CN103465524A - Windproof and high moisture permeable composite fabric and its production method - Google Patents
Windproof and high moisture permeable composite fabric and its production method Download PDFInfo
- Publication number
- CN103465524A CN103465524A CN 201310350709 CN201310350709A CN103465524A CN 103465524 A CN103465524 A CN 103465524A CN 201310350709 CN201310350709 CN 201310350709 CN 201310350709 A CN201310350709 A CN 201310350709A CN 103465524 A CN103465524 A CN 103465524A
- Authority
- CN
- China
- Prior art keywords
- fabric
- single brush
- singly
- windproof
- looped pile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a windproof and high moisture permeable composite fabric and its production method. The composite fabric comprises a first single brushed and single napped fabric, on which a microporous windproof and high moisture permeable membrane and a second single brushed and single napped fabric are attached in order by a glue. The first single brushed and single napped fabric and the second single brushed and single napped fabric are both formed by weft knitting of plain stitch coils and terry coils with elongated settlement arcs. The plain stitch coils and terry coils are both made of polyester yarns. The first single brushed and single napped fabric and the second single brushed and single napped fabric have 35 polyester yarns warpwise within each inch and 25 polyester yarns weftwise within each inch. With a windproof effect, the composite fabric provided in the invention has the efficacy of discharging the moisture in clothes, and has very high moisture permeability. The product is light, thin, and soft, and has pilling resistance, so that people cannot have discomfort after wearing it.
Description
Technical field
The present invention relates to textile technology field, especially relate to a kind of windproof height wet composite material and production method thereof thoroughly.
Background technology
Raising day by day along with people's living standard, to the fabric of making the clothes use, require also more and more higher, a lot of fabrics in the market all only have windproof or a kind of effect that thoroughly wets, under rainy day or burning sun, wearing the clothes that such fabric makes can make people not feel well, therefore, wind-proof performance and the water vapour permeability of fabric are had higher requirement, and easy fuzz balls.
Summary of the invention
The present invention does not have the problem of windproof and saturating wet function concurrently in order to solve a lot of fabrics in the market, a kind of windproof height wet composite material thoroughly is provided for this reason, comprise that first single brush singly shakes fabric, described first single brush singly shakes on fabric the windproof high moisture permeable membrane and the second single brush that are fitted with successively micro-porous by glue and singly shakes fabric; Described first single brush singly shakes fabric and second single brush and singly shakes fabric and form by plain loop with the looped pile coil weft knitting of elongating sinker loop, the raw material of described plain loop and looped pile coil is spun polyester thread, the spun polyester thread specification that described first single brush singly shakes plain loop in fabric is 75D/36F, and the spun polyester thread specification of looped pile coil is 75D/72F; The spun polyester thread specification that second single brush singly shakes plain loop in fabric is 100D/36F, the spun polyester thread specification of looped pile coil is 100D/144F, described first single brush singly shakes fabric and second single brush, and singly to shake spun polyester thread in each inch of fabric warp-wise be 35, and in each inch of broadwise, spun polyester thread is 25.
The windproof height of the present invention is the production method of wet composite material thoroughly, and described production stage comprises: make the step that first single brush singly shakes grey cloth; Make the step that second single brush singly shakes grey cloth; The first single brush made is singly shaken to grey cloth and second single brush and singly shake that grey cloth dye and rear arrangement, make first single brush and singly shake fabric and second single step of singly shaking fabric of brushing; First single brush is singly shaken to fabric, windproof high moisture permeable membrane and second single brush and singly shake the step that fabric is fitted successively.
The windproof height of the present invention is the production method of wet composite material thoroughly, the step that the single brush of described making first singly shakes grey cloth comprises: the spun polyester thread with 75D/36F is woven into plain loop, as the ground tissue, the spun polyester thread that simultaneously feeds 75D/72F is woven into the looped pile coil, plain loop and looped pile coil are gone here and there mutually cover, and the sinker loop of looped pile coil is elongated, form looped pile, be made into grey cloth.
