CN103773014B - 一种丁苯橡胶改性沥青防水材料 - Google Patents
一种丁苯橡胶改性沥青防水材料 Download PDFInfo
- Publication number
- CN103773014B CN103773014B CN201410023422.0A CN201410023422A CN103773014B CN 103773014 B CN103773014 B CN 103773014B CN 201410023422 A CN201410023422 A CN 201410023422A CN 103773014 B CN103773014 B CN 103773014B
- Authority
- CN
- China
- Prior art keywords
- parts
- butadiene rubber
- styrene
- modified asphalt
- proof material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种丁苯橡胶改性沥青防水材料,其组成成份以质量份数表示法为:沥青100份;甲苯20-40份;石油烃15-25份;硬脂基三甲基氯化铵2-3份;丁苯橡胶8-12份;松香油酸钠皂8-10份;硫磺0.2-0.5份;烷基苯磺酸钠为1-2份;盐酸为5-8份;氢氧化钠0.1-0.3份;聚乙烯醇2-5份;四氯化碳40-50份;阳离子表面活性剂20-30份;产品固含量65-75%,表干3-4h,实干22-24h;耐阳光照射,耐90-110℃高温,100℃下5h不起泡不流淌;0.1-0.2MPa、30min不透水,粘度175Pa·s;产品耐磨强度高,耐候性好,耐寒性强,回弹率高,可以广泛生产并不断代替现有材料。
Description
技术领域
本申请属于沥青防水材料领域,尤其涉及一种丁苯橡胶改性沥青防水材料。
背景技术
现代公路和道路发生许多变化:交通流量和行驶频度急剧增长,货运车的轴重不断增加,普遍实行分车道单向行驶,要求进一步提高路面抗流动性,即高温下抗车辙的能力;提高柔性和弹性,即低温下抗开裂的能力;提高耐磨耗能力和延长使用寿命。现代建筑物普遍采用大跨度预应力屋面板,要求屋面防水材料适应大位移,更耐受严酷的高低温气候条件,耐久性更好,有自粘性,方便施工,减少维修工作量。使用环境发生的这些变化对石油沥青的性能提出了严峻的挑战。对石油沥青改性,使其适应上述苛刻使用要求,引起了人们的重视。经过数十年研究开发,已出现品种繁多的改性道路沥青、防水卷材和涂料,表现出一定的工程实用效果。但鉴于改性后的材料价格通常比普通石油沥青高2~7倍,用户对材料工程性能尚未能充分把握,改性沥青产量增长缓慢。当前改性道路沥青主要用于机场跑道、防水桥面、停车场、运动场、重交通路面、交叉路口和路面转弯处等特殊场合的铺装应用。这段时间欧洲将改性沥青应用到公路网的养护和补强,较大地推动了改性道路沥青的普遍应用。沥青是原油加工过程的一种产品,在常温下是黑色或黑褐色的粘稠液体或者是固体,它是一种棕黑色有机胶凝状物质,包括天然沥青、石油沥青、页岩沥青和煤焦油沥青等四种。主要成分是沥青质和树脂,其次有高沸点矿物油和少量的氧、硫和氯的化合物。有光泽,呈液体、半固体或固体状态,低温时质脆,粘结性和防腐性能良好。
改性沥青防水涂料运用高分子合成技术,加入了环氧树脂和树脂基团使本产品更具多功能与环保合一体,赋予新产品更具防水,防腐,防潮,防霉等功效。选用进口材料和国内优质辅料,按照国家行业标准最高等级指示生产的优质产品。列为国家建设部重点推广产品,寿命长,施工方便,长期浸泡在水里寿命在50年以上。沥青是原油加工过程的一种产品,在常温下是黑色或黑褐色的粘稠液体或者是固体,主要含有可溶液三氯乙烯烃类衍生物,其性质和组成随来源和生成方法的不同而变化。沥青同石油一样,是复杂的有机混合物,没有固定的化学成分和物理常数,并且许多油矿物以过渡形式构成连续系列。这就给分类和鉴别带来很多困难。随着社会城市化、科技化、人性化的发展,设计一种耐热,不透水的改性沥青防水材料以满足市场需求,是非常必要的。
发明内容
解决的技术问题:
本申请针对现有丁苯橡胶改性沥青防水材料耐热性能差和易透水等技术问题,提供一种丁苯橡胶改性沥青防水材料。
