CN103818093A - Room-temperature finishing process for composite inorganic plates - Google Patents
Room-temperature finishing process for composite inorganic plates Download PDFInfo
- Publication number
- CN103818093A CN103818093A CN201310617582.3A CN201310617582A CN103818093A CN 103818093 A CN103818093 A CN 103818093A CN 201310617582 A CN201310617582 A CN 201310617582A CN 103818093 A CN103818093 A CN 103818093A
- Authority
- CN
- China
- Prior art keywords
- composite inorganic
- substrate
- finishing process
- roll
- inorganic board
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a finishing process for enamel base plates. Through secondary flat pressing at room temperature, a composite inorganic plate which cannot be finished at high temperature is finished at room temperature, so that the problem that the enamel base plates cannot be finished at high temperature is solved. The problem that the composite inorganic plate using an enamel plate as a base plate cannot be finished at high temperature is solved by performing flat pressing on the composite inorganic plate subjected to roll pressing, a PVC (polyvinyl chloride) membrane is better stuck to the base plate, the surface flatness of the composite inorganic plate is improved, and the bonding force is increased. The working efficiency is increased, and the working time is reduced.
Description
Technical field
The present invention relates to a kind of timber floor " finishing process, relate in particular to a kind of " finishing process of enamel substrate.
Background technology
In the time making the composite inorganic board that enamel plate is substrate, need to be at its surface bonding one deck PVC film, but because composite surface after gummed PVC film is uneven, can cause the quality of composite inorganic board to decline, and because the gummed place of enamel plate and PVC film can cause material to melt once heating, cannot carry out facing processing by hot paste pressing plate.Therefore, solve the problem that enamel substrate cannot carry out the processing of high temperature facing and just seem particularly important.
Summary of the invention
The invention provides a kind of " finishing process of enamel substrate, by the secondary concora crush under normal temperature, composite inorganic board that cannot high temperature facing carries out normal temperature facing, has solved the problem that enamel substrate cannot carry out the processing of high temperature facing.
The object of this invention is to provide a kind of composite inorganic board normal temperature " finishing process, comprise the following steps:
Step 1: get surperficial untreated enamel plate as substrate;
Step 2: PVC film is carried out to gluing by glue spreader;
Step 3: glue-coated PVC film is bonded on substrate;
Step 4: the substrate that pasted film is put into roll squeezer and carry out roll-in;
Step 5: carry out concora crush, output finished product in spreader bar by sending into through the substrate of roll-in.
Further improve and be: in described step 5, the pressure of spreader bar is 5-20MPa.
Further improve and be: in described step 5, material time of pressing in spreader bar is no more than 10min.
Beneficial effect of the present invention: carry out concora crush processing by the composite inorganic board to after roll-in, solve the problem that composite inorganic board using enamel plate as substrate can not high temperature facing, and PVC film is better fitted on substrate, composite inorganic board surface smoothness is increased, improve bonding force, and lifting operating efficiency, reduces the working time.
The specific embodiment
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, and this embodiment only, for explaining the present invention, does not form limiting the scope of the present invention.
Embodiment mono-
The present embodiment provides a kind of composite inorganic board normal temperature " finishing process, comprises the following steps:
Step 1: get surperficial untreated enamel plate as substrate;
Step 2: PVC film is carried out to gluing by glue spreader;
Step 3: glue-coated PVC film is bonded on substrate;
Step 4: the substrate that pasted film is put into roll squeezer and carry out roll-in;
Step 5: carry out concora crush, output finished product in spreader bar by sending into through the substrate of roll-in.
In described step 5, the pressure of spreader bar is 13MPa.
In described step 5, the time of material pressing in spreader bar is 5min.
Embodiment bis-
The present embodiment provides a kind of composite inorganic board normal temperature " finishing process, comprises the following steps:
Step 1: get surperficial untreated enamel plate as substrate;
Step 2: PVC film is carried out to gluing by glue spreader;
Step 3: glue-coated PVC film is bonded on substrate;
Step 4: the substrate that pasted film is put into roll squeezer and carry out roll-in;
Step 5: carry out concora crush, output finished product in spreader bar by sending into through the substrate of roll-in.
In described step 5, the pressure of spreader bar is 5MPa.
In described step 5, the time of material pressing in spreader bar is 3min.
Embodiment tri-
The present embodiment provides a kind of composite inorganic board normal temperature " finishing process, comprises the following steps:
Step 1: get surperficial untreated enamel plate as substrate;
Step 2: PVC film is carried out to gluing by glue spreader;
Step 3: glue-coated PVC film is bonded on substrate;
Step 4: the substrate that pasted film is put into roll squeezer and carry out roll-in;
Step 5: carry out concora crush, output finished product in spreader bar by sending into through the substrate of roll-in.
In described step 5, the pressure of spreader bar is 20MPa.
In described step 5, the time of material pressing in spreader bar is 10min.
Above three embodiment carry out concora crush processing by the composite inorganic board to after roll-in, solve the problem that composite inorganic board using enamel plate as substrate can not high temperature facing, and PVC film is better fitted on substrate, composite inorganic board surface smoothness is increased, improve bonding force, and lifting operating efficiency, reduces the working time.
Claims (3)
1. a composite inorganic board normal temperature " finishing process, is characterized in that: comprise the following steps:
Step 1: get surperficial untreated enamel plate as substrate;
Step 2: PVC film is carried out to gluing by glue spreader;
Step 3: glue-coated PVC film is bonded on substrate;
Step 4: the substrate that pasted film is put into roll squeezer and carry out roll-in;
Step 5: carry out concora crush, output finished product in spreader bar by sending into through the substrate of roll-in.
2. composite inorganic board normal temperature " finishing process as claimed in claim 1, is characterized in that: in described step 5, the pressure of spreader bar is 5-20MPa.
3. composite inorganic board normal temperature " finishing process as claimed in claim 1 or 2, is characterized in that: in described step 5, material time of pressing in spreader bar is no more than 10min.