CN103864330A - 聚羧酸减水剂及其碱性环境合成方法 - Google Patents

聚羧酸减水剂及其碱性环境合成方法 Download PDF

Info

Publication number
CN103864330A
CN103864330A CN201410090567.2A CN201410090567A CN103864330A CN 103864330 A CN103864330 A CN 103864330A CN 201410090567 A CN201410090567 A CN 201410090567A CN 103864330 A CN103864330 A CN 103864330A
Authority
CN
China
Prior art keywords
water
polycarboxylate superplasticizer
reducer
synthetic method
polycarboxylate water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410090567.2A
Other languages
English (en)
Other versions
CN103864330B (zh
Inventor
宫振鑫
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DALIAN MINGYUANQUAN TECHNOLOGY DEVELOPMENT Co Ltd
Original Assignee
DALIAN MINGYUANQUAN TECHNOLOGY DEVELOPMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DALIAN MINGYUANQUAN TECHNOLOGY DEVELOPMENT Co Ltd filed Critical DALIAN MINGYUANQUAN TECHNOLOGY DEVELOPMENT Co Ltd
Priority to CN201410090567.2A priority Critical patent/CN103864330B/zh
Publication of CN103864330A publication Critical patent/CN103864330A/zh
Application granted granted Critical
Publication of CN103864330B publication Critical patent/CN103864330B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种聚羧酸减水剂及其碱性环境合成方法，其原料组成为：a.甲基丙烯醇聚氧乙烯醚，b.丙烯酸或者甲基丙烯酸或者两者混合，c.氢氧化钠，d.甲基丙烯磺酸钠，e.双氧水；所述原料的摩尔比为：a：b: c：d=1：2.5～3.5:3.5～4.5:0.3～0.6，e用量为总物料重量0.5～0.8%。本发明的有益效果为：本发明的聚羧酸减水剂在碱性条件下合成，合成后的产品坍落度保持效果明显好于普通方法合成产品。

