CN103865223A - 一种雾面耐油弹性体电缆料 - Google Patents
一种雾面耐油弹性体电缆料 Download PDFInfo
- Publication number
- CN103865223A CN103865223A CN201410102512.9A CN201410102512A CN103865223A CN 103865223 A CN103865223 A CN 103865223A CN 201410102512 A CN201410102512 A CN 201410102512A CN 103865223 A CN103865223 A CN 103865223A
- Authority
- CN
- China
- Prior art keywords
- parts
- add
- cable material
- raw material
- mixed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种雾面耐油弹性体电缆料,它是由下述重量份的原料组成的:聚丙烯30-34、氢化苯乙烯-丁二烯-苯乙烯50-60、四水八硼酸二钠1-3、壬二酸二辛酯6-10、乙氧基化烷基酚硫酸铵1-2、丙酸钙2-3、夕线石粉6-10、凹凸棒土10-13、氟化钙2-3、双酚a二缩水甘油醚0.8-1、环氧硬脂酸辛酯6-9、复合填料10-13。本发明的电缆料提高了材料的雾面效果及耐油性能,柔韧性好,具有很好的抗拉伸和断裂伸长强度,可广泛用于电脑数据线、电子线、耳机线等。
Description
技术领域
本发明主要涉及电缆领域,尤其涉及一种雾面耐油弹性体电缆料。
背景技术
随着电缆事业的快速发展,高质量的电缆料受到越来越多的青睐,高质量的电缆料不仅耐候性好,使用寿命长,而且安全环保,因此追求更高质量的电缆料不仅可以赢得市场的竞争,还对现代化建设起到了重大的支持和帮助。
发明内容
本发明目的就是提供一种雾面耐油弹性体电缆料。
本发明是通过以下技术方案实现的:
一种雾面耐油弹性体电缆料,它是由下述重量份的原料组成的:
聚丙烯30-34、氢化苯乙烯- 丁二烯- 苯乙烯50-60、四水八硼酸二钠1-3、壬二酸二辛酯6-10、乙氧基化烷基酚硫酸铵1-2、丙酸钙2-3、夕线石粉6-10、凹凸棒土10-13、氟化钙2-3、双酚a二缩水甘油醚0.8-1、环氧硬脂酸辛酯6-9、复合填料10-13;
所述的复合填料是由下述重量份的原料组成的:
线性低密度聚乙烯25-30、海泡石粉10-16、季戊四醇三丙烯酸酯2-3、轻质碳酸钙5-10、磷酸二氢铝2-3、聚四氟乙烯3-5、聚二甲基硅氧烷1-2;
将上述线性低密度聚乙烯、海泡石粉混合,在500-600℃下搅拌加热4-10分钟,冷却至常温,加入聚四氟乙烯,球磨搅拌混合6-8分钟,得预混料,将上述轻质碳酸钙、磷酸二氢铝混合,在60-70℃下搅拌混合3-5分钟,加入季戊四醇三丙烯酸酯,搅拌至常温,与上述预混料混合,加入剩余各原料,搅拌均匀后烘干,研磨,即得所述复合填料。
一种雾面耐油弹性体电缆料的制备方法,包括以下步骤:
将上述夕线石粉、凹凸棒土、氟化钙混合,加入壬二酸二辛酯,80-100℃下搅拌混合10-14分钟,加入剩余各原料,熔融挤出,冷却、造粒,即得所述电缆料。
本发明的优点是:
本发明的电缆料提高了材料的雾面效果及耐油性能,柔韧性好,具有很好的抗拉伸和断裂伸长强度,可广泛用于电脑数据线、电子线、耳机线等。
具体实施方式
实施例1
一种雾面耐油弹性体电缆料,它是由下述重量份(公斤)的原料组成的:
聚丙烯34、氢化苯乙烯- 丁二烯- 苯乙烯60、四水八硼酸二钠3、壬二酸二辛酯6、乙氧基化烷基酚硫酸铵1、丙酸钙2、夕线石粉10、凹凸棒土13、氟化钙2、双酚a二缩水甘油醚0.8、环氧硬脂酸辛酯6、复合填料13;
所述的复合填料是由下述重量份的原料组成的:
线性低密度聚乙烯30、海泡石粉16、季戊四醇三丙烯酸酯3、轻质碳酸钙10、磷酸二氢铝2、聚四氟乙烯3、聚二甲基硅氧烷1;
将上述线性低密度聚乙烯、海泡石粉混合,在600℃下搅拌加热10分钟,冷却至常温,加入聚四氟乙烯,球磨搅拌混合8分钟,得预混料,将上述轻质碳酸钙、磷酸二氢铝混合,在70℃下搅拌混合3分钟,加入季戊四醇三丙烯酸酯,搅拌至常温,与上述预混料混合,加入剩余各原料,搅拌均匀后烘干,研磨,即得所述复合填料。
一种如权利要求1所述的种雾面耐油弹性体电缆料的制备方法,其特征在于包括以下步骤:
将上述夕线石粉、凹凸棒土、氟化钙混合,加入壬二酸二辛酯,100℃下搅拌混合14分钟,加入剩余各原料,熔融挤出,冷却、造粒,即得所述电缆料。
性能测试:
拉伸强度:9.5MPa;
断裂伸长率:437%;
硬度邵氏(A):86。
Claims (2)
1.一种雾面耐油弹性体电缆料,其特征在于它是由下述重量份的原料组成的:
聚丙烯30-34、氢化苯乙烯- 丁二烯- 苯乙烯50-60、四水八硼酸二钠1-3、壬二酸二辛酯6-10、乙氧基化烷基酚硫酸铵1-2、丙酸钙2-3、夕线石粉6-10、凹凸棒土10-13、氟化钙2-3、双酚a二缩水甘油醚0.8-1、环氧硬脂酸辛酯6-9、复合填料10-13;
所述的复合填料是由下述重量份的原料组成的:
线性低密度聚乙烯25-30、海泡石粉10-16、季戊四醇三丙烯酸酯2-3、轻质碳酸钙5-10、磷酸二氢铝2-3、聚四氟乙烯3-5、聚二甲基硅氧烷1-2;
将上述线性低密度聚乙烯、海泡石粉混合,在500-600℃下搅拌加热4-10分钟,冷却至常温,加入聚四氟乙烯,球磨搅拌混合6-8分钟,得预混料,将上述轻质碳酸钙、磷酸二氢铝混合,在60-70℃下搅拌混合3-5分钟,加入季戊四醇三丙烯酸酯,搅拌至常温,与上述预混料混合,加入剩余各原料,搅拌均匀后烘干,研磨,即得所述复合填料。
2.一种如权利要求1所述的雾面耐油弹性体电缆料的制备方法,其特征在于包括以下步骤:
将上述夕线石粉、凹凸棒土、氟化钙混合,加入壬二酸二辛酯,80-100℃下搅拌混合10-14分钟,加入剩余各原料,熔融挤出,冷却、造粒,即得所述电缆料。