The windproof height of the present invention is the production method of wet composite material thoroughly, the step that the single brush of described making second singly shakes grey cloth comprises: the spun polyester thread with 100D/36F is woven into plain loop, as the ground tissue, the spun polyester thread that simultaneously feeds 100D/144F is woven into the looped pile coil, plain loop and looped pile coil are gone here and there mutually cover, and the sinker loop of looped pile coil is elongated, form looped pile, be made into grey cloth.
The windproof height of the present invention is the production method of wet composite material thoroughly, the first single brush made is singly shaken to grey cloth and second single brush and singly shake the step that grey cloth dye with rear arrangement, grey cloth is immersed in dye liquor and dyeed, add in dye liquor disperse dyes and auxiliary agent are arranged, auxiliary agent is glacial acetic acid 0.8g/L, high temperature levelling agent 1.2g/L, sodium acetate 0.5g/L, dyeing temperature is 130 ℃, temperature retention time 35 minutes, bath raio 1:10-12, the pH value is 4.5-5, carry out reduction cleaning after having dyeed, the medicament used is sodium hydrosulfite 1-2g/L, caustic soda 2-3g/L, bath raio 1:10-12, temperature is 80 ℃, scavenging period is 20 minutes, continuation neutralizes washing to grey cloth, the medicament used is glacial acetic acid 1g/L, bath raio 1:10-12, temperature 60 C, 15 minutes time, then grey cloth is dried, temperature is 130 ℃, cloth speed 20m/min, described rear arrangement comprises plucking, bristle, cropping, shakes grain and typing, wherein gigging speed is 20m/min, the plucking number of times is 4 times, the plucking dynamics is followed successively by gear 55,50,45,45 teeth, bristle speed is 20m/min, bristle power is 19-25N, the cloth speed of cropping is 25-30m/min, hobboing cutter speed is 1200r/min, and the temperature of shaking grain is 60-80 ℃, and the dry milling time is 10-40 minute, dry milling finishes latter cooling 10-20 minute to 30 ℃, the cloth speed of typing is 30m/min, and wind speed is 900-1200r/min, and temperature is 140-160 ℃,
First single brush is singly shaken to fabric, windproof high moisture permeable membrane and second single brush and singly shake the step that fabric is fitted successively, first the one side at windproof high moisture permeable membrane applies glue, first single brush is singly shaken to fabric to be fitted on windproof high moisture permeable membrane, then standing 12-24 hour, complete the laminating that first single brush singly shakes fabric and windproof high moisture permeable membrane, then the another side at windproof high moisture permeable membrane applies glue, second single brush is singly shaken on the another side that fabric is fitted in windproof high moisture permeable membrane, still standing 12-24 hour, finally complete.
It is that main glue 6191 is 70% that described first single brush singly shakes the glue component ratio adopted when fabric, windproof high moisture permeable membrane and second single brush singly shake the fabric laminating, and bridging agent 6775 is 9%, ethyl acetate 21%.
The invention has the beneficial effects as follows:
The present invention is owing to singly shaking between fabric and accompanying the windproof high moisture permeable membrane of one deck at two-layer single brush, and therefore existing windproof effect, have again the effect that the moisture of clothes the inside is discharged, poisture-penetrability is high, and product is frivolous, softness, be through people and do not have discomfort with it, be difficult for fuzz balls.
The accompanying drawing explanation
Examples of the present invention will be described by way of reference to the accompanying drawings, wherein:
Fig. 1 is schematic diagram of the present invention;
Fig. 2 is the schematic diagram that in the present invention, single brush singly shakes fabric.
The specific embodiment
Disclosed all features in this specification, or the step in disclosed all methods or process, except mutually exclusive feature and/or step, all can combine by any way.
Disclosed arbitrary feature in this specification (comprising any accessory claim, summary and accompanying drawing), unless special narration all can be replaced by other equivalences or the alternative features with similar purpose.That is,, unless special narration, each feature is an example in a series of equivalences or similar characteristics.
