CN103740096A - Light low-density ABS/PA (Acrylonitrile-Butadiene-Styrene/Polyamide) alloy material and preparation process thereof - Google Patents
Light low-density ABS/PA (Acrylonitrile-Butadiene-Styrene/Polyamide) alloy material and preparation process thereof Download PDFInfo
- Publication number
- CN103740096A CN103740096A CN201310692512.4A CN201310692512A CN103740096A CN 103740096 A CN103740096 A CN 103740096A CN 201310692512 A CN201310692512 A CN 201310692512A CN 103740096 A CN103740096 A CN 103740096A
- Authority
- CN
- China
- Prior art keywords
- alloy material
- abs
- low density
- material according
- density lightweight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a light low-density ABS/PA (Acrylonitrile-Butadiene-Styrene/Polyamide) alloy material and a preparation process of the light low-density ABS/PA alloy material, belonging to the polymer processing field. The ABS/PA alloy material is prepared from the following components in percentage by weight: 10-30 parts of acrylonitrile-butadiene-styrene grafted copolymer, 25-60 parts of nylon, 5-45 parts of hollow glass beads, 0.1-1 part of lubricating agent, 0.3-5 parts of coupling reagent, 0.1-1 part of antioxidant and 0.1-10 parts of compatilizer. The light low-density ABS/PA alloy material has good mechanical property and low density, has high application value for manufacturing light automobiles, can be used for manufacturing bumpers, instrument boards, door panels, interior trimming parts and the like, and has wide application prospect.
Description
Technical field
The present invention relates to a kind of low density lightweight ABS/PA alloy material and preparation technology thereof, be mainly used in the automotive parts such as dashboard, inside gadget, water tank face shield.
Background technology
Acrylonitrile-butadiene-phenylethene grafted copolymer (ABS) has that surface gloss is good, mechanical property is high, be easy to the features such as forming process, and there is good spraying property and electroplate performance, the ABS/PA alloy forming with nylon has the functional advantage such as resistance to solvent, wear-resisting, oil-proofness, thereby is widely used in auto industry field.At present, the effective measure that automotive light weight technology becomes and reduces motor vehicle emission, improves efficiency of combustion, are also the main directions of automobile plastic Materials.Tare is directly connected to the oil consumption of automobile unit's mileage, and the integral part of bodywork parts has become the important topic of automotive energy-saving emission-reducing now as the lightweight of the plastic component such as collision bumper, dashboard, door-plate, inside gadget.Therefore, in the situation that guaranteeing automotive part use properties, develop light weight vehicle material and to reduce complete vehicle weight, reach the effect of energy-saving and emission-reduction, create good economic and social benefit.
Summary of the invention
In order to overcome above-mentioned defect, the invention provides a kind of low density lightweight ABS/PA alloy material and preparation technology thereof, to meet the light-weighted requirement that day by day becomes of trolley part.
The present invention for the technical scheme that solves its technical problem and adopt is: a kind of low density lightweight ABS/PA alloy material, comprises the component of following mass fraction:
As a further improvement on the present invention, described ABS is vinyl cyanide, divinyl, cinnamic terpolymer, and the weight content of rubber is 18-68%.
As a further improvement on the present invention, described PA be Nylon 6, PA6B32 and PA6VOLGAMID one of them.
As a further improvement on the present invention, the tap density of described hollow glass micropearl is 0.01~1g/cm
3, size distribution is between 5 microns~20 microns.
As a further improvement on the present invention, described lubricant is calcium stearate.
As a further improvement on the present invention, described coupling agent is to contain amino silane coupling agent.
As a further improvement on the present invention, described oxidation inhibitor is primary antioxidant 1,3,5-trimethylammonium-2,4,6-tri-(3,5-di-t-butyl-4-hydroxyl benzyl) benzene and auxiliary antioxidant 2, the mixture of 2-ethylene (4,6-, bis--tert-butyl benzene) fluorine phosphorous acid.
As a further improvement on the present invention, described compatilizer is maleic anhydride graft AS.
The preparation technology who the invention provides a kind of lightweight of low density as mentioned above ABS/PA alloy material, comprises the following steps:
(1) by weight accurately taking each component, insert super mixer, mix at ambient temperature, the super mixer rotating speed using is at 650~1300 revs/min;
(2) mixture of step (1) being sent into length-to-diameter ratio is in 40:1 twin screw extruder, and the screw speed of twin screw extruder is controlled at 250~300 revs/min, and barrel zone temperature is controlled at 200 ℃~230 ℃, and the water temperature of supporting tank is between 25 ℃~50 ℃; The rotating speed of the tablets press using is at 500~800 revs/min;
(3) extrude rear cooling, pelletizing, dry, packing.
The invention has the beneficial effects as follows: ABS/PA alloy material of the present invention had both had good mechanical property, comprise stretching, bending, shock-resistant, thermotolerance, there is again good low density, the characteristic of low-shrinkage simultaneously, for automotive light weight technology, manufacture has very high using value for it, can be used for manufacturing bumper, dashboard, door-plate, inside gadget etc., have broad application prospects
Embodiment
Below in conjunction with embodiment, the present invention is elaborated, but be not limited to these embodiment.
In following examples:
ABS resin can be selected Taiwan Qi Mei company production and selling: ABS757(general purpose grade), ABS727(electroplates level), ABS777(is high temperature resistant level), the high flow stage of ABS756(), ABS765(prevent fires grade) and ABS920(transparent stage) in one or more mixture;
PA is PA6B32, or PA6VOLGAMID;
The spendable commercial product of hollow glass micropearl comprises the hollow glass micropearl of 3M company production and selling;
It is Luwax that lubricant is preferably BASF AG's product trade mark;
Coupling agent is conventional commercially available prod KH792 amino silicane coupling agent;
Oxidation inhibitor is the composite mixture of Hinered phenols antioxidant and phosphorous acid ester, specifically can use Ethanox330 and the Ethanox398 of U.S. Ya Bao company production and selling to carry out composite;
Compatilizer is maleic anhydride graft AS, is MS-NA or the MS-L2A of Japan's electrification.
