CN103741325B - Manufacturing method for blended yarn weaved fabric resistant to fracture - Google Patents

Manufacturing method for blended yarn weaved fabric resistant to fracture Download PDF

Info

Publication number
CN103741325B
CN103741325B CN 201310687608 CN201310687608A CN103741325B CN 103741325 B CN103741325 B CN 103741325B CN 201310687608 CN201310687608 CN 201310687608 CN 201310687608 A CN201310687608 A CN 201310687608A CN 103741325 B CN103741325 B CN 103741325B
Authority
CN
Grant status
Grant
Patent type
Prior art keywords
parts
blended
polyvinyl alcohol
cotton
preparation
Prior art date
Application number
CN 201310687608
Other languages
Chinese (zh)
Other versions
CN103741325A (en )
Inventor
袁洪兵
陈红霞
Original Assignee
葛小飞
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Grant date

Abstract

一种抗断裂的混纺面料的制备方法,包括以下步骤:(1)混纺面料为棉和聚酯纤维按照以下重量比组成:棉为30~45份、聚酯纤维为25~30份,经向为棉,纬向为聚酯纤维,通过成条、纺纱、织布而成;(2)将混纺布料烘烤后备用;(3)取乙基纤维素为3~6份,聚乙烯醇为2~4份,用70℃的乙醇水溶液进行溶解,溶解后密封;(3)将乙基纤维素和聚乙烯醇的溶液喷洒到混纺面料外表面;(4)将喷洒乙基纤维素和聚乙烯醇后的混纺面料在70℃下真空干燥;(5)干燥后保存,制备得抗断裂的混纺面料。 A method of preparing blended fabrics fracture resistance, comprising the steps of: (1) blended fabric of cotton and polyester fibers of the following composition by weight: 30 to 45 parts cotton, polyester fiber is 25 to 30 parts, warp cotton, polyester fibers as weft, into strip, spinning, weaving formed; (2) baking the blended fabric after use; (3) take the ethyl cellulose is 3 to 6 parts of polyvinyl alcohol 2 to 4 parts, carried out with aqueous ethanol of 70 deg.] C and the dissolution after sealing; (3) a solution of ethyl cellulose and polyvinyl alcohol blend is sprayed onto the outer surface of the fabric; (4) and the spray ethylcellulose polyvinyl alcohol blended fabrics after vacuum drying at 70 deg.] C; (5) after dry storage, preparation of blended fabrics have fracture resistance.

Description

一种抗断裂的混纺面料的制备方法 A method of preparing an anti-fracture blended fabrics

技术领域 FIELD

[0001] 本发明涉及一种混纺面料的制备方法,特别是涉及一种抗断裂的混纺面料的制备方法。 [0001] The present invention relates to a method for preparing a blended fabric, particularly to a method for preparing an anti-blended fabrics fracture.

背景技术 Background technique

[0002] 纺织物品种较多,混纺面料的品种也较多。 [0002] more kinds of textile articles, is greater variety of blended fabrics. 常规的混纺面料由于其多采用棉质,得到的混纺面料的断裂强度较低,一方面由于混纺面料的材料的组成的原因,另一方面是由于未经过特殊的整理工艺,因此得到的混纺面料的抗断裂强度也较低,在一些对纺织产品的抗断裂强度要求较高的领域,不能得到很好的应用。 Conventional blended fabrics because of its use more cotton, a lower breaking strength of the obtained blended fabric, on the one hand because of the composition of a material blended fabrics, on the other hand because of the special blend fabric finishing process has not elapsed, thus obtained the break strength is low, the application of some good breaking strength textile products require a higher field can not be obtained. 如一些弹性衣服、布料等。 For example, some elastic clothes, fabrics and so on. 因此,提高混纺面料的抗断裂强度,具有非常好的前景。 Therefore, to improve the fracture strength of blended fabrics having very good prospects.