Windproof height as depicted in figs. 1 and 2 is wet composite material thoroughly, comprise that first single brush singly shakes fabric 1, described first single brush singly shakes on fabric 1 successively the windproof high moisture permeable membrane 2 and the second single brush that are fitted with micro-porous by glue and singly shakes fabric 3, described first single brush singly shakes the bottom surface of fabric 1 and first fits by glue with the one side of windproof high moisture permeable membrane 2, after standing 12-24 hour, again second single brush is singly shaken to the bottom surface of fabric 3 and the another side of windproof high moisture permeable membrane 2 is fitted by glue, then standing 12-24 hour, form windproof height wet composite material thoroughly, the glue component ratio adopted is that main glue 6191 is 70%, bridging agent 6775 is 9%, ethyl acetate 21%.
First single brush described in the present invention singly shakes that fabric 1 and second single brush singly shake that fabric 3 is all that single brush singly shakes that grey cloth is dyed, after oven dry and rear arrangement, the list brush become singly shakes fabric, the grey cloth that wherein first single brush singly shakes fabric 1 is that the spun polyester thread with 75D/36F is woven into plain loop, as the ground tissue, the spun polyester thread that simultaneously feeds 75D/72F is woven into the looped pile coil, and plain loop and looped pile coil are gone here and there mutually cover, and the sinker loop of looped pile coil is elongated, form looped pile, braiding forms.And the grey cloth that second single brush singly shakes fabric 3 to be spun polyester thread with 100D/36F be woven into plain loop, as the ground tissue, the spun polyester thread that simultaneously feeds 100D/144F is woven into the looped pile coil, plain loop and looped pile coil are gone here and there mutually cover, and the sinker loop of looped pile coil is elongated, forming looped pile, braiding forms, described first single brush singly shakes fabric 1 and second single brush, and singly to shake spun polyester thread in each inch of fabric 3 warp-wises be 35, and in each inch of broadwise, spun polyester thread is 25.
The first single brush made is singly shaken to grey cloth and second single brush and singly shake the step that grey cloth dye with rear arrangement, grey cloth is immersed in dye liquor and dyeed, add in dye liquor disperse dyes and auxiliary agent are arranged, auxiliary agent is glacial acetic acid 0.8g/L, high temperature levelling agent 1.2g/L, sodium acetate 0.5g/L, dyeing temperature is 130 ℃, temperature retention time 35 minutes, bath raio 1:10-12, the pH value is 4.5-5, carry out reduction cleaning after having dyeed, the medicament used is sodium hydrosulfite 1-2g/L, caustic soda 2-3g/L, bath raio 1:10-12, temperature is 80 ℃, scavenging period is 20 minutes, continuation neutralizes washing to grey cloth, the medicament used is glacial acetic acid 1g/L, bath raio 1:10-12, temperature 60 C, 15 minutes time, then grey cloth is dried, temperature is 130 ℃, cloth speed 20m/min, described rear arrangement comprises plucking, bristle, cropping, shakes grain and typing, wherein gigging speed is 20m/min, the plucking number of times is 4 times, the plucking dynamics is followed successively by gear 55,50,45,45 teeth, bristle speed is 20m/min, bristle power is 19-25N, the cloth speed of cropping is 25-30m/min, hobboing cutter speed is 1200r/min, and the temperature of shaking grain is 60-80 ℃, and the dry milling time is 10-40 minute, dry milling finishes latter cooling 10-20 minute to 30 ℃, the cloth speed of typing is 30m/min, and wind speed is 900-1200r/min, and temperature is 140-160 ℃.
The existing windproof effect of the present invention, have again the effect that the moisture of clothes the inside is discharged, and poisture-penetrability is high, and product is frivolous, and softness is through people and does not have discomfort with it, is difficult for fuzz balls.
The present invention is not limited to the aforesaid specific embodiment.The present invention expands to any new feature or any new combination disclosed in this manual, and the arbitrary new method disclosed or step or any new combination of process.
