CN103862826A - Production method of super-soft knitted composite fabric - Google Patents
Production method of super-soft knitted composite fabric Download PDFInfo
- Publication number
- CN103862826A CN103862826A CN201210546485.5A CN201210546485A CN103862826A CN 103862826 A CN103862826 A CN 103862826A CN 201210546485 A CN201210546485 A CN 201210546485A CN 103862826 A CN103862826 A CN 103862826A
- Authority
- CN
- China
- Prior art keywords
- fabric
- cloth
- subjected
- production method
- tpu film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production method of super-soft knitted composite fabric. According to the production method, qualified fabric is obtained via bleaching, washing, brightening, and then washing, dehydrating, and wet stentering of fabric; the obtained fabric is subjected to antibacterial treatment, wherein the obtained fabric is immersed in an antibacterial solution for 30min at a temperature of 38 to 42 DEG C, and then is dried with cold wind; the fabric is subjected to softening treatment, wherein the fabric is immersed in a softening liquid with a temperature of 40 DEG C for 20min, and then is collected and is subjected to blow drying at a temperature of 20 to 30 DEG C; the fabric is subjected to combined treatment, wherein thermoplastic polyurethane (TPU) thin film is taken as a composite layer, the surface of the TPU thin film is subjected to gluing, and then is subjected to preheating using an infrared lamp, and at last, the preheated TPU thin film and the obtained knitted fabric are subjected to hotpressing.
Description
Technical field
The invention belongs to Strand Feeding Technique field, be specifically related to a kind of production method of super soft knitting composite material-feeding.
Background technology
Along with improving constantly of social development and people's living standard, people more and more pursue high-grade cloth, in pursuing high-quality cloth, also more and more changeable to the demand of its style, style.Real silk has good insulation, moisture absorption, loose wet and ventilative performance, and skin is had to certain protective effect, liked by masses.The compound real silk cloth of researching and developing a kind of softness, health care, will meet the pursuit of people to Novel cloth.
Summary of the invention
The above-mentioned technical problem existing in order to overcome prior art field, the object of the invention is to, and a kind of production method of super soft knitting composite material-feeding is provided, technique is simple, and production efficiency is high, also can effectively utilize the offal of real silk cloth, energy-conserving and environment-protective, soft, smooth, good springiness.
The production method of super soft knitting composite material-feeding provided by the invention, comprises the following steps:
(1) raw material selection, selecting cocoon fiber looped fabric is raw material;
(2) fabric is made: by fibrous raw material by shredding, cut cotton, then comb and parallel cotton fibers prior to spinning, is organized into sliver, afterwards sliver is spun into spun silk, and spun silk is made into fabric;
(3) fabric processing: after fabric process is bleached, washed, brightens, then obtain qualified cloth after washing, dehydration, wet expanding;
(4) cloth antibacterial treatment, puts into cloth the antimicrobial fluid of 38-42 ℃ and soaks 30 minutes, and cold wind is dried afterwards;
(5) cloth soft treatment, puts into softening agent by cloth and soaks 20 minutes, and taking-up dries up, and the temperature of described softening agent is 40 ℃, dries up temperature and is 20-30 ℃;
(6) fabric is compound: select thermoplastic polyurethane TPU film as composite bed, by the gluing of TPU film surface, and by infrared lamp, the TPU film after to gluing carries out preheating, finally the TPU film after preheating and knitting cloth is carried out to hot pressing;
(7) follow-up cooling processing: will be through the composite material-feeding of hot pressing laminating, send into chill roll and carry out coolingly by drawing strap, by through the cooling composite material-feeding of chill roll, carry out wind-cooling heat dissipating taste removal, obtain compound super soft knitting cloth.
The production method of super soft knitting composite material-feeding provided by the invention, its beneficial effect is, and technique is simple, and production efficiency is high, is applicable to batch production; Also can effectively utilize the offal of real silk cloth, energy-conserving and environment-protective; Select TPU film, and carry out preheating by infrared lamp after to gluing, pressing afterwards, cohesive is good, water-tight, non-foaming; Gained cloth is nontoxic, wear-resisting, antimildew and antibacterial, non-stimulated, soft, smooth, good springiness.
The specific embodiment
Below in conjunction with an embodiment, the production method of super soft knitting composite material-feeding provided by the invention is described in detail.
Embodiment
The production method of the super soft knitting composite material-feeding of the present embodiment, comprises the following steps:
(1) raw material selection, selecting cocoon fiber looped fabric is raw material;
(2) fabric is made: by fibrous raw material by shredding, cut cotton, then comb and parallel cotton fibers prior to spinning, is organized into sliver, afterwards sliver is spun into spun silk, and spun silk is made into fabric;
(3) fabric processing: after fabric process is bleached, washed, brightens, then obtain qualified cloth after washing, dehydration, wet expanding;
(4) cloth antibacterial treatment, puts into cloth the antimicrobial fluid of 38-42 ℃ and soaks 30 minutes, and cold wind is dried afterwards;
(5) cloth soft treatment, puts into softening agent by cloth and soaks 20 minutes, and taking-up dries up, and the temperature of described softening agent is 40 ℃, dries up temperature and is 20-30 ℃;
(6) fabric is compound: select thermoplastic polyurethane TPU film as composite bed, by the gluing of TPU film surface, and by infrared lamp, the TPU film after to gluing carries out preheating, finally the TPU film after preheating and knitting cloth is carried out to hot pressing;
(7) follow-up cooling processing: will be through the composite material-feeding of hot pressing laminating, send into chill roll and carry out coolingly by drawing strap, by through the cooling composite material-feeding of chill roll, carry out wind-cooling heat dissipating taste removal, obtain compound super soft knitting cloth.
Claims (1)
1. a production method for super soft knitting composite material-feeding, is characterized in that comprising the following steps:
(1) raw material selection, selecting cocoon fiber looped fabric is raw material;
(2) fabric is made: by fibrous raw material by shredding, cut cotton, then comb and parallel cotton fibers prior to spinning, is organized into sliver, afterwards sliver is spun into spun silk, and spun silk is made into fabric;
(3) fabric processing: after fabric process is bleached, washed, brightens, then obtain qualified cloth after washing, dehydration, wet expanding;
(4) cloth antibacterial treatment, puts into cloth the antimicrobial fluid of 38-42 ℃ and soaks 30 minutes, and cold wind is dried afterwards;
(5) cloth soft treatment, puts into softening agent by cloth and soaks 20 minutes, and taking-up dries up, and the temperature of described softening agent is 40 ℃, dries up temperature and is 20-30 ℃;
(6) fabric is compound: select thermoplastic polyurethane TPU film as composite bed, by the gluing of TPU film surface, and by infrared lamp, the TPU film after to gluing carries out preheating, finally the TPU film after preheating and knitting cloth is carried out to hot pressing;
(7) follow-up cooling processing: will be through the composite material-feeding of hot pressing laminating, send into chill roll and carry out coolingly by drawing strap, by through the cooling composite material-feeding of chill roll, carry out wind-cooling heat dissipating taste removal, obtain compound super soft knitting cloth.