CN1037386A - Sound and thermal insulating material - Google Patents
Sound and thermal insulating material Download PDFInfo
- Publication number
- CN1037386A CN1037386A CN87108121A CN87108121A CN1037386A CN 1037386 A CN1037386 A CN 1037386A CN 87108121 A CN87108121 A CN 87108121A CN 87108121 A CN87108121 A CN 87108121A CN 1037386 A CN1037386 A CN 1037386A
- Authority
- CN
- China
- Prior art keywords
- fiber
- structural material
- carbon
- batts
- fluff
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of thermal insulation and/or sound-absorbing material include elasticity, yielding, easy elongation, non-linear, nonflammable, carbon-containing fiber flossing pad, and its reversible deflection ratio was greater than 1.2: 1, and long wealthy ratio was greater than 10: 1, and limited oxygen index is greater than 40.
Description
The present invention relates to nonflammable insulating material, this material low bulk density has the height thermal insulating properties and has good sound insulation or noise reduction character.More particularly, the relevant structural material made from carbonaceous material of the present invention, used carbonaceous material heat conductivity is low, and adiabaticity is good and/or sound absorption properties is of fine quality good, and the structural material good springiness of making easily changes shape, quality is light and nonflammable.The feature of this structural material is that also its shape and volume keep functional, is keeping its body through still stablizing after repeatedly the pressurization unloading circulates.
Excellent thermal insulating material must satisfy environmental requirement.The smog toxicity that material may cause or produce.Venting, dust and other spur also are problems to human body but also to equipment not only.
Insulated synthetic resin material commonly used is inapplicable, because these materials are inflammable and can produce a large amount of toxicity smog.As be used for launch vehicle such as commercial aircraft, spaceship, satellite etc., the smog of generation or venting are fatal to the passenger not only, but also may damage the high sensitivity instrument and pollute potosensitive surface etc. or with launch vehicle respectively operate part generation chemical reaction.If select suitable fiber, coating for use and flammable material carried out pretreatment or reprocessing to reduce discharge quantity as far as possible, then can partly control the discharging of these pollutants.Most of applications require to exist in the aircraft the least possible volatile material again as being used for aircraft.Adopted crystallization fully, crosslinked or thermoset polymerization material though these materials demonstrate suitable inert behavior to flame, but still is flammable fully.
Be used as the asbestos that comprise of different thermoinsulation materials in the prior art in many cases, glass wool, mineral cotton, polyester and polypropylene fiber, carbon element and the graphite felt pads made with narrow and shallow relatively fiber, various synthetic resin shape foamed materials such as various materials such as poultry feather and polyurethane foam are as the thermoinsulation material of many purposes.Although asbestos, carbon element and graphite felt pads, glass fibre and mineral cotton are considered to nonflammable, and other above-mentioned thermoinsulation material still is considered to flammable.The packing density of well-known some thermoinsulation material is 5.6~32kg/m
3To 32~80kg/m
3, the former is used for the thermoinsulation material that temperature is no more than 120 ℃, and the latter is used for the thermoinsulation material under the higher temperature.Even by NASA disclosed up-to-date " light-duty " thermoinsulation material 32~96kg/m is arranged also recently
3Packing density, this material is made of stupalith, wherein burned carbonaceous material.In addition, the synthetic polymeric fibers that many light-duty thermoinsulation materials are by the long filament of diameter 3~12 μ m and twist with the fingers, stretch, curl and cut off and mix to synthetic polymer short fibre up to 50 μ m more than the diameter 12 μ m and make, good sound absorption character can not be prevented fires and lack to these materials.
U.S. Patent No. 4,167,604(William E.Aldrich) suggestion adopts the voided polyester long filament that curls to make multiple layer fabric with (poultry) eider down, and the reusable heat thermosetting resin is handled and made adiabatic cotton-wool.But said fabric does not have flame-retardant nature, and sound-absorbing character is also bad.
U.S. Patent No. 4,321,154(Francois Ledru) what speak of is the high temperature thermal insulation material that is made of mineral fibre and RESEARCH OF PYROCARBON.For making light-duty thermoinsulation material, adopted the hollow pellet of stabilizer or hollow bead such as microballoon.
U.S. Patent No. 4,193,252(Shepherd, et al) has illustrated with the cellulose ester that has been knitted into fabric and has prepared partially carbonized graphite and carbon fiber.When this fabric is taken out stitches, partially carbonizedly will contain knot with fiber carbonization.Carbonization or graphite fiber also form knot, and its character is more permanent.The claimant finds, and partially carbonized cellulose ester can not keep its reversible deflection and can lose its knot under extremely low temperature or when stretching.Carbonization or graphite yarn are easily crisp, after taking out stitches, handle, even be not impossible, also be difficult.And the carbon fiber made of known artificial silk has very high moisture absorption and its heat conductivity is lower than the fiber of the higher fiber of content of graphite as making with acrylic acid composition.
