yard industry
Maintain the affinity sensation of solid wooden floor board, there is again good protection against the tide water-fast, acid and alkali-resistance, antifungal, anti-
Electrostatic, the performance such as Anti-moth-eating, is the another pioneering act of plastic-wood floor series and Floor Industry cooperation.Utilize
The series wood-plastic composite that wood flour, Caulis et Folium Oryzae, waste plastics the like waste produce just is stepping into finishing, building
In field.
Plastic-wood floor as mould wood series in one, it have environmental protection and energy saving, woodiness touch is good, tinctorial pattern is abundant,
Waterproof, anticorrosion, mildew-resistant, fire prevention, antibacterial, ant prevention, do not chap, without processing stupid, easy, exempt from paint,
The features such as use time length.In daily life, it is poor to there is shock resistance in plastic-wood floor, and fragility is big, easily
Damage fracture, warpage, deformation.
Summary of the invention
The present invention proposes a kind of preparation method mixing plastic-wood floor material, excellent in cushion effect, resistance to compression energy
Power and ability of anti-deformation are more excellent.
A kind of preparation method mixing plastic-wood floor material that the present invention proposes, comprises the steps: by weight
It is compatible that percentage ratio weighs 5-15% Inorganic Non-metallic Materials, 40-60% wood powder, 30-40%PE particle, 0.3-2%
Agent, 0.3-2% lubricant, 0.2-1% antioxidant, 0.4-1% ultraviolet-resistant absorbent, 0.8-2% light stabilizer,
1-2% heat stabilizer, 0.5-2% antifungus agent, 0.5-2% insect-proof agent and 1-2% fireproof agent, wherein, wood powder is aqueous
Amount for 0.3-0.45%, by PE particle, lubricant, antioxidant, ultraviolet-resistant absorbent, light stabilizer,
Heat stabilizer, antifungus agent, insect-proof agent and fireproof agent send into and mix 4-8min in batch mixer, wherein batch mixer
Stirring vane is 0.2-0.35cm with the gap of barrel, is then added thereto to the inorganic non-metallic material of 58-72%
Material mix homogeneously, after continuously adding wood powder and compatilizer mix homogeneously, adds remaining Inorganic Non-metallic Materials
It is sufficiently stirred for 10-13min；Being sent in comminutor by the material obtained and carry out pelletize, pelletize is done after completing
Dry, baking temperature is 90-93 DEG C, and dried material is delivered to extruder extrusion molding, and the material obtained exists
Vacuum is to cool down under the conditions of 7-12MPa, and chilling temperature is 1-4 DEG C, and sanding obtains mixing plastic-wood floor
Material.
Preferably, the weight ratio of described Inorganic Non-metallic Materials, wood powder and PE particle is 10:(40-60):
(30-40).
Preferably, by weight percentage, described Inorganic Non-metallic Materials content in the feed is no less than 8%.
Preferably, described raw material backs up ratio by weight and includes: 10% Inorganic Non-metallic Materials, 45-50% wood powder,
30-34%PE particle, 0.5-1% compatilizer, 1-1.5% lubricant, 0.5-0.8% antioxidant, 0.5-0.7% are anti-
UV absorbent, 1.2-1.5% light stabilizer, 1.5-1.8% heat stabilizer, 1-1.3% antifungus agent, 0.8-1.3%
Insect-proof agent and 1.5-1.7%.
In the present invention, because the crystal structure of Inorganic Non-metallic Materials having than metallic bond and pure covalent bond more
Strong ionic bond and mixing key, Inorganic Non-metallic Materials uses with wood powder and PE mix particles, and conservative control
The proportioning of three, is remarkably improved the mixing fusing point of Wood-plastic floor and hardness, its corrosion-resistant, non-oxidizability and
Abrasion resistance properties is excellent, and heat-proof quality is preferable.By the water content of conservative control wood powder, and in preparation process
Inorganic Non-metallic Materials is also added by the charging order of middle control raw material by several times, and product properties is excellent, and with one
As plastic-wood floor compare, goods are hardly damaged fracture, warpage and deformation, and it is excellent in cushion effect, resistance to compression energy
Power and ability of anti-deformation are more excellent.
