CN103738024B - A kind of preparation method of antistatic polypropylene fiber fabric - Google Patents
A kind of preparation method of antistatic polypropylene fiber fabric Download PDFInfo
- Publication number
- CN103738024B CN103738024B CN201310688439.3A CN201310688439A CN103738024B CN 103738024 B CN103738024 B CN 103738024B CN 201310688439 A CN201310688439 A CN 201310688439A CN 103738024 B CN103738024 B CN 103738024B
- Authority
- CN
- China
- Prior art keywords
- fiber fabric
- polypropylene fiber
- daiflon
- preparation
- pressing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A preparation method for antistatic polypropylene fiber fabric, comprises the following steps: (1) gets woven polypropylene fiber fabric, launches to pave, stand-by; (2) get daiflon, after being heated to 60 DEG C, with scraper by two-layer up and down in polypropylene fiber fabric of daiflon blade coating, the THICKNESS CONTROL of daiflon is 0.1mm ~ 0.3mm; (3) the polypropylene fiber fabric constant-temperature hot press scribbling daiflon is carried out high-temperature laminating, pressing pressure is 5Mpa ~ 8Mpa, and pressing-in temp is 90 DEG C ~ 120 DEG C; (4) polypropylene fiber fabric be immersed in after pressing in the chitosan solution of 10wt% ~ 20wt% and soak 2h ~ 4h under room temperature, soak post-drying, bake out temperature is 80 DEG C; Anlistatig polypropylene fabric is obtained after oven dry.
Description
Technical field
The present invention relates to a kind of preparation method of polypropylene fabric, particularly relate to a kind of preparation method of antistatic polypropylene fiber fabric.
Background technology
Polypropylene fibre is conventional a kind of artificial synthetic fiber, and polypropylene fabric is also more common a kind of fabric.The antistatic property quality of fabric, has larger impact to the use of fabric.If resistance is excessive on polypropylene fabric, can electrostatic effect be produced, increase the sense of discomfort that people wear polypropylene fabric.If polypropylene fabric is applied in the middle of industrial circle, the accumulation of electrostatic, may produce electric spark, affects the production work in workshop.More serious may produce the disasters such as fire.Therefore, need the resistance as far as possible reducing fabric face, improve the safety index that it uses.
Summary of the invention
The technical problem solved: the problem of common polypropylene fabric antistatic property difference.
Technical scheme: the preparation method that the invention discloses a kind of antistatic polypropylene fiber fabric, the preparation method of antistatic polypropylene fiber fabric comprises the following steps: (1) gets woven polypropylene fiber fabric, launches to pave, stand-by; (2) get daiflon, after being heated to 60 DEG C, with scraper by two-layer up and down in polypropylene fiber fabric of daiflon blade coating, the THICKNESS CONTROL of daiflon is 0.1mm ~ 0.3mm; (3) the polypropylene fiber fabric constant-temperature hot press scribbling daiflon is carried out high-temperature laminating, pressing pressure is 5Mpa ~ 8Mpa, and pressing-in temp is 90 DEG C ~ 120 DEG C; (4) polypropylene fiber fabric be immersed in after pressing in the chitosan solution of 10wt% ~ 20wt% and soak 2h ~ 4h under room temperature, soak post-drying, bake out temperature is 80 DEG C; Anlistatig polypropylene fabric is obtained after oven dry.In preparation process, in polypropylene fiber fabric, the thickness of daiflon is preferably 0.3mm.During hot pressing, the pressing pressure of pressing machine is preferably 8Mpa.The pressing-in temp of pressing machine is preferably 120 DEG C.The chitosan solution concentration of soaking is preferably 20wt%.
Beneficial effect: the polypropylene fabric sheet resistance prepared according to preparation method of the present invention is 1 × 10
6ohm ~ 6 × 10
6ohm, has good antistatic property.
