CN103773230B - A kind of anti-scraping coating of electromechanical equipment - Google Patents
A kind of anti-scraping coating of electromechanical equipment Download PDFInfo
- Publication number
- CN103773230B CN103773230B CN201410023905.0A CN201410023905A CN103773230B CN 103773230 B CN103773230 B CN 103773230B CN 201410023905 A CN201410023905 A CN 201410023905A CN 103773230 B CN103773230 B CN 103773230B
- Authority
- CN
- China
- Prior art keywords
- parts
- electromechanical equipment
- coating
- scraping coating
- scraping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A kind of anti-scraping coating of electromechanical equipment, wherein: coating is made up of the component of following mass fraction: epoxy modified silicone resin 45 65 parts, 12 22 parts of phenolic resin, filler 12 18 parts, titanium dioxide 5 12 parts, white carbon 59 parts, amino silicone 7 12 parts, alumina silicate fibre 5 10 parts and diluent 10 25 parts.The anti-scraping coating of electromechanical equipment that technical solution of the present invention provides, not only has good Wear-resistant scratch-resistant performance, and curing of coatings speed is fast, and stable performance, weather resistance is strong, it is possible to lasting protection electromechanical equipment.
Description
Technical field
The present invention relates to a kind of coating, particularly to a kind of anti-scraping coating of electromechanical equipment.
Background technology
Electromechanical equipment is in normal operation, meeting is often as operating or foeign element cause friction, and form scratch in equipment surface, and some equipment are the most only possible after there is scratch all can the normal operation of equipment have an impact, it is also possible to further result in surface be etched, oxidation or other corrosion phenomenons occur, thus causes the often maintenance of equipment needs or safeguard, reduce the work efficiency of equipment.The coating of existing protection electromechanical equipment, curing of coatings efficiency is low, and Wear-resistant scratch-resistant limited capacity, and for increasing anti-wear performance, and abandon the stability of whole coating, and causing using for a long time, this is disadvantageous for protection electromechanical equipment.
Summary of the invention
Goal of the invention: for above-mentioned deficiency, it is an object of the invention to provide the coating of a kind of electromechanical equipment with good Wear-resistant scratch-resistant performance.
Technical scheme: a kind of anti-scraping coating of electromechanical equipment, wherein: coating is made up of the component of following mass fraction: epoxy modified silicone resin 45-65 part, phenolic resin 12-22 part, filler 12-18 part, titanium dioxide 5-12 part, white carbon 5-9 part, amino silicone 7-12 part, alumina silicate fibre 5-10 part and diluent 10-25 part.
As preferably, filler is barium sulfate or bentonite.
As preferably, diluent is butyl glycidyl ether or phenyl glycidyl ether.
Beneficial effect: the anti-scraping coating of electromechanical equipment that technical solution of the present invention provides, not only has good Wear-resistant scratch-resistant performance, and curing of coatings speed is fast, and stable performance, weather resistance is strong, it is possible to lasting protection electromechanical equipment.
Detailed description of the invention
In order to be further appreciated by the present invention, below in conjunction with embodiment, the preferred embodiment of the invention is described, but it is to be understood that these describe simply as further illustrating the features and advantages of the present invention rather than limiting to the claimed invention.
Embodiment 1
A kind of anti-scraping coating of electromechanical equipment, wherein: coating is made up of the component of following mass fraction: epoxy modified silicone resin 45 parts, 12 parts of phenolic resin, 12 parts of barium sulfate, titanium dioxide 5 parts, white carbon 5 parts, amino silicone 7 parts, alumina silicate fibre 5 parts and phenyl glycidyl ether 10 parts.
Embodiment 2
A kind of anti-scraping coating of electromechanical equipment, wherein: coating is made up of the component of following mass fraction: epoxy modified silicone resin 65 parts, 22 parts of phenolic resin, 18 parts of barium sulfate, titanium dioxide 12 parts, white carbon 9 parts, amino silicone 12 parts, alumina silicate fibre 10 parts and phenyl glycidyl ether 25 parts.
Embodiment 3
A kind of anti-scraping coating of electromechanical equipment, wherein: coating is made up of the component of following mass fraction: epoxy modified silicone resin 60 parts, 18 parts of phenolic resin, bentonite 16 parts, titanium dioxide 9 parts, white carbon 7 parts, amino silicone 8 parts, alumina silicate fibre 8 parts and butyl glycidyl ether 22 parts.
The coating that above-mentioned detailed description of the invention is made is made model, for experimental group；Taking common anti-scraping coating is matched group, carries out scratch resistant performance test and weather resistance test, and result is as follows:
Scratch resistant test (scrapes trace): embodiment 1 is 315, and embodiment 2 is 309, and embodiment 3 is 294, and matched group is 865；
Weatherability (1000 hours degradations): embodiment 1-3 is non-foaming, does not falls off；Matched group has slight foaming.
It follows that the anti-scraping coating of electromechanical equipment that the present invention provides has good scratch resistant performance and weather resistance.
Described above to the disclosed embodiments, makes professional and technical personnel in the field be capable of or uses the present invention.Multiple amendment to these embodiments will be apparent from for those skilled in the art, and generic principles defined herein can realize without departing from the spirit or scope of the present invention in other embodiments.Therefore, the present invention is not intended to be limited to the embodiments shown herein, and is to fit to the widest scope consistent with principles disclosed herein and features of novelty.
Claims (2)
1. the anti-scraping coating of electromechanical equipment, it is characterised in that: coating is made up of the component of following mass fraction: epoxy modified silicone resin 45-65 part, phenolic resin 12-22 part, barium sulfate or bentonite 12-18 part, titanium dioxide 5-12 part, white carbon 5-9 part, amino silicone 7-12 part, alumina silicate fibre 5-10 part and diluent 10-25 part.
The anti-scraping coating of electromechanical equipment the most according to claim 1, it is characterised in that: diluent is butyl glycidyl ether or phenyl glycidyl ether.