发明内容 SUMMARY

[0003] 要解决的技术问题:普通的混纺面料的抗断裂、拉伸性能差的问题。 [0003] Technical Problem to be Solved: Common blended fabrics fracture resistance, tensile poor performance issues.

[0004] 技术方案:本发明公开了一种抗断裂的混纺面料的制备方法,包括以下步骤:(1) 混纺面料为棉和聚酯纤维按照以下重量比组成:棉为30〜45份、聚酯纤维为25〜30份, 经向为棉,纬向为聚酯纤维,通过成条、纺纱、织布而成;(2)将混纺布料在60°C下烘烤4〜 5h,烘烤后备用;(3)取乙基纤维素为3〜6份,聚乙烯醇为2〜4份,用70°C的10〜15份50wt%的乙醇水溶液进行溶解,溶解后密封;(3)将乙基纤维素和聚乙烯醇的溶液以喷雾形式喷洒到混纺面料外表面;(4)将喷洒乙基纤维素和聚乙烯醇后的混纺面料在70°C下真空干燥;(5)干燥后保存,制备得抗断裂的混纺面料。 [0004] Technical Solution: The present invention discloses a method for preparing a blended fabrics fracture resistance, comprising the steps of: (1) blended fabric of cotton and polyester fibers of the following composition by weight: 30~45 parts of cotton, poly parts of 25~30 ester fibers, cotton warp, weft are polyester fibers, into strip, spinning, weaving formed; (2) a blended fabric 4~ 5h baked at 60 ° C, drying after baking spare; (3) taken as 3 ~ 6 parts ethylcellulose, polyvinylalcohol parts of 2 ~ 4, 10 ~ 15 parts of 50wt% aqueous solution was 70 ° C and dissolved in ethanol, dissolved seal; (3 ) a solution of ethyl cellulose and polyvinyl alcohol is sprayed in a spray form to the outer surface of the blended fabrics; blended fabrics after (4) the ethyl cellulose and polyvinyl alcohol is sprayed and dried in vacuo at 70 ° C; (5) after drying storage, preparation of blended fabrics have fracture resistance.

[0005] 其中,所述的混纺面料经密优选为70根/10cm,纬密优选为65根/10cm。 [0005] wherein the warp density of the blended fabric is preferably 70 / 10cm, preferably weft density of 65 / 10cm. 所述的乙基纤维素优选为6份。 The ethylcellulose preferably 6 parts. 所述的聚乙烯醇优选为4份。 The polyvinyl alcohol preferably 4 parts. 50wt%的乙醇水溶液优选为15份。 50wt% aqueous solution of ethanol is preferably 15 parts.

[0006] 有益效果:本发明方法得到的混纺面料具有较高的抗断裂强度和拉伸性能,拉伸强度经向为13〜15Mpa,纬向为12Mpa〜13Mpa,断裂伸长率经向为32%〜33%,纬向为28% 〜30%。 [0006] Advantageous Effects: The method of the present invention obtained blended fabric having a high fracture resistance and tensile properties, a tensile strength of warp 13~15Mpa, weft direction 12Mpa~13Mpa, the elongation at break was 32 warp % ~33%, weft 28% ~ 30%.

具体实施方式[0007] 实施例1 DETAILED DESCRIPTION Example 1 [0007]

