CN103739267A - 一种高效净化室内空气污染的硅藻泥涂覆材料 - Google Patents

一种高效净化室内空气污染的硅藻泥涂覆材料 Download PDF

Info

Publication number
CN103739267A
CN103739267A CN201410020621.6A CN201410020621A CN103739267A CN 103739267 A CN103739267 A CN 103739267A CN 201410020621 A CN201410020621 A CN 201410020621A CN 103739267 A CN103739267 A CN 103739267A
Authority
CN
China
Prior art keywords
parts
diatom ooze
coating material
ooze coating
aggregate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410020621.6A
Other languages
English (en)
Other versions
CN103739267B (zh
Inventor
王艳
唐林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JILIN YUANYE ENVIRONMENTAL PROTECTION MATERIAL Co Ltd
Original Assignee
JILIN YUANYE ENVIRONMENTAL PROTECTION MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JILIN YUANYE ENVIRONMENTAL PROTECTION MATERIAL Co Ltd filed Critical JILIN YUANYE ENVIRONMENTAL PROTECTION MATERIAL Co Ltd
Priority to CN201410020621.6A priority Critical patent/CN103739267B/zh
Publication of CN103739267A publication Critical patent/CN103739267A/zh
Application granted granted Critical
Publication of CN103739267B publication Critical patent/CN103739267B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高效净化室内空气污染的硅藻泥涂覆材料，其中，其按照重量份包括：无机成膜材料：25份-40份；无机颜料：0.1份-0.5份；硅藻土：30份-50份；骨料：10份-40份；粉末助剂：0.2份-2份。通过多空的硅藻泥吸附室内的有害物质，尤其是甲醛等化学物质，然后通过骨料以及粉末助剂逐步降解吸附的有害物质，提高了对室内有害物质的降解率与去除率，本发明的硅藻泥涂覆材料对室内甲醛的去除率达到80％以上。

