CN103850043A - Waterproof elastic single-resistant fabrics and production method thereof - Google Patents

Abstract

The invention discloses waterproof elastic single-resistant fabrics and a production method thereof. Coarse needle one-side brushes comprise surface filaments and bottom filaments; the surface filaments are formed by 75 deniers every 72 filaments of polyester heavy nets through weaving; the bottom filaments comprise 75 deniers every 72 filaments of polyester and 41 deniers of spandex; the surface filaments and the bottom filaments are stringed and sleeve together in turn; presetting, dyeing, after-finish and waterproof finishing are performed on grey fabrics which are formed through weaving. According to the waterproof elastic single-resistant fabrics and the production method thereof, the obtained fabrics are good in extensibility and elastic resilience and excellent in waterproof performance.

Description

A kind of anti-one side material of waterproof elastic force and production method thereof

Technical field

The present invention relates to the anti-one side material of a kind of waterproof elastic force and production method thereof, belong to textile technology field.

Background technology

The anti-one side material of common elastic force has good extensibility and resilience, the clothing laminating human body of making, and comfortableness is better, once but running into the rainy day, fabric does not have water resistance, after rainwater infiltrates, clothing can stick together more in variable color, makes on the contrary people uncomfortable, is difficult to take off simultaneously.General fabric waterproof reaches waterproof effect by applying water-repellent paint at fabric bottom, but the cohesiveness of water-repellent paint and fabric is bad, easily aging coming off of coating simultaneously, once Paint Falling, not only the outward appearance of fabric is plain, the effect of the waterproof that simultaneously can lose.

Summary of the invention

The present invention, in order to address the above problem, provides the anti-one side material of a kind of waterproof elastic force and production method thereof.

The present invention is for realizing this purpose, the method adopting is: the anti-one side material of a kind of waterproof elastic force, comprise face silk and end silk, gone here and there successively to overlap by face silk and end silk and form, described the heavily net terylene that silk raw material is 75D/72F, silk of the described end comprises the terylene of 75D/72F and the spandex of 41D, on the anti-one side material of described waterproof elastic force, is attached with waterproofing agent.

A production method for the anti-one side material of waterproof elastic force, described production stage is as follows:

Using the heavily net terylene of 75D/72F as face silk, the terylene of 75D/72F and the spandex of 41D are as end silk;

Face silk and end silk are gone here and there to cover successively and become grey cloth;

The grey cloth making carries out after pre-setting, dyeing oven dry, and the looped pile coil that face silk is formed carries out plucking, bristle, cropping and shakes grain, and fabric is shaped;

The method of rolling of soaking of employing is immersed in fabric in water repellent solution completely, and making fabric liquid carrying rate through pressure rolling is 80%;

Fabric, 130 DEG C of oven dry, is then baked to 2 minutes at 160 DEG C.

Its beneficial effect is: this kind of fabric has good extensibility and resilience, has the feature of water proofing property simultaneously, and the dress ornament of making has good waterproof effect.

Brief description of the drawings

Fig. 1 is the structure chart of the anti-one side material of waterproof elastic force of the present invention.

Detailed description of the invention

Disclosed all features in this description, or step in disclosed all methods or process, except mutually exclusive feature and/or step, all can combine by any way.

Disclosed arbitrary feature in this description (comprising any accessory claim, summary, accompanying drawing), unless narration especially all can be replaced by other equivalences or the alternative features with similar object.,, unless narration especially, each feature is an example in a series of equivalences or similar characteristics.

As shown in Figure 1, the present invention proposes the anti-one side material of a kind of waterproof elastic force, this kind of fabric is to be gone here and there to overlap by face silk 2 and end silk 1 to form, face silk 2 is heavily net terylene of 75D/72F, end silk comprises the terylene 1 of 75D/72F and the spandex 4 of 41D, can give like this extensibility and resilience that fabric is good, keep the version type of fabric.The grey cloth forming after string cover is carried out after pre-setting, dyeing, oven dry, and the looped pile coil 3 that face silk 2 is woven into carries out plucking, bristle, cropping and shakes grain, then fabric is shaped.The method of rolling of soaking of employing is immersed in fabric in water repellent solution, and after fabric soaks completely, through pressure rolling, to make fabric liquid carrying rate be 80%, at 130 DEG C, dries, and then at 160 DEG C, bakes 2 minutes, can make evenly to adhere on fabric waterproofing agent.

Embodiment 1

Water repellent solution comprises waterproofing agent TG-521B, crosslinking agent TF-630 and the promoting agent F-630C of Daikin, and wherein waterproofing agent TG-521B content is 80g/L, and crosslinking agent TF-630 content is 5g/L, and promoting agent F-630C content is 2g/L, and solvent is water.

Embodiment 2

Water repellent solution comprises waterproofing agent AG-E081 (077), the crosslinking agent TP-10 of Japan AGC, and wherein waterproofing agent AG-E081 (077) content is 80g/L, and crosslinking agent TP-10 content is 3g/L, and solvent is water.

Embodiment 3

Water repellent solution comprises U.S.'s Hensel waterproofing agent CP-NH advanced in years, waterproofing agent RSH, crosslinking agent XAN and bleeding agent WDN, wherein waterproofing agent CP-NH content is 40g/L, and waterproofing agent RSH content is 40g/L, and crosslinking agent XAN content is 5g/L, bleeding agent WDN content is 0.5g/L, and solvent is water.

Embodiment 4

Water repellent solution comprises teflon CP-S, bleeding agent WDN and the glacial acetic acid of Switzerland's Clariant, and wherein the content of teflon CP-S is 50g/L, and the content of bleeding agent WDN is 0.5g/L, and glacial acetic acid content is 0.05g/L, and solvent is water.

Embodiment 5

Water repellent solution comprises not waterproofing agent X018, crosslinking agent 504M and the softener S228 of de-Nanotex, and wherein the content of waterproofing agent X018 is 80g/L, and the content of crosslinking agent 504M is 10g/L, and the content of softener S228 is 10g/L, and solvent is water.

This kind of fabric has good extensibility and resilience, has the feature of water proofing property simultaneously, and the dress ornament of making has good waterproof effect, avoided the caducous problem of traditional coating waterproof coating.

The present invention is not limited to aforesaid detailed description of the invention.The present invention expands to any new feature or any new combination disclosing in this manual, and the arbitrary new method disclosing or step or any new combination of process.

Claims (2)

1. the anti-one side material of waterproof elastic force, it is characterized in that, comprise face silk (2) and end silk, gone here and there successively to overlap by face silk and end silk and form, described the heavily net terylene that silk raw material is 75D/72F, silk of the described end comprises the terylene (1) of 75D/72F and the spandex (4) of 41D, on the anti-one side material of described waterproof elastic force, is attached with waterproofing agent.

2. a production method for the anti-one side material of waterproof elastic force, is characterized in that, described production stage is as follows:

Using the heavily net terylene of 75D/72F as face silk (2), the terylene (1) of 75D/72F and the spandex (4) of 41D are as end silk;

Face silk and end silk are gone here and there to cover successively and become grey cloth;

The grey cloth making carries out after pre-setting, dyeing oven dry, and the looped pile coil (3) that face silk is formed carries out plucking, bristle, cropping and shakes grain, and fabric is shaped;

The method of rolling of soaking of employing is immersed in fabric in water repellent solution completely, and making fabric liquid carrying rate through pressure rolling is 80%;

Fabric, 130 DEG C of oven dry, is then baked to 2 minutes at 160 DEG C.