CN103756342A - Inorganic nanoscale flame-retardant wood plastic composite material - Google Patents

Inorganic nanoscale flame-retardant wood plastic composite material Download PDF

Info

Publication number
CN103756342A
CN103756342A CN201310667608.5A CN201310667608A CN103756342A CN 103756342 A CN103756342 A CN 103756342A CN 201310667608 A CN201310667608 A CN 201310667608A CN 103756342 A CN103756342 A CN 103756342A
Authority
CN
China
Prior art keywords
mass parts
mass
parts
composite material
plastic composite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310667608.5A
Other languages
Chinese (zh)
Inventor
黄建荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHU XINLEI WOOD FACTORY
Original Assignee
CHANGSHU XINLEI WOOD FACTORY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHU XINLEI WOOD FACTORY filed Critical CHANGSHU XINLEI WOOD FACTORY
Priority to CN201310667608.5A priority Critical patent/CN103756342A/en
Publication of CN103756342A publication Critical patent/CN103756342A/en
Pending legal-status Critical Current

Abstract

The invention discloses an inorganic nanoscale flame-retardant wood plastic composite material. Through mixing, granulation and extrusion molding, the inorganic nanoscale flame-retardant wood plastic composite material is prepared from 1-2 parts by mass of lignosulfonate, 6-8 parts by mass of organosilane, 1-5 parts by mass of a coloring agent, 7-9 parts by mass of nanoscale magnesium hydroxide, 50 parts by mass of granular recovered PE, 60 parts by mass of granular recovered PP, 80 parts by mass of wooden fibers of 40 meshes, 6-8 parts by mass of zinc stearate, 1-2 parts by mass of molybdenum trioxide, 1-2 parts by mass of zinc borate, 1-2 parts by mass of glycol monostearate, 1-5 parts by mass of an anti-aging agent, 2-3 parts by mass of maleic anhydride-modified polyethylene, 4-5 parts by mass of paraffin, 20 parts by mass of nanoscale aluminum hydroxide, 7-8 parts by mass of titanate, 1-2 parts by mass of ammonium molybdate, 2-3 parts by mass of calcium stearate, 1-5 parts by mass of an anti-oxidant and 3-5 parts by mass of an aluminate. The inorganic nanoscale flame-retardant wood plastic composite material has high flame retardation efficiency, obvious smoke inhibitive ability and balanced physical and mechanical properties.

