CN103756126A - PP (Polypropylene) plastic window sash - Google Patents

PP (Polypropylene) plastic window sash Download PDF

Info

Publication number
CN103756126A
CN103756126A CN201310595888.3A CN201310595888A CN103756126A CN 103756126 A CN103756126 A CN 103756126A CN 201310595888 A CN201310595888 A CN 201310595888A CN 103756126 A CN103756126 A CN 103756126A
Authority
CN
China
Prior art keywords
parts
coupling agent
antioxidant
polypropylene
window sash
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201310595888.3A
Other languages
Chinese (zh)
Inventor
董建中
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUJIANG DONGXIN PLASTIC PACKAGING FACTORY
Original Assignee
WUJIANG DONGXIN PLASTIC PACKAGING FACTORY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUJIANG DONGXIN PLASTIC PACKAGING FACTORY filed Critical WUJIANG DONGXIN PLASTIC PACKAGING FACTORY
Priority to CN201310595888.3A priority Critical patent/CN103756126A/en
Publication of CN103756126A publication Critical patent/CN103756126A/en
Withdrawn legal-status Critical Current

Abstract

A PP (Polypropylene) plastic window sash comprises the following components: by mass, 100 parts of PP; 1-5 parts of epoxy soybean oil; 70-80 parts of wood flour; 1-3 parts of calcium carbonate; 6-8 parts of zinc stearate; 20-30 parts of wollastonite fiber; 2-4 parts of carbon black; 0.1-0.5 part of a coupling agent; 0.5-1 part of antioxidant 1010; 0.5-1 parts of calcium stearate; 0.1-0.5 part of antioxidant DLTP (dilauryl thiodipropionate); 0.5-1 parts of absolute ethanol and 10-12 parts of maleic anhydride modified polyethylene; the product tensile elongation is 38-40MPa, the elongation is 8-10%, the relative density is 0.98-0.99, the elastic modulus is 1550-1650MPa, the cantilever beam impact strength is 58-60J / m, the bending strength is 38-50MPa, the product impact strength is 12-15KJ / m at room temperature, 10-12KJ / m at 0 DEG C, and 9.5-10KJ / m at 5 DEG C, and the PP (Polypropylene) plastic window sash can be widely used in production and continuous replacement of materials in the prior art.