Detailed description of the invention
Embodiment 1
(1) get woven polypropylene fiber fabric, launch to pave, stand-by; (2) get daiflon, after being heated to 60 DEG C, with scraper by two-layer up and down in polypropylene fiber fabric of daiflon blade coating, the THICKNESS CONTROL of daiflon is 0.1mm; (3) the polypropylene fiber fabric constant-temperature hot press scribbling daiflon is carried out high-temperature laminating, pressing pressure is 5Mpa, and pressing-in temp is 90 DEG C; (4) polypropylene fiber fabric be immersed in after pressing in the chitosan solution of 20wt% and soak 2h under room temperature, soak post-drying, bake out temperature is 80 DEG C; Anlistatig polypropylene fabric is obtained after oven dry.
Embodiment 2
(1) get woven polypropylene fiber fabric, launch to pave, stand-by; (2) get daiflon, after being heated to 60 DEG C, with scraper by two-layer up and down in polypropylene fiber fabric of daiflon blade coating, the THICKNESS CONTROL of daiflon is 0.3mm; (3) the polypropylene fiber fabric constant-temperature hot press scribbling daiflon is carried out high-temperature laminating, pressing pressure is 7Mpa, and pressing-in temp is 110 DEG C; (4) polypropylene fiber fabric be immersed in after pressing in the chitosan solution of 10wt% and soak 4h under room temperature, soak post-drying, bake out temperature is 80 DEG C; Anlistatig polypropylene fabric is obtained after oven dry.
Embodiment 3
(1) get woven polypropylene fiber fabric, launch to pave, stand-by; (2) get daiflon, after being heated to 60 DEG C, with scraper by two-layer up and down in polypropylene fiber fabric of daiflon blade coating, the THICKNESS CONTROL of daiflon is 0.2mm; (3) the polypropylene fiber fabric constant-temperature hot press scribbling daiflon is carried out high-temperature laminating, pressing pressure is 8Mpa, and pressing-in temp is 120 DEG C; (4) polypropylene fiber fabric be immersed in after pressing in the chitosan solution of 15wt% and soak 3h under room temperature, soak post-drying, bake out temperature is 80 DEG C; Anlistatig polypropylene fabric is obtained after oven dry.
The sheet resistance of the polypropylene fabric of mensuration embodiment 1, embodiment 2, embodiment 3, the results are shown in following table.
| Embodiment 1 | Embodiment 2 | Embodiment 3 | |
| Sheet resistance (ohm) | 6×10 6 | 1×10 6 | 4×10 6 |
The polypropylene fabric that the inventive method prepares has possessed good antistatic property, has expanded the application of polypropylene fabric.
Claims (5)
1. a preparation method for antistatic polypropylene fiber fabric, is characterized in that the preparation method of antistatic polypropylene fiber fabric comprises the following steps: (1) gets woven polypropylene fiber fabric, launches to pave, stand-by; (2) get daiflon, after being heated to 60 DEG C, with scraper by two-layer up and down in polypropylene fiber fabric of daiflon blade coating, the THICKNESS CONTROL of daiflon is 0.1mm ~ 0.3mm; (3) the polypropylene fiber fabric constant-temperature hot press scribbling daiflon is carried out high-temperature laminating, pressing pressure is 5Mpa ~ 8Mpa, and pressing-in temp is 90 DEG C ~ 120 DEG C; (4) polypropylene fiber fabric be immersed in after pressing in the chitosan solution of 10wt% ~ 20wt% and soak 2h ~ 4h under room temperature, soak post-drying, bake out temperature is 80 DEG C; Anlistatig polypropylene fabric is obtained after oven dry.
2. the preparation method of a kind of antistatic polypropylene fiber fabric according to claim 1, is characterized in that the thickness of daiflon in polypropylene fiber fabric is 0.3mm.
3. the preparation method of a kind of antistatic polypropylene fiber fabric according to claim 1, is characterized in that pressing pressure is 8Mpa.
4. the preparation method of a kind of antistatic polypropylene fiber fabric according to claim 1, is characterized in that pressing-in temp is 120 DEG C.
5. the preparation method of a kind of antistatic polypropylene fiber fabric according to claim 1, is characterized in that the chitosan solution concentration of soaking is 20wt%.