According to the present invention, light-duty nonflammable structural material has been proposed, this material is made of many nonlinearity carbon fiber-containings, and used fiber has good thermal insulating properties and/or sound-absorbing character.More particularly, the relevant structural material that constitutes by many elasticity carbon containings or carbon fiber of the present invention, used fiber has sine or coil shape, its reversible deflection ratio was at least about 1.2: 1, long wealthy than (l/d) greater than 10: 1, and the limited oxygen index value is greater than 40.The packing density of this structural material is 2.4~32kg/m
3, be preferably 2.4~8kg/m for the lightweight structural material that is used to wear clothes goods etc.
3, and be preferably 8~32kg/m for the more weight structure material that is used for the smelting furnace insulation
3
The particularly relevant structural material that is made of nonflammable carbon containing of many nonlinearities or carbon filament of the present invention contains at least 65% carbon in the long filament.Concrete long filament is represented with its degree of carbonisation and/or its specific conductance, thereby can be determined its optimum purposes.
According to first kind of embodiment of the present invention, the non-linear carbon filament that contains that is used for thermal insulation of the present invention and/or sound-absorbing material is non-conductive long filament, this is partially carbonized and make with stablizing acrylic fiber or fabric or some other stable carbon fiber parent material, and its carbonization condition is suitable for making fiber to reach sine and/or coiled type configuration.Outward appearance all was the soft state of ulotrichy with organizing when the feature of this long filament also was to be made into non-woven pad or batts.It is evident that the long filament amount is big more in the structural material, the ulotrichy tissue will be many more, and elasticity is also high more.This fibrid can be used with non-carbon fiber-containing or linear carbon fiber-containing.
Here it is that 7~20 μ m are preferably the resistance of the 6k fiber tuft that the fiber of 7~12 μ m makes greater than 4 * 10 that used " non-conductive " speech means with diameter
6Ohm/cm.When precursor fiber is acrylic fiber, found that Kohlenstoffgehalt can form non-conductive fiber greater than 18.8% o'clock.
According to second kind of embodiment of the present invention, what be used for structural material of the present invention non-linearly contains carbon filament low and Kohlenstoffgehalt is less than 85% the carbon filament that contains and constitutes by specific conductance.The carbon fiber-containing acrylic fiber of handy oxidation is made, and its nitrogen content 10~35% is preferably 20~25%.Kohlenstoffgehalt is high more in the fiber, and then specific conductance is high more.The fiber that these Kohlenstoffgehalts are high still can keep its wool-like appearance when particularly most of fibers are coiled type when making pad or batts.And the coil-like fiber ratio is big more in the structural material, and then the elasticity of this structural material is high more.Kohlenstoffgehalt is high more, and the sound-absorbing character of the structural material made from long filament of the present invention is better and can more form more effective heat insulation layer under the high temperature." low conductivity " is meant that the resistance of 6k fiber tuft is 4 * 10
6~4 * 10
3Ohm/cm.
According to the third embodiment of the present invention, the non-linear carbon containing or the carbon filament Kohlenstoffgehalt that are used for thermal insulation of the present invention and/or sound-absorbing material are at least 85%.The most handy stable acrylic fiber of used fiber is made, and its nitrogen content is lower than 10%.Kohlenstoffgehalt is high more, and then the specific conductance of structural material is high more, and promptly the resistance of 6k fiber tuft is lower than 4 * 10
3Ohm/cm.These fibers can be used to replace conventional linarity or Linear Carbon fiber.And, beat all be make pad or during batts coiled type carbon containing or carbon filament more far better to the insulation effect of high heat and louder volume than the Linear Carbon fiber of same weight.With sine or linear fibre by comparison, the coil-like fiber amount is big more in the structural material, then the sound-insulating and heat-insulating effect is good more.
Fig. 1 shows the thermal insulating properties schematic representation of ulotrichy soft fiber of the present invention as the smelting furnace thermoinsulation material.
Thermal insulation of the present invention and/or sound-absorbing material by with non-linear, nonflammable, elasticity, can elongate the batts that carbon fiber-containing makes and consist of, the reversible deflection of used fiber is than greater than 1.2: 1, long wealthy than (l/d) greater than 10: 1, and the limited oxygen index value is greater than 40. This carbon fiber-containing can have sine or coil configuration or be more complicated configuration, i.e. the distorted-structure of these two kinds of configurations.
When fiber of the present invention was tested by ASTM D2863-77 method of testing, its LOI value was greater than 40. Test method is also referred to as " oxygen index (OI) " or " limited oxygen index " (LOI) test method(s). Determine that according to this method oxygen is at O2/N
2Concentration in the mixture is wherein lighted the upper end of vertical arrangement sample and is burnt away this (being exposed in the air). Wide 0.65~the 0.3cm of sample, long 7~15cm. The LOI value is calculated as follows:
LOI= ([O
2])/([O
2]+[N
2]) ×100
The LOI value of various fibers is as follows:
Polypropylene fibre 17.4
Polyethylene fibre 17.4
Styroflex 18.1
Cellulose ester 18.6
Cotton fiber 20.1
Nylon fiber 20.1
Polycarbonate 22
Rigid polyvinyl chloride fiber 40
Oxidation polyacrylonitrile fiber>40
Graphite fiber 55
These carbon fiber-containings are heat-treated with suitable stable matrix material and are made, used parent material can be enumerated for example with stablizing pan based fibers, asphaltic base (oil or coal tar oil) fiber or make with other polymeric material boundling, these materials can make nonlinear fiber or filament structure or configuration and be heat-staple.