Description

A kind of PP plastics sash
Technical field
The application belongs to plastic material field, relates in particular to a kind of PP plastics sash.
Background technology
Plastic door-window, the door and window that adopts U-PVC plastic material to be made.Plastic door-window has the superperformances such as wind resistance, waterproof, insulation; Plastic-steel door and window is the door and window of making of plastic-steel section bar, plastic-steel section bar is that plastics are made with shaped steel mixing section bar, the window frame section of plastic-steel heat insulation window is along with the development of Building technology and human living standard's a raising, and the structure of window is also increasingly sophisticated to meet higher thermal technology's requirement.Senior building can adopt even three layers of vacuum Low-E glass of bilayer, and two pass rubber weather strip, with the thermal and insulating performance that guarantees that it is best.The unit without frame can be made in horizontal skylight, is also referred to as dome skylight.Glass curtain wall can be considered to a kind of special window, and whole external wall has all become the window of light-permeable.
Window refers to the hole of building on wall or roof on architecture, and with so that light or air enter indoorly, the window in window modern times that can bidirectional opening is comprised of window frame, middle transparent part and movable part three parts.Window frame is responsible for supporting the main structure of forms, can be timber, metal, pottery or plastic material, and transparent part is attached on window frame, can be paper, cloth, silk or glass material.Movable part is mainly take metallic substance as main, and the place of touching at staff also may be wrapped up with thermal insulation materials such as plastics.Along with the development of social city, technicalization, hommization, design a kind of tensile strength high, Young's modulus is large, and the high PP plastics sash of elongation and cantilever beam impact strength, to meet the need of market, is very important.
Summary of the invention
the technical problem solving:
The technical problems such as the application is low for existing PP plastics sash tensile strength, and Young's modulus is little, and elongation and cantilever beam impact strength are low, provide a kind of PP plastics sash.
technical scheme:
A kind of PP plastics sash, be comprised of following raw materials according, take mass fraction representation as PP100 part; Epoxy soybean oil 1-5 part; Wood powder 70-80 part; Calcium carbonate 1-3 part; Zinic stearas 6-8 part; Wollastonite fibre 20-30 part; Carbon black 2-4 part; Coupling agent is 0.1-0.5 part; Antioxidant 1010 is 0.5-1 part; Calcium stearate 0.5-1 part; Anti-oxidant DLTP 0.1-0.5 part; Dehydrated alcohol 0.5-1 part; Maleic anhydride modified polyethylene 10-12 part.
As a preferred technical solution of the present invention: described PP plastics sash, its moiety, take mass fraction representation as: its composition take mass fraction representation as PP100 part; 3 parts of epoxy soybean oils; 75 parts of wood powders; 2 parts, calcium carbonate; 7 parts of Zinic stearass; 25 parts of wollastonite fibres; 3 parts of carbon blacks; Coupling agent is 0.4 part; Antioxidant 1010 is 0.7 part; 0.7 part of calcium stearate; 0.3 part of anti-oxidant DLTP; 0.7 part of dehydrated alcohol; 11 parts of maleic anhydride modified polyethylene.
As a preferred technical solution of the present invention: described coupling agent adopts coupling agent KR-212.
beneficial effect:
A kind of PP plastics sash of the present invention adopts above technical scheme compared with prior art, has following technique effect: 1, product tensile elongation 38-40MPa, elongation 8-10%; 2, relative density 0.98-0.99, Young's modulus 1550-1650MPa; 3, cantilever beam impact strength 58-60J/m, flexural strength 38-50MPa; 4, product shock strength 12-15KJ/m normal temperature, 0 ℃ of 10-12KJ/m ,-5 ℃ of 9.5-10 KJ/m, can the not division of history into periods of widespread production replace current material.
Embodiment
embodiment 1:
A kind of PP plastics sash, its composition is take mass fraction representation as PP100 part; 1 part of epoxy soybean oil; 70 parts of wood powders; 1 part, calcium carbonate; 6 parts of Zinic stearass; 20 parts of wollastonite fibres; 2 parts of carbon blacks; Coupling agent KR-212 is 0.1 part; Antioxidant 1010 is 0.5 part; 0.5 part of calcium stearate; 0.1 part of anti-oxidant DLTP; 0.5 part of dehydrated alcohol; 10 parts of maleic anhydride modified polyethylene.
Tensile elongation 38MPa, elongation 8%; Relative density 0.98, Young's modulus 1550MPa; Cantilever beam impact strength 58J/m, flexural strength 38MPa; Product shock strength 12KJ/m normal temperature, 0 ℃ of 10KJ/m ,-5 ℃ of 9.5KJ/m.
embodiment 2:
A kind of PP plastics sash, its composition is take mass fraction representation as PP100 part; 5 parts of epoxy soybean oils; 80 parts of wood powders; 3 parts, calcium carbonate; 8 parts of Zinic stearass; 30 parts of wollastonite fibres; 4 parts of carbon blacks; Coupling agent KR-212 is 0.5 part; Antioxidant 1010 is 1 part; 1 part of calcium stearate; 0.5 part of anti-oxidant DLTP; 1 part of dehydrated alcohol; 12 parts of maleic anhydride modified polyethylene.
Tensile elongation 39MPa, elongation 9%; Relative density 0.985, Young's modulus 1600MPa; Cantilever beam impact strength 59J/m, flexural strength 44MPa; Product shock strength 13KJ/m normal temperature, 0 ℃ of 11KJ/m ,-5 ℃ of 9.9KJ/m.
embodiment 3:
A kind of PP plastics sash, is characterized in that: its composition is take mass fraction representation as PP100 part; 3 parts of epoxy soybean oils; 75 parts of wood powders; 2 parts, calcium carbonate; 7 parts of Zinic stearass; 25 parts of wollastonite fibres; 3 parts of carbon blacks; Coupling agent KR-212 is 0.4 part; Antioxidant 1010 is 0.7 part; 0.7 part of calcium stearate; 0.3 part of anti-oxidant DLTP; 0.7 part of dehydrated alcohol; 11 parts of maleic anhydride modified polyethylene.
Tensile elongation 40MPa, elongation 10%; Relative density 0.99, Young's modulus 1650MPa; Cantilever beam impact strength 60J/m, flexural strength 50MPa; Product shock strength 15KJ/m normal temperature, 0 ℃ of 12KJ/m ,-5 ℃ of 10KJ/m.
Composition all components in above embodiment all can business be bought.
Above-described embodiment is just for content of the present invention is set forth, rather than restriction, and therefore any change in implication and the scope suitable with claims of the present invention, all should think to be included in the scope of claims.

Claims (3)

1. a PP plastics sash, is characterized in that: its composition is take mass fraction representation as PP100 part; Epoxy soybean oil 1-5 part; Wood powder 70-80 part; Calcium carbonate 1-3 part; Zinic stearas 6-8 part; Wollastonite fibre 20-30 part; Carbon black 2-4 part; Coupling agent is 0.1-0.5 part; Antioxidant 1010 is 0.5-1 part; Calcium stearate 0.5-1 part; Anti-oxidant DLTP 0.1-0.5 part; Dehydrated alcohol 0.5-1 part; Maleic anhydride modified polyethylene 10-12 part.
2. a kind of PP plastics sash according to claim 1, is characterized in that: its composition is take mass fraction representation as PP100 part; 3 parts of epoxy soybean oils; 75 parts of wood powders; 2 parts, calcium carbonate; 7 parts of Zinic stearass; 25 parts of wollastonite fibres; 3 parts of carbon blacks; Coupling agent is 0.4 part; Antioxidant 1010 is 0.7 part; 0.7 part of calcium stearate; 0.3 part of anti-oxidant DLTP; 0.7 part of dehydrated alcohol; 11 parts of maleic anhydride modified polyethylene.
3. a kind of PP plastics sash according to claim 1, is characterized in that: described coupling agent adopts coupling agent KR-212.
CN201310595888.3A 2013-11-25 2013-11-25 PP (Polypropylene) plastic window sash Withdrawn CN103756126A (en)