Detailed description of the invention
A kind of preparation method mixing plastic-wood floor material that the present invention proposes, comprises the steps: by weight
It is compatible that percentage ratio weighs 5-15% Inorganic Non-metallic Materials, 40-60% wood powder, 30-40%PE particle, 0.3-2%
Agent, 0.3-2% lubricant, 0.2-1% antioxidant, 0.4-1% ultraviolet-resistant absorbent, 0.8-2% light stabilizer,
1-2% heat stabilizer, 0.5-2% antifungus agent, 0.5-2% insect-proof agent and 1-2% fireproof agent, wherein, wood powder is aqueous
Amount for 0.3-0.45%, by PE particle, lubricant, antioxidant, ultraviolet-resistant absorbent, light stabilizer,
Heat stabilizer, antifungus agent, insect-proof agent and fireproof agent send into and mix 4-8min in batch mixer, wherein batch mixer
Stirring vane is 0.2-0.35cm with the gap of barrel, is then added thereto to the inorganic non-metallic material of 58-72%
Material mix homogeneously, after continuously adding wood powder and compatilizer mix homogeneously, adds remaining Inorganic Non-metallic Materials
It is sufficiently stirred for 10-13min；Being sent in comminutor by the material obtained and carry out pelletize, pelletize is done after completing
Dry, baking temperature is 90-93 DEG C, and dried material is delivered to extruder extrusion molding, and the material obtained exists
Vacuum is to cool down under the conditions of 7-12MPa, and chilling temperature is 1-4 DEG C, and sanding obtains mixing plastic-wood floor
Material.
Embodiment 1
A kind of preparation method mixing plastic-wood floor material, comprises the steps: to weigh by weight percentage 10%
Inorganic Non-metallic Materials, 46.7% wood powder, 33%PE particle, 0.8% compatilizer, 1.2% lubricant, 0.6% resist
Oxygen agent, 0.8% ultraviolet-resistant absorbent, 1.4% light stabilizer, 1.5% heat stabilizer, 1.2% antifungus agent, 1.5%
Insect-proof agent and 1.3% fireproof agent, wherein, wood powder water content is 0.3-0.45%, by PE particle, lubricant,
Antioxidant, ultraviolet-resistant absorbent, light stabilizer, heat stabilizer, antifungus agent, insect-proof agent and fireproof agent send
Entering in batch mixer mixing 4min, wherein the stirring vane of batch mixer is 0.2cm with the gap of barrel, then to
Wherein add the Inorganic Non-metallic Materials mix homogeneously of 60%, after continuously adding wood powder and compatilizer mix homogeneously,
Add remaining Inorganic Non-metallic Materials and be sufficiently stirred for 12min；The material obtained is sent in comminutor and makes
Grain, pelletize is dried after completing, and baking temperature is 92 DEG C, and dried material is delivered to extruder extrusion
Molding, the material obtained cools down under the conditions of vacuum is 12MPa, and chilling temperature is 3 DEG C, and sanding obtains
To mixing plastic-wood floor material.
Embodiment 2
A kind of preparation method mixing plastic-wood floor material, comprises the steps: to weigh by weight percentage
12.8% Inorganic Non-metallic Materials, 41.7% wood powder, 38%PE particle, 0.3% compatilizer, 0.7% lubricant, 0.2%
Antioxidant, 0.6% ultraviolet-resistant absorbent, 0.9% light stabilizer, 1.8% heat stabilizer, 0.6% antifungus agent,
0.8% insect-proof agent and 1.6% fireproof agent, by PE particle, lubricant, antioxidant, ultraviolet-resistant absorbent, light
Stabilizer, heat stabilizer, antifungus agent, insect-proof agent and fireproof agent are sent into and are mixed 7min in batch mixer, wherein mix
The stirring vane of material machine and the gap of barrel are 0.23cm, are then added thereto to the inorganic non-metallic material of 58%
Material mix homogeneously, after continuously adding wood powder and compatilizer mix homogeneously, adds remaining Inorganic Non-metallic Materials
It is sufficiently stirred for 10min；Being sent in comminutor by the material obtained and carry out pelletize, pelletize is dried after completing,
Baking temperature is 90 DEG C, and dried material is delivered to extruder extrusion molding, and the material obtained is in vacuum
For cooling down under the conditions of 7MPa, chilling temperature is 1 DEG C, and sanding obtains mixing plastic-wood floor material.
