CN103881165A - Rubber dipping type insulation gloves and manufacture method thereof - Google Patents
Rubber dipping type insulation gloves and manufacture method thereof Download PDFInfo
- Publication number
- CN103881165A CN103881165A CN201410155212.7A CN201410155212A CN103881165A CN 103881165 A CN103881165 A CN 103881165A CN 201410155212 A CN201410155212 A CN 201410155212A CN 103881165 A CN103881165 A CN 103881165A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- dipping
- manufacture method
- type insulating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a pair of rubber dipping type insulation gloves and a manufacture method thereof. A dipping liquor comprises the following raw materials in parts by weight: natural rubber, zinc oxide, sulphur, an accelerant, an anti-aging agent, stearic acid and light calcium carbonate. The manufacture method comprises the steps: dissolving plastified rubber and the raw materials into liquid after being conventionally mixed; performing dipping for multiple times in the liquor according to a certain speed by using a glove model through dipping equipment, and drying after dipping; and sulfurizing according to a designed temperature, pressure and time; finally, testing a voltage, verifying and packaging. The pair of rubber dipping type insulation gloves has the advantages of attractive appearance, good cold resistance, good water repellency, good insulation, safety and reliability, and accords with the requirement of IEC60903 (International Electrotechnical Commission).
Description
Technical field
The present invention relates to a kind of rubber-insulation gloves and manufacture method thereof, particularly relate to a kind of attractive in appearance, winter hardiness, repellency is good, flexibility is good, good insulating, rubber impregnated type insulating gloves and manufacture method thereof that comfort level is good.
Background technology
As everyone knows, existing rubber-insulation gloves is a kind of is the gloves with spue line of making through molded vulcanization with rubber, the gloves that this method is produced are owing to there being spue line, not attractive in appearance, be subject to the restriction of punching block, finger sinuousness is little, can not meet operator's demand simultaneously, and equipment, die cost are high, pliability is not as softness of the present invention simultaneously; Another kind is produced by latex impregnation, but owing to being water miscible, insulating property are unstable, particularly high level gloves, and qualification rate is not high, and winter hardiness is bad simultaneously.
Summary of the invention
Main purpose of the present invention be to overcome above deficiency and a kind of winter hardiness is provided, repellency is good, flexibility is good, good insulating, rubber impregnated type insulating gloves and manufacture method thereof that comfort level is good.
The technical solution adopted for the present invention to solve the technical problems is:
A kind of rubber impregnated type insulating gloves, is characterized in that: the moiety of steeping fluid comprises following by the former batching of umber proportioning:
100 parts of natural rubbers, 3.0-6.0 parts, zinc oxide,
3.0 parts, sulphur, 1.0-3.0 parts of promotor,
1.0-2.0 parts, anti-aging agent, 1.5-3.0 parts of stearic acids,
10.0-30.0 parts of light calcium carbonates;
The present invention can also adopt following technical measures:
Described rubber impregnated type insulating gloves, is characterized in that: steeping fluid moiety comprises following by the former batching of umber proportioning:
100 parts of natural rubbers, 3.0 parts, zinc oxide,
2.0 parts, sulphur, 1.0 parts of promotor,
1.0 parts, anti-aging agent, 1.5 parts of stearic acids,
20.0 parts of light calcium carbonates;
Described rubber impregnated type insulating gloves, is characterized in that: steeping fluid moiety comprises following by the former batching of umber proportioning:
100 parts of natural rubbers, 3.0 parts, zinc oxide,
3.0 parts, sulphur, 2.0 parts of promotor,
2.0 parts, anti-aging agent, 1.5 parts of stearic acids,
18.0 parts of light calcium carbonates;
A manufacture method for rubber impregnated type insulating gloves, is characterized in that:
Steeping fluid moiety described in it comprises following by the former batching of umber proportioning:
100 parts of natural rubbers, 3.0-6.0 parts, zinc oxide,
1.5-3.0 parts, sulphur, 1.0-3.0 parts of promotor,
1.0-2.0 parts, anti-aging agent, 1.5-3.0 parts of stearic acids,
10.0-30.0 parts of light calcium carbonates;
The step of the manufacture method of its rubber impregnated type insulating gloves is as follows:
1.. the rubber after plasticating is carried out together with above-mentioned former batching conventional be dissolved into liquid with rubber solvent mixing afterwards;
2.. use glove model in aforesaid liquid, to flood 5-60 times by impregnating equipment, its impregnating speed is to need to dry after the each dipping of 1.0-5.0mm/s; The impregnating equipment adopting should possess energy automatic turning and automatically regulate the function of rising or falling speed;
3.. sulfidizing: its temperature is 130-150 DEG C, pressure is 3.0-5.0MPa, the time is after 10-40 minutes, to go out tank, the demoulding;
4.. examination voltage;
5.. inspection, packaging.
Advantage and positively effect that the present invention has are: therefore rubber-insulation gloves is owing to being the spue line that do not have that repeatedly floods production, overcome electrical breakdown, make insulativity higher, finger sinuousness more meets operator's requirement, number is complete, more comfortable, winter hardiness is good, repellency is good, flexibility is good, safe and reliable and meet IEC60903 standard-required.
Brief description of the drawings
Fig. 1 is manufacture method operation schematic diagram of the present invention.