For example, under the situation of the basic fiber of using polypropylene nitrile (PAN), be that the suitable fluidised form composition of the parent material of 4~25 μ m carries out melt-spun or wet spinning promptly can be made into used fiber with conventional nominal diameter.Fiber is formed by many continuous filament yarn boundlings, (carries out oxidation under PAN base fiber situation) then according to a conventional method and makes it stable.Oxidation-stabilized fiber tuft (or with cutting off or break the staple fiber yarn that short fibre is made) forms coil and/or sinusoidal shape by the inventive method then.Wherein fiber tuft or yarn are knitted into fabric or cloth (should be noted that and also can adopt its braiding and lopping method).The knitted fabric that to make like this or cloth are heat-treated afterwards, this in inert atmosphere in 525~750 ℃ and under loose or unstress state, carry out, heat treatment time is enough to reach the heat settability reaction that is caused by heating, wherein also carries out other crosslinked and/or interlinkage cyclization in former polymeric chain.Under 150~525 ℃ of so lower temperature, carry out in different piece in the fiber temporary transient to permanent " setting ", and 525 ℃ with higher temperature under, fiber carries out forever " setting ".Used " permanent set " speech means fiber and has elasticity, and this shows as " the reversible flexibility " of fiber, when promptly being subjected to stress fiber shape be linear basically and when eliminating stress fiber be returned to its unstress state.Certainly it should be noted that as long as heat-treat, then fiber or fiber tuft are to heat-treat under higher temperature at first, coiled type and/or sinusoidal configuration then realize in inertia or nonoxidizing atmosphere under loose or unstress state.Heat-treat under higher temperature, then the coiled type of permanent curing or sinusoidal configuration or structure just can realize in the fiber of yarn, tow or line.The nonlinear organization fiber of making.Bundle or yarn (take out stitches form by weaving cotton cloth) also can be handled to realize shredding by other method known in the art, even the fiber in weaving cotton cloth, yarn or bundle are divided into mixed and disorderly non-linear wool fluff material, wherein single fiber still keeps its coiled type or sinusoidal configuration, thereby forms quite soft velvet-like or flock.
Of the present invention velvet-like or flock can use separately or use with suitable flexibility sheet material or metal dielectric layer as required.
The fiber of stablizing by the inventive method as earlier knitting then being higher than heats under about 550 ℃ temperature and still can keep its elasticity and reversible flexibility when forever being solidified into desired structure.It should be noted that adoptable temperature can be up to 1500 ℃.But, when producing woollen goods shape fine hair, found that the fiber and/or the long filament of heat-treating interrupt minimum and the easiest control of rhegma mistake under 525~750 ℃.
Be used for the present invention's carbonaceous material adiabatic and sound-absorbing material and can be divided into three groups by the environment of its concrete purposes and the placement of its structure.
Non-linear nonflammable carbon fiber-containing in first group is non-conductive, so its fibrous batt is owing to good washability and agent of low hygroscopicity can be used for clothing or bedding etc.These fibers can with cotton fiber, wool, polyester fibre, polyolefine fiber, other synthetic or natural fibre blend such as nylon fiber and artificial fiber.
For the hygroscopicity of advance copy invention ulotrichy fine hair, be 2.4~8kg/m with density
3Batts carried out several tests.Carbon-containing fiber flossing pad sample immersion back is taken out and extracted till anhydrous oozing with hand.In the batts gross weight, in the sample hydropexis amount be 10%~<20%(weight).Under the situation of a spot of like this hydropexis in batts, this batts has still kept its thermal insulating properties.
Non-linear nonflammable carbon fiber-containing in second group can be thought partially conductive (being that specific conductance is low), and its Kohlenstoffgehalt is lower than 85%.When the stable matrix fiber is an acrylic fiber when being pan based fibers, nitrogen content is 10~35% to be preferably 20~25%.These specialty fibers are suitable for the ulotrichy fluff material also especially wishing wherein that as the launch vehicle thermoinsulation material of commercialization or military aircraft particularly this heat insulating construction texture material is light most, and are nonflammable and have an acoustical absorbance properties.These insulation system materials in the place of mainly considering public safety as in public buildings such as hospital, hotel, office building, also pressing for.The structural material made from ulotrichy fine hair is also light especially, and is also nonflammable and have an agent of low hygroscopicity, good scurf resistance and good surface appearance and handlability.
Fiber in the 3rd group has at least 85% Kohlenstoffgehalt.These fibers have extremely excellent thermal insulation and acoustical absorbance properties because of its Kohlenstoffgehalt is high.Coil structure in the ulotrichy fluff material makes insulating material have good compressibility and elasticity, and can keep its good adiabatic efficiency simultaneously.The structural material made from these fibers is particularly suitable for being used as high temperature insulating material in equipment such as smelting furnace and in each place of high heat and high noisy.
