The production method of sisal fiber elastic material and product
Technical field
The present invention relates to production method and the product of a kind of production method and product of string, particularly a kind of sisal fiber elastic material.
Background technology
At present, string makes bedding and has the advantages such as the feature of environmental protection is good, gas permeability is high, long service life, is therefore the product that a kind of quality is very high.Present plant-fiber mattress needs the quality of good processing technology ability improving product, and the elasticity improving material is one of them important step, and the elasticity how improving material under the prerequisite of controlling cost is a difficult problem.
Summary of the invention
Technical problem to be solved by this invention is: the production method and the product that provide a kind of sisal fiber elastic material, and it effectively can improve the elasticity of sponge, and with low cost, to overcome the deficiencies in the prior art.
The present invention is achieved in that the production method of sisal fiber elastic material, sisal hemp is made the sisal hemp filament that diameter is 0.2 ~ 0.7mm, sisal hemp weaving filaments is reticulated, again the code that the webbed sisal hemp filament of braiding is placed on every layer of string sheet is folded on face, and apply glue, then string sheet code poststack is carried out hot pressing, after hot pressing completes, obtain sisal fiber elastic material.
The thickness of every layer of string sheet is 10 ~ 30mm.
Hot pressing temperature is 80 DEG C ~ 140 DEG C, and hot pressing time is 20min ~ 50min.
Be 2 ~ 6mm by webbed for sisal hemp weaving filaments mesh diameter.
Fold between face at the code of string lamella and be provided with netted sisal hemp enhancement layer.
Owing to have employed technique scheme, compared with prior art, the filament of sisal fiber is made network structure by the present invention, sisal fiber is utilized to be placed between string lamella, make it after hot pressing, sulfuration, have good elasticity, improve the quality of product with this, and control its production cost.The inventive method is simple, and easily implement, made product quality is outstanding, and result of use is good.
Accompanying drawing explanation
Accompanying drawing 1 is structural representation of the present invention.
Detailed description of the invention
Embodiments of the invention 1: the production method of sisal fiber elastic material, sisal hemp is made the sisal hemp filament that diameter is 0.5mm, reticulated by sisal hemp weaving filaments, its mesh diameter is 4mm, makes and obtains sisal hemp enhancement layer 2, code sisal hemp enhancement layer 2 being placed on string lamella 1 is again folded between face, and apply glue, then string sheet code poststack is carried out hot pressing, hot pressing temperature is 110 DEG C, hot pressing time is 30min, obtains sisal fiber elastic material after hot pressing completes; The thickness of every layer of string sheet is 20mm.
Embodiments of the invention 2: the production method of sisal fiber elastic material, sisal hemp is made the sisal hemp filament that diameter is 0.2mm, reticulated by sisal hemp weaving filaments, its mesh diameter is 2mm, makes and obtains sisal hemp enhancement layer 2, code sisal hemp enhancement layer 2 being placed on string lamella 1 is again folded between face, and apply glue, then string sheet code poststack is carried out hot pressing, hot pressing temperature is 140 DEG C, hot pressing time is 20min, obtains sisal fiber elastic material after hot pressing completes; The thickness of every layer of string sheet is 10mm.
Embodiments of the invention 3: the production method of sisal fiber elastic material, sisal hemp is made the sisal hemp filament that diameter is 0.7mm, reticulated by sisal hemp weaving filaments, its mesh diameter is 6mm, makes and obtains sisal hemp enhancement layer 2, code sisal hemp enhancement layer 2 being placed on string lamella 1 is again folded between face, and apply glue, then string sheet code poststack is carried out hot pressing, hot pressing temperature is 80 DEG C, hot pressing time is 50min, obtains sisal fiber elastic material after hot pressing completes; The thickness of every layer of string sheet is 30mm.