Embodiment 1:
The formula of the low density lightweight ABS/PA alloy material of the present embodiment is listed in table 1:
Table 1
Component | Content % (Wt) |
ABS757 | 30 |
PA6B32 | 60 |
Hollow glass micropearl (production of 3M company) | 5 |
Lubricant L uwaX | 0.5 |
Coupling agent KH972 | 3 |
Oxidation inhibitor EthanoX330 | 0.5 |
Oxidation inhibitor EthanoX398 | 0.5 |
Compatilizer MS-NA | 0.5 |
Embodiment 2:
The formula of the low density lightweight ABS/PA alloy material of the present embodiment is listed in table 2:
Table 2
Component | Content %(wt) |
ABS757 | 15 |
PA6B32 | 25 |
Hollow glass micropearl (production of 3M company) | 45 |
Lubricant L uwax | 0.8 |
Coupling agent KH972 | 5 |
Oxidation inhibitor Ethanox330 | 0.1 |
Oxidation inhibitor Ethanox398 | 0.1 |
Compatilizer MS-NA | 9 |
Embodiment 3:
The formula of the low density lightweight ABS/PA alloy material of the present embodiment is listed in table 3:
Table 3
Component | Content %(wt) |
ABS757 | 28 |
PA6B32 | 28 |
Hollow glass micropearl (production of 3M company) | 35 |
Lubricant L uwax | 0.4 |
Coupling agent KH972 | 4 |
Oxidation inhibitor Ethanox330 | 0.3 |
Oxidation inhibitor Ethanox398 | 0.3 |
Compatilizer MS-NA | 4 |
Embodiment 4:
The formula of the low density lightweight ABS/PA alloy material of the present embodiment is listed in table 4:
Table 4
Component | Content %(wt) |
ABS757 | 11 |
PA6B32 | 54 |
Hollow glass micropearl (production of 3M company) | 30 |
Lubricant L uwax | 0.2 |
Coupling agent KH972 | 4 |
Oxidation inhibitor Ethanox330 | 0.3 |
Oxidation inhibitor Ethanox398 | 0.3 |
Compatilizer MS-NA | 0.2 |
Embodiment 5:
The formula of the low density lightweight ABS/PA alloy material of the present embodiment is listed in table 5:
Table 5
Component | Content %(wt) |
ABS757 | 25 |
PA6B32 | 45 |
Hollow glass micropearl (production of 3M company) | 25 |
Lubricant L uwax | 0.2 |
Coupling agent KH972 | 4 |
Oxidation inhibitor Ethanox330 | 0.3 |
Oxidation inhibitor Ethanox398 | 0.3 |
Compatilizer MS-NA | 0.2 |
The product making in embodiment 1-5 is tested to its performance perameter by each relevant criterion, and test result is as table 6:
Table 6
ABS/PA alloy material of the present invention had both had good mechanical property as can be seen from the table, low density and low-shrinkage are feature of the present invention places simultaneously, for automotive light weight technology, manufacture has very high using value for it, spy is applied to can be used for manufacturing bumper, dashboard, door-plate, inside gadget etc., has broad application prospects.
In the present invention, unless have other explanation, the content range of each component of composition with and preferable range between can mutually be combined to form new technical scheme.
Above-described embodiment is only preference of the present invention, is not used for limiting the present invention, and all within principle of the present invention, any modifications and variations of doing, all within protection scope of the present invention.
Claims (9)
2. low density lightweight ABS/PA alloy material according to claim 1, is characterized in that: described ABS is vinyl cyanide, divinyl, cinnamic terpolymer, and the weight content of rubber is 18-68%.
3. low density lightweight ABS/PA alloy material according to claim 1, is characterized in that: described PA be Nylon 6, PA6B32 and PA6VOLGAMID one of them.
4. low density lightweight ABS/PA alloy material according to claim 1, is characterized in that: the tap density of described hollow glass micropearl is 0.01~1g/cm
3, size distribution is between 5 microns~20 microns.
5. low density lightweight ABS/PA alloy material according to claim 1, is characterized in that: described lubricant is calcium stearate.
6. low density lightweight ABS/PA alloy material according to claim 1, is characterized in that: described coupling agent is to contain amino silane coupling agent.
7. low density lightweight ABS/PA alloy material according to claim 1, it is characterized in that: described oxidation inhibitor is primary antioxidant 1,3,5-trimethylammonium-2,4,6-tri-(3,5-di-t-butyl-4-hydroxyl benzyl) benzene and auxiliary antioxidant 2, the mixture of 2-ethylene (4,6-, bis--tert-butyl benzene) fluorine phosphorous acid.
8. low density lightweight ABS/PA alloy material according to claim 1, is characterized in that: described compatilizer is maleic anhydride graft AS.
9. a preparation technology for low density lightweight ABS/PA alloy material as described in any one in claim 1 to 8, is characterized in that, comprises the following steps:
(1) by weight accurately taking each component, insert super mixer, mix at ambient temperature, the super mixer rotating speed using is at 650~1300 revs/min;
(2) mixture of step (1) being sent into length-to-diameter ratio is in 40:1 twin screw extruder, and the screw speed of twin screw extruder is controlled at 250~300 revs/min, and barrel zone temperature is controlled at 200 ℃~230 ℃, and the water temperature of supporting tank is between 25 ℃~50 ℃; The rotating speed of the tablets press using is at 500~800 revs/min;
(3) extrude rear cooling, pelletizing, dry, packing.