The carbon containing parent material that can be used for preparing stable fibers of the present invention and ulotrichy fine hair effectively is selected from acrylonitrile homopolymer, acrylonitrile copolymer (particularly PANOX or GRAFIL-01) and acrylonitrile terpolymer.These copolymers preferably contain 85%(mole at least) the acrylonitrile unit segment and up to the 15%(mole) one or more and vinyl benzene, methyl acrylate, methyl methacrylate, vinyl chloride, vinylidene chloride, the vinyl units segment of copolymerization such as vinylpyridine.And the acrylic acid long filament can be made of terpolymer, and acrylonitrile unit segment wherein is preferably the mole at least about 85%().
Should also be noted that can be with fiber in nonoxidizing atmosphere, and ulotrichy fluff material or batts shape material are heated to the temperature more than 1000 ℃ and make the carbon containing parent material have the conduction property that is similar to metallic conductor.Selected additional parent material such as pitch (oil or coal tar oil), polyacetylene, polyphenylene, poly-vinylidene chloride resin (SARAN, the trade mark of Dow Chemical Company) etc. can obtain this conduction property.
Best parent material is that parent material is become the mono filament fiber by known method melt-spun or wet spinning, and filament yarn or fiber tuft make.Weave cotton cloth or the looped fabric usable fibers, yarn or bundle make by a series of any methods of the prior art.In inert atmosphere, stable material is heated to more than 525 ℃ the preferably temperature more than 550 ℃ then.This carbonization looped fabric being taken apart afterwards again and carried out combing can be by the ulotrichy fluff material of batts shape form lay to make.
Ulotrichy fluff material of the present invention is can be according to the purposes of structural material different with environment to be used the organic or inorganic tackiness agent to handle and can carry out acupuncture, overlaps or adheres on the flexibility or rigidity support with the material and the technology of any routine with upward.Fluff material can be filled up or the batts form is put between isostructural side of smelting furnace or the member like this.
It should be noted that used all percentages all by weight here.
Embodiments of the invention such as following:
Nominal diameter is that the stable polyacrylonitrile (PAN) OX(of 12 μ m is produced by R.K Textiles) 3k or 6k(3000 or 6000 fibers continuously) bundle (calling OPF in the following text) flat knitting machine be made into 3~4 circles/centimetre cloth.The heat setting 6 hours under the temperature conditions of table shown in the I of the each several part of this cloth.When this cloth is taken apart, obtain elongation or reversible deflection than fiber tuft greater than 2: 1.Send into shredding in the Platts Shirley ANALYZER after the fiber tuft of the gained of taking out stitches like this being cut into each length of 5~25cm.The fiber tuft that cuts off is handled through combing and fiber is separated and formation ulotrichy fluff material, the product that promptly makes is similar to the ulotrichy material or the fluff material of strand unrest, wherein be after-combustion and have helical structure, so the spacing between the fiber is very wide and interlock gets closely because of fiber.Measure the length of staple of at every turn handling like this, it the results are shown in the following table I.
The table I
Tested number staple fiber length heat treatment needle tracking/cm fiber tuft fiber is counted bundle
(cm) (℃)
1 15 550 4 3K
2 5 550 4 3K
3 10 650 3 6K
4 10 950 3 6K
5 20 750 3 6K
6 25 950 4 6K
The most of length of staple of tested number fiber length ranges
(cm) (cm)
1 3.8~15 13~15
2 2.5~5 2.5~5
3 5.0~10 7.5~10
4 3.8~9.5 7.5~9.5
5 7.5~19 15.0~19
6 7.5~23 19.0~23
Every kind of long wealthy ratio of fiber is all greater than 10: 1, and the LOI value is all greater than 40.
Embodiment 2
Carry out a series of tests and determine of the influence of various heat treatment temperatures fiber.Important properties is the specific resistance of fiber.In order to determine this character, density 1.35~1.39g/cc and every bundle are had the various sample yarns of the oxidation-stabilized polyacrylonitrile of 3K or 6K long filament, and (PANOX is produced Heaton-Noris by R.K.Textiles, Stockport England) is knitted into the plain weave knitwear of 3~4 needle trackings/cm respectively.This is weaved cotton cloth to be placed on carry out oxygenless nitrogen in the adjustable quartz tube smelting furnace and mix and to roll.Furnace temperature was raised to about 750 ℃ from room temperature in 3 hours, raise 50 ℃ in promptly per 10~15 minutes.This material kept about 1 hour under this satisfactory temperature, afterwards smelting furnace was opened and was allowed it cool down and use the argon gas purge simultaneously.
Each sample is measured and with the specific resistance of each fiber of mean value calculation of measuring for 6 times, a kind of fiber is the fiber that downcuts from each angle of sample, and another kind is the fiber from each limit cutting-out in sample central authorities roughly.The results are shown in following table 2.
The table II
Final temperature loss of weight percentage measure than resistance logarithm
(℃) (ohms/cm)
500 - 4.489
550 33 -
600 2.010
650 34 -
750 37 -1.21
850 38 -2.02
900 42 -2.54
950 45 -2.84
1000 48 -3.026
1800 51 -3.295
The LOI value of all above-mentioned fibers is all greater than 40, and long wealthy ratio was greater than 10: 1.
