CN103787630A - 抗裂保温水泥砂浆及其制备方法 - Google Patents

抗裂保温水泥砂浆及其制备方法 Download PDF

Info

Publication number
CN103787630A
CN103787630A CN201310707132.3A CN201310707132A CN103787630A CN 103787630 A CN103787630 A CN 103787630A CN 201310707132 A CN201310707132 A CN 201310707132A CN 103787630 A CN103787630 A CN 103787630A
Authority
CN
China
Prior art keywords
parts
cement mortar
cement
insulating cement
cracking resistance
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310707132.3A
Other languages
English (en)
Inventor
孙改进
邹小霞
徐爱秀
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Sen Wang Construction Engineering Co., Ltd.
Original Assignee
ANHUI MEIYU ENERGY SAVING ENVIRONMENTAL PROTECTION TECHNOLOGY APPLICATION Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI MEIYU ENERGY SAVING ENVIRONMENTAL PROTECTION TECHNOLOGY APPLICATION Co Ltd filed Critical ANHUI MEIYU ENERGY SAVING ENVIRONMENTAL PROTECTION TECHNOLOGY APPLICATION Co Ltd
Priority to CN201310707132.3A priority Critical patent/CN103787630A/zh
Publication of CN103787630A publication Critical patent/CN103787630A/zh
Pending legal-status Critical Current

Abstract

本发明涉及建筑材料领域,具体的说是一种建筑工程用的抗裂保温水泥砂浆及其制备方法,其特征在于由下列组分按如下配比组成:珍珠岩60-80份,水泥30-40份,高岭土5-8份,膨润土1-5份,海泡石1-5份,纤维5-10份,河沙20-40份,水70-80份,聚氨酯硬泡颗粒30-40份,丁苯橡胶乳液1-10份,按配比取各组分,先将水泥、纤维和河沙充分混合,然后取其余组分依次加入混合物中,不断搅拌,形成水泥砂浆,本发明与现有技术相比,具有节能效果显著、附着力强、抗裂性好等显著特点。