Claims (3)
1. a windproof height wet composite material thoroughly is characterized in that: comprise that first single brush singly shakes fabric (1), described first single brush singly shakes upper windproof high moisture permeable membrane (2) and the second single brush that is fitted with successively micro-porous by glue of fabric (1) and singly shakes fabric (3); Described first single brush singly shakes fabric (1) and second single brush and singly shakes fabric (3) and form by plain loop with the looped pile coil weft knitting of elongation sinker loop, the raw material of described plain loop and looped pile coil is spun polyester thread, the spun polyester thread specification that described first single brush singly shakes plain loop in fabric (1) is 75D/36F, and the spun polyester thread specification of looped pile coil is 75D/72F; The spun polyester thread specification that second single brush singly shakes plain loop in fabric (3) is 100D/36F, the spun polyester thread specification of looped pile coil is 100D/144F, described first single brush singly shakes fabric (1) and second single brush, and singly to shake spun polyester thread in each inch of fabric (3) warp-wise be 35, and the interior spun polyester thread of each inch of broadwise is 25.
2. the windproof high production method of wet composite material thoroughly, is characterized in that, described production stage comprises:
Make the step that first single brush singly shakes grey cloth, spun polyester thread with 75D/36F is woven into plain loop, as the ground tissue, the spun polyester thread that simultaneously feeds 75D/72F is woven into the looped pile coil, plain loop and looped pile coil are gone here and there mutually cover, and the sinker loop of looped pile coil is elongated, form looped pile, be made into grey cloth;
Make the step that second single brush singly shakes grey cloth, spun polyester thread with 100D/36F is woven into plain loop, as the ground tissue, the spun polyester thread that simultaneously feeds 100D/144F is woven into the looped pile coil, plain loop and looped pile coil are gone here and there mutually cover, and the sinker loop of looped pile coil is elongated, form looped pile, be made into grey cloth;
The first single brush made is singly shaken to grey cloth and second single brush and singly shake the step that grey cloth dye with rear arrangement, grey cloth is immersed in dye liquor and dyeed, add in dye liquor disperse dyes and auxiliary agent are arranged, auxiliary agent is glacial acetic acid 0.8g/L, high temperature levelling agent 1.2g/L, sodium acetate 0.5g/L, dyeing temperature is 130 ℃, temperature retention time 35 minutes, bath raio 1:10-12, the pH value is 4.5-5, carry out reduction cleaning after having dyeed, the medicament used is sodium hydrosulfite 1-2g/L, caustic soda 2-3g/L, bath raio 1:10-12, temperature is 80 ℃, scavenging period is 20 minutes, continuation neutralizes washing to grey cloth, the medicament used is glacial acetic acid 1g/L, bath raio 1:10-12, temperature 60 C, 15 minutes time, then grey cloth is dried, temperature is 130 ℃, cloth speed 20m/min, described rear arrangement comprises plucking, bristle, cropping, shakes grain and typing, wherein gigging speed is 20m/min, the plucking number of times is 4 times, the plucking dynamics is followed successively by gear 55,50,45,45 teeth, bristle speed is 20m/min, bristle power is 19-25N, the cloth speed of cropping is 25-30m/min, hobboing cutter speed is 1200r/min, and the temperature of shaking grain is 60-80 ℃, and the dry milling time is 10-40 minute, dry milling finishes latter cooling 10-20 minute to 30 ℃, the cloth speed of typing is 30m/min, and wind speed is 900-1200r/min, and temperature is 140-160 ℃,
First single brush is singly shaken to fabric (1), windproof high moisture permeable membrane (2) and second single brush singly shake the step that fabric (3) is fitted successively, first the one side at windproof high moisture permeable membrane (2) applies glue, first single brush is singly shaken to fabric (1) to be fitted on windproof high moisture permeable membrane (2), then standing 12-24 hour, complete the laminating that first single brush singly shakes fabric (1) and windproof high moisture permeable membrane (2), then the another side at windproof high moisture permeable membrane (2) applies glue, second single brush is singly shaken on the another side that fabric (3) is fitted in windproof high moisture permeable membrane (1), still standing 12-24 hour, finally complete.
3. a kind of windproof height according to claim 2 production method of wet composite material thoroughly, it is characterized in that: it is that main glue 6191 is 70% that described first single brush singly shakes the glue component ratio adopted when fabric (1), windproof high moisture permeable membrane (2) singly shake fabric (3) laminating with second single brush, bridging agent 6775 is 9%, ethyl acetate 21%.