Description

一种高效净化室内空气污染的硅藻泥涂覆材料
技术领域
本发明涉及室内装饰装修材料，尤其涉及一种高效净化室内空气污染的硅藻泥涂覆材料。
背景技术
在现代的建筑设计中越来越考虑能源的有效利用，其与外界的通风换气越来越少，在这种情况下室内环境特别是刚刚装修完毕的环境，从各种装修材料中释放出来的污染物浓度很大，并且在通风换气不充分的条件下污染物不能排放到室外，大量的污染物长期滞留在室内，使得室内污染物浓度很高，严重时室内污染物浓度可超过室外的几十倍之多。为有效解决室内环境污染问题，在传统建材中添加纳米二氧化钛，使其增加光催化空气净化的功能。此方法虽然能有效降低环境中污染性气体的浓度，但必须有紫外光参与，否则有害物质去除率不高，应用于室内空气净化受到较大限制。近年来家装内墙涂料朝着高性能、环保型、功能型的方向发展，高品质环保涂料得到较大发展。新型涂覆材料硅藻泥是一种调节湿度和温度，降低空调、除味器等的使用率，节约能源的室内涂覆材料；同时其主要成分的多孔性自身能吸附降解室内装修产生的甲醛等有害污染物，创造舒适宜居的生活空间。但现有技术中的室内涂覆材料对有害物质降解率、去除率不高，用户长期居住在室内，容易损害用户健康。
因此，现有技术还有待于更进一步的改进和发展。
发明内容
鉴于上述现有技术的不足，本发明的目的在于提供一种高效净化室内空气污染的硅藻泥涂覆材料，以提高对室内有害物质的降解率与去除率。
本发明的技术方案如下：
一种高效净化室内空气污染的硅藻泥涂覆材料，其中，其按照重量份包括：
无机成膜材料：25份-40份；无机颜料：0.1份-0.5份；硅藻土：30份-50份；骨料：10份-40份；粉末助剂：0.2份-2份。
所述的硅藻泥涂覆材料，其中，所述无机成膜材料为非煅烧镁质凝胶材料，所述无机颜料为氧化铁无机颜料，所述骨料为精制硅砂。
所述的硅藻泥涂覆材料，其中，所述粉末助剂按照重量份包括：淀粉醚：0.1份-0.3份；憎水剂：0.01份-0.02份；锂蒙脱石粘土触变润滑剂：0.1-0.2。
所述的硅藻泥涂覆材料，其中，所述粉末助剂还包括聚羧酸减水剂、海藻酸钠增稠剂、柠檬酸钠缓凝剂与活性片层状的无机硅酸盐触变润滑剂的一种或者几种，按照重量份分别为：聚羧酸减水剂：0.01份-0.3份；海藻酸钠增稠剂：0.01份-0.3份；柠檬酸钠缓凝剂：0.01份-0.3份；活性片层状的无机硅酸盐触变润滑剂：0.01份-0.3份。
所述的硅藻泥涂覆材料，其中，所述硅藻泥涂覆材料还包括光催化材料，所述光催化材料按照重量份还包括：锐钛型二氧化钛：1份-3份；光敏化添加剂：0.1份-0.2份。
本发明提供的一种高效净化室内空气污染的硅藻泥涂覆材料，采用无机颜料、硅藻土、骨料与粉末助剂的技术形式，通过多孔的硅藻土吸附室内的有害物质，尤其是甲醛等化学物质，然后通过骨料以及粉末助剂逐步降解吸附的有害物质，提高了对室内有害物质的降解率与去除率，本发明的硅藻泥涂覆材料对室内甲醛的去除率达到80％以上。
具体实施方式
本发明提供了一种高效净化室内空气污染的硅藻泥涂覆材料，为使本发明的目的、技术方案及效果更加清楚、明确，以下对本发明进一步详细说明。应当理解，此处所描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。
本发明提供了一种高效净化室内空气污染的硅藻泥涂覆材料，其按照重量份包括：
无机成膜材料：25份-40份；无机颜料：0.1份-0.5份；硅藻土：30份-50份；骨料：10份-40份；粉末助剂：0.2份-2份。
并且所述无机成膜材料为非煅烧镁质凝胶材料，所述无机颜料为氧化铁无机颜料，所述骨料为精制硅砂。
在本发明的另一较佳实施例中，所述粉末助剂按照重量份包括：淀粉醚：0.1份-0.3份；憎水剂：0.01份-0.02份；锂蒙脱石粘土触变润滑剂：0.1-0.2。
更进一步的，所述粉末助剂还包括聚羧酸减水剂、海藻酸钠增稠剂、柠檬酸钠缓凝剂与活性片层状的无机硅酸盐触变润滑剂的一种或者几种，按照重量份分别为：聚羧酸减水剂：0.01份-0.3份；海藻酸钠增稠剂：0.01份-0.3份；柠檬酸钠缓凝剂：0.01份-0.3份；活性片层状的无机硅酸盐触变润滑剂：0.01份-0.3份。
为了更进一步优化本发明效果，所述硅藻泥涂覆材料还包括光催化材料，所述光催化材料按照重量份还包括：锐钛型二氧化钛：1份-3份；光敏化添加剂：0.1份-0.2份。
为更详尽的描述本发明，以下列举更为详尽的实施例。
实施例1
将300Kg的无机成膜材料、5Kg的无机颜料、300Kg的硅藻土、300Kg的骨料以及5Kg的粉末助剂充分混合搅匀形成所述硅藻泥涂覆材料，然后涂覆在300平方的房屋内墙上，关闭房屋60天，测试室内有害物质，其中甲醛的浓度为每立方米0.07毫克。其中5Kg的粉末助剂包括：3Kg的淀粉醚、0.2Kg的憎水剂与1.8Kg的锂蒙脱石粘土触变润滑剂。
实施例2
将400Kg的无机成膜材料、2Kg的无机颜料、400Kg的硅藻土、400Kg的骨料、30Kg的光催化材料以及15Kg的粉末助剂充分混合搅匀形成所述硅藻泥涂覆材料，然后涂覆在350平方的房屋内墙上，关闭房屋60天，测试室内有害物质，其中甲醛的浓度为每立方米0.05毫克。其中15Kg的粉末助剂包括：2Kg的淀粉醚、0.2Kg的憎水剂、2Kg的锂蒙脱石粘土触变润滑剂、1.8Kg聚羧酸减水剂、3Kg海藻酸钠增稠剂、3Kg柠檬酸钠缓凝剂、3Kg活性片层状的无机硅酸盐触变润滑剂；30Kg的光催化材料包括：28Kg的锐钛型二氧化钛与2Kg的光敏化添加剂。
实施例3
将260Kg的无机成膜材料、1Kg的无机颜料、300Kg的硅藻土、220Kg的骨料、15Kg的光催化材料以及6Kg的粉末助剂充分混合搅匀形成所述硅藻泥涂覆材料，然后涂覆在120平方的房屋内墙上，关闭房屋60天，测试室内有害物质，其中甲醛的浓度为每立方米0.07毫克。其中6Kg的粉末助剂包括：1Kg的淀粉醚、0.2Kg的憎水剂、2Kg的锂蒙脱石粘土触变润滑剂、1.8Kg聚羧酸减水剂、1Kg海藻酸钠增稠剂；15Kg的光催化材料包括：14Kg的锐钛型二氧化钛与1Kg的光敏化添加剂。
实施例4
将260Kg的无机成膜材料、3Kg的无机颜料、300Kg的硅藻土、200Kg的骨料、15Kg的光催化材料以及10Kg的粉末助剂充分混合搅匀形成所述硅藻泥涂覆材料，然后涂覆在100平方的房屋内墙上，关闭房屋60天，测试室内有害物质，其中甲醛的浓度为每立方米0.06毫克。其中10Kg的粉末助剂包括：2Kg的淀粉醚、0.2Kg的憎水剂、2Kg的锂蒙脱石粘土触变润滑剂、2Kg聚羧酸减水剂、1.8Kg海藻酸钠增稠剂、2Kg活性片层状的无机硅酸盐触变润滑剂；15Kg的光催化材料包括：13Kg的锐钛型二氧化钛与2Kg的光敏化添加剂。
应当理解的是，本发明的应用不限于上述的举例，对本领域普通技术人员来说，可以根据上述说明加以改进或变换，所有这些改进和变换都应属于本发明所附权利要求的保护范围。

