CN103773026A - 一种脲醛树脂乳化沥青 - Google Patents
一种脲醛树脂乳化沥青 Download PDFInfo
- Publication number
- CN103773026A CN103773026A CN201410023481.8A CN201410023481A CN103773026A CN 103773026 A CN103773026 A CN 103773026A CN 201410023481 A CN201410023481 A CN 201410023481A CN 103773026 A CN103773026 A CN 103773026A
- Authority
- CN
- China
- Prior art keywords
- parts
- urea
- formaldehyde
- formaldehyde resin
- product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
一种脲醛树脂乳化沥青，其组成成份以质量份数表示法为：乳化沥青100份；丙烯酸乙酯10-20份；脲醛树脂6-12份；聚乙烯醇15-20份；阳离子乳化剂1-3份；甲醛8-10份；盐酸5-8份；粉煤灰为15-35份；尿素为5-10份；十二烷基硫酸钠0.5-2份；流平剂8-10份；过硫酸铵2-5份；甲基丙烯酸甲酯20-30份；产品表干2-3h，实干22-24h；不透水性0.2-0.3MPa，硬度0.3-0.5；密度1.6g/cm3，剪切强度1.09-1.2MPa；产品抗弯强度高，表面浸润性和粘结性好，抗压强度高，可以广泛生产并不断代替现有材料。
Description
技术领域
本申请属于乳化沥青材料领域，尤其涉及一种脲醛树脂乳化沥青。
背景技术
乳化沥青是沥青和乳化剂在一定工艺作用下，生成水包油或油包水（具体谁包谁要看乳化剂的种类）的液态沥青。 乳化沥青是将通常高温使用的道路沥青，经过机械搅拌和化学稳定的方法（乳化），扩散到水中而液化成常温下粘度很低、流动性很好的一种道路建筑材料。可以常温使用，且可以和冷的和潮湿的石料一起使用。沥青是原油加工过程的一种产品，在常温下是黑色或黑褐色的粘稠液体或者是固体，它是一种棕黑色有机胶凝状物质，包括天然沥青、石油沥青、页岩沥青和煤焦油沥青等四种。主要成分是沥青质和树脂，其次有高沸点矿物油和少量的氧、硫和氯的化合物。有光泽，呈液体、半固体或固体状态，低温时质脆，粘结性和防腐性能良好。
乳化沥青分为阳离子乳化沥青、阴离子乳化沥青和非离子乳化沥青。阳离子乳化沥青的沥青微粒带正电荷，阴离子乳化沥青微粒带负电荷。当阳离子乳化沥青与骨料表面接触时，由于所带电荷不同，产生异性相吸，两者在有水膜的情况下能使沥青微粒裹覆在骨料表面，仍能很好吸附结合。因而在阴湿、低温情况下（5℃以上）仍可以施工。但阴离子乳化沥青正好相反，它与潮湿骨料表面都带负电荷，使其产生同性相斥，沥青微粒不能很快粘附在骨料表面，必须待乳化液中水分蒸发后才行，所以遇上阴湿或低温季节时就难以施工。沥青是原油加工过程的一种产品，在常温下是黑色或黑褐色的粘稠液体或者是固体，主要含有可溶液三氯乙烯烃类衍生物，其性质和组成随来源和生成方法的不同而变化。沥青同石油一样，是复杂的有机混合物，没有固定的化学成分和物理常数，并且许多油矿物以过渡形式构成连续系列。这就给分类和鉴别带来很多困难。随着社会城市化、科技化、人性化的发展，设计一种粘结性好，防水性能优异，干燥时间短的乳化沥青材料以满足市场需求，是非常必要的。
发明内容
解决的技术问题：
本申请针对现有脲醛树脂乳化沥青干燥时间长和粘结性能差等技术问题，提供一种脲醛树脂乳化沥青。
技术方案：
一种脲醛树脂乳化沥青，由下列原料组成，以质量份数表示法为：乳化沥青100份；丙烯酸乙酯10-20份；脲醛树脂6-12份;聚乙烯醇15-20份；阳离子乳化剂1-3份；甲醛8-10份；盐酸5-8份;粉煤灰为15-35份；尿素为5-10份；十二烷基硫酸钠0.5-2份；流平剂8-10份；过硫酸铵2-5份；甲基丙烯酸甲酯20-30份。
