CN103865383A - Anti-corrosion technology for metal surfaces - Google Patents
Anti-corrosion technology for metal surfaces Download PDFInfo
- Publication number
- CN103865383A CN103865383A CN201210547676.3A CN201210547676A CN103865383A CN 103865383 A CN103865383 A CN 103865383A CN 201210547676 A CN201210547676 A CN 201210547676A CN 103865383 A CN103865383 A CN 103865383A
- Authority
- CN
- China
- Prior art keywords
- coating method
- protective system
- coating
- substrate surface
- particle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-corrosion technology for metal surfaces. The technology comprises: mixing compositions such as siloxane, a solvent, silicon dioxide particles, a rear earth compound, deionized water, a catalyst, carbon fiber, polyimide and the like, performing aging processing, then filtering the aged mixture, employing spraying, brush coating or dipping to enable the filtered mixture to be on a substrate surface, after deposition, forming a coating on the substrate surface, so as to realize surface anticorrosion processing.
Description
Technical field
The present invention relates to a kind of aseptic technic of metallic surface, relate in particular to one and be applicable to metal structure surface, there is the coating method of the environmental protection coating material of excellent gloss and mechanical and physical performance and aromatic free solvent.
Background technology
In modern industry and daily life, corrosion of metal is seen everywhere, and the destruction of the forms such as crevice corrosion, stress corrosion and the corrosion fatigue especially occurring in the storage vessel of a fuel oil dangerization product, causes great potential safety hazard for people's lives.
The metal protection method adopting at present can roughly be divided three classes: a class is to carry out anodic oxidation treatment, form the anode oxide film of one deck tens micron thick in metallic surface, but because anode oxidation process power consumption is large, and electrolyte solution is seriously polluted, be difficult to process, use its application to be restricted; Equations of The Second Kind is chemical conversion film, be immersed in by metal parts in the solution of definite composition, rely at a certain temperature chemical reaction to form one deck chemical conversion film, now most widely used is the oxidation of chromic salt chemistry, but chromic salt is a kind of carcinogenic toxicant, world environments protective tissue has proposed restriction and has used chromic salt and other to contain chromate compound; The 3rd class is organic coating, applies one deck organic coating in metallic surface, to improve outward appearance and the physical and chemical performance of metal.People start rare earth element to be used in the aseptic technic of metallic surface in recent years.
Rare-earth conversion coatings film technique develops into today, and people have carried out a large amount of improvement to various film-forming process, and the performance of film is also improved.At present rare-earth conversion coatings technology is mainly immersion treatment, and this technological operation is simple, be easy to safeguard; But its drawback is, long period of soaking process treatment time is oversize, and the rete forming is thinner and poor with the sticking power of base material.Find through long-term exploratory development, in soaking solution, add strong oxidizer, as H
2o
2, KMnO
4, (NH
4)
2s
2o
8etc. strong oxide compound, rate of film build is improved greatly, the treatment time shortens dramatically, and treatment soln temperature is not high yet simultaneously, can at room temperature apply.But because the existence of strong oxidizer makes the less stable for the treatment of process.
The problem existing in order to solve rare-earth conversion coatings treatment process, the present invention proposes a kind of aseptic technic of improved metallic surface.This method anticorrosion with low cost, remarkable in economical benefits, can carry out normal temperature and spread, and coating processes is simple, and solution is environment friendly and pollution-free.
Summary of the invention
The object of the invention is for the deficiencies in the prior art part, provide a kind of coating method of environment friendly corrosion protection coating, in order to solve a protection against corrosion difficult problem for the surfaces externally and internally applications such as steel, aluminium, especially aluminium alloy, and coating aromatic free solvent, not containing strong oxidizer, without poisonous pigment, be applicable to various constructional methods, application is not subject to seasonal restrictions, and construction technology is simple and convenient, technical costs is cheap, good environmental protection.
The present invention is achieved by the following technical solutions:
(1) prepare following component (mass parts):
A3-Racemic glycidol propyl-triethoxysilicane 11-20;
B ethanol 61-80;
C SiO
2particle 6-10;
The oxide compound 1-5 of d cerium;
E deionized water 26-50;
F acetic acid 1-3;
G carbon fiber 8-10;
H polyimide 4-6;
(2) by carrying out maturation process after above component mixing, then spray, brush or be immersed in substrate surface, after deposition, form coating at substrate surface, realize surface anticorrosion processing.