[0008] (1)混纺面料为棉和聚酯纤维按照以下重量比组成:棉为30kg、聚酯纤维为25kg, 经向为棉,纬向为聚酯纤维,通过成条、纺纱、织布而成,经密为70根/10cm,纬密为65根/IOcm ; (2)将混纺布料在60°C下烘烤4h,烘烤后备用;(3)取乙基纤维素为3kg,聚乙烯醇为3kg,用70°C的IOkg的50wt%的乙醇水溶液进行溶解,溶解后密封;(3)将乙基纤维素和聚乙烯醇的溶液以喷雾形式喷洒到混纺面料外表面;(4)将喷洒乙基纤维素和聚乙烯醇后的混纺面料在70°C下真空干燥;(5)干燥后保存,制备得抗断裂的混纺面料。 [0008] (1) blended fabric of cotton and polyester fibers of the following composition by weight: Cotton is 30kg, polyester fibers 25kg, cotton warp, weft are polyester fibers, into strip, spinning, weaving cloth made with a warp density of 70 / 10cm, weft density of 65 / IOcm; (2) a blended fabric 4h baked at 60 ° C, after baking standby; (3) take 3kg ethyl cellulose polyvinyl alcohol to 3kg, with 50wt% of dissolved IOkg of 70 ° C in aqueous ethanol, dissolved seal; (3) a solution of ethyl cellulose and polyvinyl alcohol blend is sprayed onto the outer surface of the fabric as a spray; after blended fabrics (4) ethylcellulose and polyvinyl alcohol is sprayed dried in vacuo at 70 ° C for; (5) after dry storage, preparation of blended fabrics have fracture resistance.

[0009] 实施例2 [0009] Example 2

[0010] (1)混纺面料为棉和聚酯纤维按照以下重量比组成:棉为40kg、聚酯纤维为30kg, 经向为棉,纬向为聚酯纤维,通过成条、纺纱、织布而成;(2)将混纺布料在60°C下烘烤5h, 烘烤后备用;(3)取乙基纤维素为4kg,聚乙烯醇为2kg,用70°C的12kg的50wt%的乙醇水溶液进行溶解,溶解后密封;(3)将乙基纤维素和聚乙烯醇的溶液以喷雾形式喷洒到混纺面料外表面;(4)将喷洒乙基纤维素和聚乙烯醇后的混纺面料在70°C下真空干燥;(5)干燥后保存,制备得抗断裂的混纺面料。 [0010] (1) blended fabric of cotton and polyester fibers of the following composition by weight: 40kg of cotton, polyester fibers 30kg, cotton warp, weft are polyester fibers, into strip, spinning, weaving cloth made; (2) a blended fabric 5h baked at 60 ° C, after baking standby; (3) taken as ethyl cellulose 4kg, polyvinyl alcohol is 2kg, 12kg of 70 ° C using 50wt% of blended after (4) the spray ethylcellulose and polyvinyl alcohol; aqueous ethanol and dissolved, after sealing was dissolved; (3) a solution of ethyl cellulose and polyvinyl alcohol blend is sprayed onto the outer surface of the fabric as a spray fabric dried in vacuo at 70 ° C for; (5) after dry storage, preparation of blended fabrics have fracture resistance.

[0011] 实施例3 [0011] Example 3

[0012] (1)混纺面料为棉和聚酯纤维按照以下重量比组成:棉为45kg、聚酯纤维为28kg, 经向为棉,纬向为聚酯纤维,通过成条、纺纱、织布而成;(2)将混纺布料在60°C下烘烤4h, 烘烤后备用;(3)取乙基纤维素为6kg,聚乙烯醇为4kg,用7(TC的15kg的50wt%的乙醇水溶液进行溶解,溶解后密封;(3)将乙基纤维素和聚乙烯醇的溶液以喷雾形式喷洒到混纺面料外表面;(4)将喷洒乙基纤维素和聚乙烯醇后的混纺面料在70°C下真空干燥;(5)干燥后保存,制备得抗断裂的混纺面料。 [0012] (1) blended fabric of cotton and polyester fibers of the following composition by weight: 45kg of cotton, polyester fibers 28kg, cotton warp, weft are polyester fibers, into strip, spinning, weaving cloth made; (2) a blended fabric 4h baked at 60 ° C, after baking standby; (3) taken as ethyl cellulose 6kg, polyvinyl alcohol is 4kg, with 7 (TC 50wt% of 15kg of blended after (4) the spray ethylcellulose and polyvinyl alcohol; aqueous ethanol and dissolved, after sealing was dissolved; (3) a solution of ethyl cellulose and polyvinyl alcohol blend is sprayed onto the outer surface of the fabric as a spray fabric dried in vacuo at 70 ° C for; (5) after dry storage, preparation of blended fabrics have fracture resistance.