Description

Inorganic nano flame-retardant wood-plastic composite material
Technical field
The present invention relates to inorganic nano flame-retardant wood-plastic composite material.
Background technology
Wood plastic composite in the market, it is fire-retardant, press down cigarette, physical and mechanical property etc. is not very desirable.
Summary of the invention
The object of the present invention is to provide a kind of inorganic nano flame-retardant wood-plastic composite material, its highly effective flame-retardant, obviously press down cigarette, physical and mechanical property is balanced.
For achieving the above object, technical scheme of the present invention is a kind of inorganic nano flame-retardant wood-plastic composite material of design, by following raw material, by mixing, granulation and extrusion moulding, is made:
1-2 mass parts sulfonated lignin,
6-8 mass parts organosilane,
1-5 mass parts tinting material,
7-9 mass parts nanometric magnesium hydroxide,
50 mass parts particulate state reclaim PE,
60 mass parts particulate state reclaim PP,
80 mass parts 40 object xylons,
6-8 mass parts Zinic stearas,
1-2 mass parts molybdic oxide,
1-2 mass parts zinc borate,
1-2 mass parts ethylene glycol monostearate,
1-5 mass parts antiaging agent,
The maleic anhydride modified polyethylene of 2-3 mass parts,
4-5 mass parts paraffin,
20 mass parts nano level aluminium hydroxides,
7-8 mass parts titanic acid ester,
1-2 mass parts ammonium molybdate,
2-3 mass parts calcium stearate,
1-5 mass parts oxidation inhibitor,
3-5 mass parts Aluminate.
Advantage of the present invention and beneficial effect are: a kind of inorganic nano flame-retardant wood-plastic composite material is provided, its highly effective flame-retardant, obviously press down cigarette, physical and mechanical property is balanced.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples are only for technical scheme of the present invention is more clearly described, and can not limit the scope of the invention with this.
The concrete technical scheme of implementing of the present invention is:
Embodiment 1
An inorganic nano flame-retardant wood-plastic composite material, is made by mixing, granulation and extrusion moulding by following raw material:
2 mass parts sulfonated lignin,
8 mass parts organosilanes,
5 mass parts tinting materials,
9 mass parts nanometric magnesium hydroxides,
50 mass parts particulate state reclaim PE,
60 mass parts particulate state reclaim PP,
80 mass parts 40 object xylons,
8 mass parts Zinic stearass,
2 mass parts molybdic oxides,
2 mass parts zinc borates,
2 mass parts ethylene glycol monostearates,
5 mass parts antiaging agents,
The maleic anhydride modified polyethylene of 3 mass parts,
5 mass parts paraffin,
20 mass parts nano level aluminium hydroxides,
8 mass parts titanic acid ester,
2 mass parts ammonium molybdates,
3 mass parts calcium stearates,
5 mass parts oxidation inhibitor,
5 mass parts Aluminates.
Embodiment 2
An inorganic nano flame-retardant wood-plastic composite material, is made by mixing, granulation and extrusion moulding by following raw material:
1 mass parts sulfonated lignin,
6 mass parts organosilanes,
1 mass parts tinting material,
7 mass parts nanometric magnesium hydroxides,
50 mass parts particulate state reclaim PE,
60 mass parts particulate state reclaim PP,
80 mass parts 40 object xylons,
6 mass parts Zinic stearass,
1 mass parts molybdic oxide,
1 mass parts zinc borate,
1 mass parts ethylene glycol monostearate,
1 mass parts antiaging agent,
The maleic anhydride modified polyethylene of 2 mass parts,
4 mass parts paraffin,
20 mass parts nano level aluminium hydroxides,
7 mass parts titanic acid ester,
1 mass parts ammonium molybdate,
2 mass parts calcium stearates,
1 mass parts oxidation inhibitor,
3 mass parts Aluminates.
Embodiment 3
An inorganic nano flame-retardant wood-plastic composite material, is made by mixing, granulation and extrusion moulding by following raw material:
1.2 mass parts sulfonated lignin,
6.8 mass parts organosilanes,
1.5 mass parts tinting materials,
7.9 mass parts nanometric magnesium hydroxides,
50 mass parts particulate state reclaim PE,
60 mass parts particulate state reclaim PP,
80 mass parts 40 object xylons,
6.8 mass parts Zinic stearass,
1.2 mass parts molybdic oxides,
1.2 mass parts zinc borates,
1.2 mass parts ethylene glycol monostearates,
1.5 mass parts antiaging agents,
The maleic anhydride modified polyethylene of 2.3 mass parts,
4.5 mass parts paraffin,
20 mass parts nano level aluminium hydroxides,
7.8 mass parts titanic acid ester,
1.2 mass parts ammonium molybdates,
2.3 mass parts calcium stearates,
1.5 mass parts oxidation inhibitor,
3.5 mass parts Aluminates.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, do not departing under the prerequisite of the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.

Claims (1)

1. inorganic nano flame-retardant wood-plastic composite material, is characterized in that, by following raw material, by mixing, granulation and extrusion moulding, is made:
1-2 mass parts sulfonated lignin,
6-8 mass parts organosilane,
1-5 mass parts tinting material,
7-9 mass parts nanometric magnesium hydroxide,
50 mass parts particulate state reclaim PE,
60 mass parts particulate state reclaim PP,
80 mass parts 40 object xylons,
6-8 mass parts Zinic stearas,
1-2 mass parts molybdic oxide,
1-2 mass parts zinc borate,
1-2 mass parts ethylene glycol monostearate,
1-5 mass parts antiaging agent,
The maleic anhydride modified polyethylene of 2-3 mass parts,
4-5 mass parts paraffin,
20 mass parts nano level aluminium hydroxides,
7-8 mass parts titanic acid ester,
1-2 mass parts ammonium molybdate,
2-3 mass parts calcium stearate,
1-5 mass parts oxidation inhibitor,
3-5 mass parts Aluminate.
CN201310667608.5A 2013-12-11 2013-12-11 Inorganic nanoscale flame-retardant wood plastic composite material Pending CN103756342A (en)