Embodiment
The present invention relates to the aseptic technic of metallic surface, after the various components of protective system are mixed, carry out maturation process, then the mixture after slaking is filtered, then spray, brush or be immersed in substrate surface, after deposition, form coating at substrate surface, realize surface anticorrosion processing.
Described SiO
2the particle diameter of particle is 50-100 nanometer.
Described maturation process is to leave standstill at normal temperatures 50-60 hour.
Described base material is steel or aluminium, preferably aluminium alloy.
In deposition process after spraying, brushing or dipping, heat, Heating temperature is to heat 1 minute to 1 hour at 50 DEG C to 150 DEG C temperature.
The thickness of described coating is 1 micron to 10 microns, preferably 1 micron to 5 microns.The method that preferably adopts spraying or brush forms coating at substrate surface.
The aseptic technic of metallic surface disclosed by the invention is simple, convenient, quick, reliable, and raw material is cheap, this method can be simply existingly comprises the pre-treatment of coating and afterwards in the conventional production line of other postprocessing working procedures of substrate material in conjunction with entering, substantially without other adjustment of carrying out on equipment, be the highly Eco-power production technique of one.
Below the present invention is elaborated with embodiment, but protection scope of the present invention is not limited to following embodiment.
Embodiment 1
(1) prepare following component (mass parts):
A3-Racemic glycidol propyl-triethoxysilicane 11;
B ethanol 61;
C SiO
2particle 6;
The oxide compound 5 of d cerium;
E deionized water 26;
F acetic acid 1;
G carbon fiber 8;
H polyimide 4;
(2) by carrying out maturation process after above component mixing, then spray, brush or be immersed in substrate surface, after deposition, form coating at substrate surface, realize surface anticorrosion processing.
Embodiment 2
(1) prepare following component (mass parts):
A3-Racemic glycidol propyl-triethoxysilicane 20;
B ethanol 80;
C SiO
2particle 10;
The oxide compound 1 of d cerium;
E deionized water 50;
F acetic acid 2;
G carbon fiber 10;
H polyimide 5;
(2) by carrying out maturation process after above component mixing, then spray, brush or be immersed in substrate surface, after deposition, form coating at substrate surface, realize surface anticorrosion processing.
Embodiment 3
(1) prepare following component (mass parts):
A3-Racemic glycidol propyl-triethoxysilicane 15;
B ethanol 70;
C SiO
2particle 8;
The oxide compound 3 of d cerium;
E deionized water 38;
F acetic acid 3;
G carbon fiber 9;
H polyimide 6;
(2) by carrying out maturation process after above component mixing, then spray, brush or be immersed in substrate surface, after deposition, form coating at substrate surface, realize surface anticorrosion processing.
Claims (9)
1. the aseptic technic of metallic surface, comprising:
(1) prepare following component (mass parts):
A 3-Racemic glycidol propyl-triethoxysilicane 11-20;
B ethanol 61-80;
C SiO
2particle 6-10;
The oxide compound 1-5 of d cerium;
E deionized water 26-50;
F acetic acid 1-3;
G carbon fiber 8-10;
H polyimide 4-6;
(2) by carrying out maturation process after said components mixing, then spray, brush or be immersed in substrate surface, after deposition, form coating at substrate surface, realize surface anticorrosion processing.
2. the coating method of protective system according to claim 1, is characterized in that described SiO
2the particle diameter of particle is 50-100 nanometer.
3. the coating method of protective system according to claim 1, is characterized in that, described maturation process is to leave standstill at normal temperatures 50-60 hour.
4. the coating method of protective system according to claim 1, is characterized in that, described base material is steel or aluminium.
5. the coating method of protective system according to claim 1, is characterized in that, described base material is aluminium alloy.
6. the coating method of protective system according to claim 1, is characterized in that, in described deposition process, heat, Heating temperature is 50 DEG C to 150 DEG C, 1 minute to 1 hour heat-up time.
7. the coating method of protective system according to claim 1, is characterized in that, described coat-thickness is 1 micron to 10 microns.
8. the coating method of protective system according to claim 7, is characterized in that, described coat-thickness is 1 micron to 5 microns.
9. the coating method of protective system according to claim 1, is characterized in that, adopts spraying or the method for brushing forms coating at substrate surface in described step (2).