The wear-resisting switch of a kind of polyformaldehyde resin
Technical field
The application belongs to plastic material field, relates in particular to the wear-resisting switch of a kind of polyformaldehyde resin.
Background technology
Derlin is strong and hard well allusion quotation has thermoplastic (property) plastics of good fatigability and chi ten stability, its electricity has low frictional coefficient and good thermotolerance to think that Derlin is similar to nylon, but its resistance to fatigue, creep resistant, hardness and water tolerance are better than nylon.Zhang is that the creep resisting ability of Derlin is not so good as polycarbonate.As previously mentioned, Derlin has excellent resistance to molten chaste tree property, does not also find the organic solvent that can dissolve Derlin with F at 70 ℃ at present; But it can be in some solvent swelling.The acid of Derlin chicken roost, alkali and oxygenant are responsive.Although c-O key is polarity. it is balanced. and polarity is more much smaller than the carbonyl in nylon, and its result causes Derlin to have relatively low water absorbability.A small amount of moisture of absorption may cause swelling and chi dimensional change, but can not cause polymkeric substance hydrolysis and degrade.The impact of moisture is more much smaller than nylon polymer.Ultraviolet raised path between farm fields can be able to cause poly-platform thing degraded, can be by adding carbon black to reduce this degraded.Multipolymer has and the similar character of homopolymer conventionally, but the mechanical property of homopolymer is slightly higher than multipolymer. and its fusing point is also higher, but its thermostability and alkali resistance are poorer than multipolymer.Derlin and the blend of poly-krypton ester elastomer improve its toughness, and these materials can have been bought on market.
Polyoxymethylene is a kind of smooth surface, and glossiness hard and fine and close material is yellowish or white, can be at life-time service in-40-100 ° C temperature range.Its wear resistance and self lubricity are also superior than most engineering plastics, have again good oil resistant, resistance to superoxide performance.Very not acidproof, not resistance to highly basic and the not radiation of resistance to solar ultraviolet; The tensile strength of polyoxymethylene reaches 70MPa, and water-absorbent is little, and dimensional stabilizing is glossy, and these performances are all good than nylon, and the resin that polyoxymethylene is highly crystalline is the most tough and tensile in thermoplastic resin.Tool heat resistanceheat resistant intensity, flexural strength, resistance to fatigue intensity is all high, wear resistance and electrical property are good, development along with social city, technicalization, hommization, design that a kind of frictional coefficient is low, polishing scratch width is little, the high polyformaldehyde resin switch fabric of compressive strength, to meet the need of market, is very important.
Summary of the invention
the technical problem solving:
The technical problems such as the application is high for existing polyformaldehyde resin switch frictional coefficient, polishing scratch width is large, and compressive strength is low, provide a kind of polyformaldehyde resin wear-resisting switch.
technical scheme:
The wear-resisting switch of polyformaldehyde resin, be comprised of following raw materials according, take mass fraction representation as POM100 part; UHMWPE2-5 part; PA66 is 2-10 part; Graphite is 1-5 part; Dimethyl silicone oil 2-6 part; Polybenzoate 10-20 part; Tetrafluoroethylene 1-4 part; Calcium stearate is 1-2 part; UV light absorber is 1-3 part; Molybdenumdisulphide 1-6 part; Zinc oxide 0.5-2 part; Barium sulfate 3-4 part; Tensio-active agent 0.1-0.5 part.
As a preferred technical solution of the present invention: the wear-resisting switch of described polyformaldehyde resin, its moiety, take mass fraction representation as POM100 part; UHMWPE2-5 part; PA66 is 2-10 part; Graphite is 1-5 part; Dimethyl silicone oil 2-6 part; Polybenzoate 10-20 part; Tetrafluoroethylene 1-4 part; Calcium stearate is 1-2 part; UV light absorber is 1-3 part; Molybdenumdisulphide 1-6 part; Zinc oxide 0.5-2 part; Barium sulfate 3-4 part; Tensio-active agent 0.1-0.5 part.
As a preferred technical solution of the present invention: described UV light absorber adopts UV-531.
beneficial effect:
The wear-resisting switch of a kind of polyformaldehyde resin of the present invention adopts above technical scheme compared with prior art, has following technique effect: 1, product frictional coefficient 0.05-0.16, polishing scratch width 2.56-3mm; 2, compressive strength 110-120MPa, flexural strength 82-90MPa; 3,500h photoaging shock strength conservation rate 100%, elongation 30-50%; 4, product is antibacterial, tensile strength is high, can the not division of history into periods of widespread production replace current material.
Embodiment
embodiment 1:
A polyformaldehyde resin wear-resisting switch, its composition be take mass fraction representation as POM100 part; UHMWPE2 part; PA66 is 2 parts; Graphite is 1 part; 2 parts of dimethyl silicone oils; 10 parts of polybenzoate; 1 part of tetrafluoroethylene; Calcium stearate is 1 part; Ultraviolet absorbent UV-531 is 1 part; 1 part of molybdenumdisulphide; 0.5 part, zinc oxide; 3 parts, barium sulfate; 0.1 part, tensio-active agent.
Product frictional coefficient 0.16, polishing scratch width 3mm; Compressive strength 110MPa, flexural strength 82MPa; 500h photoaging shock strength conservation rate 100%, elongation 30%.
embodiment 2:
A polyformaldehyde resin wear-resisting switch, its composition be take mass fraction representation as POM100 part; UHMWPE5 part; PA66 is 10 parts; Graphite is 5 parts; 6 parts of dimethyl silicone oils; 20 parts of polybenzoate; 4 parts of tetrafluoroethylene; Calcium stearate is 2 parts; Ultraviolet absorbent UV-531 is 3 parts; 6 parts of molybdenumdisulphide; 2 parts, zinc oxide; 4 parts, barium sulfate; 0.5 part, tensio-active agent.
Product frictional coefficient 0.1, polishing scratch width 2.8mm; Compressive strength 115MPa, flexural strength 86MPa; 500h photoaging shock strength conservation rate 100%, elongation 40%.
embodiment 3:
The wear-resisting switch of polyformaldehyde resin, is characterized in that: its composition be take mass fraction representation as POM100 part; UHMWPE2-5 part; PA66 is 2-10 part; Graphite is 1-5 part; Dimethyl silicone oil 2-6 part; Polybenzoate 10-20 part; Tetrafluoroethylene 1-4 part; Calcium stearate is 1-2 part; Ultraviolet absorbent UV-531 is 1-3 part; Molybdenumdisulphide 1-6 part; Zinc oxide 0.5-2 part; Barium sulfate 3-4 part; Tensio-active agent 0.1-0.5 part.
Product frictional coefficient 0.05, polishing scratch width 2.56mm; Compressive strength 120MPa, flexural strength 90MPa; 500h photoaging shock strength conservation rate 100%, elongation 50%.
Composition all components in above embodiment all can business be bought.
Above-described embodiment is just for content of the present invention is set forth, rather than restriction, therefore in the implication suitable with claims of the present invention and any change in scope, all should think to be included in the scope of claims.