Description

聚羧酸减水剂及其碱性环境合成方法
技术领域
本发明涉及一种减水剂，具体是一种聚羧酸减水剂及其碱性环境合成方法。
背景技术
随着建筑工程技术的发展和大规模混凝土搅拌站、混凝土搅拌运输车、混凝土泵送施工设备应用的普及，大大推动了混凝土外加剂技术的发展。现代混凝土朝高性能、绿色化的方向发展，对混凝土外加剂的减水率、保坍性以及环保性的要求越来越高。
国内研制和生产并且被广泛使用的高效减水剂，按照其化学成分分类主要有以下几种：改性木质素磺酸盐高效减水剂、萘系高效减水剂、蜜胺树脂系高效减水剂、氨基磺酸盐系高效减水剂、聚羧酸盐高效减水剂。概括高效减水剂的作用有以下三个方面：(1)在保持拌合物水灰比不变的情况下，改善其工作性能；(2)在保持和易性不变的前提下，掺入减水剂可以使混凝土单位用水量减少 5%-25%，提高混凝土强度 5%-30%；(3)在保持混凝土强度不变的前提下，使用减水剂可以降低水泥用量的 5%-20%。总之，减水剂的作用最终体现在其产生了巨大的经济效益和社会效益。
发明内容
本发明的目的是提供一种聚羧酸减水剂及其碱性环境合成方法，本方法合成减水剂，坍落度保持效果都明显好于普通方法合成产品。
本发明的技术方案是这样实现的：聚羧酸减水剂，由下述原料制成：
a.甲基丙烯醇聚氧乙烯醚
b.丙烯酸或者甲基丙烯酸或者两者混合
c.氢氧化钠
d.甲基丙烯磺酸钠
e.双氧水；
所述原料的摩尔比为：a：b:  c：d = 1：2.5～3.5 : 3.5～4.5: 0.3～0.6，e用量为总物料重量0.5～0.8%。
进一步地，所述双氧水为35%～40%的双氧水。
所述原料的优选摩尔比为：a：b:  c：d=1：3 : 4 : 0.5。所述e用量优选为总物料重量0.6～0.7%。
聚羧酸减水剂的合成方法，将c溶于水中配成5%溶液，将b与水1:1混合后缓慢加入c溶液中，搅拌均匀作为滴加料A。将e溶于适量水配成滴加料B，将a，d加入装有适量水的反应釜中，溶化，搅拌混合均匀，升温至60度，开始均匀向反应釜滴加A，B两种滴加料 ,加完后继续搅拌1小时，反应结束。
所述滴加液A，B均分3小时加完。
本发明的有益效果为：本发明的聚羧酸减水剂在碱性条件下合成，合成后的产品坍落度保持效果明显好于普通方法合成产品。
具体实施方式
下面结合具体实施例对本发明作进一步解释说明。
实施例1
（1）原料组成为：
a.甲基丙烯醇聚氧乙烯醚
b.丙烯酸
c.氢氧化钠
d.甲基丙烯磺酸钠
e. 35%双氧水；
所述原料的摩尔比为：a：b:  c：d = 1：2.5 : 3.5 : 0.3 ，e用量为总物料重量0.5 %。
（2）聚羧酸减水剂的合成方法：将c溶于水中配成5%溶液，将b与水1:1混合后缓慢加入c溶液中，搅拌均匀作为滴加料A。将e溶于适量水配成滴加料B，将a，d加入装有适量水的反应釜中，溶化，搅拌混合均匀，升温至60度，开始均匀向反应釜滴加A，B两种滴加料，均分3小时加完,加完后继续搅拌1小时，反应结束。
实施例2
（1）原料组成为：
a.甲基丙烯醇聚氧乙烯醚
b. 甲基丙烯酸
c.氢氧化钠
d.甲基丙烯磺酸钠
e. 35%双氧水；
所述原料的摩尔比为：a：b:  c：d = 1：3.5 : 4.5 : 0.6 ，e用量为总物料重量0.8 %。
合成方法同实施例1。
实施例3
（1）原料组成：
a.甲基丙烯醇聚氧乙烯醚
b.丙烯酸和甲基丙烯酸的混合
c.氢氧化钠
d.甲基丙烯磺酸钠
e.40%双氧水；
原料的摩尔比为：a：b:  c：d=1：3 : 4 : 0.5。所述e用量为总物料重量0.6%。
合成方法同实施例1。
    对本产品和普通聚羧酸减水剂（20%的固体含量）进行测试，得到混凝土的坍落度/扩展度的数据如下：
Figure 2014100905672100002DEST_PATH_IMAGE002
    由表可知，在掺量1.0%的情况下，本产品减水剂的坍落度明显好于普通聚羧酸减水剂。
    以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明披露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。

Claims (7)

1. 聚羧酸减水剂，其特征在于，由下述原料制成：
a.甲基丙烯醇聚氧乙烯醚
b.丙烯酸或者甲基丙烯酸或者两者混合
c.氢氧化钠
d.甲基丙烯磺酸钠
e.双氧水；
所述原料的摩尔比为：a：b:  c：d = 1：2.5～3.5 : 3.5～4.5: 0.3～0.6，e用量为总物料重量0.5～0.8%。
2.根据权利要求1所述的聚羧酸减水剂，其特征在于，所述双氧水为35%～40%双氧水。
3.根据权利要求1所述的聚羧酸减水剂，其特征在于，所述原料的摩尔比为：a：b:  c：d=1：3 : 4 : 0.5。
4.根据权利要求1所述的聚羧酸减水剂，其特征在于，所述e用量为总物料重量0.6～0.7%。
5.如权利要求1-4任一项所述的聚羧酸减水剂的合成方法，其特征在于，将c溶于水中配成5%溶液，将b与水1:1混合后缓慢加入c溶液中，搅拌均匀作为滴加料A。
6.将e溶于适量水配成滴加料B，将a，d加入装有适量水的反应釜中，溶化，搅拌混合均匀，升温至60度，开始均匀向反应釜滴加A，B两种滴加料 ,加完后继续搅拌1小时，反应结束。
7.根据权利要求5所述的聚羧酸减水剂的合成方法，其特征在于，所述滴加液A，B均分3小时加完。
CN201410090567.2A 2014-03-13 2014-03-13 聚羧酸减水剂及其碱性环境合成方法 Active CN103864330B (zh)