技术方案:
一种丁苯橡胶改性沥青防水材料,由下列原料组成,以质量份数表示法为:沥青100份;甲苯20-40份;石油烃15-25份;硬脂基三甲基氯化铵2-3份;丁苯橡胶8-12份;松香油酸钠皂8-10份;硫磺0.2-0.5份;烷基苯磺酸钠为1-2份;盐酸为5-8份;氢氧化钠0.1-0.3份;聚乙烯醇2-5份;四氯化碳40-50份;阳离子表面活性剂20-30份。
作为本发明的一种优选技术方案:所述丁苯橡胶改性沥青防水材料,其组成成分,以质量份数表示法为:沥青100份;甲苯30份;石油烃20份;硬脂基三甲基氯化铵2.5份;丁苯橡胶10份;松香油酸钠皂9份;硫磺0.4份;烷基苯磺酸钠为1.5份;盐酸为6.5份;氢氧化钠0.2份;聚乙烯醇3.5份;四氯化碳45份;阳离子表面活性剂25份。
作为本发明的一种优选技术方案:所述阳离子表面活性剂采用聚氧乙烯烷基胺。
有益效果:
本发明所述一种丁苯橡胶改性沥青防水材料采用以上技术方案与现有技术相比,具有以下技术效果:1、产品固含量65-75%,表干3-4h,实干22-24h;2、耐阳光照射,耐90-110℃高温,100℃下5h不起泡不流淌;3、0.1-0.2MPa、30min不透水,粘度175Pa·s;4、产品耐磨强度高,耐候性好,耐寒性强,回弹率高,可以广泛生产并不断代替现有材料。
具体实施方式
实施例1:
一种丁苯橡胶改性沥青防水材料,其组成成份以质量份数表示法为:沥青100份;甲苯20份;石油烃15份;硬脂基三甲基氯化铵2份;丁苯橡胶8份;松香油酸钠皂8份;硫磺0.2份;烷基苯磺酸钠为1份;盐酸为5份;氢氧化钠0.1份;聚乙烯醇2份;四氯化碳40份;聚氧乙烯烷基胺20份。将沥青加热至220摄氏度脱水至液面无气泡产生,冷却至90摄氏度,加入其余组分,搅拌1h后即成产品。
产品固含量65%,表干4h,实干24h;耐90℃高温,100℃下5h不起泡不流淌;0.1MPa、30min不透水,粘度175Pa·s。
实施例2:
一种丁苯橡胶改性沥青防水材料,其组成成份以质量份数表示法为:沥青100份;甲苯40份;石油烃25份;硬脂基三甲基氯化铵3份;丁苯橡胶12份;松香油酸钠皂10份;硫磺0.5份;烷基苯磺酸钠为2份;盐酸为8份;氢氧化钠0.3份;聚乙烯醇5份;四氯化碳50份;聚氧乙烯烷基胺30份。将沥青加热至250摄氏度脱水至液面无气泡产生,冷却至90摄氏度,加入其余组分,搅拌1h后即成产品。
产品固含量70%,表干3.5h,实干23h;耐100℃高温,100℃下5h不起泡不流淌;0.15MPa、30min不透水,粘度175Pa·s。
实施例3:
一种丁苯橡胶改性沥青防水材料,其组成成份以质量份数表示法为:沥青100份;甲苯30份;石油烃20份;硬脂基三甲基氯化铵2.5份;丁苯橡胶10份;松香油酸钠皂9份;硫磺0.4份;烷基苯磺酸钠为1.5份;盐酸为6.5份;氢氧化钠0.2份;聚乙烯醇3.5份;四氯化碳45份;聚氧乙烯烷基胺25份。将沥青加热至250摄氏度脱水至液面无气泡产生,冷却至90摄氏度,加入其余组分,搅拌1h后即成产品。
产品固含量75%,表干3h,实干22h;耐110℃高温,100℃下5h不起泡不流淌;0.2MPa、30min不透水,粘度175Pa·s。
以上实施例中的所有组分均可以商业购买。
上述实施例只是用于对本发明的内容进行阐述,而不是限制,因此在与本发明的权利要求书相当的含义和范围内的任何改变,都应该认为是包括在权利要求书的范围内。
Claims (2)
1.一种丁苯橡胶改性沥青防水材料,其特征在于:其组成成分以质量份数表示法为:沥青100份;甲苯20-40份;石油烃15-25份;硬脂基三甲基氯化铵2-3份;丁苯橡胶8-12份;松香油酸钠皂8-10份;硫磺0.2-0.5份;烷基苯磺酸钠为1-2份;盐酸为5-8份;氢氧化钠0.1-0.3份;聚乙烯醇2-5份;四氯化碳40-50份;聚氧乙烯烷基胺20-30份。
2.根据权利要求1所述的一种丁苯橡胶改性沥青防水材料,其特征在于:其组成成分以质量份数表示法为:沥青100份;甲苯30份;石油烃20份;硬脂基三甲基氯化铵2.5份;丁苯橡胶10份;松香油酸钠皂9份;硫磺0.4份;烷基苯磺酸钠为1.5份;盐酸为6.5份;氢氧化钠0.2份;聚乙烯醇3.5份;四氯化碳45份;聚氧乙烯烷基胺25份。