Description

抗裂保温水泥砂浆及其制备方法
 
技术领域:
    本发明涉及建筑材料领域,具体的说是一种建筑工程用的抗裂保温水泥砂浆及其制备方法。
背景技术:
    水泥作为一种水硬性胶凝材料在建筑工程领域得到广泛的应用,其主要特性为加入适量水后具有的可塑性,不仅能够在空气中硬化,也能够在水中硬化。水泥特别适用于制造混凝土,并被广泛的应用于路面铺设、房屋建筑等场合。现有技术中,由水泥混凝土铺就的路面在寒冷天气条件下,因冰雪冻融作用,往往过早断裂和被破坏,远远达不到设计指标的使用年限,给人们的生产生活带来不便和浪费。
   此外,自2001年10月1日起,我国发布了行业标准《夏热冬冷地区居住建筑节能设计标准》(JGJ134-2001),要求对建筑物外墙做保温隔热处理,全面实现建筑节能50%的目标,而实际施工过程中,在保温层上用普通水泥砂浆抹面更容易龟裂,进一步增加了建筑物表面抗裂难度。聚氨酯硬泡是一种节能效果较好的保温材料,目前聚氨酯硬泡保温层的抹面抗裂处理方法是水泥砂浆加钢网、加玻纤,或者复合保温,加聚合物砂浆,导致工序繁琐,造价高,工期长。
  发明内容:
    本发明针对现有技术中存在的缺点和不足,提出一种能够显著提高产品耐久性和抗腐蚀性的抗裂保温水泥砂浆及其制备方法。
    本发明可以通过以下措施达到:
    一种抗裂保温水泥砂浆,其特征在于由下列组分按如下配比组成:
珍珠岩 60-80份,水泥 30-40份,高岭土5-8份,膨润土1-5份,海泡石1-5份,纤维5-10份,河沙20-40份,水70-80份,聚氨酯硬泡颗粒30-40份,丁苯橡胶乳液1-10份。
    本发明中所述纤维为聚丙纤维或矿物纤维,用于提高砂浆的抗渗、抗裂、抗冲磨以及抗冻能力。
    本发明还包括硫酸钙,其中硫酸钙1-5份,用于调节砂浆的凝结时间。
    本发明中所述水泥可以为硫铝酸盐水泥。
    本发明还可以包含增稠剂,增稠剂1-3份,优选纤维素醚类有机增稠剂或者丙烯类有机增稠剂,用于保水增稠,改善施工性能和砂浆湿粘性。
本发明各组分优选为珍珠岩 70份,水泥 35份,高岭土6份,膨润土3份,海泡石3份,纤维6份,河沙40份,水70份,硫酸钙3份,聚氨酯硬泡颗粒35份,丁苯橡胶乳液5份,其中通过添加珍珠岩,能够提高砂浆的抗裂、抗冻性能,通过添加高岭土、膨润土和海泡石,来调节砂浆的黏结度,提高产品的抗裂性能。
    一种抗裂保温水泥砂浆的制备方法,其特征在于按上述配比取各组分,先将水泥、纤维和河沙充分混合,然后取其余组分依次加入混合物中,不断搅拌,形成水泥砂浆。
     本发明与现有技术相比,将各原料组分按配比混合、拌匀后可以直接向建筑物外墙施工,由于添加了聚氨酯硬泡颗粒,采用本发明所述水泥砂浆形成的涂抹层具有显著的节能效果,同时利用珍珠岩重量轻、导热系数低、耐腐蚀、耐冻融、干燥收缩率及浸水线性变形率小等特点,提高了水泥砂浆的抗裂性能,同时利用高岭土、膨润土、海泡石等组分,调节砂浆黏结度,使本发明所述水泥砂浆具有附着力强、抗裂性好等显著特点。
具体实施方式:
下面结合实施例,对本发明作进一步的说明。
实施例1:
一种抗裂保温水泥砂浆,其特征在于由下列组分按如下配比组成:
珍珠岩 75份,水泥 37份,高岭土6份,膨润土3份,海泡石3份,纤维8份,所述纤维为聚丙纤维,河沙30份,水70份,硫酸钙3份,增稠剂1份,聚氨酯硬泡颗粒35份,丁苯橡胶乳液9份,其中通过添加珍珠岩,能够提高砂浆的抗裂、抗冻性能,通过添加高岭土、膨润土和海泡石,来调节砂浆的黏结度,提高产品的抗裂性能。
    使用时按上述配比取各组分,先将水泥、纤维和河沙充分混合,然后取其余组分依次加入混合物中,不断搅拌,形成水泥砂浆,采用本砂浆对工程建筑表面进行施工,能够有效提高抗裂性能。
实施例2:
    一种抗裂保温水泥砂浆,其特征在于由下列组分按如下配比组成:
珍珠岩 70份,水泥 32份,高岭土2份,膨润土4份,海泡石4份,纤维5份,所述纤维为聚丙纤维,河沙35份,水70份,硫酸钙4份,聚氨酯硬泡颗粒40份,丁苯橡胶乳液5份其中通过添加珍珠岩,能够提高砂浆的抗裂、抗冻性能,通过添加高岭土、膨润土和海泡石,来调节砂浆的黏结度,提高产品的抗裂性能。
    使用时按上述配比取各组分,先将水泥、纤维和河沙充分混合,然后取其余组分依次加入混合物中,不断搅拌,形成水泥砂浆,采用本砂浆对工程建筑表面进行施工,能够有效提高抗裂性能。
实施例3:
一种抗裂保温水泥砂浆,其特征在于由下列组分按如下配比组成:
珍珠岩 75份,水泥 37份,高岭土6份,膨润土3份,海泡石3份,纤维8份,所述纤维为聚丙纤维,河沙30份,水70份,硫酸钙3份,增稠剂1.5份,聚氨酯硬泡颗粒36份,丁苯橡胶乳液4份,其中通过添加珍珠岩,能够提高砂浆的抗裂、抗冻性能,通过添加高岭土、膨润土和海泡石,来调节砂浆的黏结度,提高产品的抗裂性能。
    使用时按上述配比取各组分,先将水泥、纤维和河沙充分混合,然后取其余组分依次加入混合物中,不断搅拌,形成水泥砂浆,采用本砂浆对工程建筑表面进行施工,能够有效提高抗裂性能。
     本发明与现有技术相比,将各原料组分按配比混合、拌匀后可以直接向建筑物外墙施工,由于添加了聚氨酯硬泡颗粒,采用本发明所述水泥砂浆形成的涂抹层具有显著的节能效果,同时利用珍珠岩重量轻、导热系数低、耐腐蚀、耐冻融、干燥收缩率及浸水线性变形率小等特点,提高了水泥砂浆的抗裂性能,同时利用高岭土、膨润土、海泡石等组分,调节砂浆黏结度,使本发明所述水泥砂浆具有附着力强、抗裂性好等显著特点。

Claims (7)

1.一种抗裂保温水泥砂浆,其特征在于由下列组分按如下配比组成:
珍珠岩 60-80份,水泥 30-40份,高岭土5-8份,膨润土1-5份,海泡石1-5份,纤维5-10份,河沙20-40份,水70-80份,聚氨酯硬泡颗粒30-40份,丁苯橡胶乳液1-10份。 
2.根据权利要求1所述的一种抗裂保温水泥砂浆,其特征在于所述纤维为聚丙纤维或矿物纤维。
3.根据权利要求2所述的一种抗裂保温水泥砂浆,其特征在于还包括硫酸钙,其中硫酸钙1-5份。
4.根据权利要求3所述的一种抗裂保温水泥砂浆,其特征在于所述水泥为硫铝酸盐水泥。
5.根据权利要求4所述的一种抗裂保温水泥砂浆,其特征在于包含增稠剂,增稠剂1-3份,增稠剂为纤维素醚类有机增稠剂或者丙烯类有机增稠剂。
6.根据权利要求5所述的一种抗裂保温水泥砂浆,其特征在于本发明各组分优选为珍珠岩 70份,水泥 35份,高岭土6份,膨润土3份,海泡石3份,纤维6份,河沙40份,水70份,硫酸钙3份,聚氨酯硬泡颗粒35份,丁苯橡胶乳液5份。
7.一种如权利要求6所述的抗裂保温水泥砂浆的制备方法,其特征在于按配比取各组分,先将水泥、纤维和河沙充分混合,然后取其余组分依次加入混合物中,不断搅拌,形成水泥砂浆。 
CN201310707132.3A 2013-12-20 2013-12-20 抗裂保温水泥砂浆及其制备方法 Pending CN103787630A (zh)