Analysis result such as following table III to heat treatment of fibre are represented.
The table III
Temperature %C %N %H
(℃)
Room temperature (OPF) 58.1 19.6 3.8
450 66.8 19.4 2.2
550 69.9 18.9 1.9
650 69.7 18.1 1.6
750 73.0 17.8 1.1
Embodiment 3
Produce by R.K.Texfiltes with 3K or 6K PANOX OPF() the continous-stable endless tow is made into cloth and heat-treating until thermal distortion at a certain temperature on the Singer flat knitting machine.Then fabric is taken apart and spring shape coil-like fiber bundle is directly sent in the carding machine.Gained ulotrichy fluff material is bundled on the rotary drum and with it and is bundled to a certain degree so that can handle it at an easy rate.
The fiber of handling and make the wool fluff material under 550 ℃ is specially adapted to be used as the thermal-protective material of clothing such as storm coat, sleeping rug because of its good feel.This fluff material also can be used to various structures are carried out sound insulation and can be stoped excessive temperature.
The fiber of handling and make fluff material under the temperature that slightly raises than 550 ℃~650 ℃ is particularly suitable for being used in as insulating material launch vehicle particularly in the structure such as aircraft.
Have very high electric conductivity at 950 ℃ of fluffy goods of the ulotrichy of handling, in the fluffy goods of this ulotrichy, choose the resistance of any detection length measuring all less than 75ohms in a good distance away distance.This fiber is suitable for twining as insulation and for example coats motor or turbogenerator to absorb noise.More than result's IV that all is listed in the table below of each test.
The table IV
Tested number staple fiber length heat treatment needle tracking/cm
(cm) (℃)
1 7.5 550 4
2 10 650 3
3 15 650 3
4 20 950 3
5 25 950 3
Tested number fiber tuft fiber is counted fiber length ranges
(cm)
1 3K 2.5~7.5
2 6K 2.5~10
3 6K 2.5~13.3
4 6K 2~15.0
5 6K 2~12.5
Test shows that also the high temperature heating can make filament contraction.
Embodiment 4
3K OPF PANOX stable fibers bundle carries out knitting on the Singer flat knitting machine with the speed of 4 needle trackings/cm, fabric is placed on 950 ℃ then and heat-treats.Afterwards fabric is taken apart (fiber tuft that obtains has coil elongation or the reversible deflection ratio greater than 2: 1), it is long this fiber tuft to be cut into 7.5cm again.On the miniature carding machine of Platt, the combing of cut staple bundle grown up the again then fluffy goods of ulotrichy of 2.5~6.5cm.(resistance is less than 4 * 10 for the specific conductance height of this ulotrichy fluff material
3And all high until the 60cm specific conductance ohm/cm), in any length of being tested.
The copolymer of also available stable pitch-based fiber or polyacrylonitrile or terpolymer replace PANOX.
Embodiment 5
According to the method that is similar to embodiment 4, the part that will cut from identical knitting socks is placed under 1550 ℃ heat-treats.The fabric itself and the fiber tuft that forms of taking out stitches all have very high specific conductance.The cut staple Shu Jinhang combing that 15cm is long and make the fluffy goods of ulotrichy, the long 2.5~7.5cm of its fiber and on average long 5cm.Therefore, taking out stitches by combing becomes continuous long strand, still can make the ulotrichy fluff material with this filament yarn fabric of the heat treatment more than 1000 ℃.
Embodiment 6
To make adiabatic jacket by having carried out heat treatment below 550 ℃ until heat setting and non electrically conductive material among the embodiment 3, wherein adopt the unique filler of the fluffy goods of about 140gm as this jacket.This jacket has and is similar to the effect of heat insulation that adopts 400~700gm eider down to make thermoinsulation material gained jacket.Therefore, with (poultry) eider down by comparison, if, then only need it 1/3~1/5 can reach same insulation effect with the wool fluff material of invention.In case of necessity, this fiber also can with other synthetic fiber such as nylon fiber, artificial fiber or poly-fiber blended.
Embodiment 7
3K OPF fiber tuft is made into socks and under 525 ℃, heat-treats, take out stitches then and be cut into the length of nominal 18~19cm until heat setting.Tin Lay (shirley) the teaser shredding of staple fiber bundle, and then on the many net making machines of indigo plant (Rando Webber machine) (a kind of air web system that produces the supatex fabric batts), handle.Advancing the distance of separating between the yarn plate combing axle is that 0.3mm and dispersion are contained in the baking oven, and rotation speed of the fan is decided to be 1200rpm.A small amount of low melting point ethylene/acrylic acid copolymer fiber (by the PRI-MACOR of Dow Chemical Company, 440 resins are made) when sending into tin Lay teaser, is mixed mutually with it segment OPF fiber tuft.The gained batts is sent into hot blast stove, and temperature is decided to be 260 ℃ in the stove, and the batts transfer rate is 2m/min, thereby the time of batts in stove reaches about 1 minute.This is enough to make the ethylene/acrylic acid copolymer fusing and carbon fiber-containing illumination is bonded to batts.