[0013] 实施例1、实施例2、实施例3的混纺面料的拉伸强度和断伸长率如下表,测定方法为GB/T3923. 1-1997。 [0013] Example 1, Example 2, Example 3 of the embodiment blended fabric tensile strength and elongation at break in the following table, measurement method of GB / T3923. 1-1997.

[00141 [00141

Figure CN103741325BD00041

[0015] 混纺面料具有了较高的拉伸强度和较大的断裂伸长率,增大了抗断裂面料的应用范围。 [0015] The blended fabric with a higher tensile strength and greater elongation at break, fracture resistance increases the range of applications of the fabric.

Claims (5)

  1. 1. 一种抗断裂的混纺面料的制备方法,其特征在于包括以下步骤:(1)混纺面料为棉和聚酯纤维按照以下重量比组成:棉为30〜45份、聚酯纤维为25〜30份,经向为棉,纬向为聚酯纤维,通过成条、纺纱、织布而成;(2)将混纺布料在60°C下烘烤4〜5h,烘烤后备用;(3)取乙基纤维素为3〜6份,聚乙烯醇为2〜4份,用70°C的10〜15份50wt%的乙醇水溶液进行溶解,溶解后密封;(3)将乙基纤维素和聚乙烯醇的溶液以喷雾形式喷洒到混纺面料外表面;(4)将喷洒乙基纤维素和聚乙烯醇后的混纺面料在70°C下真空干燥;(5) 干燥后保存,制备得抗断裂的混纺面料。 Preparation blended fabrics 1. A fracture-resistant, characterized by comprising the steps of: (1) blended fabric of cotton and polyester fibers of the following composition by weight: 30~45 parts of cotton, polyester fibers 25~ 30 parts of cotton warp, weft are polyester fibers, into strip, spinning, weaving formed; (2) a blended fabric 4~5h baked at 60 ° C, after baking standby; ( 3) take 3 ~ 6 parts of ethyl cellulose, polyvinyl alcohol ~ 4 parts, 10 ~ 15 parts of 50wt% aqueous solution was 70 ° C and dissolved in ethanol, dissolved seal; (3) ethyl cellulose pigment and polyvinyl alcohol solution as a spray to spray the outer surface of blended fabrics; (4) after spraying the blended fabric ethylcellulose and polyvinyl alcohol dried under vacuum at 70 ° C; (5) after dry storage, preparation the obtained blended fabrics fracture.
  2. 2. 根据权利要求1所述的一种抗断裂的混纺面料的制备方法,其特征在于所述的混纺面料经密为70根/10cm,纬密为65根/10cm。 The method of preparation of an anti-blended fabric according to claim 1 break, wherein said blended fabric warp density 70 / 10cm, weft density of 65 / 10cm.
  3. 3. 根据权利要求1所述的一种抗断裂的混纺面料的制备方法,其特征在于所述的乙基纤维素为6份。 3. Preparation method of claim 1 anti-breakage blend fabrics according to claim, wherein said ethyl cellulose is 6 parts.
  4. 4. 根据权利要求1所述的一种抗断裂的混纺面料的制备方法,其特征在于所述的聚乙烯醇为4份。 The method of preparation of an anti-blended fabric according to claim 1 fracture, wherein the polyvinyl alcohol 4 parts.
  5. 5. 根据权利要求1所述的一种抗断裂的混纺面料的制备方法,其特征在于50wt%的乙醇水溶液为15份。 The method of preparation of an anti-blended fabric according to claim 1 break, wherein 50wt% aqueous ethanol is 15 parts.
CN 201310687608 2013-12-17 2013-12-17 Manufacturing method for blended yarn weaved fabric resistant to fracture CN103741325B (en)