Embodiment 3
A kind of preparation method mixing plastic-wood floor material, comprises the steps: to weigh by weight percentage 10%
Inorganic Non-metallic Materials, 48.15% wood powder, 32%PE particle, 0.7% compatilizer, 1.3% lubricant, 0.6%
Antioxidant, 0.6% ultraviolet-resistant absorbent, 1.4% light stabilizer, 1.7% heat stabilizer, 1.1% antifungus agent,
0.8% insect-proof agent and 1.65% fireproof agent, wherein, wood powder water content is 0.3-0.45%, by PE particle, profit
Lubrication prescription, antioxidant, ultraviolet-resistant absorbent, light stabilizer, heat stabilizer, antifungus agent, insect-proof agent and anti-
Fire agent is sent into and is mixed 6min in batch mixer, and wherein the stirring vane of batch mixer is 0.35cm with the gap of barrel,
Then it is added thereto to the Inorganic Non-metallic Materials mix homogeneously of 72%, continuously adds wood powder and compatilizer mixing is equal
After even, add remaining Inorganic Non-metallic Materials and be sufficiently stirred for 13min；The material obtained is sent in comminutor
Carrying out pelletize, pelletize is dried after completing, and baking temperature is 93 DEG C, and dried material is delivered to extruding
Machine extrusion molding, the material obtained cools down under the conditions of vacuum is 10MPa, and chilling temperature is 4 DEG C,
Sanding obtains mixing plastic-wood floor material.
The above, the only present invention preferably detailed description of the invention, but protection scope of the present invention not office
Being limited to this, any those familiar with the art is in the technical scope that the invention discloses, according to this
The technical scheme of invention and inventive concept thereof in addition equivalent or change, all should contain the protection in the present invention
Within the scope of.
Claims (3)
1. the preparation method mixing plastic-wood floor material, it is characterised in that comprise the steps: by weight
Amount percentage ratio weighs 5-15% Inorganic Non-metallic Materials, 40-60% wood powder, 30-40%PE particle, 0.3-2% phase
Appearance agent, 0.3-2% lubricant, 0.2-1% antioxidant, 0.4-1% ultraviolet-resistant absorbent, 0.8-2% light are stablized
Agent, 1-2% heat stabilizer, 0.5-2% antifungus agent, 0.5-2% insect-proof agent and 1-2% fireproof agent, wherein, wood powder
Water content is 0.3-0.45%, by stable to PE particle, lubricant, antioxidant, ultraviolet-resistant absorbent, light
Agent, heat stabilizer, antifungus agent, insect-proof agent and fireproof agent are sent into and are mixed 4-8min, wherein batch mixing in batch mixer
The stirring vane of machine and the gap of barrel are 0.2-0.35cm, are then added thereto to the inorganic non-gold of 58-72%
Belong to material mixing uniform, after continuously adding wood powder and compatilizer mix homogeneously, add remaining inorganic non-metallic
Material is sufficiently stirred for 10-13min；Being sent in comminutor by the material obtained and carry out pelletize, pelletize completes laggard
Row is dried, and baking temperature is 90-93 DEG C, dried material is delivered to extruder extrusion molding, obtains
Material cools down under the conditions of vacuum is 7-12MPa, and chilling temperature is 1-4 DEG C, and sanding is mixed
Plastic-wood floor material；
The weight ratio of described Inorganic Non-metallic Materials, wood powder and PE particle is 10:(40-60): (30-40).
The preparation method of mixing plastic-wood floor material the most according to claim 1, it is characterised in that press
Percentage by weight, described Inorganic Non-metallic Materials content in the feed is no less than 8%.
3., according to the preparation method of the mixing plastic-wood floor material according to any one of claim 1-2, it is special
Levying and be, described raw materials by weight includes: 10% Inorganic Non-metallic Materials, 45-50% wood powder,
30-34%PE particle, 0.5-1% compatilizer, 1-1.5% lubricant, 0.5-0.8% antioxidant, 0.5-0.7% are anti-
UV absorbent, 1.2-1.5% light stabilizer, 1.5-1.8% heat stabilizer, 1-1.3% antifungus agent, 0.8-1.3%
Insect-proof agent and 1.5-1.7% fireproof agent.