作为本发明的一种优选技术方案：所述脲醛树脂乳化沥青，其组成成分，以质量份数表示法为：乳化沥青100份；丙烯酸乙酯15份；脲醛树脂9份;聚乙烯醇18份；阳离子乳化剂2份；甲醛9份；盐酸6份;粉煤灰为25份；尿素为7.5份；十二烷基硫酸钠1份；流平剂9份；过硫酸铵3.5份；甲基丙烯酸甲酯25份。
作为本发明的一种优选技术方案：所述流平剂采用聚醚改性聚二甲基硅氧烷。
有益效果：
本发明所述一种脲醛树脂乳化沥青采用以上技术方案与现有技术相比，具有以下技术效果：1、产品表干2-3h，实干22-24h；2、不透水性0.2-0.3MPa，硬度0.3-0.5；3、密度1.6g/cm3，剪切强度1.09-1.2MPa；4、产品抗弯强度高，表面浸润性和粘结性好，抗压强度高，可以广泛生产并不断代替现有材料。
具体实施方式
实施例1:
一种脲醛树脂乳化沥青，其组成成份以质量份数表示法为：乳化沥青100份；丙烯酸乙酯10份；脲醛树脂6份;聚乙烯醇15份；阳离子乳化剂1份；甲醛8份；盐酸5份;粉煤灰为15份；尿素为5份；十二烷基硫酸钠0.5份；聚醚改性聚二甲基硅氧烷8份；过硫酸铵2份；甲基丙烯酸甲酯20份。将沥青加入反应釜中，升温搅拌在150摄氏度脱水，加入其余组分，控制温度在190摄氏度，搅拌15h后，即得产品。
产品表干3h，实干24h；不透水性0.2MPa，硬度0.3；密度1.6g/cm3，剪切强度1.09MPa。
实施例2:
一种脲醛树脂乳化沥青，其组成成份以质量份数表示法为：乳化沥青100份；丙烯酸乙酯20份；脲醛树脂12份;聚乙烯醇20份；阳离子乳化剂3份；甲醛10份；盐酸8份;粉煤灰为35份；尿素为10份；十二烷基硫酸钠2份；聚醚改性聚二甲基硅氧烷10份；过硫酸铵5份；甲基丙烯酸甲酯30份。将沥青加入反应釜中，升温搅拌在150摄氏度脱水，加入其余组分，控制温度在190摄氏度，搅拌15h后，即得产品。
产品表干2.5h，实干23h；不透水性0.25MPa，硬度0.4；密度1.6g/cm3，剪切强度1.15MPa。
实施例3:
一种脲醛树脂乳化沥青，其组成成份以质量份数表示法为：乳化沥青100份；丙烯酸乙酯15份；脲醛树脂9份;聚乙烯醇18份；阳离子乳化剂2份；甲醛9份；盐酸6份;粉煤灰为25份；尿素为7.5份；十二烷基硫酸钠1份；聚醚改性聚二甲基硅氧烷9份；过硫酸铵3.5份；甲基丙烯酸甲酯25份。将沥青加入反应釜中，升温搅拌在150摄氏度脱水，加入其余组分，控制温度在190摄氏度，搅拌15h后，即得产品。
产品表干2h，实干22h；不透水性0.3MPa，硬度0.5；密度1.6g/cm3，剪切强度1.2MPa。
以上实施例中的所有组分均可以商业购买。
上述实施例只是用于对本发明的内容进行阐述，而不是限制，因此在与本发明的权利要求书相当的含义和范围内的任何改变，都应该认为是包括在权利要求书的范围内。
Claims (3)
1.一种脲醛树脂乳化沥青，其特征在于：其组成成份以质量份数表示法为：乳化沥青100份；丙烯酸乙酯10-20份；脲醛树脂6-12份;聚乙烯醇15-20份；阳离子乳化剂1-3份；甲醛8-10份；盐酸5-8份;粉煤灰为15-35份；尿素为5-10份；十二烷基硫酸钠0.5-2份；流平剂8-10份；过硫酸铵2-5份；甲基丙烯酸甲酯20-30份。
2.根据权利要求1所述的一种脲醛树脂乳化沥青，其特征在于：其组成成份以质量份数表示法为：乳化沥青100份；丙烯酸乙酯15份；脲醛树脂9份;聚乙烯醇18份；阳离子乳化剂2份；甲醛9份；盐酸6份;粉煤灰为25份；尿素为7.5份；十二烷基硫酸钠1份；流平剂9份；过硫酸铵3.5份；甲基丙烯酸甲酯25份。
3.根据权利要求1所述的一种脲醛树脂乳化沥青，其特征在于：所述流平剂采用聚醚改性聚二甲基硅氧烷。