Embodiment 8
According to embodiment's 7 described modes staple fiber is put into tin Lay teaser and draw back into line, put into blue many air net making machine then equally and handle, but do not add the low melting point ethylene/acrylic acid copolymer.The gained batts is wadded a quilt with cotton admittedly and is handled in the machine (Hunter Fiber Locker) enjoying special fiber, thereby and makes it reach bonding through needling process.The resulting structures material is suitable for being layered on below the synthetic fibre rug as sound-absorbing pad.
Embodiment 9
In order to determine the heat conductivity of carbon fiber itself, make two kinds of ulotrichy fluff material according to embodiment 6, each sample size is 20 * 20cm
2, thick 7.5cm.The heavily about 43gm of sample 1, the heavily about 52gm of sample 2, then it is pressed into respectively 2.9 and 2.1cm thick.Press the ASTM-C-518 method with 38 ℃ of hot plates and 10 ℃ of cold drawings and measure R value and K value.The results are shown in the following table V.
The table V
Sample compressed thickness R value K value
(cm) Hr-ft
2BIU-In/Hr-ft
2
oF/BTU °F
1 2.9 4.11 0.28
2 2.1 4.03 0.21
Embodiment 10
According to the method that is similar to embodiment 9, knitting 6K OPF tow, and after heat-treating under 550 ℃, take apart.It is long that the tow of will take out stitches and getting is cut into 15~25cm, then it sent into the tin Lay teaser of full production and also collected.The part of sample is used for the aircraft insulation.
Embodiment 11
In another test, the fluffy goods insulation of ulotrichy that the above top of heating cabinet makes with embodiment 10 in the Electric furnace.Make thick 20cm and be of a size of 139 * 133cm
2Promptly as the hassock sheet in the zone more than the furnace heats case.The packing density of fluffy goods is 2kg/m
3, its thermal insulating properties is inserted with two thermocouples and is reached 15cm in the hassock sheets and measure, and wherein one is inserted from the above 2.5cm of furnace heats device, and another root is then from the following 2.5cm insertion in fluffy goods upper end.The position of thermocouple should be able to guarantee to eliminate skin effect.Be shown among Fig. 1 by the deviation between the temperature curve of two thermocouple gained and two thermocouples, wherein show from furnace wall to its outer field temperature and reduce to about 350 ℃.This smelting furnace will be used heavily about 480kg/m in the past
3The thermal insulation of about 20.3cm carbon black just can reach same temperature.Therefore, be lower than its fluffy goods of ulotrichy of the present invention of 0.5% with packing density and can reach same insulation effect.
Embodiment 12
Measure single-engine aircraft Mooney Model 20C(by Mooney Aviation, Kerville, Texas makes) noise level, wherein make sound source with the outer backplate of making aircraft freight house outer wall.The acoustic instrument is placed on the interior place from inwall 15cm of aircraft.The results are shown in the following table VI with several frequency measurements.
The table VI
Frequency internal-internal inside
The Hz decibel
※Decibel
※ ※Decibel
※ ※ ※
250 77 59 53
500 79 63 49
1000 72 69 57
2000 86 69 51
※No soundproof material
※ ※Standard lead/vinyl/glass fibre
※ ※ ※The present invention
The original sound insulation packing layer of aircraft is by 16kg/m
3The standard fiber glass of thick 2.5cm constitute, clamp by the aluminium foil that places interior of aircraft wallboard back.The heavily about 10kg of packing layer also has thermal resistor or the R value of about 3.5-4.Filler of the present invention is listed in following table VII.Total acoustic area is about 7.5m
3End face and freight house are of a size of 5.3m
2, wherein adopt about 5kg filler sound insulation of the present invention.This filler is to downcut some batts of the present invention and make, and it contains the fiber of making under 500 ℃ with 23% polyester binder among the 3.2-3.8cm embodiment 3 and has also made non-woven batts with blue many net making machines.The batts sheet is glued on the high-grade aluminium foil so that the batts sheet gathers into folds.Again each lamination is packed in the polyester enhanced film bag, and loading onto some glass fiber meshs so that soundproof material is ventilative in the face of a side of interior of aircraft.Aircraft basal area 1.2m
2, with the sound insulation of 850gm packed aluminum fiber structural material, material therefor is put into same polyester bag for the carbon-containing fiber flossing pad of thickening latex bonding and after being stacked on the aluminium foil.Soundproof material gross weight 5.5kg wherein has the fluffy goods of 2kg actual ulotrichy of the present invention, and all the other are aluminium foil and polyester film packing.Polyester of the present invention bonding fluffy thermal resistance of products rate of ulotrichy or R value are about 7.3, and this is worth and is about twice of original used soundproof material respective value.
Typical prior art sound insulation filler is made of acoustic board, glass fibre and vinyl lead, and the heavy 25kg of inner face adds the heavy 2kg in bottom surface, gross weight 27kg.Compare with common fillers (its R value also is 6~7), the weight that adopts ulotrichy fluff material batts (being used filler of the present invention) to reduce shows that carbon containing fluff material of the present invention only is 22% of an original filler.
