CN103878301B - A kind of iron castings face coat coating - Google Patents
A kind of iron castings face coat coating Download PDFInfo
- Publication number
- CN103878301B CN103878301B CN201410075612.7A CN201410075612A CN103878301B CN 103878301 B CN103878301 B CN 103878301B CN 201410075612 A CN201410075612 A CN 201410075612A CN 103878301 B CN103878301 B CN 103878301B
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- face coat
- iron castings
- composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A kind of iron castings face coat coating, formed by the proportions of 1:2 by deionized water and coating composition, wherein said coating composition is made up of the composition of following parts by weight, epoxy resin 2 3.5 parts, andalusite 1 1.5 parts, 1 2.5 parts of zirconium English powder, cellulose 1.5 2 parts, 2.5 3 parts of Suzhou soil, Ludox 2 3.5 parts, emulsifying agent 0.5 1 parts.Instant component is simple, cost-effective, little to human injury, and flawless, non-foaming, coating uniform after strength of coating height, coating application, surface quality is good.
Description
Technical field
The present invention relates to technical field of coatings, be specifically related to a kind of iron castings face coat coating.
Background technology
Foundry goods coating typically uses refractory aggregate, suspending agent, binding agent, carrier fluid to synthesize at present, in casting
Making water quantity in coating is 5%, and foundry goods causes foundry goods to have the disqualification rate of 20% due to gas hole defect, by
In coating, there is secondary water, make foundry goods easily produce pore；And owing to have employed combustion adjuvant, toxicity is big.
Along with Environmental and the attention of labor protection, there is presently no a kind of environment protecting good, can maximum limit
The foundry facing of volatilizable harmful components in the reduction cast paint of degree.
Summary of the invention
The technical problem to be solved is to provide a kind of composition simple, applies effective, environmental protection
Iron castings face coat coating.
The technical problem to be solved realizes by the following technical solutions:
A kind of iron castings face coat coating, is joined in the ratio of 1:2 by deionized water and coating composition
System forms, and wherein said coating composition is made up of the composition of following parts by weight,
Described cellulose is plant cellulose, readily soluble.
The invention has the beneficial effects as follows: instant component is simple, cost-effective, little to human injury, be coated with
Flawless, non-foaming, coating uniform after layer intensity height, coating application, surface quality is good.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and effect and be readily apparent from
Solve, below in conjunction with specific embodiment, the present invention is expanded on further.
Embodiment 1
A kind of iron castings face coat coating, is joined in the ratio of 1:2 by deionized water and coating composition
System forms, and wherein said coating composition is made up of the composition of following parts by weight,
Described cellulose is plant cellulose, readily soluble.
Embodiment 2
A kind of iron castings face coat coating, is joined in the ratio of 1:2 by deionized water and coating composition
System forms, and wherein said coating composition is made up of the composition of following parts by weight,
Described cellulose is plant cellulose, readily soluble.
Embodiment 3
A kind of iron castings face coat coating, is joined in the ratio of 1:2 by deionized water and coating composition
System forms, and wherein said coating composition is made up of the composition of following parts by weight,
Described cellulose is plant cellulose, readily soluble.
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.One's own profession
Skilled person will appreciate that of industry, the present invention is not restricted to the described embodiments, above-described embodiment and explanation
The principle that the present invention is simply described described in book, without departing from the spirit and scope of the present invention,
The present invention also has various changes and modifications, and these changes and improvements both fall within claimed invention model
In enclosing.Claimed scope is defined by appending claims and equivalent thereof.
Claims (1)
1. an iron castings face coat coating, is pressed the ratio of 1:2 by deionized water and coating composition
Example is formulated, it is characterised in that wherein said coating composition is made up of the composition of following parts by weight:
Described cellulose is plant cellulose.