Embodiment
For further understanding hereby following examples for example of summary of the invention Characteristic of the present invention, and coordinate accompanying drawing to be described in detail as follows, refer to Fig. 1.
embodiment 1be illustrated as an example of 00 grade of insulation glove for hot-line work example
As shown in Figure 1: described rubber impregnated type insulating gloves, is characterized in that: steeping fluid moiety comprises following by the former batching of umber proportioning:
100 parts of natural rubbers, 3.0 parts, zinc oxide,
2.0 parts, sulphur, 1.0 parts of promotor,
1.0 parts, anti-aging agent, 1.5 parts of stearic acids,
20.0 parts of light calcium carbonates;
The step of the manufacture method of its rubber impregnated type insulating gloves is as follows:
1.. the rubber after plasticating is carried out together with above-mentioned former batching conventional be dissolved into liquid with rubber solvent mixing afterwards;
2.. use glove model in aforesaid liquid, to flood 10 times by impregnating equipment, its impregnating speed is to need to dry after the each dipping of 1.0mm/s; Described impregnating equipment should possess energy automatic turning and automatically regulate the function of rising or falling speed;
3.. sulfidizing: its temperature is 140 DEG C, pressure is 4.0MPa, the time is within 10 minutes, to go out tank, the demoulding;
4.. examination voltage;
5.. inspection, packaging.
Its advantage is: winter hardiness is good, repellency is good, good insulating, flexibility is good, comfort level is good, safe and reliable and meet IEC60903 standard-required.
embodiment 2be illustrated as example with rubber impregnated type insulating gloves taking 4 grades of hot line work
As shown in Figure 1: described rubber impregnated type insulating gloves, is characterized in that: steeping fluid moiety comprises following by the former batching of umber proportioning:
100 parts of natural rubbers, 3.0 parts, zinc oxide,
3.0 parts, sulphur, 2.0 parts of promotor,
2.0 parts, anti-aging agent, 1.5 parts of stearic acids,
18.0 parts of light calcium carbonates.
The step of the manufacture method of its rubber impregnated type insulating gloves is as follows:
1.. the rubber after plasticating is carried out together with above-mentioned former batching conventional be dissolved into liquid with rubber solvent mixing afterwards;
2.. use glove model in aforesaid liquid, to flood 60 times by impregnating equipment, its impregnating speed is to need to dry after the each dipping of 1.0mm/s; Described impregnating equipment should possess energy automatic turning and automatically regulate the function of rising or falling speed;
3.. sulfidizing: its temperature is 140 DEG C, pressure is 4.0MPa, the time is to go out tank, the demoulding after 20 minutes;
4.. examination voltage;
5.. inspection, packaging.
Its advantage is: attractive in appearance, winter hardiness good, repellency good, good insulating, flexibility is good, comfort level is good, safe and reliable and meet IEC60903 standard-required.
Above-described embodiment is described the preferred embodiment of the present invention; not scope of the present invention is limited; design under the prerequisite of spirit not departing from the present invention; various distortion and improvement that those of ordinary skill in the art make technical scheme of the present invention, all should fall in the definite protection domain of the claims in the present invention book.
Claims (4)
1. a rubber impregnated type insulating gloves, is characterized in that: the moiety of steeping fluid comprises following by the former batching of umber proportioning:
100 parts of natural rubbers, 3.0-6.0 parts, zinc oxide,
1.5-3.0 parts, sulphur, 1.0-3.0 parts of promotor,
1.0-2.0 parts, anti-aging agent, 1.5-3.0 parts of stearic acids,
10.0-30.0 parts of light calcium carbonates.
2. rubber impregnated type insulating gloves according to claim 1, is characterized in that: described steeping fluid moiety comprises following by the former batching of umber proportioning:
100 parts of natural rubbers, 3.0 parts, zinc oxide,
2.0 parts, sulphur, 1.0 parts of promotor,
1.0 parts, anti-aging agent, 1.5 parts of stearic acids,
20.0 parts of light calcium carbonates.
3. rubber impregnated type insulating gloves according to claim 1, is characterized in that: described steeping fluid moiety comprises following by the former batching of umber proportioning:
100 parts of natural rubbers, 3.0 parts, zinc oxide,
3.0 parts, sulphur, 2.0 parts of promotor,
2.0 parts, anti-aging agent, 1.5 parts of stearic acids,
18.0 parts of light calcium carbonates.
4. a manufacture method for rubber impregnated type insulating gloves, is characterized in that:
Steeping fluid moiety described in it comprises following by the former batching of umber proportioning:
100 parts of natural rubbers, 3.0-6.0 parts, zinc oxide,
1.5-3.0 parts, sulphur, 1.0-3.0 parts of promotor,
1.0-2.0 parts, anti-aging agent, 1.5-3.0 parts of stearic acids,
10.0-30.0 parts of light calcium carbonates;
The step of the manufacture method of its rubber impregnated type insulating gloves is as follows:
1.. the rubber after plasticating is carried out together with above-mentioned former batching conventional be dissolved into liquid with rubber solvent mixing afterwards;
2.. by specifying impregnating equipment also to flood 5-60 times in above-mentioned steeping fluid with glove model, its impregnating speed is 1.0-5.0mm/s
at every turnafter dipping, need to dry; Described impregnating equipment should possess energy automatic turning and automatically regulate the function of rising or falling speed;
3.. sulfidizing: its temperature is 130-150 DEG C, pressure is 3.0-5.0MPa, the time is after 10-40 minutes, to go out tank, the demoulding;
4.. examination voltage;
5.. inspection, packaging.