Acoustic on above-mentioned aircraft, aircraft flight height are 1500m, install original soundproof material around the common engine and test, and install the novel sound insulating filler then and test.The results are shown in the following table VII.Under 500-2000Hz talked situation about disturbing, the value when this aircraft is installed original soundproof material was 93.3dB.And loading onto after new packing carries out sound insulation, the value that disturbs of talking drops to the every decline 3dB of 83dB(, and sound promptly reduces half).Therefore, with regard to pilot's the sense of hearing, adopt soundproof material of the present invention sound can be reduced more than 8 times.These tests are to make under the situation that original inner facility of boarding a plane in bulk is taken a flight test.Then the new internal facility is emplaned and under the 1500m height, carry out acoustic once more.With regard to pilot's sense of hearing, talk to disturb the level that drops to 76.3dB, and when the height of 2850m even further be reduced to the level of 78.9dB.
The table VII
The standard for sound insulation sound insulation of the present invention of soundproof material originally
The structural material structural material
FG
※
Heavy (kg) 10 5.5 27
Thermal resistor (R) 488
Value (SILA) 93.5 83 86~87
(dB)
SILA=talk interference level 500+1K+2K/3
※Glass fibre
Studies show that, with the effect that sound insulation that carbon fiber-containing-aluminium foil of the present invention-carbon fiber-containing lamination filler reaches and sound-absorbing effect are far superior to used conventional glass fibre/vinyl lead stuffing in the prior art, the following low frequency environments of the plumbous specific 1000Hz of being used for of vinyl is carried out sound-absorbing in the prior art.
Embodiment 13
Be similar to embodiment 12, adopt Falcon 50 S/N 51 aircrafts to test, wherein replacing thick about 5cm and density with batts of the present invention is 9.6kg/m
3Original little white glass fiber (FG) soundproof material.The results are shown in the following table VIII.
The table VIII
Original FG
※Standard FG of the present invention
Heavy (kg) 67 58 110
Batts thickness (cm) 5 10 10
Thermal resistor (R) 7 14 14
Value (SILA) (dB) 60.5 57 61
SILA=talk interference level 1K+2K+4K/3
※Little white glass fiber
Embodiment 14
A. make with artificial screw body and contain carbon filament
300 Denier and 1650 Denier cellulose ester continuous tow yarns are knitted into diameter for roughly two ankle socks samples of about 2.5cm and be cut into 4 short sections on the flat pin circular knitting machine of single head.To go in the tube furnace with 3 slugs that 300 Denier rayon tow yarns are made in the ankle socks again, fill in 1 section at every turn.This stove all seals and with purging with nitrogen gas 15 minutes under every kind of situation.Then the first socks section furnace temperature slowly is raised to 370 ℃, lasts 1 1/2 hours; The second socks section furnace temperature is raised to 550 ℃, lasts 1 3/4 hours; And the 3rd socks section furnace temperature is raised to 1050 ℃, last 1 1/4 hours.
Each section is black in the stove, and first section of being heated to 370 ℃ is flexible fine and non-conductive basically.The yarn bundle can carefully be taken apart by hand.The tow of taking out stitches and getting becomes sinusoidal configuration and can be drawn into straight line (linearity), and can make the single fiber fracture hardly.If to this fiber tuft blowing hot-air, then this fiber tuft can lose its sinusoidal shape with hot-air syringe (electric hair drier), this explanation " setting " (sine or coil shape) is temporary transient.Observed loss of weight is very little after the heat treatment.
Be heated to that 550 ℃ second section is flexible to conduct electricity basically for medium, its specific resistance is 7 * 10
9Ohm/sq.Fiber tuft can carefully be taken apart by hand, but fragments into the short fibre of 2.5-5cm simultaneously.Broken section after fiber tuft is taken out stitches becomes sinusoidal configuration, but can not carry out reversible full elongation (reversible deflection) in non-cracking ground, think to stretch gently and when making the fiber tuft of sinusoidal configuration become near straight line (linearity) configuration, the single fiber of then taking apart also can fragment into short broken section even that is to say.
As if although the fiber of heating duration 2.5-5cm can not lose its sinusoidal configuration, the effect of blowing hot air power because of hot-air syringe can make fiber breakage.The yarn thread that is made of the short fibre bundle is easily crisp, even and carry out the slightest processing, also can not make it separately obtain the single fiber of length greater than about 1cm.
Be heated to 1050 ℃ the 3rd section even flexible lower than the preceding paragraph, wherein lost more than 75% of its original dry weight, caused fiber diameter to greatly reduce, and conduct electricity basically, its specific resistance is 70ohm/sq.Even carry out manual operations carefully, also can not after the knitwear heating, take out stitches.Fracture was short broken section when fiber was taken apart from fabric.Obtain the sinusoidal configuration fiber tuft of length less than 1.25cm after fabric taken out stitches, these fibers can not extend, and become shorter because stretching can make fiber breakage.
B. by the carbon filament that contains of the present invention
By described operation of above-mentioned A part, just replace cellulose ester and be made into the socks cover with oxidation-stabilized polyacrylonitrile-radical (PANOX) fiber tuft (3000 long filaments).