Claims (5)

1.一种高效净化室内空气污染的硅藻泥涂覆材料，其特征在于，其按照重量份包括：
无机成膜材料：25份-40份；无机颜料：0.1份-0.5份；硅藻土：30份-50份；骨料：10份-40份；粉末助剂：0.2份-2份。
2.根据权利要求1所述的硅藻泥涂覆材料，其特征在于，所述无机成膜材料为非煅烧镁质凝胶材料，所述无机颜料为氧化铁无机颜料，所述骨料为精制硅砂。
3.根据权利要求1所述的硅藻泥涂覆材料，其特征在于，所述粉末助剂按照重量份包括：淀粉醚：0.1份-0.3份；憎水剂：0.01份-0.02份；锂蒙脱石粘土触变润滑剂：0.1-0.2。
4.根据权利要求3所述的硅藻泥涂覆材料，其特征在于，所述粉末助剂还包括聚羧酸减水剂、海藻酸钠增稠剂、柠檬酸钠缓凝剂与活性片层状的无机硅酸盐触变润滑剂的一种或者几种，按照重量份分别为：聚羧酸减水剂：0.01份-0.3份；海藻酸钠增稠剂：0.01份-0.3份；柠檬酸钠缓凝剂：0.01份-0.3份；活性片层状的无机硅酸盐触变润滑剂：0.01份-0.3份。
5.根据权利要求1所述的硅藻泥涂覆材料，其特征在于，所述硅藻泥涂覆材料还包括光催化材料，所述光催化材料按照重量份还包括：锐钛型二氧化钛：1份-3份；光敏化添加剂：0.1份-0.2份。
CN201410020621.6A 2014-01-10 2014-01-10 一种高效净化室内空气污染的硅藻泥涂覆材料 Expired - Fee Related CN103739267B (zh)