CN103790336A - Antistatic rubber floor production process - Google Patents
Antistatic rubber floor production process Download PDFInfo
- Publication number
- CN103790336A CN103790336A CN201210431062.9A CN201210431062A CN103790336A CN 103790336 A CN103790336 A CN 103790336A CN 201210431062 A CN201210431062 A CN 201210431062A CN 103790336 A CN103790336 A CN 103790336A
- Authority
- CN
- China
- Prior art keywords
- antistatic
- floor
- production technology
- carbon black
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antistatic rubber floor production process which sequentially includes the steps of firstly, selecting ethylene propylene rubber, antistatic agent, white carbon black and butadiene styrene rubber as raw materials; secondly, mixing the ethylene propylene rubber, antistatic agent, white carbon black and butadiene styrene rubber according to the proportion of 4:2:1:3; thirdly, melting the mixture at high temperature of 430 DEG C, and integrally extruding the melted mixture in a die at the pressure of 220MPa; fourthly, cooling, sanding, trimming periphery, and finishing and forming. The production process is simple to operate, and the produced antistatic rubber floor is good in antistatic performance.
Description
Technical field
The present invention relates to a kind of production technology of rubber floor covering, relate in particular to the production technology on a kind of antistatic rubber floor.
Background technology
There are wood flooring and ceramic floor in domestic common floor at present, and ceramic floor is a current domestic most popular class floor decorative material, and high, medium and low floor tile has supply on market, and beautiful in colour, various in style, be applicable to the building finishing of different class, price is also moderate.But ceramic tile is that skid resistance is poor as the weakness of earth material maximum, and frangible, and feel is bad, construction trouble, weight capacity is poor, is not suitable for the busy area of vehicular traffic and uses; Wood floors are elegant gentle, and class is higher, be more and more subject to liking of people, but tone is single, non-moistureproof, not water-fast, not fire-retardant yielding, application life is short, and maintaining trouble, especially some composite floor boards inferior, contain a large amount of pernicious gases, as formaldehyde etc.By harmful other healthy of living in ground of such floor finiss.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of production technology of antistatic rubber floor simple to operate.
For solving the problems of the technologies described above, the invention provides a kind of production technology of antistatic floor, this production technology in turn includes the following steps: the first step: choose raw material, described raw material is EP rubbers, antistatic additive, White Carbon black, butadiene-styrene rubber; Second step: by described EP rubbers, antistatic additive, White Carbon black, butadiene-styrene rubber according to 4: 2: 1: 3 ratio is mixed; The 3rd step: by described mixture high temperature melt, be placed in mould and be squeezed into one, described temperature is 410 ℃-450 ℃, and described pressure is 150-300MPa; The 4th step: cooling, sanding, prunes surrounding, finishing moulding.
Described temperature is 430 ℃.
Described pressure is 220MPa.
Compared with prior art, beneficial effect of the present invention is:
The present invention is simple to operate, and because the present invention has added antistatic additive, the floor making has good antistatic behaviour, and due to floor one-shot forming, save the trouble of splicing, so production efficiency is higher, therefore the present invention is simple to operate, and has good antistatic behaviour.
The specific embodiment
By the specific embodiment, the present invention is described in further details below
A production technology for antistatic floor, this production technology in turn includes the following steps: the first step: choose raw material, described raw material is EP rubbers, antistatic additive, White Carbon black, butadiene-styrene rubber; Second step: by described EP rubbers, antistatic additive, White Carbon black, butadiene-styrene rubber according to 4: 2: 1: 3 ratio is mixed; The 3rd step: by described mixture high temperature melt, be placed in mould and be squeezed into one, described temperature is 410 ℃-450 ℃, and described pressure is 150-300MPa; The 4th step: cooling, sanding, prunes surrounding, finishing moulding.
Embodiment 1:
A production technology for antistatic floor, this production technology in turn includes the following steps: the first step: choose raw material, described raw material is EP rubbers, antistatic additive, White Carbon black, butadiene-styrene rubber; Second step: by described EP rubbers, antistatic additive, White Carbon black, butadiene-styrene rubber according to 4: 2: 1: 3 ratio is mixed; The 3rd step: by described mixture high temperature melt, be placed in mould and be squeezed into one, described temperature is 430 ℃, and described pressure is 220MPa; The 4th step: cooling, sanding, prunes surrounding, finishing moulding.
In sum, the present invention is simple to operate, and has good antistatic behaviour.
The foregoing is only preferred embodiments of the present invention; protection scope of the present invention is not limited with above-mentioned embodiment; in every case the equivalence that those of ordinary skills do according to disclosed content is modified or is changed, and all should include in the protection domain of recording in claims.
Claims (3)
1. a production technology for antistatic floor, is characterized in that this production technology in turn includes the following steps: the first step: choose raw material, described raw material is EP rubbers, antistatic additive, White Carbon black, butadiene-styrene rubber; Second step: by described EP rubbers, antistatic additive, White Carbon black, butadiene-styrene rubber according to 4: 2: 1: 3 ratio is mixed; The 3rd step: by described mixture high temperature melt, be placed in mould and be squeezed into one, described temperature is 410 ℃-450 ℃, and described pressure is 150-300MPa; The 4th step: cooling, sanding, prunes surrounding, finishing moulding.
2. the production technology on a kind of anti-slip rubber according to claim 1 floor, is characterized in that: described temperature is 430 ℃.
3. the production technology on a kind of anti-slip rubber according to claim 1 floor, is characterized in that: described pressure is 220MPa.