Fiber tuft is heated to 1000 ℃, and its loss of weight is 46.5%.The resistance of the fiber tuft of taking out stitches that 5cm is long is 48ohm.
After being heated to 1500 ℃, the resistance of 2.5 * 5cm section is 1.9ohm in the preceding socks of taking out stitches, and the resistance of the fiber tuft elastic force section of taking out stitches of long 2.5cm is 2.9ohm.
C.
By described operation of above-mentioned B part, two similar oxidation-stabilized polyacrylonitrile-radicals (PANOX, 600 endless tows) knitwear are heated to 372 ℃ and 564 ℃ respectively.Be heated to 564 ℃ of fabrics of heat-treating and lose wash with watercolours QiKang 1%, and the resistance of this fabric is 1 * 10
6Ohm/sq.The resistance of fiber tuft was 400K ohm/cm after knitwear were taken out stitches.
Be heated to 372 ℃ material and lose the about 31% of its original weight, its resistance is greater than about 10 * 10
12Ohm/sq.
Test shows, it is evident that when carrying out same heat treatment, and because of parent material, the character of oxidation-stabilized polyacrylonitrile and can reach the inaccessiable characteristic of cellulose ester.
Embodiment 15
Nonflammable test
By 14FAR 25.853(b) described in test method determine the nonflammable character of fiber of the present invention.Test is operation as follows:
The sample of minimum 3 2.5 * 15 * 15cm is put into the air conditioning chamber regulate before test, temperature is 70 ± 5 °F in the air conditioning chamber, and relative moisture is 50 ± 5%, and sample was placed 24 hours therein.
With each sample upright support and be exposed on this generation Turill lamp, have nominal I.D. pipe in the used stove, then its flame height is adjusted to about 3.8cm.To calibrate thermocouple pyrometer and put into flame central authorities to record flame temperature.The sample lower end is about 1.9cm place more than the lamp upper end.Flame is shifted to sample lower end center line and was kept for 12 seconds, removes then.
According to this test, material can put out certainly.Average burning length is no more than 20cm.After the burning, on average be no more than for 15 seconds, and do not find sample to ablate and drip.
Beat all is that the LOI value of fiber of the present invention is all greater than 40.
Claims (16)
1, a kind of thermal insulation and/or sound-absorbing material include elasticity, and be yielding, and easily elongation is non-linear, nonflammable, carbon-containing fiber flossing pad, and its reversible deflection ratio was greater than 1.2: 1, and long wealthy ratio was greater than 10: 1, and limited oxygen index is greater than 40.
2, according to the structural material of claim 1, wherein said fiber is non-conductive basically.
3, according to the structural material of claim 2, wherein said fiber diameter is that the stable acrylic fiber of 7-20 μ m constitutes, and the resistance of its 6K fiber tuft is greater than 4 * 10
6Ohm/cm.
4, according to the structural material of claim 3, wherein the nitrogen content of said fiber is greater than 18.8%.
5, according to claim 2,3 or 4 structural material, wherein said fiber does not have antistatic property.
6, according to the structural material of claim 1, wherein said fiber is that the stable polyacrylonitrile based polyalcohol of 10-35% is made by nitrogen content.
7, require according to aforesaid right in each structural material, wherein said batts is made of the ulotrichy fluff material, said fluff material hygroscopicity is low, is suitable for being used for making the clothing goods as thermal-protective material.
8, require according to aforesaid right in each structural material, wherein said batts is made of the ulotrichy fluff material, carbon fiber-containing has sine or coiled type configuration in the said fluff material, and wherein said batts can be with other synthetic or natural fibre or synthetic resin shape material Bond use with.
9, according to the structural material of claim 1, wherein said fiber conduction.
10, according to the structural material of claim 9, wherein said fiber by Kohlenstoffgehalt greater than 85% and nitrogen content constitute less than 10% stable acrylic fiber, and the resistance of its 6K fiber tuft is less than 4 * 10
3Ohm/cm.
11, according to the structural material of claim 10, wherein the packing density of said structural material is less than 8kg/m
3
12, according to the structural material of right , wherein said fiber by Kohlenstoffgehalt less than 85% and the diameter 7-20 μ m of nitrogen content 10-35% stablize acrylic fiber and constitute, and the resistance of its 6K fiber tuft is 4 * 10
6-4 * 10
3Ohm/cm.
13, according to the structural material of claim 12, wherein said fiber is made of the stable pan based fibers of nitrogen content 20-25%.
14, require according to aforesaid right in each structural material, wherein said fiber contains the curable polymer Bond.
15, require according to aforesaid right in each structural material, wherein the packing density of said structural material is 2.4-32kg/m
3
16, require according to aforesaid right in each structural material, wherein said carbon fiber-containing is made by the carbon containing parent material that is selected from acrylonitrile homopolymer, acrylonitrile copolymer and acrylonitrile terpolymer, and contains the mole at least about 85%(in the acrylonitrile polymer) acrylonitrile unit and up to the 15%(mole) one or more mono-vinyl unit.